CN106245046A - Line and technique are produced in a kind of precision equipment renovation - Google Patents
Line and technique are produced in a kind of precision equipment renovation Download PDFInfo
- Publication number
- CN106245046A CN106245046A CN201610720707.9A CN201610720707A CN106245046A CN 106245046 A CN106245046 A CN 106245046A CN 201610720707 A CN201610720707 A CN 201610720707A CN 106245046 A CN106245046 A CN 106245046A
- Authority
- CN
- China
- Prior art keywords
- water
- precision equipment
- parts
- antirust
- hydro
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
nullLine is produced in the renovation that the invention provides a kind of precision equipment，Including: jetter (3)，Material spray storage device (4)，Antirust processing unit (plant) (7),Coating apparatus (8)，Wherein said material spray storage device (4) is connected with described jetter (3)，To carry what storage in described material spray storage device (4) had: with the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water，With glass sand 20%，The hydro-peening medium that water 80% ratio is deployed into，To described jetter (3)，For described jetter (3) with the pressure hydro-peening of 0.3MPa，It is filled with in described antirust processing unit (plant) (7): with 5 parts of water，1 part of antirust solution，The working fluid of 1 part of water solublity lotion proportioning，And by this antirust processing unit (plant) (7) be heated to 50 ° ~ 70 ° for soak after，Plating supplement material to described coating apparatus (8).
Description
Technical field
The present invention relates to the renovation of a kind of precision equipment and produce line, particularly relate to a kind of carry out renovating for equipment metal parts
Produce line and technique.
Background technology
Imported Precision equipment manufacturing cost costly, uses to certain time limit, even if maintenance is preferably, and its internal metallic material
As time goes on, can have certain abrasion and oxidation the most unavoidably, thus without continue up to original normal deviate scope with
Interior use state, even cannot use, and therefore the most existing precision can be set by one by certain process
Standby carry out renovation processing, until its original performance can be recovered to the technical scheme of normal operating condition.
Summary of the invention
Line and technique are produced in a kind of precision equipment renovation of the present invention, it is possible to preferably remove precision equipment internal metal parts
Patina, and improve oxidation resistance further, can also supply simultaneously this metal parts top layer disappearance patina,
So that metal parts recovers its original structure size, so that precision equipment can recover original normal operating conditions.
To achieve these goals, the invention provides a kind of precision equipment renovation and produce line, including: jetter,
Material spray storage device, antirust processing unit (plant), coating apparatus, wherein said material spray storage device is connected with described jetter, with
Carry in described material spray storage device what storage had: with the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water, with glass
Sand 20%, the hydro-peening medium that water 80% ratio is deployed into, in described jetter, for described jetter with the pressure of 0.3MPa
Power hydro-peening, is filled with in described antirust processing unit (plant): with 5 parts of water, 1 part of antirust solution, the processing of 1 part of water solublity lotion proportioning
Liquid, and by this antirust processing unit (plant) be heated to 50 ° ~ 70 ° for soaking after, to plating supplement material in described coating apparatus.
Further, also include: disassembling region, oil strain unit, wherein said region of disassembling is work platforms, for described essence
After close equipment is disassembled as parts, sorting metal parts in described oil strain unit, wherein the parts supporting region of this oil strain unit in
Netted, use flexible material to make.
Further, the preferred plastics/resin material of described oil strain unit is made.
Further, in described coating apparatus, the supplement material of plating is Teflon.
To achieve these goals, another aspect of the present invention additionally provides a kind of precision equipment renovation and produces line, including:
Jetter, material spray storage device, antirust processing unit (plant), coating apparatus, wherein said material spray storage device fills with described hydro-peening
Put connection, to carry in described material spray storage device what storage had: with the glass sand of 120 mesh and pH value 8 alkalescent water,
With glass sand 25%, the hydro-peening medium that water 75% ratio is deployed into, to described jetter, for described jetter with
The pressure hydro-peening of 0.4MPa, is filled with in described antirust processing unit (plant): with 5 parts of water, 1 part of antirust solution, 1 part of water solublity lotion proportioning
Working fluid, and by this antirust processing unit (plant) be heated to 60 ° for soaking after, to plating supplement in described coating apparatus
Material.
Further, also include: disassembling region, oil strain unit, wherein said region of disassembling is work platforms, for described essence
After close equipment is disassembled as parts, sorting metal parts in described oil strain unit, wherein the parts supporting region of this oil strain unit in
Netted, use flexible material to make.
Further, the preferred plastics/resin material of described oil strain unit is made.
Further, in described coating apparatus, the supplement material of plating is Teflon.
