CN106273719B - Polychrome transparent fabric and its manufacturing method - Google Patents
Polychrome transparent fabric and its manufacturing method Download PDFInfo
- Publication number
- CN106273719B CN106273719B CN201510303851.8A CN201510303851A CN106273719B CN 106273719 B CN106273719 B CN 106273719B CN 201510303851 A CN201510303851 A CN 201510303851A CN 106273719 B CN106273719 B CN 106273719B
- Authority
- CN
- China
- Prior art keywords
- transparent base
- color
- weight
- transparent
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention is about a kind of polychrome transparent fabric and its manufacturing method, wherein the method for the manufacture polychrome transparent fabric, including：Transparent base is provided；The presumptive area that a surface is applied in one surface of transparent base has the color film of coloured sizing material；And color film is torn off.By the method for the present invention, it can allow fabric two sides that different colours are presented, be on one side the color of coloured sizing material, another side is then the color of color film so that the color and sense of touch on fabric two sides all differ.
Description
Technical field
The application is espespecially a kind of that the saturating of different colours can be presented in area of the pattern in tow sides in relation to a kind of transparent fabric
Bright fabric.
Background technology
The application of cloth is extremely wide, and practicability of the visual effect that cloth can be presented for cloth is extremely heavy
It wants, in order to increase the diversity of cloth appearance, generally different stamp patterns, mesh can be presented in design on fabric surface using printing technology
Cloth printing technology used in preceding includes screen painting, idler wheel printing, thermal transfer and ink-jet etc..
Other than stamp pattern, color in referring now to for the application of cloth also be considerable link.Platform
Gulf announces No. 275680 patent of invention cases of I and discloses a kind of polychrome artificial leather, and it includes multilayered structures, and are existed by laser beam
One surface carves groove, so that the leather can show the color of outer layer and middle layer on a surface；Taiwan bulletin the
M472718 new patents case is also to provide a kind of cloth of multilayered structure, and multilayer stereo sense and special vision can be presented
Effect；Taiwan discloses No. 201006687 patent of invention case and proposes to print cloth by lithography technique, passes through environment protection oil
The four primaries of ink generate the color of changeableization combination, increase the vivid degree of the color change and color on cloth.
However, the technology that above-mentioned Patent Case is provided is only capable of making cloth to be presented color in front, and the reverse side of cloth is then still
For the color of cloth itself, if the identical color with cloth front is then presented as transparent person, in the reverse side of cloth in cloth sheet,
It is very dull.To increase the variability on cloth two sides, Taiwan bulletin M354520 new patents case is distinguished by two transfer papers
Pattern is transferred in the obverse and reverse of cloth, and allows cloth two sides that different patterns and/or color is presented, but the method will certainly
Increase cost and the complexity of processing procedure.
Invention content
In view of this, present invention aims at the fabric that different colours can be presented in area of the pattern in tow sides is provided,
So that the variation of fabric more diversification and more practicability.
In order to achieve the above object, the present invention provides a kind of method of manufacture polychrome transparent fabric, including：
Transparent base is provided；
The presumptive area that a surface is applied in a surface of the transparent base has the color film of coloured sizing material；And
Color film is torn off, which includes adhesive and stain；
Wherein, a surface of the transparent base is presented the shape and color of the color film, and another surface of the transparent base
The shape and color of the coloured sizing material is presented in perspective.
The present invention separately provides a kind of polychrome transparent fabric, including：
Transparent base；
Coloured compound layer is distributed in the presumptive area on one surface of transparent base；And
Color film chromatograph attaches on the coloured compound layer.
The present invention provides a kind of polychrome transparent fabric again, including：
Transparent base；
Coloured compound layer is distributed in the presumptive area on a surface of the transparent base, and the wherein presumptive area is to account for this
The 10% to 90% of one surface area of transparent base；And
Color film chromatograph attaches on the coloured compound layer；
Wherein, the shape and color of the color film chromatograph is presented in a surface of the transparent base, and the transparent base is another
Surface is flat, and the shape and color of the coloured compound layer are presented by another surface perspective；
Wherein, the shape and color of the color film chromatograph is presented in a surface of the transparent base, and the transparent base is another
The shape and color of the coloured compound layer is presented in surface perspective.
By the method for the invention, it can allow fabric two sides that color is presented, be on one side the color of sizing material, another side is then color film
Color so that the color and sense of touch on fabric two sides all differ so that the selection of fabric is more diversified, and more practicability.
