CN106273719A - Polychrome transparent fabric and manufacture method thereof - Google Patents
Polychrome transparent fabric and manufacture method thereof Download PDFInfo
- Publication number
- CN106273719A CN106273719A CN201510303851.8A CN201510303851A CN106273719A CN 106273719 A CN106273719 A CN 106273719A CN 201510303851 A CN201510303851 A CN 201510303851A CN 106273719 A CN106273719 A CN 106273719A
- Authority
- CN
- China
- Prior art keywords
- fabric
- weight
- transparent
- transparent base
- coloured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention about a kind of polychrome transparent fabric and manufacture method thereof, the method for wherein said manufacture polychrome transparent fabric, including: transparent base is provided；The presumptive area being applied to a surface in this transparent base one surface has the color film of coloured sizing material；And color film is torn off.By the inventive method, fabric two sides can be allowed to present different colours, one side is the color of coloured sizing material, and another side is then the color of color film so that color and the sense of touch on fabric two sides all differ.
Description
Technical field
The relevant a kind of transparent fabric of the application, a kind of can present the saturating of different colours at tow sides in area of the pattern
Bright fabric.
Background technology
The application of cloth is extremely wide, and the practicality that the visual effect that cloth can present is for cloth is the heaviest
Want, in order to increase the multiformity of cloth outward appearance, printing technology typically can be used to present different stamp figures in design on fabric surface
Sample, the cloth printing technology used at present includes screen painting, roller printing, thermal transfer and ink-jet etc..
In addition to stamp pattern, color in referring now to being also considerable link for the application of cloth.Platform
Gulf is announced I275680 patent of invention case and is disclosed a kind of polychrome artificial leather, and it comprises multiple structure, and passes through laser
Shu Yi surface carves groove, so that this leather can represent the color in outer layer and intermediate layer on a surface；Taiwan is public
Accusing M472718 new patent case and be also to provide the cloth of a kind of multiple structure, it can present multilayer stereo sense and spy
Different visual effect；Taiwan discloses No. 201006687 patent of invention case and proposes to print cloth by lithography technique,
Produced the color of many change combinations by the four primaries of environment-friendly ink, increase the fresh of the color change on cloth and color
Brightness.
But, the technology that above-mentioned Patent Case is provided is only capable of making cloth present color in front, and the reverse side of cloth is the most still
For the color of cloth itself, if cloth is originally as transparent person, then the reverse side at cloth then presents identical with cloth front
Color is the most dull.For increasing the variability on cloth two sides, M354520 new patent case is announced by two in Taiwan
Transfer paper transfers pattern at the obverse and reverse of cloth respectively, and allows cloth two sides present different patterns and/or color,
But the method will certainly increase the complexity of cost and processing procedure.
Summary of the invention
In view of this, offer is provided and can present the fabric of different colours at tow sides in area of the pattern,
So that the change of fabric more diversification and more practicality.
For reaching above-mentioned purpose, the present invention provides a kind of method manufacturing polychrome transparent fabric, including:
Transparent base is provided；
The presumptive area being applied to a surface in a surface of this transparent base has the color film of coloured sizing material；And
Color film is torn off.
The present invention separately provides a kind of polychrome transparent fabric, including:
Transparent base；
Coloured compound layer, it is distributed in the presumptive area on this transparent base one surface；And
Color film chromatograph, it attaches on this coloured compound layer.
The present invention provides again a kind of polychrome transparent fabric, including:
Transparent base；
Coloured compound layer, it is distributed in the presumptive area on a surface of this transparent base, and wherein this presumptive area is to account for this
The 10% to 90% of transparent base one surface area；And
Color film chromatograph, it attaches on this coloured compound layer；
Wherein, a surface of this transparent base presents shape and the color of this color film chromatograph, and another of this transparent base
Surface is smooth, and is presented shape and the color of this coloured compound layer by this another surface perspective.
By the inventive method, fabric two sides can be allowed to present color, one side is the color of sizing material, and another side is then color film
Color so that color and the sense of touch on fabric two sides all differ so that the selection of fabric is more diversified, and the most real
The property used.
Accompanying drawing explanation
Fig. 1 is the side cross sectional views of polychrome transparent fabric of the present invention.
Fig. 2 is the front view on polychrome transparent fabric one surface of the present invention.
