CN106222587A - A kind of automotive axle and preparation method thereof - Google Patents
A kind of automotive axle and preparation method thereof Download PDFInfo
- Publication number
- CN106222587A CN106222587A CN201610697250.4A CN201610697250A CN106222587A CN 106222587 A CN106222587 A CN 106222587A CN 201610697250 A CN201610697250 A CN 201610697250A CN 106222587 A CN106222587 A CN 106222587A
- Authority
- CN
- China
- Prior art keywords
- parts
- strand
- raw material
- preparation
- hot rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of automotive axle and preparation method thereof, the raw material of following parts by weight prepare: 59 parts of carbon, 47 parts of manganese, 25 parts of nickel, ferrum 9 11 parts, silicon metal 8 10 parts, 26 parts of carbon fiber, calcium silicide 58 parts, zirconium oxide 37 parts, titanium dioxide 69 parts and clay 35 parts.The invention has the beneficial effects as follows: composition proportion is scientific and reasonable, save the cost of raw material, the automotive axle made is durable in use, solves the technical problem that compression capability in the middle part of prior art automobile axle housing is low and service life is short, is the material of a kind of preferable automobile axle housing.
Description
Technical field
The present invention relates to automobile automotive field, be specifically related to a kind of automotive axle and preparation method thereof.
Background technology
Automotive axle is one of vehicle key parts, and it is the ingredient of power train, is also the important of running gear
Ingredient.Automobile axle housing, as the main part of vehicle bridge, is to ensure that the properly functioning critical component with service life of automobile, institute
So that its mechanical strength, rigidity and fatigue performance etc. are all had higher requirements.Axle housing production cost accounts for driving axis basis
30 percent.Particularly heavy-duty car is operationally severe due to road and operating mode, and axle housing subjects strong shock loading,
Higher to the quality requirements of axle housing.Plate weldering axle housing is owing to being limited by self structure and welding procedure, the most easily
Deform, the phenomenon such as leakage of oil and crackle occurs, it is difficult to meet the job demand of heavy-duty car.To this end, in order to meet automobile
The needs that bearing capacity increases, the especially demand of heavy-duty car, need a kind of cast steel material of research and development, meet the need of automotive axle
Want, certain economic and social benefit can be obtained simultaneously.The intensity hardness of as cast condition cast steel is the lowest, impact is poor, it is impossible to full
The use requirement of foot material, it is necessary to carry out suitable heat treatment, to guarantee the safety applications of high-strength toughness low alloy cast steel, profit simultaneously
Excavate cast steel potential by Technology for Heating Processing, expand its range of application.
Summary of the invention
In sum, in order to overcome the deficiencies in the prior art, the technical problem to be solved is to provide a kind of vapour
Car vehicle bridge and preparation method thereof.
The technical scheme is that a kind of automotive axle, former by following parts by weight
Material prepare: carbon 5-9 part, manganese 4-7 part, nickel 2-5 part, ferrum 9-11 part, silicon metal 8-10 part, carbon fiber 2-6 part, calcium silicide 5-8 part,
Zirconium oxide 3-7 part, titanium dioxide 6-9 part and clay 3-5 part.
The preparation method of a kind of automotive axle, is prepared by the steps:
(1) each raw material of following parts by weight is weighed respectively: carbon 5-9 part, manganese 4-7 part, nickel 2-5 part, ferrum 9-11 part, crystallization
Silicon 8-10 part, carbon fiber 2-6 part, calcium silicide 5-8 part, zirconium oxide 3-7 part, titanium dioxide 6-9 part and clay 3-5 part;
(2) raw material step (1) weighed obtains strand after smelting;
(3) strand is put into heating furnace to heat;
(4) strand after heating is put into milling train to roll, it is thus achieved that hot rolled plate;
(5) hot rolled plate is cooled down;
(6) hot rolled plate after cooling is batched, it is thus achieved that steel plate finished product.
Further, described strand is put into heating furnace and heats, including: described strand is heated in described heating furnace
To 1500-2000 DEG C;
Described strand is incubated after being heated to design temperature, and described temperature retention time controls as more than 200min.
Further, the described strand after heating is put into milling train and rolls, including: described strand is carried out roughing;Institute
Stating and carry out finish rolling after roughing completes, the inlet temperature of described finishing stands controls as 800-900 DEG C, and finishing temperature control is 700-
800℃。
The invention has the beneficial effects as follows: composition proportion is scientific and reasonable, saved the cost of raw material, the automotive axle warp made
The most durable, solve the technical problem that compression capability in the middle part of prior art automobile axle housing is low and service life is short, be a kind of preferable
The material of automobile axle housing.
Detailed description of the invention
Being described principle and the feature of the present invention below in conjunction with instantiation, example is served only for explaining this
Bright, it is not intended to limit the scope of the present invention.
