CN106244763A - A kind of vanadium-bearing hot metal is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter - Google Patents
A kind of vanadium-bearing hot metal is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter Download PDFInfo
- Publication number
- CN106244763A CN106244763A CN201610807156.XA CN201610807156A CN106244763A CN 106244763 A CN106244763 A CN 106244763A CN 201610807156 A CN201610807156 A CN 201610807156A CN 106244763 A CN106244763 A CN 106244763A
- Authority
- CN
- China
- Prior art keywords
- vanadium
- blowing
- converter
- rifle position
- 2min
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to field of iron and steel smelting, be specifically related to a kind of vanadium-bearing hot metal method of Simultaneous Oxidation separation of phosphorus vanadium in converter.It is an object of the invention to solve the problem that conventional method vanadium extraction from hot metal dephosphorization is relatively low, and reduce TFe content in vanadium slag, thus reduce steel technology and provide low-phosphorous half steel for steelmaking converter.Vanadium-bearing hot metal of the present invention is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter, and after comprising the steps: that A, converter extracting vanadium have converted ferrum, fall oxygen rifle blows, and whole-process control oxygen flow is 1.5～3.0Nm3/t.Min, bottom blowing nitrogen intensity is 0.2～0.4Nm3/t.Min B, blowing are initially added into Calx, and before blowing, 2min presses control rifle position, more than benchmark rifle position 10～30mm；Iron scale or other high oxides-containing iron is added after blowing 1～2min；Press benchmark rifle position after blowing 2min and control rifle position；Before finishing blowing, 2min presses control rifle position, more than benchmark rifle position 30～50mm；Half steel and vanadium slag is gone out after C, finishing blowing.
Description
Technical field
The invention belongs to field of iron and steel smelting, be specifically related to a kind of vanadium-bearing hot metal Simultaneous Oxidation separation of phosphorus vanadium in converter
Method.
Background technology
Phosphorus is the harmful element in most steel grade.In recent years, along with scientific and technical develops rapidly, cryogenic steel,
Marine steel, anti-hydrogen induced cracking steel and part slab steel, should have extremely low sulfur content, also require that phosphorus content ＜ in steel
0.01% or 0.005%.1980, since the age, for molten iron pre-dephosphorization problem, develop various processing method, most represented
Property have two kinds: a kind of is to carry out dephosphorization in containing the ladle of molten iron or fish torpedo ladle, and another kind is to carry out molten iron in converter
Dephosphorizing pretreatment, both approaches has all obtained commercial Application.Ladle or fish torpedo ladle dephosphorization mainly have that temperature drop is relatively big, oxygen blast is mended
Splash especially severe again when repaying temperature drop, the impact of ferrum treatment time of water length produces the problems such as direct motion, and applicable cases is undesirable.And converter
Pre-dephosphorization realizes industrial-scale production in the iron and steel enterprise of Japan and Korea S, and China Baosteel, Wuhan Iron and Steel Plant etc. are producing Low-phosphorus Steel
Time, use the duplex dephosphorized technique of twin furnace to smelt, molten steel [P] can be down to 0.003%～0.008%, excellent effect from 0.08%.
Pan Gangdeng enterprise uses v-bearing titanomagnetite smelting, and molten iron is after desulfurization processes, and sulfur can be down to less than 0.005%, but
Phosphorus is but without effective treatment measures, and during converter smelting, dephosphorization treatment pressure is big.V element is contained, at steel making working procedure owing to climbing steel water
Needing molten iron is carried out vanadium extraction by converter blowing process, vanadium extraction by converter blowing is a kind of maturation process, and vanadium slag uses converter producing completely before.Vanadium extraction-
Steelmaking process has similarity with domestic and international used duplex converter dephosphorization process for making in equipment, technique, therefore, uses vanadium extraction
It is entirely possible in equipment, technology that converter carries out vanadium-bearing hot metal vanadium extraction and dephosphorization simultaneously.The enforcement of Dephosphorization vanadium extraction technology, can be
Steel making working procedure alleviates dephosphorization burden, changes significant to steelmaking process.At present, the calcium method process for extracting vanadium of steel independent research is climbed
Through maturation, being characterized in that vanadium slag CaO content is looser than the requirement of former wet method vanadium extraction, this carries out converter Dephosphorization for the present invention and carries
Vanadium research creates condition.
