CN106221584A - A kind of low VOC clean taste antimicrobial chamber interior trim emulsion paint and preparation method thereof - Google Patents
A kind of low VOC clean taste antimicrobial chamber interior trim emulsion paint and preparation method thereof Download PDFInfo
- Publication number
- CN106221584A CN106221584A CN201610737133.6A CN201610737133A CN106221584A CN 106221584 A CN106221584 A CN 106221584A CN 201610737133 A CN201610737133 A CN 201610737133A CN 106221584 A CN106221584 A CN 106221584A
- Authority
- CN
- China
- Prior art keywords
- agent
- emulsion paint
- emulsion
- interior trim
- chamber interior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of low VOC clean taste antimicrobial chamber interior trim emulsion paint and preparation method thereof, this emulsion paint is to add major part water, hydroxyethyl cellulose and pH adjusting agent in reactor, dispersed with stirring, it is subsequently added into freeze-thaw stabiliser FT100, wetting agent, dispersant and part defoamer, dispersed with stirring, put into titanium dioxide, Kaolin and calcium carbonate again, stir to fineness≤50um, finally put into coalescents COASOL, Tao Shi silver-ion antibiotic emulsion, antifungus agent, antibacterial, thickening agent, remaining water and remaining defoamer, stirring, to obtain final product.The present invention uses Tao Shi silver-ion antibiotic emulsion to be basic emulsion, make the silver ion with polymer complex can be along with ambient humidity self regulation emission levels, to maintain concentration of silver ions long-acting, stable and suitable, effectively kill harmful microorganism, extend the antibacterial timeliness of metope, be difficult to eluting of swiping, and there is self-cleaning function, wall color sustains its quality through age, and more has the active function of self-regeneration.
Description
Technical field
The invention belongs to paint field, relate to a kind of interior decoration emulsion paint, be specifically related to a kind of low VOC clean taste antimicrobial chamber
Interior trim emulsion paint, also relates to the preparation method of this emulsion paint.
Background technology
Along with people are increasingly stronger to the pursuit of healthy clean ecology living environment, new environmental regulation requires increasingly
Strictly, make coating industry the most wilful.The organic volatile of indoor decorative paint release, such as benzene, Tvoc and formaldehyde etc., is to cause
One major reason of indoor pollution so that the emulsion paint with water as diluent is also faced with more challenge.Moist metope
Mould mark is full of stains or spots, and long-term difficulty is removed, and is the hotbed of antibacterial, mycete, more can cause the allergic condition such as skin eczema, asthma.Public environment
The pathogenic bacteria naked eyes that middle circulation is grown cannot be discovered at all, the most out of hand, it is likely that causes fearful infectious disease tide.Additionally by
Constantly making a variation and drug resistance ground strengthens day by day in superbacteria, the threat of the mankind is made academia and media more by it in recent years
More pay close attention to.For protection human health, all circles are devoted to research and develop various new technique and product, make every effort to restrain and the harmful micro-life of prevention
The propagation growth of thing.Although the most also there being some emulsion paints passing through to add sterilization auxiliary agent, it uses the initial stage to antibacterial
Really have and kill and inhibitory action, but along with the constantly variation of antibacterial ground and drug resistance ground strengthen day by day, the sterilization in emulsion paint
Amount of auxiliary is also increasing, and antibacterial gradually loses effect, and the auxiliary agent itself that sterilizes also has certain harm to environment.In view of above-mentioned
The shortcoming of interior decoration paint, the antibacterial interior decoration emulsion paint of research and development health environment-friendly, clean taste is to face the class being badly in need of solving
Topic.
Summary of the invention
The technical problem to be solved is: the raw material existed for above-mentioned prior art interior decoration emulsion paint
The difficult control of safety, the deficiency of the aspect such as the most lasting of bactericidal property, it is provided that a kind of low VOC clean taste antimicrobial chamber interior trim emulsion paint and
Preparation method, by effectively controlling VOC content, selects abnormal smells from the patient antibacterial breast ultralow, that prepare without formaldehyde and APEO antimicrobial emulsion
Shellac varnish, makes metope reach more stable, safe, lasting antibacterial effect.
In order to solve the problems referred to above, the technical solution adopted in the present invention is: a kind of low VOC clean taste antimicrobial chamber interior trim breast
Shellac varnish, this emulsion paint is made up of following substances by weight: the silver-ion antibiotic emulsion 25 of Dow Chemical~32 parts, film forming
Auxiliary agent COASOL 0.8~1.5 parts, hydroxyethyl cellulose 0.3~0.5 part, pH adjusting agent 0.05~0.1 part, freeze-thaw stabiliser
FT-100 0.5~1.0 parts, wetting agent 0.1~0.2 part, dispersant 0.5~1.0 parts, defoamer 0.4~0.6 part, titanium dioxide 20
~25 parts, Kaolin 5~10 parts, calcium carbonate 10~15 parts, antifungus agent 0.2~0.5 part, antibacterial 0.2~0.3 part, thickening agent
0.3~0.6 part and water 21~27 parts.