Embodiment 1
The preparation method of a kind of automotive axle, is prepared by the steps:
(1) each raw material of following parts by weight is weighed respectively: 5 parts of carbon, 4 parts of manganese, 2 parts of nickel, ferrum 9 parts, silicon metal 8 parts, carbon
Fiber 2 parts, calcium silicide 5 parts, zirconium oxide 3 parts, titanium dioxide 6 parts and clay 3 parts;
(2) raw material step (1) weighed obtains strand after smelting;
(3) strand is put into heating furnace to heat, including: described strand is heated to 1500 in described heating furnace
℃;Described strand is incubated after being heated to design temperature, and described temperature retention time controls as more than 200min;
(4) strand after heating is put into milling train to roll, it is thus achieved that hot rolled plate, including: described strand is carried out roughing;
Described roughing carries out finish rolling after completing, it is 800 DEG C that the inlet temperature of described finishing stands controls, and finishing temperature control is 700 DEG C;
(5) hot rolled plate is cooled down;
(6) hot rolled plate after cooling is batched, it is thus achieved that steel plate finished product.
Embodiment 2
The preparation method of a kind of automotive axle, is prepared by the steps:
(1) each raw material of following parts by weight is weighed respectively: 7 parts of carbon, 5 parts of manganese, 4 parts of nickel, ferrum 10 parts, silicon metal 9 parts, carbon
Fiber 4 parts, calcium silicide 7 parts, zirconium oxide 5 parts, titanium dioxide 7 parts and clay 4 parts;
(2) raw material step (1) weighed obtains strand after smelting;
(3) strand is put into heating furnace to heat, including: described strand is heated to 1700 in described heating furnace
℃;Described strand is incubated after being heated to design temperature, and described temperature retention time controls as more than 200min;
(4) strand after heating is put into milling train to roll, it is thus achieved that hot rolled plate, including: described strand is carried out roughing;
Described roughing carries out finish rolling after completing, it is 850 DEG C that the inlet temperature of described finishing stands controls, and finishing temperature control is 750 DEG C;
(5) hot rolled plate is cooled down;
(6) hot rolled plate after cooling is batched, it is thus achieved that steel plate finished product.
Embodiment 3
The preparation method of a kind of automotive axle, is prepared by the steps:
(1) weigh each raw material of following parts by weight respectively: 9 parts of carbon, 7 parts of manganese, 5 parts of nickel, ferrum 11 parts, silicon metal 10 parts,
6 parts of carbon fiber, calcium silicide 8 parts, zirconium oxide 7 parts, titanium dioxide 9 parts and clay 5 parts;
(2) raw material step (1) weighed obtains strand after smelting;
(3) strand is put into heating furnace to heat, including: described strand is heated to 2000 in described heating furnace
℃;Described strand is incubated after being heated to design temperature, and described temperature retention time controls as more than 200min;
(4) strand after heating is put into milling train to roll, it is thus achieved that hot rolled plate, including: described strand is carried out roughing;
Described roughing carries out finish rolling after completing, it is 900 DEG C that the inlet temperature of described finishing stands controls, and finishing temperature control is 800 DEG C;
(5) hot rolled plate is cooled down;
(6) hot rolled plate after cooling is batched, it is thus achieved that steel plate finished product.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (4)
1. an automotive axle, it is characterised in that prepared by the raw material of following parts by weight: carbon 5-9 part, manganese 4-7 part, nickel 2-5
Part, ferrum 9-11 part, silicon metal 8-10 part, carbon fiber 2-6 part, calcium silicide 5-8 part, zirconium oxide 3-7 part, titanium dioxide 6-9 part and viscous
Soil 3-5 part.
2. the preparation method of an automotive axle, it is characterised in that prepared by the steps:
(1) each raw material of following parts by weight is weighed respectively: carbon 5-9 part, manganese 4-7 part, nickel 2-5 part, ferrum 9-11 part, silicon metal 8-
10 parts, carbon fiber 2-6 part, calcium silicide 5-8 part, zirconium oxide 3-7 part, titanium dioxide 6-9 part and clay 3-5 part;
(2) raw material step (1) weighed obtains strand after smelting;
(3) strand is put into heating furnace to heat;
(4) strand after heating is put into milling train to roll, it is thus achieved that hot rolled plate;
(5) hot rolled plate is cooled down;
(6) hot rolled plate after cooling is batched, it is thus achieved that steel plate finished product.
Preparation method the most according to claim 2, it is characterised in that described strand is put into heating furnace and heats, bag
Include: described strand is heated to 1500-2000 DEG C in described heating furnace;Described strand is protected after being heated to design temperature
Temperature, described temperature retention time controls as more than 200min.
4. according to the preparation method described in Claims 2 or 3, it is characterised in that the described strand after heating is put into milling train and enters
Row rolling, including: described strand is carried out roughing;Described roughing carries out finish rolling, the inlet temperature of described finishing stands after completing
Controlling as 800-900 DEG C, finishing temperature control is 700-800 DEG C.