CN106240991B - A kind of high intensity aviation case PE drawer preparation method and its product - Google Patents
A kind of high intensity aviation case PE drawer preparation method and its product Download PDFInfo
- Publication number
- CN106240991B CN106240991B CN201610671042.7A CN201610671042A CN106240991B CN 106240991 B CN106240991 B CN 106240991B CN 201610671042 A CN201610671042 A CN 201610671042A CN 106240991 B CN106240991 B CN 106240991B
- Authority
- CN
- China
- Prior art keywords
- drawer
- storage box
- plate
- preparation
- aviation case
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of high-intensitive aviation case PE drawer, match with the pallet storage box used including the pallet that is prepared by modified polyethylene material and by pulling slide rail component.Invention additionally discloses a kind of preparation methods of high-intensitive aviation case PE drawer.Using polyethylene as primary raw material, by be added polyolefin elastomer with it is polythene blending modified, further increase polyethylene wearproof, heatproof, corrosion-resistant, UV resistant, ageing-resistant performance, modified resin stretched intensity can achieve 24Mpa, elongation at break reaches 500%, and impact strength reaches 25kj/m2, heat distortion temperature reaches 140 DEG C.A kind of modified polyethylene material is finally obtained, high-intensitive drawer is prepared by the modified polyethylene material.
Description
Technical field
The present invention relates to a kind of aviation case drawers, and in particular to a kind of high intensity aviation case PE drawer preparation method and its system
Product.
Background technique
Currently, 19 inch in width cabinet aviation cases have become the mainstream of the equipment installation of audio-video industry, due to storage
Drawer is needed to configure if correlative (such as sundries accessory etc.), but drawer matched at present is all metal drawer or wooden
Drawer, due to metal drawer, the heavier-weight of wooden drawer, flowing use will increase overall weight, cause transportation cost height and
It is more heavy;Moisture resistance, corrosion resistance is more general, and fire line is poor;Drawer inner wall must paste cotton, could effective protection valuables
Part, such as microphone, instrument;Environmental-protecting performance is relatively difficult to achieve;Certain use is caused to limit to, it cannot comprehensive embodiment convenience
Property.
Summary of the invention
In view of the above deficiencies, the purpose of the present invention is to provide a kind of high-intensitive aviation case PE drawer preparation method and its systems
Product, the present invention, as primary raw material, improve the comprehensive mechanical property of polyethylene compound system by blend modification technology using polyethylene
Can, and a kind of modified polyethylene material is finally obtained, high-intensitive drawer is prepared by the modified polyethylene material.
The technical scheme adopted by the invention to achieve the purpose is as follows:
A kind of preparation method of high intensity aviation case PE drawer, comprising the following steps:
(1) raw material of the following parts by weight of preparation: 65~75 parts of high-density polyethylene resin, polyolefin elastomer 10~15
Part, 2~3 parts of stabilizer, 3~5 parts of anti-staining agent;
(2) high-density polyethylene resin, polyolefin elastomer, stabilizer, anti-staining agent high-speed mixer is added to mix
Mutually uniformly, it and is stirred;
(3) mixed each component is added to extrusion mixing, wire drawing and pelletizing is carried out in extruder, modified poly- second is made
Alkene particle;
(4) modified poly ethylene particle is subjected to crosslinking with radiation processing;
(5) by crosslinking with radiation, treated that modified poly ethylene particle is added to injection molding machine, and temperature control is arranged on injection molding machine
System processed controls injection mold temperature, and mold temperature is 30 DEG C~90 DEG C, under the conditions of melt temperature is 210~280 DEG C, to changing
Property polyethylene particle melting after carry out injection molding, be made semi-finished product;
(6) semi-finished product are transferred to press machine, high pressure shape is carried out to semi-finished product according to required appearance profile, size, point
It does not prepare and obtains drawer tray and the drawer storage box used that matches with the pallet.
It is further improved, further includes following steps:
(7) drawer tray after molding and drawer storage box are gone into hot press, to drawer tray and drawer storage box
One PVC protective film of hot pressing on surface, the PVC protection for occurring residue glue, ghost defect on surface can be prevented by forming one on the surface thereof
Layer.
