CN106221374A - Ball pen ink film former - Google Patents
Ball pen ink film former Download PDFInfo
- Publication number
- CN106221374A CN106221374A CN201610612063.1A CN201610612063A CN106221374A CN 106221374 A CN106221374 A CN 106221374A CN 201610612063 A CN201610612063 A CN 201610612063A CN 106221374 A CN106221374 A CN 106221374A
- Authority
- CN
- China
- Prior art keywords
- parts
- film former
- ball pen
- pen ink
- ink film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The open a kind of ball pen ink film former of the present invention, belongs to novel office table separation.The present invention uses the raw material of following weight portion to make: polyurethane 15 parts～20 parts, rosin polymer 5 parts～8 parts, nanometer silicon carbide 1 part～5 parts, Corii Bovis seu Bubali cream 1 part～5 parts, ethylene glycol 5 parts～8 parts, lignosulfonate 1 part～5 parts and sodium bicarbonate 0.5 part～1 part.Compared with traditional film former, the present invention has more excellent combination property.
Description
Technical field
The invention belongs to novel office table separation, especially a kind of ball pen ink film former.
Background technology
Ball pen, or claim ballpoint pen, it is to use dry consistence ink, relies on the upper freely rotatable steel ball of nib to bring out transcription
A kind of writing implement on paper.Ball pen have simple in construction, easy to carry, write lubrication, and be suitable for for making carbon copies
Advantage, thus, all it is happy to from people from all walks of life such as the civilian personnel of the student of school to office building use.
In ballpoint pen oil ink formulations, main component includes dyestuff, film former, solvent, dispersant and other auxiliary agents.Wherein, become
Membrane is the important component part of Ball-point pen ink, and its effect mainly can be at paper surface homogeneous film formation and as dyestuff
Carrier.Require that it is presented with certain adhesion to paper, be difficult to peel off, but available erasing rubber is wiped gently, and coloring agent has
Strong adhesive force, dissolubility is good in a solvent, and the most stable with other compositions, can preserve for a long time.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of new ball pen ink film former.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
The raw material using following weight portion is made:
Polyurethane 15 parts～20 parts, rosin polymer 5 parts～8 parts, nanometer silicon carbide 1 part～5 parts, Corii Bovis seu Bubali cream 1 part～5 parts,
Ethylene glycol 5 parts～8 parts, lignosulfonate 1 part～5 parts and sodium bicarbonate 0.5 part～1 part.
Owing to using technique scheme, there is advantages that
Compared with traditional film former, the present invention has more excellent combination property.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Embodiment 1 ball pen ink film former
The raw material used is as follows: polyurethane 150g, rosin polymer 50g, nanometer silicon carbide 10g, Corii Bovis seu Bubali cream 10g, ethylene glycol
50g, lignosulfonate 10g and sodium bicarbonate 5g；
Its concrete preparation method is: by above-mentioned raw materials according to predetermined ratio at 100 DEG C of mix homogeneously.
Finding through test, its surface tension force (25 DEG C) that the present embodiment prepares is 40mN/m, and viscosity (25 DEG C) is
6MPa s, film-forming temperature is-5 DEG C.
Embodiment 2 ball pen ink film former
The raw material used is as follows: polyurethane 200g, rosin polymer 80g, nanometer silicon carbide 50g, Corii Bovis seu Bubali cream 50g, ethylene glycol
80g, lignosulfonate 50g and sodium bicarbonate 10g；
Its concrete preparation method is: by above-mentioned raw materials according to predetermined ratio at 95 DEG C of mix homogeneously.
Finding through test, its surface tension force (25 DEG C) that the present embodiment prepares is 40mN/m, and viscosity (25 DEG C) is
6MPa s, film-forming temperature is-5 DEG C.
Embodiment 3 ball pen ink film former
The raw material used is as follows: polyurethane 160g, rosin polymer 70g, nanometer silicon carbide 40g, Corii Bovis seu Bubali cream 20g, ethylene glycol
70g, lignosulfonate 30g and sodium bicarbonate 6g；
Its concrete preparation method is: by above-mentioned raw materials according to predetermined ratio at 95 DEG C of mix homogeneously.
Finding through test, its surface tension force (25 DEG C) that the present embodiment prepares is 40mN/m, and viscosity (25 DEG C) is
6MPa s, film-forming temperature is-5 DEG C.
Claims (1)
1. a ball pen ink film former, it is characterised in that use the raw material of following weight portion to make:
Polyurethane 15 parts～20 parts, rosin polymer 5 parts～8 parts, nanometer silicon carbide 1 part～5 parts, Corii Bovis seu Bubali cream 1 part～5 parts,
Ethylene glycol 5 parts～8 parts, lignosulfonate 1 part～5 parts and sodium bicarbonate 0.5 part～1 part.