Fig. 3 is the front view on another surface of polychrome transparent fabric of the present invention.
Detailed description of the invention
Unless Wen Zhongyou additionally illustrates, in this specification (especially in following claims book), used
" one ", " being somebody's turn to do " and similar term are interpreted as comprising odd number and plural form.Separately, for clarity, can in graphic
The size in each assembly and region can be lavished praise on oneself, and do not illustrate according to actual ratio.
Should be appreciated that all underranges that any numerical range cited in this description is included in being intended to comprise it.Example
As, institute between the minimum value 50 DEG C of statement and the greatest measure 70 DEG C of statement is included from the scope of " 50 DEG C to 70 DEG C "
Some underranges (as from 58 DEG C to 67 DEG C, 53 DEG C to 62 DEG C, 60 DEG C or 78 DEG C) and comprise this two numerical value, that is comprise
Minima equal to or more than 50 DEG C and the scope of the maximum equal to or less than 70 DEG C.Because disclosed numerical value model
Enclosing is continuous print, and therefore they comprise each numerical value between minima and maximum.Unless otherwise noted, otherwise this
The various numerical rangies indicated in description are outline values.
The present invention provides a kind of method manufacturing polychrome transparent fabric, including:
Transparent base is provided；
The presumptive area being applied to a surface in a surface of this transparent base has the color film of coloured sizing material；
Via drying and shaping；And
Color film is torn off, to form color film chromatograph at this coloured sizing material relative to the surface of transparent base.
Wherein, this transparent base refer to any can the base material of color thoroughly, can be natural fiber or staple fibre, this artificial fibre
Dimension can be any staple fibre, such as but not limited to rayon fibers, nylon fiber, polyester fiber or acryl fiber.
This base material can be any tissue-ings such as woven, knitted fabric, adhesive-bonded fabric or screen cloth.
Wherein, this presumptive area refers to that the personage of the inventive method to be implemented needs institute sets itself person according to it, and it does not limits
In any shape, position, color or pattern.
Wherein, stain, before using, is added in transparent gross rubber, so that this coloured sizing material comprises by this coloured sizing material
The adhesive of less than about 100 weight % and the stain of greater than about 0 weight %, preferably comprise about 80 weight % to about 99
The adhesive of weight % and the stain of about 1 weight % to about 20 weight %, more preferably comprise about 90 weight % to about 99
The adhesive of weight % and the stain of about 1 weight % to about 10 weight %.
Wherein, this adhesive can be aqueous adhesive or solvent-borne type adhesive.This aqueous adhesive can for example, polyethylene
Alcohols Aqueous Adhesives, vinyl acetate esters Aqueous Adhesives, acrylic compounds Aqueous Adhesives, polyurethanes water-base cement
Glutinous agent, epoxy Aqueous Adhesives, phenolic aldehyde Aqueous Adhesives, silicone Aqueous Adhesives, rubber-like Aqueous Adhesives
Or the aqueous adhesive used in other technical field；This solvent-borne type adhesive can for example, polyamine group formic acid
Ester (PU), acrylic resin, isobutene rubber resin, SBR styrene butadiene rubbers resin, isoprene rubber tree
Solvent-borne type adhesive used in fat, caoutchouc resin, polysilicone or other technical field.
Wherein, this stain is any dyestuff, pigment or the coloured powder of any tool or fraction, there is no limit especially
System；Furthermore, this stain can be any inorganic or organic pigment, disperse dyes, acid stain, oil-soluble
Dyestuff, direct dyes, basic stain, mordant dye, acid mordant dyes, ink etc., wherein these disperse dyes
Comprise azo type disperse dyes, ahthraquinone disperse dye, heterocyclic type disperse dyes etc.；This acid stain comprises azo
Type, anthraquinone type, triaryl methane type etc.；Particularly, this stain can such as but be not limited in triphenyl methane system dye
Material, diphenyl methane based dye, quinoline based dye, thiazine based dye, thiazole based dye, ton based dye, flavin
Based dye, aulamine (Auramine) based dye, sarranine (safranine) based dye, rose-red (phloxine) based dye,
Methylene blue based dye etc..
Wherein, this color film is polyethylene terephthalate (PET), thermoplastic polyurethane (TPU), polyamine group
Formic acid esters (PU) or other materials known in the technical field of the invention.
