CN106245320A - A kind of acrylate antistatic fibre spreading mass - Google Patents
A kind of acrylate antistatic fibre spreading mass Download PDFInfo
- Publication number
- CN106245320A CN106245320A CN201610614774.2A CN201610614774A CN106245320A CN 106245320 A CN106245320 A CN 106245320A CN 201610614774 A CN201610614774 A CN 201610614774A CN 106245320 A CN106245320 A CN 106245320A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- added
- acrylic ester
- ester monomer
- antistatic fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of acrylate antistatic fibre spreading mass, by mass percentage, it includes graphene oxide 1 10% and acrylic ester monomer 90 99%, and its preparation method includes prepared by pre-emulsion preparation and acrylate antistatic fibre spreading mass.
Description
Technical field
The present invention relates to a kind of fiber spreading mass, be specifically related to a kind of antistatic fibre spreading mass.
Background technology
Imitative wool product is popular in market, but goods antistatic effect is the key of product quality.At present, imitative sheep
The antistatic effect of woolen is general.
Summary of the invention
Goal of the invention: the invention aims to overcome deficiency of the prior art, it is provided that one has good anti-quiet
Electricity and the acrylate antistatic fibre spreading mass of electromagnetic protection performance.
Technical scheme: in order to solve above-mentioned technical problem, a kind of acrylate antistatic fibre starching of the present invention
Material, by mass percentage, it includes,
Graphene oxide 1-10%;
Acrylic ester monomer 90-99%;
Described acrylic ester monomer include butyl acrylate, 2-Isooctyl acrylate monomer, ethyl acrylate, 2-(Acryloyloxy)ethanol,
Methyl methacrylate, styrene, acrylonitrile, hydroxyethyl methylacrylate, Hydroxypropyl methacrylate;
Its preparation method includes,
(1) prepared by pre-emulsion;
(2) prepared by acrylate antistatic fibre spreading mass;
Wherein, step (1) includes,
A, deionized water, emulsifying agent are added in pre-emulsification still and stir;
B, acrylic ester monomer is added in pre-emulsification still, stir 10-60min;
Wherein, step (2) includes,
A, deionized water, emulsifying agent are added in reactor and stirs, open condensation reflux unit, be warming up to 78-80 DEG C;
B, initiator is added in reactor, be warming up to 80-85 DEG C;
C, by esters of acrylic acid pre-emulsion dropping add reactor, react 60-180min;
D, insulation 30-60min.
Antistatic fibre spreading mass pass through graphene oxide modified aqueous acrylic acid ester, described fiber including but not limited to
Terylene, polypropylene, spandex, acrylon, cotton etc..
Beneficial effect: compared with prior art, its remarkable advantage is the present invention: the present invention uses the material of graphene oxide
Modification acrylate class slurry so that the antistatic property of slurry promotes, and after being coated into thin film, antistatic film surface resistivity can
Reach 106Ω, has good antistatic and electromagnetic protection performance so that imitative wool product antistatic effect significantly promotes.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1:
A kind of acrylate antistatic fibre spreading mass of the present invention, by mass percentage, it includes,
Graphene oxide 4%;
Acrylic ester monomer 96%;
Described acrylic ester monomer include butyl acrylate, 2-Isooctyl acrylate monomer, ethyl acrylate, 2-(Acryloyloxy)ethanol,
Methyl methacrylate, styrene, acrylonitrile, hydroxyethyl methylacrylate, Hydroxypropyl methacrylate;
Its preparation method includes,
(1) prepared by pre-emulsion;
(2) prepared by acrylate antistatic fibre spreading mass;
Wherein, step (1) includes,
A, deionized water, emulsifying agent SC-09 are added in pre-emulsification still and stir;
B, acrylic ester monomer is added in pre-emulsification still, stir 20min;
Wherein, step (2) includes,
A, deionized water, emulsifying agent SC-09 are added in reactor and stirs, open condensation reflux unit, be warming up to 78 DEG C;
B, initiator ammonium persulfate is added in reactor, be warming up to 81 DEG C;
C, by esters of acrylic acid pre-emulsion dropping add reactor, react 80min;
D, insulation 35min.