It is further improved, step (2) is further comprising the steps of:
(2.1) preparation modifying agent, modifying agent is added in blender, to high-density polyethylene resin and polyolefin elastic
Body is pre-processed, its surface compatibility is improved, and is prevented and air reaction, and high-density polyethylene resin and polyolefin elastic are reinforced
Binding force between body;
(2.2) preparation brightener, brightener is added in blender, and to high-density polyethylene resin, polyolefin bullet
Property body pre-processed, improve its clean surface, nonpolarity, remove impurity;
It is further improved, step (3) is further comprising the steps of:
(3.1) preparation carbon black and SiO2Nanoparticle, by carbon black and SiO2Nanoparticle is uniformly adhered in the form of misty sprinkling
On polyethylene particle surface, the hydrophobic stain resistant surface layer of oleophobic is formed.
It is further improved, modifying agent is nonionic surface active agent;The brightener is by acrylic acid, acrylic acid
The aqueous brightener that ester, styrene monomer, polydimethylsiloxane, lauryl sodium sulfate, potassium peroxydisulfate form.
Further, step (4) is further comprising the steps of: the crosslinking with radiation processing is Co 60 treatment with irradiation or is infrared ray
Radiation treatment is handled for electron accelerator.
A kind of high intensity aviation case PE drawer, including the pallet being prepared by modified polyethylene material and passes through pull
Slide track component matches the storage box used with the pallet.
Further, pallet includes top plate, back plate, left plate, right side plate and by top plate, back plate, left plate, right side plate structure
At one for accommodating the storage space of storage box;The pallet top plate, which has to outwardly protrude, to distribute as net shape in top plate table
For reinforcing the reinforcing rib of bottom plate mechanical strength on face;
Storage box includes bottom plate and the foreboard for being disposed around bottom plate surrounding, back plate, left plate and right side plate, wherein institute
It states storing box plate and has to outwardly protrude and distribute as net shape for reinforcing the reinforcing rib of bottom plate mechanical strength on backplate surface,
The top edge of the storage box left plate and right side plate, which is equipped with, hangs side;The storage box foreboard is equipped with door-plate, the door-plate tool
Outwardly convex be in that " [distribution of " shape is on the surface thereof for reinforcing the reinforcing rib of bottom plate mechanical strength out.
It is further improved, further includes strengthening interior mesh sheet, mesh sheet is built in the corner position of pallet and storage box in the reinforcing
It sets, increases it by angular position structural strength
It is further improved, the medial surface of pallet and storage box is all covered with an electro-magnetic screen layer, the electro-magnetic screen layer
With a thickness of 10 μm~20 μm;The outer surface of the pallet and storage box is all covered with a PVC protective layer, the PVC protective layer
With a thickness of 2 μm~5 μm.
The invention has the benefit that the preparation method of high intensity aviation case PE drawer provided by the invention, using poly- second
Alkene as primary raw material, by be added polyolefin elastomer with it is polythene blending modified, further increase polyethylene wearproof, resistance to
Warm, corrosion-resistant, UV resistant, ageing-resistant performance, modified resin stretched intensity can achieve 24Mpa, and elongation at break reaches
To 500%, impact strength reaches 25kj/m2, heat distortion temperature reaches 140 DEG C.A kind of modified polyethylene material is finally obtained, is led to
It crosses the modified polyethylene material and prepares high-intensitive drawer.
This preparation method in stock preparation process also by being added modifying agent and brightener, to high-density polyethylene resin
It is modified processing and surface impurity processing with polyolefin elastomer, the substances such as oxide, the dross on surface is removed, increases surface
Glossiness, improve the surface smoothness of product, enhance its surface adhesion force;
This preparation method in stock preparation process also by being added carbon black and SiO2Nanoparticle, in the form of misty sprinkling
It is uniformly attached to polyethylene particle surface, the hydrophobic stain resistant surface layer of oleophobic is formed, makes it have the hydrophobic contaminated resistance of oleophobic
Meanwhile the transparency also with higher, it is able to maintain original color of product surface, and the fine and smooth hand of product can be further increased
Sense.
This preparation method also by one PVC protective film of hot pressing on the surface to this product drawer tray and drawer storage box,
Make formation one on its surface that can prevent the PVC protective layer for occurring residue glue, ghost defect on surface.
