CN106242393A - 一种c25混凝土配制方法 - Google Patents
一种c25混凝土配制方法 Download PDFInfo
- Publication number
- CN106242393A CN106242393A CN201610586542.0A CN201610586542A CN106242393A CN 106242393 A CN106242393 A CN 106242393A CN 201610586542 A CN201610586542 A CN 201610586542A CN 106242393 A CN106242393 A CN 106242393A
- Authority
- CN
- China
- Prior art keywords
- concrete
- formulating method
- sand
- water
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种C25混凝土配制方法,所述的原材料包括水泥、砂、石子、减水剂、粉煤灰和水,其每立方米的质量比是:240:795:1090:4.3:60:190,高性能C25混凝土凝结硬化后,结构密实,孔隙率低,强度高,并且不易产生裂缝,具有优异的抗渗性能,适用于乡村公路和广场。
Description
技术领域
本发明涉及一种C25混凝土配制方法。
背景技术
混凝土具有原料丰富,价格低廉,生产工艺简单的特点,因而使其用量越来越大。同时混凝土还具有抗压强度高,耐久性好,强度等级范围宽等特点。这些特点使其使用范围十分广泛,不仅在各种土木工程中使用,就是造船业,机械工业,海洋的开发,地热工程等,混凝土也是重要的材料。
混凝土是一种充满生命力的建筑材料。随着混凝土组成材料的不断发展,人们对材料复合技术认识不断提高。对混凝土的性能要求不仅仅局限于抗压强度,而是在立足强度的基础上,更加注重混凝土的耐久性、变形性能等综合指标的平衡和协调。混凝土各项性能指标的要求比以前更明确、细化和具体。同时,建筑设备水平的提升,新型施工工艺的不断涌现和推广,使混凝土技术适应了不同的设计、施工和使用要求,发展很快。
发明内容
本发明的目的是提供一种C25混凝土配制方法。
本发明采用的技术方案是:一种C25混凝土配制方法,所述的原材料包括水泥、砂、石子、减水剂、粉煤灰和水,其每立方米的质量比是:240:795:1090:4.3:60:190。
作为本发明的进一步改进,砂的含水率是5.4%。
本发明的有益效果是:高性能C25混凝土凝结硬化后,结构密实,孔隙率低,强度高,并且不易产生裂缝,具有优异的抗渗性能,适用于乡村公路和广场。
具体实施方式
一种C25混凝土配制方法,所述的原材料包括水泥、砂、石子、减水剂、粉煤灰和水,其每立方米的质量比是:240:795:1090:4.3:60:190,砂的含水率是5.4%。
以上对本发明的实施方式作了说明,但是本发明不限于上述实施方式,在所属技术领域普通技术人员所具备的知识范围内,还可以在不脱离本发明宗旨的前提下做出各种变化。
Claims (2)
1.一种C25混凝土配制方法,其特征是:所述的原材料包括水泥、砂、石子、减水剂、粉煤灰和水,其每立方米的质量比是:240:795:1090:4.3:60:190。
2.根据权利要求1所述的一种C25混凝土配制方法,其特征是所述的砂的含水率是5.4%。