CN106269441A - A kind of manufacture method of Composite bottle cap - Google Patents

A kind of manufacture method of Composite bottle cap Download PDF

Info

Publication number
CN106269441A
CN106269441A CN201610661453.8A CN201610661453A CN106269441A CN 106269441 A CN106269441 A CN 106269441A CN 201610661453 A CN201610661453 A CN 201610661453A CN 106269441 A CN106269441 A CN 106269441A
Authority
CN
China
Prior art keywords
bottle cap
composite
composite bottle
manufacture method
prepared
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610661453.8A
Other languages
Chinese (zh)
Inventor
郑贤付
倪永策
胡汝宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI VENUS PACKAGING Co Ltd
Original Assignee
ANHUI VENUS PACKAGING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI VENUS PACKAGING Co Ltd filed Critical ANHUI VENUS PACKAGING Co Ltd
Priority to CN201610661453.8A priority Critical patent/CN106269441A/en
Publication of CN106269441A publication Critical patent/CN106269441A/en
Pending legal-status Critical Current

Abstract

The present invention relates to the manufacture method of a kind of Composite bottle cap, said method comprising the steps of, prepared by stock, according to businessman's demand, uses common method to produce out common bottle cap；Gluing, applies glue at conventional bottle cap outer surface；Heat treatment, is placed into the conventional bottle cap coating glue in baking oven；Prepared by exterior material, chosen material, processes material；Compound, by the Material cladding produced to conventional bottle cap surface, produce Composite bottle cap；Cooling, processes the Composite bottle cap room temperature cooling produced；Polishing, will polish to the Composite bottle cap cooled down；Profile processes, and the Composite bottle cap surface of air exercise milled carries out outward appearance, pattern makes；Inspection, carries out qualified sampling observation to the above-mentioned product completed.The present invention, by the protective layer at original common plastics one layer of green safety of bottle cap surface recombination, makes bottle cap reach the demand of food safety, and input price is low, achieves many things at one stroke, and suitably promotes.

Description

A kind of manufacture method of Composite bottle cap
Technical field
The present invention relates to the manufacture method of a kind of Composite bottle cap, belong to packaging manufacture field.
Background technology
With the quickening pace of modern life, disposable plastic food-case is widely used, existing plastics food It is raw material that product box uses polystyrene, adds ethane foaming and form after high-temperature fusion, present present plastic bottle closure Mostly adopt in this way, but the disposable tableware made of this material also exists problems with: having in this plastic bottle closure Pest matter will penetrate in food, causes damage liver, kidney and the central nervous system etc. of people.If but the most more Change the raw material making bottle cap, or plus some special minimizing technology, such input price is lost more than gain, not profit Can say, so on the basis of guaranteed price is cheap, proposing the manufacture method of a kind of Composite bottle cap.
Summary of the invention
The technical problem to be solved is: provide the manufacture of a kind of Composite bottle cap putting into low, green safety Method.The technical problem to be solved takes techniques below scheme to realize:
The manufacture method of a kind of Composite bottle cap, said method comprising the steps of:
A. prepared by stock: according to businessman's demand, uses common method to produce out common bottle cap, outside omitting finally See the step beautified；
B. gluing: apply glue at conventional bottle cap outer surface；
C. heat treatment: the conventional bottle cap coating glue is placed in baking oven；
D. prepared by exterior material: chosen material, processes material；
E. it is combined: by the Material cladding produced to conventional bottle cap surface, produce Composite bottle cap；
F. cooling: the Composite bottle cap room temperature cooling produced is processed；
G. polishing: the Composite bottle cap cooled down will be polished；
H. profile processes: the Composite bottle cap surface of air exercise milled carries out outward appearance, pattern makes；
I. inspection: the above-mentioned product completed is carried out qualified sampling observation.
Preferably, in the preparation of described step A stock, the selected general polystyrene of conventional bottle cap is the general of major ingredient Logical vinyl cover, cheap.
Preferably, the gluing of described step B: the glue chosen is polyethylene glue.
Preferably, the step that prepared by the exterior material of described D step is:
Preferably, the step that prepared by the exterior material of described D step is: choose phenolic resin, amino resins, bamboo charcoal fibre The material such as dimension, broomcorn straw fiber, potato starch, glucose, nanoclay, sodium carbonate is according to certain ratio mixing, then Add ethanol solution, be stirred, when in liquid without particulate matter, stop stirring, put in the baking oven that temperature is 300 DEG C and heat Take out after 20min, be then placed in the baking oven of 60 DEG C placing.
Preferably, the compound step of described E step is:
Take out the exterior material prepared, then exterior material be coated onto the conventional bottle cap surface with Polyvinyl glue, Being then placed in temperature is to take out after heated baking 10min 45 DEG C add in hot tank, and then room temperature places dry in the sun.
Beneficial effect:
The present invention, by the protective layer at original common plastics one layer of green safety of bottle cap surface recombination, makes bottle cap reach The demand of food safety, and input price is low, achieves many things at one stroke, and suitably promotes.
Detailed description of the invention
In order to the technological means of the present invention, creation characteristic, reach purpose and be easy to understand with effect, further below Illustrate the present invention.
The manufacture method of a kind of Composite bottle cap, said method comprising the steps of:
A. prepared by stock: according to businessman's demand, uses common method to produce out common bottle cap, outside omitting finally See the step beautified；
B. gluing: apply glue at conventional bottle cap outer surface；
C. heat treatment: the conventional bottle cap coating glue is placed in baking oven；
D. prepared by exterior material: chosen material, processes material；
E. it is combined: by the Material cladding produced to conventional bottle cap surface, produce Composite bottle cap；
F. cooling: the Composite bottle cap room temperature cooling produced is processed；
G. polishing: the Composite bottle cap cooled down will be polished；
H. profile processes: the Composite bottle cap surface of air exercise milled carries out outward appearance, pattern makes；
I. inspection: the above-mentioned product completed is carried out qualified sampling observation.
Preferably, in the preparation of described step A stock, the selected general polystyrene of conventional bottle cap is the general of major ingredient Logical vinyl cover, cheap.
The gluing of described step B: the glue chosen is polyethylene glue.
Step prepared by the exterior material of described D step is:
Choose phenolic resin, amino resins, bamboo carbon fiber, broomcorn straw fiber, potato starch, glucose, nanoclay, The materials such as sodium carbonate, according to certain ratio mixing, are subsequently adding ethanol solution, are stirred, when in liquid without particulate matter, Stop stirring, put into and take out after the baking oven that temperature is 300 DEG C heats 20min, be then placed in the baking oven of 60 DEG C placing.
The compound step of described E step is:
Take out the exterior material prepared, then exterior material be coated onto the conventional bottle cap surface with Polyvinyl glue, Being then placed in temperature is to take out after heated baking 10min 45 DEG C add in hot tank, and then room temperature places dry in the sun.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry Personnel are it should be appreciated that the present invention is not restricted to the described embodiments, without departing from the spirit and scope of the present invention, and this Bright also having various changes and modifications, these changes and improvements both fall within scope of the claimed invention.Application claims Protection domain is defined by appending claims and equivalent thereof.