Description of the drawings
Fig. 1 is the side cross sectional views of polychrome transparent fabric of the present invention.
Fig. 2 is the front view on one surface of polychrome transparent fabric of the present invention.
Fig. 3 is the front view on another surface of polychrome transparent fabric of the present invention.
Specific implementation mode
Unless in addition Wen Zhongyou illustrates, it is used in this manual (especially in following claims book)
" one ", "the" and similar term are interpreted as comprising odd number and plural form.In addition, for clarity, in schema may lavish praise on oneself each
The size in component and region, and be not painted according to actual ratio.
It should be appreciated that any numberical range cited in this description is intended to comprising all underranges included in it.Example
Such as, include time all between 50 DEG C of the minimum value of statement and 70 DEG C of the greatest measure of statement from the range of " 50 DEG C to 70 DEG C "
Range (such as from 58 DEG C to 67 DEG C, 53 DEG C to 62 DEG C, 60 DEG C or 78 DEG C) and include two numerical value, that is, include equal to or more than 50
DEG C minimum value and maximum value equal to or less than 70 DEG C range.Because revealed numberical range is continuous, therefore
They include each numerical value between minimum value and maximum value.Unless otherwise noted, the various numbers otherwise indicated in this specification
Value range is approximate value.
The present invention provides a kind of method of manufacture polychrome transparent fabric, including：
Transparent base is provided；
The presumptive area that a surface is applied in a surface of the transparent base has the color film of coloured sizing material；
Via drying and shaping；And
Color film is torn off, to form color film chromatograph relative to the surface of transparent base in the coloured sizing material.
Wherein, the transparent base refer to it is any can thoroughly color base material, can be natural fiber or staple fibre, the staple fibre
Can be any staple fibre, such as, but not limited to rayon fibers, nylon fiber, polyester fiber or acryl fiber.The base material can
For any tissue-ing such as woven, knitted fabric, non-woven fabrics or screen cloth.
Wherein, which refers to that the personage of the method for the present invention to be implemented needs institute sets itself person according to it, unlimited
In any shape, position, color or pattern.
Wherein, which stain is added in transparent gross rubber before use, so that the coloured sizing material includes small
Preferably include about 80 weight % to about 99 weights in the adhesive of about 100 weight % and the stain of greater than about 0 weight %
The adhesive of % and the stain of about 1 weight % to about 20 weight % are measured, more preferably includes about 90 weight % to about 99 weights
Measure the adhesive of % and the stain of about 1 weight % to about 10 weight %.
Wherein, which can be aqueous adhesive or solvent type adhesive.The aqueous adhesive may be, for example, polyethylene
Alcohols Aqueous Adhesives, vinyl acetate esters Aqueous Adhesives, acrylic compounds Aqueous Adhesives, polyurethanes Aqueous Adhesives,
Epoxy Aqueous Adhesives, phenolic aldehyde Aqueous Adhesives, organic silicon Aqueous Adhesives, rubber Aqueous Adhesives or other present invention
Aqueous adhesive used in technical field；The solvent type adhesive may be, for example, polyurethane (PU), acrylic acid series
Resin, isobutene rubber resin, SBR styrene butadiene rubbers resin, isoprene rubber resin, caoutchouc resin, poly- silicon
Solvent type adhesive used in oxygen resin or other technical fields.
Wherein, which is any dyestuff, pigment or the coloured powder of any tool or liquid material, has no special limit
System；Furthermore, the stain can be any inorganic or organic pigment, it is disperse dyes, acid dyes, oil-soluble dyes, straight
Dyestuff, basic dye, mordant dye, acid mordant dyes, ink etc. are connect, wherein the disperse dyes include azo-type dispersion dye
Material, ahthraquinone disperse dye, heterocyclic type disperse dyes etc.；The acid dyes includes azo-type, anthraquinone type, triaryl methane type etc.；
Particularly, the stain can for example but be not limited in triphenyl methane based dye, diphenyl methane based dye, quinoline based dye,
Thiazine based dye, thiazole based dye, xanthene based dye, flavine based dye, aulamine (Auramine) based dye, sarranine
(safranine) based dye, rose-red (phloxine) based dye, methylenum careuleum based dye etc..
Wherein, which is polyethylene terephthalate (PET), thermoplastic polyurethane (TPU), polyamine group first
Acid esters (PU) or other known materials in the technical field of the invention.