Above-mentioned pH adjusting agent is selected from BS168 (Wacker Chemical Co., Ltd of Germany), Rheinamin VP195 (Germany's BASF
Company) or AMP95 (DOW chemical company of the U.S.).
Above-mentioned wetting agent selected from BD-405 (DOW chemical company of the U.S.), E9289 (Germany BASF chemical company) or
LCN407 (Clariant chemical company of Germany).
Above-mentioned dispersant is selected from fast easily dispersant (DOW chemical company of the U.S.), 731A (DOW chemical company of the U.S.) or SN-
DISPERSANT5040 (chemical company of Sheng Ruopu section of Japan).
Above-mentioned defoamer is selected from AP7015 (this chemical company of sea name of the U.S.), CF1366 (England Blackburn chemical company)
Or ST2410 (BASF chemical company of Germany).
Above-mentioned antifungus agent selected from 678 (TROY chemical companies of the U.S.), TRYSAN107 (TROY chemical company of the U.S.) or
CF1100 (DOW chemical company of the U.S.).
(Germany's Clariant chemical industry is public selected from LXE (DOW chemical company of the U.S.) or Nipacide CI15HS for above-mentioned antibacterial
Department).
Above-mentioned thickening agent is selected from RHEOLATE420 (this chemical company of sea name of the U.S.), TT-935 (DOW chemical company of the U.S.)
Or DR-180 (DOW chemical company of the U.S.).
Present invention simultaneously provides the preparation method of above-mentioned low VOC clean taste antimicrobial chamber interior trim emulsion paint, the method be prior to
Reactor adds the total consumption of water 80~the water of 85%, hydroxyethyl cellulose and pH adjusting agent, to be not less than turning of 600r/min
Speed disperses at least 8min, is subsequently added into freeze-thaw stabiliser FT100, wetting agent, dispersant and 50~the defoamer of 60% weight, and
Disperse at least 2min with same rotating speed, then put into titanium dioxide, Kaolin and calcium carbonate, divide being not less than the rotating speed of 1000r/min
It is dissipated to fineness≤50um, finally puts into coalescents COASOL, silver-ion antibiotic emulsion, the antifungus agent of Dow Chemical, kill
Microbial inoculum, thickening agent, remaining water and remaining defoamer, stir at least 10min being not less than the rotating speed of 600r/min,.
Preferably, the method is prior to adding the total consumption of water 80~the water of 85%, hydroxyethyl cellulose and pH in reactor
Regulator, the rotating speed with 600~800r/min disperses 8~12min, is subsequently added into freeze-thaw stabiliser FT100, wetting agent, dispersion
Agent and 50~60% defoamer of weight, and disperse 2~3min with the rotating speed of 600~800r/min, then put into titanium dioxide, kaolinite
Soil and calcium carbonate, be dispersed to fineness≤50um with the rotating speed of 1000~1200r/min, finally put into coalescents COASOL, pottery
The silver-ion antibiotic emulsion of family name chemical company, antifungus agent, antibacterial, thickening agent, remaining water and remaining defoamer, with 600
~the rotating speed stirring 10~20min of 800r/min,.
The low VOC clean taste antimicrobial chamber interior trim emulsion paint that the present invention provides is the present inventor through deep theory analysis and anti-
Retrial is tested, and sieve especially has selected the basic emulsion using Tao Shi silver-ion antibiotic emulsion as emulsion paint, with the freeze thawing of Sol dimension Diamond Search
Stabilizer FT-100 is as emulsion paint freeze-thaw stabiliser, with watt gram BS168, Rheinamin VP195 or AMP95 as pH regulator
Agent.The present invention is using Sol dimension freeze-thaw stabiliser FT-100 as emulsion paint freeze-thaw stabiliser, with conventional antifreezing agent (propylene glycol or second
Glycol) compare, without organic volatile, considerably reduce VOC content, and improve the low temperature freeze-thaw resistance property of emulsion paint.
The pH adjusting agent selected, the most effectively controls pH value, product other 2-amino-2-methyl-1-propanol on year-on-year basis itself
Abnormal smells from the patient is lower.The basic emulsion of emulsion paint selects low abnormal smells from the patient, silver-ion antibiotic emulsion without APEO, itself has self-crosslinking performance
Good and low minimum film formation temperature MFT, it is not necessary to be equipped with more coalescents as conventional emulsions, be only equipped with lesser amount of low
The coalescents COASOL of abnormal smells from the patient Diamond Search, and without APEO, therefore prepared emulsion paint has clean taste, the feature of low VOC,
Having reached DB44/T1105-2012 " low VOCs synthetic resin emulsion coating " standard (see table 1), HG/T3950-2007 is " antibacterial
Coating " test result see table 2, is the interior decoration emulsion paint of a kind of zero VOC.