Embodiment 2:
A kind of acrylate antistatic fibre spreading mass of the present invention, by mass percentage, it includes,
Graphene oxide 6%;
Acrylic ester monomer 94%;
Described acrylic ester monomer include butyl acrylate, 2-Isooctyl acrylate monomer, ethyl acrylate, 2-(Acryloyloxy)ethanol,
Methyl methacrylate, styrene, acrylonitrile, hydroxyethyl methylacrylate, Hydroxypropyl methacrylate;
Its preparation method includes,
(1) prepared by pre-emulsion;
(2) prepared by acrylate antistatic fibre spreading mass;
Wherein, step (1) includes,
A, deionized water, emulsifying agent SC-09 are added in pre-emulsification still and stir;
B, acrylic ester monomer is added in pre-emulsification still, stir 40min;
Wherein, step (2) includes,
A, deionized water, emulsifying agent SC-09 are added in reactor and stirs, open condensation reflux unit, be warming up to 79 DEG C;
B, initiator ammonium persulfate is added in reactor, be warming up to 82 DEG C;
C, by esters of acrylic acid pre-emulsion dropping add reactor, react 120min;
D, insulation 45min.
Embodiment 3:
A kind of acrylate antistatic fibre spreading mass of the present invention, by mass percentage, it includes,
Graphene oxide 8%;
Acrylic ester monomer 92%;
Described acrylic ester monomer include butyl acrylate, 2-Isooctyl acrylate monomer, ethyl acrylate, 2-(Acryloyloxy)ethanol,
Methyl methacrylate, styrene, acrylonitrile, hydroxyethyl methylacrylate, Hydroxypropyl methacrylate;
Its preparation method includes,
(1) prepared by pre-emulsion;
(2) prepared by acrylate antistatic fibre spreading mass;
Wherein, step (1) includes,
A, deionized water, emulsifying agent SC-09 are added in pre-emulsification still and stir;
B, acrylic ester monomer is added in pre-emulsification still, stir 50min;
Wherein, step (2) includes,
A, deionized water, emulsifying agent SC-09 are added in reactor and stirs, open condensation reflux unit, be warming up to 80 DEG C;
B, initiator ammonium persulfate is added in reactor, be warming up to 84 DEG C;
C, by esters of acrylic acid pre-emulsion dropping add reactor, react 160min;
D, insulation 55min.
The present invention uses the material modification esters of acrylic acid slurry of graphene oxide so that the antistatic property of slurry carries
Rising, after being coated into thin film, antistatic film surface resistivity is up to 106Ω, has good antistatic and electromagnetic protection performance, makes
Wool product antistatic effect must be imitated significantly promote.
The invention provides a kind of thinking and method, the method and the approach that implement this technical scheme are a lot, above institute
State is only the preferred embodiment of the present invention, it is noted that for those skilled in the art, without departing from
On the premise of the principle of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should be regarded as the guarantor of the present invention
Protecting scope, each ingredient the clearest and the most definite in the present embodiment all can use prior art to be realized.
Claims (1)
1. an acrylate antistatic fibre spreading mass, it is characterised in that: by mass percentage, it includes,
Graphene oxide 1-10%;
Acrylic ester monomer 90-99%;
Described acrylic ester monomer include butyl acrylate, 2-Isooctyl acrylate monomer, ethyl acrylate, 2-(Acryloyloxy)ethanol,
Methyl methacrylate, styrene, acrylonitrile, hydroxyethyl methylacrylate, Hydroxypropyl methacrylate;
Its preparation method includes,
(1) prepared by pre-emulsion;
(2) prepared by acrylate antistatic fibre spreading mass;
Wherein, step (1) includes,
A, deionized water, emulsifying agent are added in pre-emulsification still and stir;
B, acrylic ester monomer is added in pre-emulsification still, stir 10-60min;
Wherein, step (2) includes,
A, deionized water, emulsifying agent are added in reactor and stirs, open condensation reflux unit, be warming up to 78-80 DEG C;
B, initiator is added in reactor, be warming up to 80-85 DEG C;
C, by esters of acrylic acid pre-emulsion dropping add reactor, react 60-180min;
D, insulation 30-60min.