The method of the present invention still includes the cloth known by other persond having ordinary knowledge in the technical field of the present invention
Or textile finishing or procedure of processing, such as, but not limited to, concise, sizing, it is dry, fixed, soap, final finishing, coating, fitting plus
The post-processing steps such as work, spill resistant and moisture absorbing and sweat releasing processing.
Please refer to Fig. 1 to 3, polychrome transparent fabric of the present invention, including transparent base 10, coloured compound layer 20 and color film chromatograph
30, which is only arranged at the presumptive area on a surface 11 of the transparent base 10, and the wherein presumptive area is to account for
The 10% to 90% of one surface area of transparent base preferably accounts for the 25% to 75% of one surface area of transparent base,
The 35% to 65% of one surface area of transparent base is more preferably accounted for, which is set to the coloured compound layer 20
On, wherein the shape and color of the color film chromatograph 30 is presented in a surface 11 of the transparent base 10, and it is transparent to protrude from this slightly
One surface 11 of base material 10, and another surface 12 of the transparent base 10 is then flat, and being presented by another surface perspective should
The shape and color of coloured compound layer 20.Thereby, polychrome transparent fabric of the present invention is in transparent base tool Coloured film chromatograph 30
One surface 11 is presented color film and remaines in the color on coloured compound layer 20, and the face of the coloured compound layer 20 is then presented in another side 12
Color so that fabric two sides shows different colours and sense of touch, and increases the aesthetics and practicability of fabric 30.
Following instance illustrates the state sample implementation of the present invention, and illustrates the technical characteristic of the present invention, is not used for limiting
Make the protection category of the present invention.Any skilled person can the arrangement of unlabored change or equality arrangement belong to the present invention
The range advocated, the scope of the present invention should be subject to appended claims.
Example：
It provides an engraved wheel cylinder of tool, and in being applied with coloring agent material on the wheel cylinder, then the wheel cylinder is made to roll across color film, so that
The presumptive area obtained on the color film has the coloured sizing material, and then the color film with coloring agent material is transferred on transparent cloth, with
The transparent color film of the cloth attachment with coloring agent material is enabled, drying machine or other roasting plants give drying and shaping, remove later
The color film, you can obtain polychrome transparent fabric of the present invention.
Following table provides the example of the coloured sizing material used in the present invention.
Table 1
Claims (10)
1. a kind of method of manufacture polychrome transparent fabric, including：
Transparent base is provided；
The presumptive area that a surface is applied in a surface of the transparent base has the color film of coloured sizing material；And color film is torn
It goes, which includes adhesive and stain；
Wherein, a surface of the transparent base is presented the shape and color of the color film, and another surface perspective of the transparent base
The shape and color of the coloured sizing material is presented.
2. according to the method described in claim 1, wherein the transparent base be selected from be made of woven fabric, looped fabric and non-woven fabrics
Group.
3. according to the method described in claim 1, wherein the transparent base is selected from by rayon fibers, nylon fiber, polyester fiber
And the group that acryl fiber is formed.
4. according to the method in any one of claims 1 to 3, wherein stain is added before use for the coloured sizing material
Person formed in transparent gross rubber.
5. according to the method described in claim 4, wherein the coloured sizing material includes to be less than the adhesive of 100 weight % and be more than
The stain of 0 weight %.
6. according to the method described in claim 5, wherein the coloured sizing material include 80 weight % to 99 weight % adhesive with
And 1 weight % to 20 weight % stain.
7. a kind of polychrome transparent fabric, including：
Transparent base；
Coloured compound layer is distributed in the presumptive area on one surface of transparent base；And
Color film chromatograph attaches on the coloured compound layer；
Wherein, a surface of the transparent base is presented the shape and color of the color film chromatograph, and another surface of the transparent base
The shape and color of the coloured compound layer is presented in perspective.
8. polychrome transparent fabric according to claim 7, the wherein coloured compound layer include the viscose less than 100 weight %
Agent and stain more than 0 weight %.
9. polychrome transparent fabric according to claim 8, the wherein coloured sizing material include 80 weight % to 99 weight %'s
The stain of adhesive and 1 weight % to 20 weight %.
10. the polychrome transparent fabric according to any one of claim 7 to 9, the wherein transparent base be selected from by woven fabric,
The group that looped fabric and non-woven fabrics are formed；And the transparent base is selected from by rayon fibers, nylon fiber, polyester fiber and acryl
The group that fiber is formed.