Every Testing index of table 1 product emulsion paint of the present invention
Table 2 emulsion paint of the present invention presses HG/T3950-2007 " antibiotic paint " test result
The low VOC of the one clean taste antimicrobial chamber interior trim emulsion paint that the present invention provides, selected Tao Shi silver-ion antibiotic breast
Liquid is organic silver ion antibacterial emulsion, the organic silver ion emulsion technique of Tao Shi original creation, makes the silver ion energy with polymer complex
Along with ambient humidity self regulation emission levels, to maintain concentration of silver ions long-acting, stable and suitable, effectively kill thin
The harmful microorganisms such as bacterium, superbacteria MRSA, mycete and algae.It is micro-that metope through the process of this antibiotic emulsion paint provides mushroom
The biological environment that cannot replicate survival, had both extended the antibacterial timeliness of metope, is difficult to eluting of swiping, has again self-cleaning function, wall
Color sustains its quality through age, and more has the active function of self-regeneration.
Detailed description of the invention
Below by specific embodiment, the present invention is described further, in order to be more readily understood that the present invention.
But it is important to note that the invention is not restricted to the form described by example below, those skilled in the art is not
In the case of paying creative work, also can design other form easily, the most should be by example given below
It is interpreted as protection scope of the present invention and protection scope of the present invention is limited in given embodiment.
Embodiment 1
The component of emulsion paint of the present invention is calculated as by weight: Tao Shi silver-ion antibiotic emulsion 25 parts, coalescents COASOL
0.8 part, hydroxyethyl cellulose 0.3 part, BS168 0.08 part, freeze-thaw stabiliser FT-100 0.5 part, LCN407 wetting agent 0.1
Part, fast easily dispersant 0.5 part, ST2410 defoamer 0.4 part, titanium dioxide 20 parts, Kaolin 10 parts, calcium carbonate 15 parts,
TRYSAN107 antifungus agent 0.3 part, LXE antibacterial 0.2 part, TT-935 thickening agent 0.6 part and 27 parts of water.
Preparation method: add water, hydroxyethyl cellulose and the BS168 of 80% in reactor, with the rotating speed of 600r/min
Dispersion 12min, is subsequently added into freeze-thaw stabiliser FT100, LCN407 wetting agent, fast easily dispersant and the ST2410 froth breaking of 50%
Agent, and disperse 3min with the rotating speed of 600r/min, then put into titanium dioxide, Kaolin and calcium carbonate, divide with the rotating speed of 1200r/min
It is dissipated to fineness≤50um, finally puts into coalescents COASOL, Tao Shi silver-ion antibiotic emulsion, TRYSAN107 antifungus agent, LXE
Antibacterial, TT-935 thickening agent, remaining water and remaining ST2410 defoamer, stir 10min with the rotating speed of 800r/min, i.e.
Obtain the emulsion paint of the present invention.
Embodiment 2
The component of emulsion paint of the present invention is calculated as by weight: Tao Shi silver-ion antibiotic emulsion 32 parts, coalescents COASOL
1.5 parts, hydroxyethyl cellulose 0.5 part, Rheinamin VP195 0.1 part, freeze-thaw stabiliser FT-100 1.0 parts, E9289 profit
Humectant 0.2 part, 731A dispersant 1.0 parts, CF1366 defoamer 0.6 part, titanium dioxide 25 parts, Kaolin 5 parts, calcium carbonate 10 parts,
CF1100 antifungus agent 0.2 part, LXE antibacterial 0.3 part, RHEOLATE420 thickening agent 0.3 part and 25 parts of water.
Preparation method: add water, hydroxyethyl cellulose and the Rheinamin VP195 of 85% in reactor, with 800r/
The rotating speed dispersion 8min of min, is subsequently added into freeze-thaw stabiliser FT100, E9289 wetting agent, 731A dispersant and 60%
CF1366 defoamer, and disperse 2min with the rotating speed of 800r/min, then put into titanium dioxide, Kaolin and calcium carbonate, with 1000r/
The rotating speed of min is dispersed to fineness≤50um, and finally input coalescents COASOL, Tao Shi silver-ion antibiotic emulsion, CF1100 prevent
Mould dose, LXE antibacterial, RHEOLATE420 thickening agent, remaining water and remaining CF1366 defoamer, turning with 600r/min
Speed stirring 20min, obtains the emulsion paint of the present invention.