To achieve these goals, another aspect of the present invention additionally provides the renovation technology of a kind of precision equipment, and it includes
Step is as follows: device for disassembling and sorting operation: disassemble this precision equipment, sort out metal parts；Oil strain treatment process: to drip filter
Mode, preliminary elimination part machine oil；Hydro-peening treatment process: in order to the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water,
With glass sand 20%, the hydro-peening medium that water 80% ratio is deployed into, spray to this metal part surface with the pressure of 0.3MPa；Antirust place
Science and engineering sequence: making this metal parts is 50 ° ~ 70 ° Celsius in temperature, with 5 parts of water, 1 part of antirust solution, the ratio of 1 part of water solublity lotion
The liquid of proportioning soaks；Spraying plating manufacturing procedure: after removing liquid, augments material at this metal part surface plating.
To achieve these goals, another aspect of the present invention additionally provides the renovation technology of a kind of precision equipment, and it includes
Step is as follows: device for disassembling and sorting operation: disassemble this precision equipment, sort out metal parts；Oil strain treatment process: to drip filter
Mode, preliminary elimination part machine oil；Hydro-peening treatment process: in order to the glass sand of 120 mesh and pH value 8 alkalescent water, with glass
Glass sand 25%, the hydro-peening medium that water 75% ratio is deployed into, spray to this metal part surface with the pressure of 0.4MPa；Antirust treatment work
Sequence: making this metal parts is 60 ° Celsius in temperature, with 5 parts of water, 1 part of antirust solution, 1 part of water solublity lotion proportions
Liquid soaks；Spraying plating manufacturing procedure: after removing liquid, augments material at this metal part surface plating.
Line and method is produced, it is possible to effectively the metal parts of precision equipment is entered by one precision equipment of the present invention renovation
Row renovation and reparation, thus extend the time limit in service life of precision equipment, after recovering to renovate, the reliability of precision equipment, reduces
The use cost of user.
Accompanying drawing explanation
The accompanying drawing of the part constituting the application is used for providing a further understanding of the present invention, and the present invention's is schematic real
Execute example and illustrate for explaining the present invention, being not intended that inappropriate limitation of the present invention.In the accompanying drawings:
Fig. 1 is the schematic diagram that line is produced in a kind of precision equipment renovation according to a first embodiment of the present invention；
Fig. 2 is the schematic diagram that line is produced in a kind of precision equipment renovation according to a second embodiment of the present invention；
Fig. 3 is the schematic diagram of a kind of precision equipment renovation technology according to third and fourth embodiment of the present invention.
Detailed description of the invention
It should be noted that in the case of not conflicting, the embodiment in the application and the feature in embodiment can phases
Combination mutually.Describe the present invention below with reference to the accompanying drawings and in conjunction with the embodiments in detail.
In order to make those skilled in the art be better understood from the present invention program, below in conjunction with in the embodiment of the present invention
Accompanying drawing, is clearly and completely described the technical scheme in the embodiment of the present invention, it is clear that described embodiment is only
The embodiment of a present invention part rather than whole embodiments.Based on the embodiment in the present invention, in ordinary skill
Personnel do not make the every other embodiment obtained under creative work premise, all should belong to the protection model of the present invention
Enclose.
It should be noted that term " first " in description and claims of this specification and above-mentioned accompanying drawing, "
Two " it is etc. for distinguishing similar object, without being used for describing specific order or precedence.Should be appreciated that so use
Data can exchange in the appropriate case, in order to embodiments of the invention described herein can with except here diagram or
Order beyond those described is implemented.Additionally, term " includes " and " having " and their any deformation, it is intended that cover
Cover non-exclusive comprising.
Current existing precision equipment, is external imported product mostly, and therefore the universal machining accuracy of parts is high, if nothing
The adverse consequencess such as method correctly processes this metal parts, then may cause and scrap, damage, therefore to appropriate this precision of process
Metal parts, according to embodiments of the invention, it is provided that line and technique are produced in a kind of precision equipment renovation, and detailed description of the invention is such as
Under.