High intensity aviation case PE drawer provided by the invention, including the pallet that is prepared by modified polyethylene material and
Matched with the pallet storage box used by pulling slide rail component;Wherein the pallet has to outwardly protrude and distribute as net shape
For reinforcing the reinforcing rib of mechanical strength on top board surface;And the storing box plate has and outwardly protrudes and distribute as net shape
For reinforcing the reinforcing rib of bottom plate mechanical strength on backplate surface, the top edge of storage box left plate and right side plate, which is equipped with, is hung
Side;Storage box foreboard is equipped with door-plate, and door-plate, which has, to be outwardly protruded in " [distribution of " shape is mechanical strong for reinforcing bottom plate on the surface thereof
The reinforcing rib of degree;By above-mentioned layout, it can effectively mitigate the weight of integrating cabinet aviation case, have high intensity, it is corrosion-resistant, it is moisture-proof
It is antifreeze, the comprehensive performances such as fire protection flame retarding.
This high intensity aviation case PE drawer, further include be built in pallet and storage box angular position it is strong for increasing structure
Mesh sheet in the reinforcing of degree.The medial surface of pallet and storage box is all covered with an electro-magnetic screen layer, the increasable electricity on medial surface
Magnetic masking layer avoids the inside and outside electromagnetic interference in the course of work.The outer surface uniform fold of pallet and storage box has one
PVC protective layer makes formation one on its surface that can prevent the PVC protective layer for occurring residue glue, ghost defect on surface.
In order to explain the structural features and functions of the invention more clearly, come with reference to the accompanying drawing with specific embodiment to its into
Row is described in detail.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention;
In figure: 1, pallet 2, storage box 3, reinforcing rib 4, reinforcing rib 5, extension side 6, door-plate 7, reinforcing rib.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Refering to fig. 1: a kind of preparation method of high intensity aviation case PE drawer, comprising the following steps:
(1) raw material of the following parts by weight of preparation: 65~75 parts of high-density polyethylene resin, polyolefin elastomer 10~15
Part, 2~3 parts of stabilizer, 3~5 parts of anti-staining agent;
(2) high-density polyethylene resin, polyolefin elastomer, stabilizer, anti-staining agent high-speed mixer is added to mix
Mutually uniformly, it and is stirred;
(3) mixed each component is added to extrusion mixing, wire drawing and pelletizing is carried out in extruder, modified poly- second is made
Alkene particle;
(4) modified poly ethylene particle is subjected to crosslinking with radiation processing;
(5) by crosslinking with radiation, treated that modified poly ethylene particle is added to injection molding machine, and temperature control is arranged on injection molding machine
System processed controls injection mold temperature, and mold temperature is 30 DEG C~90 DEG C, under the conditions of melt temperature is 210~280 DEG C, to changing
Property polyethylene particle melting after carry out injection molding, be made semi-finished product;
(6) semi-finished product are transferred to press machine, high pressure shape is carried out to semi-finished product according to required appearance profile, size, point
It does not prepare and obtains drawer tray and the drawer storage box used that matches with the pallet.
It further includes following steps:
(7) drawer tray after molding and drawer storage box are gone into hot press, to drawer tray and drawer storage box
One PVC protective film of hot pressing on surface, the PVC protection for occurring residue glue, ghost defect on surface can be prevented by forming one on the surface thereof
Layer.
Further, step (2) is further comprising the steps of:
(2.1) preparation modifying agent, modifying agent is added in blender, to high-density polyethylene resin and polyolefin elastic
Body is pre-processed, its surface compatibility is improved, and is prevented and air reaction, and high-density polyethylene resin and polyolefin elastic are reinforced
Binding force between body;
(2.2) preparation brightener, brightener is added in blender, and to high-density polyethylene resin, polyolefin bullet
Property body pre-processed, improve its clean surface, nonpolarity, remove impurity;
Further, step (3) is further comprising the steps of:
(3.1) preparation carbon black and SiO2Nanoparticle, by carbon black and SiO2Nanoparticle is uniformly adhered in the form of misty sprinkling
On polyethylene particle surface, the hydrophobic stain resistant surface layer of oleophobic is formed.
Modifying agent nonionic surface active agent;The brightener be by acrylic acid, acrylate, styrene monomer,
The aqueous brightener that polydimethylsiloxane, lauryl sodium sulfate, potassium peroxydisulfate form.
