CN106223014A - A kind of production technology of nano-antibacterial knitted dress - Google Patents
A kind of production technology of nano-antibacterial knitted dress Download PDFInfo
- Publication number
- CN106223014A CN106223014A CN201610642626.1A CN201610642626A CN106223014A CN 106223014 A CN106223014 A CN 106223014A CN 201610642626 A CN201610642626 A CN 201610642626A CN 106223014 A CN106223014 A CN 106223014A
- Authority
- CN
- China
- Prior art keywords
- nano
- knitted dress
- antibacterial
- dress
- knitted
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the production technology of a kind of nano-antibacterial knitted dress, comprise the following steps that: a, first the knitted dress woven is put in container, adding nano-antibacterial solution to soak, immersion treatment is after 12 hours, and the consumption of nano-antibacterial solution is 60 70 times of knitted dress;B, the knitted dress taking-up will soaked in step a, be preliminary drying 1.5 2.5 minutes between 40 50 DEG C in temperature, then bakee 4.5 5 minutes at temperature is 120 130 DEG C, make nano anti-biotic material be adsorbed onto in knitted dress;C, the clothing carrying out in step b having bakeed are scouringed and bleaching, finally carry out dyeing sizing, obtain nano-antibacterial knitted dress.The invention has the beneficial effects as follows: preparation technology is simple, use nano-antibacterial solution, strong with the adhesion of knitted dress, resistance to rinsing, there is the antibiotic property of often effect, human body is free from side effects, free from environmental pollution, safety is good, can improve the quality of knitted dress.
Description
Technical field
The present invention relates to the production technology of a kind of knitted dress, particularly relate to the production work of a kind of nano-antibacterial knitted dress
Skill.
Background technology
The special loop construction of weft-knitted fabric makes product have a good breathability, and with good springiness and soft and
Enjoying the hobby of consumer, along with the development of society, the raising of living standards of the people, the requirement to weaving face fabric improves day by day,
Particularly society, pursues that nature is comfortable has become a kind of fashion, and the natural fibre product such as cotton textiles, hair, fiber crops, silk is increasingly subject to people
Favor.
Notification number is a kind of nano antifouling antimicrobial coating textile and the processing technique of clothing of CN1552973, describes
A kind of antifouling and antibiosis technology of clothing, but this technology does not add antibacterial finishing agent, and sterilizing is led to the most in process of production
Being irradiated usually through uviol lamp, its sterilization effect is the best, it is impossible to meet demand.
Therefore, for solving the problems referred to above, a kind of new technical scheme of special offer.
Summary of the invention
The present invention provides the production technology of a kind of nano-antibacterial knitted dress.
The technical solution used in the present invention is:
The production technology of a kind of nano-antibacterial knitted dress, comprises the following steps that:
A, first the knitted dress woven is put in container, add nano-antibacterial solution and soak, immersion treatment 1-2 hour
After, the consumption of nano-antibacterial solution is 60-70 times of knitted dress;
B, the knitted dress taking-up will soaked in step a, preliminary drying 1.5-2.5 minute between temperature is 40-50 DEG C, then
Temperature bakees 4.5-5 minute at being 120-130 DEG C, makes nano anti-biotic material be adsorbed onto in knitted dress;
C, the clothing carrying out in step b having bakeed are scouringed and bleaching, finally carry out dyeing sizing, obtain nano-antibacterial knitted clothes
Dress.
Preferably, described nano-antibacterial solution is mixed by nanometer silver, titania powder and ethanol, described nanometer
Mass ratio silver-colored, between titania powder and ethanol is 1:0.5:3.
Preferably, solvent used in processing of scouringing and bleaching in described step c includes hydrogen peroxide, sodium silicate and refining agent, its
Middle hydrogen peroxide is 16-18mL/L, sodium silicate 4-5g/L, refining agent 1-2g/L, is controlled by pH value at 9-10, and temperature is 68-72 DEG C
Under carry out bleach 25-30min.
Preferably, the setting process in described step c is for pressing sizing, during sizing with vapour iron at 120-130 DEG C
Between be 0.5-1 minute.
The invention has the beneficial effects as follows: preparation technology is simple, use nano-antibacterial solution, with the adhesion of knitted dress
By force, resistance to rinsing, there is the antibiotic property of often effect, human body is free from side effects, free from environmental pollution, safety is good, can improve knitted clothes
The quality of dress.
Detailed description of the invention
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, this embodiment
It is only used for explaining the present invention, is not intended that the restriction to protection scope of the present invention.
Embodiment 1
The production technology of a kind of nano-antibacterial knitted dress, comprises the following steps that:
A, first the knitted dress woven is put in container, add nano-antibacterial solution and soak, immersion treatment 1 hour
After, the consumption of nano-antibacterial solution is 60 times of knitted dress, and nano-antibacterial solution is by nanometer silver, titania powder and ethanol
Mixing, the mass ratio between nanometer silver, titania powder and ethanol is 1:0.5:3;
B, the knitted dress taking-up will soaked in step a, be preliminary drying 1.5 minutes between 40 DEG C in temperature, then in temperature be
Bakee 4.5 minutes at 120 DEG C, make nano anti-biotic material be adsorbed onto in knitted dress;
C, being scouringed and bleaching by the clothing carrying out in step b having bakeed, solvent used in processing of scouringing and bleaching includes hydrogen peroxide, silicic acid
Sodium and refining agent, wherein hydrogen peroxide is 16mL/L, sodium silicate 4g/L, refining agent 1g/L, is controlled by pH value 9, and temperature is 68 DEG C
Under carry out bleach 25min, finally carrying out dyeing sizing, at 120 DEG C, press sizing with vapour iron, shaping time is 0.5 point
Clock, obtains nano-antibacterial knitted dress.