Embodiment one
Referring to Fig. 1, the renovation of a kind of precision equipment of the present invention is produced line and is included: disassemble region 1, oil strain unit 2, jetter 3,
Material spray storage device 4, antirust processing unit (plant) 7, coating apparatus 8.Concrete when precision equipment is on the work platforms disassembling region 1
After being disassembled as parts, part metals parts then will be placed in this oil strain unit 2, and wherein this oil strain unit 2 is in netted,
And use flexible material to make, owing to the metal parts general size required precision of precision equipment is higher, therefore to dripping filter
While this metal parts machine oil, it is to avoid damage this metal parts, the preferred plastics of parts supporting region that in the present embodiment, this is netted/
Resin material is made.Further after this metal part surface part machine oil is by filtering, i.e. enter in jetter 3 and spray
Wash processing, to remove the impurity such as this metal part surface oxide, rusty stain, spot.Certainly it will be understood by those skilled in the art that
This oil strain unit 2 and disassemble region 1 for the preferred embodiment of the present invention, and it is not turning over of this precision equipment to the present invention
The new function producing line and structure limit, and therefore it may occur to persons skilled in the art that this dismounting region 1 also can be divided with producing line
From, and this oil strain unit 2 also can omit.
Can be mentioned that the hydro-peening medium that this jetter 3 is used forms through special allotment, and be stored in
In this material spray storage device 4, to be delivered in this jetter 3 by feeding engine, concrete, this hydro-peening medium includes: glass
Sand, water, wherein this glass sand preferably 100 ~ 250 mesh, this hydromining pH value 7 alkalescent water, with glass sand 20%, water 80%
Ratio allotment forms, and by this feeding engine, after delivering to this jetter 3, is sprayed by the pressure with 0.3MPa in this jetter 3
To this metal part surface, thereby can effectively in short several seconds by the oxide of this metal part surface, rusty stain, spot etc.
Impurity removal, this metal part surface that causes that simultaneously will not be rough excessively weares and teares.
Further, after this metal part surface is processed by hydro-peening, i.e. enter in this antirust processing unit (plant) 7, further
Carrying out antirust and cleaning treatment, specifically, be filled with working fluid in this antirust processing unit (plant) 7, wherein this working fluid includes:
Water, antirust solution, water-soluble washing agent, respectively with 5(water): 1(antirust solution): 1(water solublity lotion) proportions form, and lead to
Cross this antirust processing unit (plant) 7 and be heated to 50 ° ~ 70 °, after thereby this metal parts being carried out, this metal portion can be effectively improved
The oxidation resistance of part, and remove the surface impurity of this metal parts further.
Embodiment two
Referring to Fig. 2, the renovation of a kind of precision equipment of the present invention is produced line and is included: disassemble region 1, oil strain unit 2, jetter 3,
Material spray storage device 4, antirust processing unit (plant) 7, coating apparatus 8, circulation filter 5.Concrete disassembling district when precision equipment
After being disassembled as parts on the work platforms in territory 1, part metals parts then will be placed in this oil strain unit 2, wherein should
Oil strain unit 2 is in netted, and uses flexible material to make, due to precision equipment metal parts general size required precision relatively
Height, therefore to while dripping this metal parts machine oil of filter, it is to avoid damage this metal parts, the portion that in the present embodiment, this is netted
Preferred plastics/the resin material of part supporting region is made.Further after this metal part surface part machine oil is by filtering, i.e. enter
Jetter 3 carries out hydro-peening processing, to remove the impurity such as this metal part surface oxide, rusty stain, spot.Certainly this area
Technical staff is it is to be appreciated that this oil strain unit 2 and disassemble region 1 for the preferred embodiment of the present invention, and is not to this
Function and the structure of the renovation product line of this bright precision equipment limit, and therefore it may occur to persons skilled in the art that this dismounting
Region 1 also can separate with producing line, and this oil strain unit 2 also can omit.
Can be mentioned that the hydro-peening medium that this jetter 3 is used forms through special allotment, and be stored in
In this material spray storage device 4, to be delivered in this jetter 3 by feeding engine, concrete, this hydro-peening medium includes: glass
Sand, water, wherein this glass sand preferably 120 mesh, this hydromining pH value 8 alkalescent water, with glass sand 25%, water 75% ratio is adjusted
Join and form, and by this feeding engine, after delivering to this jetter 3, in this jetter 3, this gold will be sprayed to the pressure of 0.4MPa
Belong to parts surface, thereby can effectively in short several seconds, the impurity such as the oxide of this metal part surface, rusty stain, spot be gone
Removing, this metal part surface that causes that simultaneously will not be rough excessively weares and teares.
In addition this hydro-peening medium is after this jetter 3 sprays, it will flow in this circulation filter 5, by this
After circulation filter 5 precipitation filters, this water of this hydro-peening medium and this glass sand will separate, this water by after filtering again
Enter in this material spray storage device 4, mix with this glass sand, thus form a process recycled, disappear reducing resource
Consume cost-effective, it is to avoid add water the most frequently, to improve production efficiency.This used glass sand is then owing to being mixed with gold
Belong to the impurity on parts, then discard.