CN102796840A discloses " converter dephosphorization vanadium extraction coolant and production method, converter dephosphorization extraction vanadium method ",
The production method of described converter dephosphorization vanadium extraction coolant comprises the following steps: by sodium salt granule, iron scale granule, bauxite
Fine powder and water mixing, form compound；Through ball press, compound is pressed into bead；Baking bead, to remove moisture removal, obtains
Cooled agglomerated pellet finished product.The invention have the advantages that and can realize vanadium extraction and dephosphorization during vanadium extraction by converter blowing simultaneously；Operation letter
Single；Impact on existing process for extracting vanadium and half steel quality is less；Dephosphorization efficiency is high, can guarantee that the production efficiency of converter extracting vanadium.This
Outward, the part dephosphorization task of steelmaking converter can be moved forward to converter extracting vanadium by the present invention, it is achieved half steel low cost pneumatic steelmaking, just
In the molten steel obtaining composition, temperature is qualified.CN101215619 discloses the " method of vanadium extraction and dephosphorization and utilization from vanadium-bearing hot metal
The process for making of the method ", described from vanadium-bearing hot metal the method for vanadium extraction and dephosphorization include: vanadium-bearing hot metal is being carried out oxygen supply blowing
During, in described molten iron, adding vanadium extraction and dephosphorization agent and coolant, described vanadium extraction and dephosphorization agent is Na2CO3, obtain after blowing
Vanadium slag and low-phosphorous half steel.The method can extract dephosphorization while vanadium, thus can not only ensure effective extraction of vanadium, Er Qieneng
Phosphorus in enough effectively removal molten iron.From above-mentioned patent it can be seen that two kinds of methods are all with the compound of sodium as Dephosphorising agent, though this
So can play certain dephosphorization effect, but dephosphorization effect is inconspicuous, and sodium compound joins, and converter is interior invades furnace lining
Erosion is relatively big, affects life of converter.The present invention fully phases out the compound of sodium as Dephosphorising agent, it is to avoid the too fast erosion of furnace lining, with
Time can reduce TFe content in vanadium slag, the beneficially steel technology of dephosphorization vanadium extracting process.
Summary of the invention
The invention provides a kind of vanadium-bearing hot metal method of Simultaneous Oxidation separation of phosphorus vanadium in converter.The method can obtain
TFe content in the half steel that phosphorus content is relatively low, and production process gained vanadium slag, reduces production pressure for follow-up steel-making vanadium extraction and dephosphorization
Power.
A kind of vanadium-bearing hot metal of the present invention is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter, comprises the following steps:
After A, converter extracting vanadium have converted ferrum, fall oxygen rifle blows, and whole-process control oxygen flow is 1.5～3.0Nm3/
T.min, bottom blowing nitrogen intensity is 0.2～0.4Nm3/t.min；
B, blowing are initially added into Calx, and before blowing, 2min presses control rifle position, more than benchmark rifle position 10～30mm；Blowing 1～
Iron scale or other high oxides-containing iron is added after 2min；Press benchmark rifle position after blowing 2min and control rifle position；Before finishing blowing
2min presses more than benchmark rifle position 30～50mm and controls rifle position；
Half steel and vanadium slag is gone out after C, finishing blowing；
Wherein, in step B, the addition of described Calx is 1.4～1.7 for making slag dual alkalinity；Described iron scale
Or other high oxides-containing iron addition is 15～25kg/tFe.
Preferably, in said method step B, other high oxides-containing iron described be grade ＞ 55% iron mine, pellet or
Any one in sintering deposit.
Preferably, in said method step B, blowing total time is 5～7min.
Preferably, in said method step C, after described finishing blowing, half steel temperature is 1350～1400 DEG C.
The pass key control operation of the present invention is: starts just to add Calx in blowing and can preferably form dephosphorized slag；Simultaneously
Coordinating three sections of blowing modes, first paragraph adds steelmaking converter finishing slag and realizes main dephosphorization；Second stage adds iron scale, simultaneously
Strengthen bottom blowing stirring, oxygen lance position is lower, realize molten bath strong mixing, is more beneficial for dephosphorization and vanadium extraction；Phase III continues vanadium extraction
Dephosphorization.The inventive method is provided with suitable technique and parameter, both can realize the extraction of vanadium, and the part that also can realize phosphorus takes off
Removing, after can alleviating, operation carries out the pressure of converter ultra-low phosphoretic steel smelting process.
Present invention utilizes vanadium extraction steel mill converter extracting vanadium and become the feature of duplex with steelmaking converter, in converter extracting vanadium simultaneously
Carry out the operation of dephosphorization and vanadium extraction, to alleviate dephosphorization task during steelmaking converter smelting molten steel, few for low phosphorus steel by smelting and realization
Slag steel-making creates conditions.The inventive method have selected suitable Dephosphorising agent, have adjusted process conditions, it is achieved that dephosphorization and vanadium extraction are double
Weight purpose, can reduce vanadium slag TFe content simultaneously, serves good effect to reducing steel technology.
Detailed description of the invention
In order to be more fully understood that the present invention, further illustrate the present invention below in conjunction with embodiment.
In the inventive method, described benchmark rifle position refers to that oxygen gun sprayer is away from molten iron level 10mm.
In the inventive method, not making specified otherwise, ratio, content etc. all represent percentage by weight.