Embodiment 2
The production technology of a kind of nano-antibacterial knitted dress, comprises the following steps that:
A, first the knitted dress woven is put in container, add nano-antibacterial solution and soak, immersion treatment 1.5 hours
After, the consumption of nano-antibacterial solution is 65 times of knitted dress, and nano-antibacterial solution is by nanometer silver, titania powder and ethanol
Mixing, the mass ratio between nanometer silver, titania powder and ethanol is 1:0.5:3;
B, the knitted dress taking-up will soaked in step a, be preliminary drying 2 minutes between 45 DEG C in temperature, then be 125 in temperature
Bakee 4.5 minutes at DEG C, make nano anti-biotic material be adsorbed onto in knitted dress;
C, being scouringed and bleaching by the clothing carrying out in step b having bakeed, solvent used in processing of scouringing and bleaching includes hydrogen peroxide, silicic acid
Sodium and refining agent, wherein hydrogen peroxide is 17mL/L, sodium silicate 4.5g/L, refining agent 1.5g/L, is controlled by pH value 9.5, temperature
Being to carry out bleaching 27min at 70 DEG C, finally carry out dyeing sizing, press sizing with vapour iron at 125 DEG C, shaping time is
0.5 minute, obtain nano-antibacterial knitted dress.
Embodiment 3
The production technology of a kind of nano-antibacterial knitted dress, comprises the following steps that:
A, first the knitted dress woven is put in container, add nano-antibacterial solution and soak, immersion treatment 2 hours
After, the consumption of nano-antibacterial solution is 70 times of knitted dress, and nano-antibacterial solution is by nanometer silver, titania powder and ethanol
Mixing, the mass ratio between nanometer silver, titania powder and ethanol is 1:0.5:3;
B, the knitted dress taking-up will soaked in step a, be preliminary drying 2.5 minutes between 50 DEG C in temperature, then in temperature be
Bakee 5 minutes at 130 DEG C, make nano anti-biotic material be adsorbed onto in knitted dress;
C, being scouringed and bleaching by the clothing carrying out in step b having bakeed, solvent used in processing of scouringing and bleaching includes hydrogen peroxide, silicic acid
Sodium and refining agent, wherein hydrogen peroxide is 18mL/L, sodium silicate 5g/L, refining agent 2g/L, is controlled by pH value 10, and temperature is 72 DEG C
Under carry out bleach 30min, finally carrying out dyeing sizing, at 130 DEG C, press sizing with vapour iron, shaping time is 1 minute,
Obtain nano-antibacterial knitted dress.
The invention has the beneficial effects as follows: preparation technology is simple, use nano-antibacterial solution, with the adhesion of knitted dress
By force, resistance to rinsing, there is the antibiotic property of often effect, human body is free from side effects, free from environmental pollution, safety is good, can improve knitted clothes
The quality of dress.
The above, be only presently preferred embodiments of the present invention, is not the limit that the present invention makees any other form
System, and any amendment made according to the technical spirit of the present invention or equivalent variations, still fall within present invention model required for protection
Enclose.
Claims (4)
1. the production technology of a nano-antibacterial knitted dress, it is characterised in that: comprise the following steps that:
A, first the knitted dress woven is put in container, add nano-antibacterial solution and soak, immersion treatment 1-2 hour
After, the consumption of nano-antibacterial solution is 60-70 times of knitted dress;
B, the knitted dress taking-up will soaked in step a, preliminary drying 1.5-2.5 minute between temperature is 40-50 DEG C, then
Temperature bakees 4.5-5 minute at being 120-130 DEG C, makes nano anti-biotic material be adsorbed onto in knitted dress;
C, the clothing carrying out in step b having bakeed are scouringed and bleaching, finally carry out dyeing sizing, obtain nano-antibacterial knitted clothes
Dress.
The production technology of a kind of nano-antibacterial knitted dress the most according to claim 1, it is characterised in that: described nanometer resists
Bacterium solution is mixed by nanometer silver, titania powder and ethanol, between described nanometer silver, titania powder and ethanol
Mass ratio is 1:0.5:3.
The production technology of a kind of nano-antibacterial knitted dress the most according to claim 1, it is characterised in that: described step c
In scouring and bleaching process in used solvent include hydrogen peroxide, sodium silicate and refining agent, wherein hydrogen peroxide is 16-18mL/L, silicic acid
Sodium 4-5g/L, refining agent 1-2g/L, control pH value at 9-10, and temperature carries out at being 68-72 DEG C bleaching 25-30min.
The production technology of a kind of nano-antibacterial knitted dress the most according to claim 1, it is characterised in that: described step c
In setting process for pressing sizing at 120-130 DEG C with vapour iron, shaping time is 0.5-1 minute.