Further, after this metal part surface is processed by hydro-peening, i.e. enter in this antirust processing unit (plant) 7, further
Carrying out antirust and cleaning treatment, specifically, be filled with working fluid in this antirust processing unit (plant) 7, wherein this working fluid includes:
Water, antirust solution, water-soluble washing agent, respectively with 5(water): 1(antirust solution): 1(water solublity lotion) proportions form, and lead to
Cross this antirust processing unit (plant) 7 and be heated to 60 °, after thereby this metal parts being carried out, this metal parts can be effectively improved
Oxidation resistance, and remove the surface impurity of this metal parts further.
This metal part surface impurity in above-mentioned steps, above-mentioned two embodiment can reach to remove effect, but
Also can change the size of this metal parts, this is the surface oxidation owing to eliminating this metal parts in above-mentioned technique simultaneously
After the impurity such as thing, rust, spot, this metal part surface will certainly be worn and torn, therefore to supply this metal parts chi
Very little, then need to augment material at this metal part surface plating, this metal part surface is entered by the present invention preferred Teflon material
Row this metal part surface plating supplement material, the present invention preferred Teflon material carries out plating to this metal part surface, with
Within supplying this metal parts size extremely original dimensional tolerance range.To realize the renovation to this metal parts, and at this metal
After parts re-assembly, recover original normal operating conditions of this precision equipment, thus extend the service life of precision equipment
In the time limit, after recovering to renovate, the reliability of precision equipment, reduces the use cost of user.
Embodiment three
Referring to Fig. 3, the renovation technology of a kind of precision equipment of the present invention mainly comprises the following steps that
Device for disassembling and sorting operation 11: oil strain treatment process 12；Hydro-peening treatment process 13；Antirust treatment operation 14；Spraying plating adds
Work operation 15.
Specifically, after this device for disassembling and sorting operation 11 are by disassembling this precision equipment, sort out metal parts, and
By oil strain treatment process 12, to drip filter mode, preliminary elimination part machine oil, think that rear road hydro-peening treatment process 13 improves hydro-peening
Efficiency, wherein this hydro-peening treatment process 13 includes: in order to the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water, with glass
Glass sand 20%, the hydro-peening medium that water 80% ratio is deployed into, spray to this metal part surface with the pressure of 0.3MPa, for clearance complete should
After metal part surface impurity, enter in antirust treatment operation 14.
Wherein this antirust treatment operation 14 specifically includes: make this metal parts temperature be Celsius 50 ° ~ 70 ° with 5 parts of water, 1
Part antirust solution, soaks in the liquid of the proportions of 1 part of water solublity lotion.Liquid on this this metal parts of rear removal,
Carrying out spraying plating manufacturing procedure 15, to augment material at this metal part surface plating, the present invention preferred Teflon material is to this gold
Belong to parts surface and carry out plating, to supply this metal parts size, complete metal parts renovation, complete precision being assembled into equipment
Equipment renovates.
Embodiment four
Referring to Fig. 3, the renovation technology of a kind of precision equipment of the present invention mainly comprises the following steps that
Device for disassembling and sorting operation 11: oil strain treatment process 12；Hydro-peening treatment process 13；Antirust treatment operation 14；Spraying plating adds
Work operation 15.
Specifically, after this device for disassembling and sorting operation 11 are by disassembling this precision equipment, sort out metal parts, and
By oil strain treatment process 12, to drip filter mode, preliminary elimination part machine oil, think that rear road hydro-peening treatment process 13 improves hydro-peening
Efficiency, wherein this hydro-peening treatment process 13 includes: in order to the glass sand of 120 mesh and pH value 8 alkalescent water, with glass sand
25%, the hydro-peening medium that water 75% ratio is deployed into, spray to this metal part surface, this metal complete for clearance with the pressure of 0.4MPa
After parts surface impurity, enter in antirust treatment operation 14.
Wherein this antirust treatment operation 14 specifically includes: make this metal parts temperature be Celsius 60 ° with 5 parts of water, prevent for 1 part
Rust liquid, soaks in the liquid of the proportions of 1 part of water solublity lotion.Liquid on this this metal parts of rear removal, is carried out
Spraying plating manufacturing procedure 15, to augment material at this metal part surface plating, the present invention preferred Teflon material is to this metal portion
Part surface carries out plating, to supply this metal parts size, completes metal parts renovation, completes precision equipment being assembled into equipment
Renovation.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, for the skill of this area
For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, that is made any repaiies
Change, equivalent, improvement etc., should be included within the scope of the present invention.