Further, step (4) is further comprising the steps of: the crosslinking with radiation processing is Co 60 treatment with irradiation or is infrared ray
Radiation treatment is handled for electron accelerator.
The preparation method of high intensity aviation case PE drawer provided by the invention is passed through using polyethylene as primary raw material
Be added polyolefin elastomer with it is polythene blending modified, further increase polyethylene wearproof, heatproof, corrosion-resistant, UV resistant, resistance to
Ageing properties, modified resin stretched intensity can achieve 24Mpa, and elongation at break reaches 500%, and impact strength reaches
25kj/m2, heat distortion temperature reaches 140 DEG C.A kind of modified polyethylene material is finally obtained, the modified polyethylene material system is passed through
Standby drawer high-intensitive out.
This preparation method in stock preparation process also by being added modifying agent and brightener, to high-density polyethylene resin
It is modified processing and surface impurity processing with polyolefin elastomer, the substances such as oxide, the dross on surface is removed, increases surface
Glossiness, improve the surface smoothness of product, enhance its surface adhesion force;
This preparation method in stock preparation process also by being added carbon black and SiO2Nanoparticle, in the form of misty sprinkling
It is uniformly attached to polyethylene particle surface, the hydrophobic stain resistant surface layer of oleophobic is formed, makes it have the hydrophobic contaminated resistance of oleophobic
Meanwhile the transparency also with higher, it is able to maintain original color of product surface, and the fine and smooth hand of product can be further increased
Sense.
This preparation method also by one PVC protective film of hot pressing on the surface to this product drawer tray and drawer storage box,
Make formation one on its surface that can prevent the PVC protective layer for occurring residue glue, ghost defect on surface.
The present embodiment also provides the high-intensitive aviation case PE drawer being prepared by the above method, including by modified poly ethylene
Pallet 1 that material is prepared and matched with the pallet 1 storage box 2 used by pulling slide rail component.Pallet 1 includes
Top plate, back plate, left plate, right side plate and be made of top plate, back plate, left plate, right side plate one are for accommodating storage box 2
Storage space;1 top plate of pallet, which has to outwardly protrude, to distribute as net shape on top board surface for reinforcing 1 mechanical strength of bottom plate
Reinforcing rib 3;
Storage box 2 includes bottom plate and the foreboard, back plate, left plate and the right side plate that are disposed around bottom plate surrounding, wherein storage
2 bottom plate of object box, which has to outwardly protrude, to distribute as net shape on backplate surface for reinforcing the reinforcing rib 4 of bottom plate mechanical strength, storage
The top edge of 2 left plate of object box and right side plate, which is equipped with, hangs side 5;2 foreboard of storage box is equipped with door-plate 6, and door-plate 6, which has, to be outwardly protruded
In " [distribution of " shape is on the surface thereof for reinforcing the reinforcing rib 7 of mechanical strength.
By above-mentioned layout, it can effectively mitigate the weight of integrating cabinet aviation case, have high intensity, it is corrosion-resistant, it is moisture-proof anti-
Freeze, the comprehensive performances such as fire protection flame retarding.
It is further improved, this high intensity aviation case PE drawer, further includes the angular position for being built in pallet 1 and storage box 2
Mesh sheet in reinforcing for increasing structural strength.The medial surface of pallet 1 and storage box 2 is all covered with an electro-magnetic screen layer, electromagnetism
Shielded layer with a thickness of 10 μm~20 μm;The increasable electro-magnetic screen layer on medial surface, avoids the inside and outside in the course of work
Electromagnetic interference.The outer surface uniform fold of pallet 1 and storage box 2 has a PVC protective layer, PVC protective film with a thickness of 2 μm
~5 μm.Make formation one on its surface that can prevent the PVC protective layer for occurring residue glue, ghost defect on surface.
The above described is only a preferred embodiment of the present invention, being not intended to limit the present invention in any form.Appoint
What those skilled in the art, without departing from the scope of the technical proposal of the invention, all using the side of the disclosure above
Method and technology contents make many possible changes and modifications to technical solution of the present invention, or are revised as the equivalent reality of equivalent variations
Apply example.Therefore anything that does not depart from the technical scheme of the invention, equivalent change made by shape according to the present invention, construction and principle
Change, should all be covered by protection scope of the present invention.