The inventive method still can comprise the cloth known by other persond having ordinary knowledge in the technical field of the present invention or
Textile finishing or procedure of processing, such as, but not limited to concise, shape, be dried, set, soap, Final finishing, painting
The post-processing steps such as cloth, laminating processing, spill resistant and moisture absorbing and sweat releasing processing.
Refer to Fig. 1 to 3, polychrome transparent fabric of the present invention, including transparent base 10, coloured compound layer 20 and color film color
Layer 30, this coloured compound layer 20 is only arranged at the presumptive area on a surface 11 of this transparent base 10, wherein this fate
Territory is account for this transparent base one surface area 10% to 90%, preferably accounts for the 25% of this transparent base one surface area
To 75%, more preferably accounting for the 35% to 65% of this transparent base one surface area, this color film chromatograph 30 is arranged at this to be had
On the coloring agent bed of material 20, wherein a surface 11 of this transparent base 10 presents shape and the color of this color film chromatograph 30, and a bit
Dimpling is then smooth for a surface 11 of this transparent base 10, another surface 12 of this transparent base 10, and by this
Another surface perspective presents shape and the color of this coloured compound layer 20.Thereby, polychrome transparent fabric of the present invention is saturating at this
One surface 11 of bright base material tool Coloured film chromatograph 30 presents color film and remaines in the color on coloured compound layer 20, another side 12
Then present the color of this coloured compound layer 20 so that fabric two sides represents different colours and sense of touch, and increases fabric 30
Aesthetic property and practicality.
Following instance illustrates the enforcement aspect of the present invention, and the technical characteristic of the explaination present invention, is not used for limiting
The protection category of the present invention processed.Any skilled person the arrangement of unlabored change or isotropism can belong to this
The scope that invention is advocated, the scope of the present invention should be as the criterion with appending claims.
Example:
The one engraved cylinder of taking turns of tool is provided, and takes turns on cylinder, be applied with coloring agent material in this, then make this take turns cylinder to roll across color film, with
Make the presumptive area on this color film have this coloured sizing material, then the color film with coloring agent material is transferred to transparent cloth
On, to make the attachment of this transparent cloth have the color film of coloring agent material, drying machine or other roasting plants are dried fixed
Type, removes this color film afterwards, can obtain polychrome transparent fabric of the present invention.
Following table provides the example of the coloured sizing material used in the present invention.
Table 1
Claims (10)
1. the method manufacturing polychrome transparent fabric, including:
Transparent base is provided；
The presumptive area being applied to a surface in a surface of this transparent base has the color film of coloured sizing material；And
Color film is torn off.
Method the most according to claim 1, the wherein choosing of this transparent base free woven fabric, looped fabric
And the group that adhesive-bonded fabric is formed.
Method the most according to claim 1, the wherein choosing of this transparent base free rayon fibers, nylon
The group that fiber, polyester fiber and acryl fiber are formed.
The most according to the method in any one of claims 1 to 3, wherein this coloured sizing material in use
Before, stain is added person formed in transparent gross rubber.
Method the most according to claim 4, wherein this coloured sizing material comprises less than about 100 weight %
Adhesive and the stain of greater than about 0 weight %.
Method the most according to claim 5, wherein this coloured sizing material comprises about 80 weight % to about 99
The adhesive of weight % and the stain of about 1 weight % to about 20 weight %.
7. a polychrome transparent fabric, including:
Transparent base；
Coloured compound layer, it is distributed in the presumptive area on this transparent base one surface；And
Color film chromatograph, it attaches on this coloured compound layer.
Polychrome transparent fabric the most according to claim 7, wherein this coloured compound layer comprises less than about
The adhesive of 100 weight % and the stain of greater than about 0 weight %.
Polychrome transparent fabric the most according to claim 8, wherein this coloured sizing material comprises about 80 weight
The adhesive of % to about 99 weight % and the stain of about 1 weight % to about 20 weight %.
10., according to the polychrome transparent fabric according to any one of described in claim 7 to 9, wherein this is transparent
Base material selects the group that free woven fabric, looped fabric and adhesive-bonded fabric are formed；And this transparent base selects free rayon fine
The group that dimension, nylon fiber, polyester fiber and acryl fiber are formed.