Claims (10)
1. line is produced in precision equipment renovation, it is characterised in that including: jetter (3), material spray storage device (4), antirust adds
Frock is put (7), coating apparatus (8), and wherein said material spray storage device (4) is connected with described jetter (3), described with conveying
Storage has in material spray storage device (4): with the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water, with glass sand
20%, the hydro-peening medium that water 80% ratio is deployed into, to described jetter (3), for described jetter (3) with 0.3MPa
Pressure hydro-peening, be filled with in described antirust processing unit (plant) (7): with 5 parts of water, 1 part of antirust solution, 1 part of water solublity lotion proportioning and
The working fluid become, and by this antirust processing unit (plant) (7) be heated to 50 ° ~ 70 ° for soaking after, in described coating apparatus (8)
Plating supplement material.
Line is produced in a kind of precision equipment renovation the most according to claim 1, it is characterised in that also include: disassemble region (1),
Oil strain unit (2), wherein said region (1) of disassembling is work platforms, after disassembling as parts for described precision equipment, sorts metal
Parts are interior to described oil strain unit (2), and wherein the parts supporting region of this oil strain unit (2) is netted, use flexible material to make.
Line is produced in a kind of precision equipment renovation the most according to claim 2, it is characterised in that: described oil strain unit (2) is preferred
Plastics/resin material is made.
Line is produced in a kind of precision equipment renovation the most according to claim 1, it is characterised in that: described coating apparatus (8)
The supplement material of middle plating is Teflon.
5. line is produced in precision equipment renovation, it is characterised in that including: jetter (3), material spray storage device (4), antirust adds
Frock is put (7), coating apparatus (8), and wherein said material spray storage device (4) is connected with described jetter (3), described with conveying
Storage has in material spray storage device (4): with the glass sand of 120 mesh and pH value 8 alkalescent water, with glass sand 25%, water
The hydro-peening medium that 75% ratio is deployed into, in described jetter (3), for described jetter (3) with the pressure of 0.4MPa
Hydro-peening, is filled with in described antirust processing unit (plant) (7): with 5 parts of water, 1 part of antirust solution, adding of 1 part of water solublity lotion proportioning
Work liquid, and by this antirust processing unit (plant) (7) be heated to 60 ° for soaking after, to plating supplement material in described coating apparatus (8)
Material.
Line is produced in a kind of precision equipment renovation the most according to claim 5, it is characterised in that also include: disassemble region (1),
Oil strain unit (2), wherein said region (1) of disassembling is work platforms, after disassembling as parts for described precision equipment, sorts metal
Parts are interior to described oil strain unit (2), and wherein the parts supporting region of this oil strain unit (2) is netted, use flexible material to make.
Line is produced in a kind of precision equipment renovation the most according to claim 6, it is characterised in that: described oil strain unit (2) is preferred
Plastics/resin material is made.
Line is produced in a kind of precision equipment renovation the most according to claim 5, it is characterised in that: described coating apparatus (8)
The supplement material of middle plating is Teflon.
9. a precision equipment renovation technology, it is characterised in that comprise the following steps that
Device for disassembling and sorting operation (11): disassemble this precision equipment, sort out metal parts；
Oil strain treatment process (12): to drip filter mode, preliminary elimination part machine oil；
Hydro-peening treatment process (13): in order to the glass sand of 100 ~ 250 mesh and pH value 7 alkalescent water, with glass sand 20%, water
The hydro-peening medium that 80% ratio is deployed into, sprays to this metal part surface with the pressure of 0.3MPa；
Antirust treatment operation (14): making this metal parts is 50 ° ~ 70 ° Celsius in temperature, with 5 parts of water, 1 part of antirust solution, 1 part of water
The liquid of the proportions of dissolubility lotion soaks；
Spraying plating manufacturing procedure (15): after removing liquid, augments material at this metal part surface plating.
10. a precision equipment renovation technology, it is characterised in that comprise the following steps that
Device for disassembling and sorting operation (11): disassemble this precision equipment, sort out metal parts；
Oil strain treatment process (12): to drip filter mode, preliminary elimination part machine oil；
Hydro-peening treatment process (13): in order to the glass sand of 120 mesh and pH value 8 alkalescent water, with glass sand 25%, water 75% compares
The hydro-peening medium that example is deployed into, sprays to this metal part surface with the pressure of 0.4MPa；
Antirust treatment operation (14): making this metal parts is 60 ° Celsius in temperature, with 5 parts of water, 1 part of antirust solution, 1 part of water solublity
The liquid of lotion proportions soaks；
Spraying plating manufacturing procedure (15): after removing liquid, augments material at this metal part surface plating.