Claims (4)
1. a kind of preparation method of high intensity aviation case PE drawer, which is characterized in that itself the following steps are included:
(1) raw material of the following parts by weight of preparation: 65~75 parts of high-density polyethylene resin, 10~15 parts of polyolefin elastomer, surely
Determine 2~3 parts of agent, 3~5 parts of anti-staining agent;
(2) high-density polyethylene resin, polyolefin elastomer, stabilizer, anti-staining agent are added to high-speed mixer and be uniformly mixed;
The step (2) is further comprising the steps of:
(2.1) preparation modifying agent, modifying agent is added in blender, to high-density polyethylene resin and polyolefin elastomer into
Row pretreatment, improves its surface compatibility, prevents and air reaction, reinforce high-density polyethylene resin and polyolefin elastomer it
Between binding force;The modifying agent is nonionic surface active agent;
(2.2) preparation brightener, brightener is added in blender, and to high-density polyethylene resin, polyolefin elastomer
It is pre-processed, improves its clean surface, nonpolarity, remove impurity;The brightener is by acrylic acid, acrylate, benzene
The aqueous brightener that vinyl monomer, polydimethylsiloxane, lauryl sodium sulfate, potassium peroxydisulfate form;
(3) mixed each component is added to extrusion mixing, wire drawing and pelletizing is carried out in extruder, modified poly ethylene is made
Grain;The step (3) is further comprising the steps of:
(3.1) preparation carbon black and SiO2Nanoparticle, by carbon black and SiO2Nanoparticle is uniformly attached to poly- in the form of misty sprinkling
Ethylene particle surface forms the hydrophobic stain resistant surface layer of oleophobic;
(4) modified poly ethylene particle is subjected to crosslinking with radiation processing;The step (4) is further comprising the steps of: the radiation is handed over
Connection processing be Co 60 treatment with irradiation or be infrared radiation processing or be electron accelerator handle;
(5) by crosslinking with radiation, treated that modified poly ethylene particle is added to injection molding machine, laggard to modified poly ethylene particle fusion
Semi-finished product are made in row injection molding;
(6) semi-finished product are transferred to press machine, high pressure shape is carried out to semi-finished product according to required appearance profile, size, is made respectively
It is standby to obtain drawer tray and the drawer storage box used that matches with the drawer tray;
(7) drawer tray after molding and drawer storage box are gone into hot press, to the surface of drawer tray and drawer storage box
Upper one PVC protective film of hot pressing makes formation one on its surface that can prevent the PVC protective layer for occurring residue glue, ghost defect on surface.
2. a kind of high-intensitive aviation case PE drawer of the preparation of preparation method according to claim 1, which is characterized in that including by
What drawer tray that modified polyethylene material is prepared and being matched by pulling slide rail component with the drawer tray used
Drawer storage box;The drawer tray includes top plate, back plate, left plate, right side plate and by top plate, back plate, left plate, right side
One of plate composition is for accommodating the storage space of drawer storage box;The drawer tray top plate is grid-shaped with outwardly protruding
It is distributed on top board surface for reinforcing the reinforcing rib of bottom plate mechanical strength;The drawer storage box includes bottom plate and is disposed around
Foreboard, back plate, left plate and the right side plate of bottom plate surrounding, wherein the drawer storage box bottom plate, which has, to be outwardly protruded in net
Trellis is distributed on backplate surface for reinforcing the reinforcing rib of bottom plate mechanical strength, the drawer storage box left plate and right side plate
Top edge be equipped with hang side;The drawer storage box foreboard is equipped with door-plate, and the door-plate, which has, to be outwardly protruded in " [" shape distribution
On the surface thereof for reinforcing the reinforcing rib of bottom plate mechanical strength.
3. high-intensitive aviation case PE drawer according to claim 2, which is characterized in that it further includes strengthening interior mesh sheet, this is strong
Mesh sheet is built on the angular position of drawer tray and drawer storage box in changing, and increases it by angular position structural strength.
4. high-intensitive aviation case PE drawer according to claim 2, which is characterized in that the drawer tray and drawer storage box
Medial surface be all covered with an electro-magnetic screen layer, the electro-magnetic screen layer with a thickness of 10 μm~20 μm;The drawer tray and
The outer surface of drawer storage box is all covered with a PVC protective layer, the PVC protective layer with a thickness of 2 μm~5 μm.