Embodiment 1
After 200t converter extracting vanadium has converted ferrum, molten iron thermometric is 1310 DEG C, and thermometric completes to drop oxygen rifle afterwards and blows, omnidistance
Oxygen flux control is at 1.5Nm3/ t.min, bottom blowing nitrogen intensity presses 0.3Nm3/ t.min controls；Stone is added while starting blowing
Ash controls slag dual alkalinity about 1.4；Before blowing, the above 10mm in benchmark rifle position is pressed in 2min rifle position；Add subsequently after blowing 2min
Entering iron scale, the amount of iron scale is controlled by 25kg/tFe, and oxygen rifle drops to benchmark rifle position simultaneously；2min before finishing blowing
Control of lance position is to the above 30mm in benchmark rifle position；Half steel and vanadium slag is gone out after finishing blowing.
In molten iron, content of vanadium is 0.330%, and phosphorus content is 0.070%, and after finishing blowing, half steel content of vanadium is 0.043%,
Phosphorus content is 0.021%, half steel temperature 1380 DEG C, vanadium slag TFe 15.32%.
Embodiment 2
After 120t converter extracting vanadium has converted ferrum, molten iron thermometric is 1280 DEG C, and thermometric completes to drop oxygen rifle afterwards and blows, omnidistance
Oxygen flux control is at 3.0Nm3/ t.min, bottom blowing nitrogen intensity presses 0.2Nm3/ t.min controls；Stone is added while starting blowing
Ash controls slag dual alkalinity about 1.7；Before blowing, the above 20mm in benchmark rifle position is pressed in 2min rifle position；Add subsequently after blowing 2min
Entering iron scale, the amount of iron scale is controlled by 20kg/tFe, and oxygen rifle drops to benchmark rifle position simultaneously；2min before finishing blowing
Control of lance position is to the above 40mm in benchmark rifle position；Half steel and vanadium slag is gone out after finishing blowing.
In molten iron, content of vanadium is 0.302%, and phosphorus content is 0.081%, and after finishing blowing, half steel content of vanadium is 0.032%,
Phosphorus content is 0.027%, half steel temperature 1395 DEG C, vanadium slag TFe 14.51%.
Embodiment 3
After 200t converter extracting vanadium has converted ferrum, molten iron thermometric is 1250 DEG C, and thermometric completes to drop oxygen rifle afterwards and blows, omnidistance
Oxygen flux control is at 2Nm3/ t.min, bottom blowing nitrogen intensity presses 0.4Nm3/ t.min controls；Calx is added while starting blowing
Control slag dual alkalinity about 1.7；Before blowing, the above 30mm in benchmark rifle position is pressed in 2min rifle position；It is subsequently added after blowing 2min
Iron scale, the amount of iron scale is controlled by 15kg/tFe, and oxygen rifle drops to benchmark rifle position simultaneously；2min oxygen before finishing blowing
Rifle rifle position controls to the above 50mm in benchmark rifle position；Half steel and vanadium slag is gone out after finishing blowing.
In molten iron, content of vanadium is 0.386%, and phosphorus content is 0.061%, and after finishing blowing, half steel content of vanadium is 0.046%,
Phosphorus content is 0.030%, half steel temperature 1392 DEG C, vanadium slag TFe 14.17%.
Claims (4)
1. vanadium-bearing hot metal method of Simultaneous Oxidation separation of phosphorus vanadium in converter, it is characterised in that: comprise the steps:
After A, converter extracting vanadium have converted ferrum, fall oxygen rifle blows, and whole-process control oxygen flow is 1.5～3.0Nm3/ t.min, bottom blowing
Nitrogen intensity is 0.2～0.4Nm3/t.min；
B, blowing are initially added into Calx, and before blowing, 2min presses control rifle position, more than benchmark rifle position 10～30mm；After blowing 1～2min
Add iron scale or other high oxides-containing iron；Press benchmark rifle position after blowing 2min and control rifle position；Before finishing blowing, 2min presses
It is more than benchmark rifle position that 30～50mm control rifle position；
Half steel and vanadium slag is gone out after C, finishing blowing；
Wherein, in step B, the addition of described Calx is 1.4～1.7 for making slag dual alkalinity；Described iron scale or its
Its high oxides-containing iron addition is 15～25kg/tFe.
Vanadium-bearing hot metal the most according to claim 1 is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter, it is characterised in that: step
In rapid B, other high oxides-containing iron described is any one in grade ＞ 55% iron mine, pellet or sintering deposit.
Vanadium-bearing hot metal the most according to claim 1 is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter, it is characterised in that: step
In rapid B, blowing total time is 5～7min.
Vanadium-bearing hot metal the most according to claim 1 is the method for Simultaneous Oxidation separation of phosphorus vanadium in converter, it is characterised in that: institute
After stating finishing blowing, half steel temperature is 1350～1400 DEG C.