Claims (5)

1. the manufacture method of a Composite bottle cap, it is characterised in that said method comprising the steps of:
A. prepared by stock: according to businessman's demand, uses common method to produce out common bottle cap, omits last outward appearance beautiful The step changed；
B. gluing: apply glue at conventional bottle cap outer surface；
C. heat treatment: the conventional bottle cap coating glue is placed in baking oven；
D. prepared by exterior material: chosen material, processes material；
E. it is combined: by the Material cladding produced to conventional bottle cap surface, produce Composite bottle cap；
F. cooling: the Composite bottle cap room temperature cooling produced is processed；
G. polishing: the Composite bottle cap cooled down will be polished；
H. profile processes: the Composite bottle cap surface of air exercise milled carries out outward appearance, pattern makes；
I. inspection: the above-mentioned product completed is carried out qualified sampling observation.
2. the manufacture method of Composite bottle cap as claimed in claim 1, it is characterised in that in the preparation of described step A stock The selected common plastics lid that the general polystyrene of conventional bottle cap is major ingredient, cheap.
3. the manufacture method of Composite bottle cap as claimed in claim 1, it is characterised in that the gluing of described step B: the glue chosen Water is polyethylene glue.
4. the manufacture method of Composite bottle cap as claimed in claim 1, it is characterised in that prepared by the exterior material of described D step Step be:
The manufacture method of Composite bottle cap as claimed in claim 1, it is characterised in that prepared by the exterior material of described D step Step is: choose phenolic resin, amino resins, bamboo carbon fiber, broomcorn straw fiber, potato starch, glucose, nanoclay, The materials such as sodium carbonate, according to certain ratio mixing, are subsequently adding ethanol solution, are stirred, when in liquid without particulate matter, Stop stirring, put into and take out after the baking oven that temperature is 300 DEG C heats 20min, be then placed in the baking oven of 60 DEG C placing.
5. the manufacture method of Composite bottle cap as claimed in claim 1, it is characterised in that the compound step of described E step is:
Take out the exterior material prepared, then exterior material is coated onto the conventional bottle cap surface with Polyvinyl glue, then Putting into temperature is to take out after heated baking 10min 45 DEG C add in hot tank, and then room temperature places dry in the sun.
CN201610661453.8A 2016-08-05 2016-08-05 A kind of manufacture method of Composite bottle cap Pending CN106269441A (en)