Embodiment 3
The component of emulsion paint of the present invention is calculated as by weight: Tao Shi silver-ion antibiotic emulsion 30 parts, coalescents COASOL
1.2 parts, hydroxyethyl cellulose 0.4 part, AMP95 0.05 part, freeze-thaw stabiliser FT-100 0.8 part, BD-405 wetting agent 0.15
Part, SN-DISPERSANT5040 dispersant 0.8 part, AP7015 defoamer 0.5 part, titanium dioxide 23 parts, Kaolin 8 parts, calcium carbonate
12.5 parts, 678 antifungus agent 0.5 part, Nipacide CI15HS antibacterial 0.2 part, DR-180 thickening agent 0.4 part and 21 parts of water.
Preparation method: add water, hydroxyethyl cellulose and the AMP95 of 82% in reactor, with the rotating speed of 700r/min
Dispersion 10min, is subsequently added into freeze-thaw stabiliser FT100, BD-405 wetting agent, SN-DISPERSANT5040 dispersant and 55%
AP7015 defoamer, and disperse 3min with the rotating speed of 700r/min, then put into titanium dioxide, Kaolin and calcium carbonate, with
The rotating speed of 1100r/min is dispersed to fineness≤50um, finally put into coalescents COASOL, Tao Shi silver-ion antibiotic emulsion, 678
Antifungus agent, NipacideCI15HS antibacterial, DR-180 thickening agent, remaining AP7015 defoamer and remaining water, with 700r/
The rotating speed stirring 15min of min, obtains the emulsion paint of the present invention.
Claims (10)
1. a low VOC clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that this emulsion paint is by weight by following substances system
Become: the silver-ion antibiotic emulsion 25 of Dow Chemical~32 parts, coalescents COASOL0.8~1.5 parts, hydroxyethyl cellulose
0.3~0.5 part, pH adjusting agent 0.05~0.1 part, freeze-thaw stabiliser FT-100 0.5~1.0 parts, wetting agent 0.1~0.2 part,
Dispersant 0.5~1.0 parts, defoamer 0.4~0.6 part, titanium dioxide 20~25 parts, Kaolin 5~10 parts, calcium carbonate 10~15
Part, antifungus agent 0.2~0.5 part, antibacterial 0.2~0.3 part, thickening agent 0.3~0.6 part and water 21~27 parts.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described pH regulator
Agent is BS168, Rheinamin VP195 or AMP-95.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described wetting agent
For BD-405, E9289 or LCN407.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described dispersant
For fast easily dispersant, 731A or SN-DISPERSANT5040.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described defoamer
For AP7015, CF1366 or ST2410.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described antifungus agent
Be 678, TRYSAN107 and CF1100.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described antibacterial
For LXE or Nipacide CI15HS.
A kind of low VOC the most as claimed in claim 1 clean taste antimicrobial chamber interior trim emulsion paint, it is characterised in that described thickening agent
For RHEOLATE420, TT-935 or DR-180.
9. the method for the preparation a kind of low VOC clean taste antimicrobial chamber interior trim emulsion paint according to any one of claim 1-8, it is special
Levying and be, the method is prior to adding the total consumption of water 80~the water of 85%, hydroxyethyl cellulose and pH adjusting agent in reactor, with
The rotating speed being not less than 600r/min disperses at least 8min, be subsequently added into freeze-thaw stabiliser FT100, wetting agent, dispersant and 50~
The defoamer of 60% weight, and disperse at least 2min with same rotating speed, then put into titanium dioxide, Kaolin and calcium carbonate, with the lowest
Rotating speed in 1000r/min is dispersed to fineness≤50um, finally puts into coalescents COASOL, the silver ion of Dow Chemical
Antimicrobial emulsion, antifungus agent, antibacterial, thickening agent, remaining water and remaining defoamer, stir being not less than the rotating speed of 600r/min
Mix at least 10min,.
10. preparation method as claimed in claim 9, it is characterised in that the method is prior to adding the total consumption of water in reactor
80~the water of 85%, hydroxyethyl cellulose and pH adjusting agent, the rotating speed with 600~800r/min disperses 8~12min, then adds
Enter freeze-thaw stabiliser FT100, wetting agent, dispersant and 50~the defoamer of 60% weight, and with the rotating speed of 600~800r/min
Dispersion 2~3min, then puts into titanium dioxide, Kaolin and calcium carbonate, with the rotating speed of 1000~1200r/min be dispersed to fineness≤
50um, finally puts into coalescents COASOL, the silver-ion antibiotic emulsion of Dow Chemical, antifungus agent, antibacterial, thickening
Agent, remaining water and remaining defoamer, the rotating speed with 600~800r/min stirs 10~20min,.