CN106215243A - A kind of novel hydrophilic antiseep absorbable medical film and preparation method thereof - Google Patents
A kind of novel hydrophilic antiseep absorbable medical film and preparation method thereof Download PDFInfo
- Publication number
- CN106215243A CN106215243A CN201610794410.7A CN201610794410A CN106215243A CN 106215243 A CN106215243 A CN 106215243A CN 201610794410 A CN201610794410 A CN 201610794410A CN 106215243 A CN106215243 A CN 106215243A
- Authority
- CN
- China
- Prior art keywords
- layer
- spinning
- hydrophilic
- preparation
- antiseep
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of novel hydrophilic antiseep absorbable medical film and preparation method thereof, described medical films includes: hydrophilic layer absorbed layer and anti-leakage layer;Described hydrophilic layer, absorbed layer and anti-leakage layer laminated structure successively, forms hydrophilic antiseep absorbable medical film;Described hydrophilic layer is for organizing docile with damage, and described absorbed layer is for the tissue hydrops of absorptive tissue seepage, and described anti-leakage layer is for preventing the seepage of tissue fluid.A kind of novel hydrophilic antiseep absorbable medical film of the present invention and preparation method thereof, possess hydrophilic layer, absorbed layer, anti-leakage layer, while making absorbed layer can be good at absorptive tissue sepage and ensure that tissue sepage will not leak into surrounding tissue, improve the sticking nature of product, absorbability, leakproof, bring great convenience to surgical field, especially have great prospect repairing of cerebral dura mater (spinal meninges) defect in the application replaced.
Description
Technical field
The present invention relates to field of medical article technology, particularly relate to a kind of novel hydrophilic antiseep absorbable medical film and
Preparation method.
Background technology
At present, viscous gram absorbable medical film commercially occupies the biggest component, is widely used in surgical operation postoperative
Prevent being adhered.Also there is a lot of similar absorbable medical film on market, all due to the unicity of its structure, be difficult to accomplish sticking nature
Good, absorption sepage completely and prevents the feature that seepage property is good from all possessing, and single its scope of application that also can limit of structure,
It is difficult to repairing and the replacement of dura defect.
Summary of the invention
The technical problem to be solved is: provide a kind of novel hydrophilic antiseep absorbable medical film and preparation thereof
Method, it is possible to improve the sticking nature of product, absorbability, leakproof, can be applicable to the repairing of cerebral dura mater (spinal meninges) defect and replaces
Change.
For solving above-mentioned technical problem, the technical scheme is that
Thering is provided a kind of novel hydrophilic antiseep absorbable medical film, described medical films includes: hydrophilic layer absorbed layer and antiseepage
Drop ply;Described hydrophilic layer, absorbed layer and anti-leakage layer laminated structure successively, forms hydrophilic antiseep absorbable medical film;Described
Hydrophilic layer is for organizing docile with damage, and described absorbed layer is used for the tissue hydrops of absorptive tissue seepage, described anti-leakage layer
In the seepage preventing tissue fluid.
Also provide for the preparation method of a kind of novel hydrophilic antiseep absorbable medical film, comprise the steps:
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 18mL/h, receiving range 23cm, and spinning syringe needle footpath is
1.07um, spinning voltage is 19KV, prepares hydrophilic layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 15mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.67um, spinning voltage is 21KV, prepares absorbed layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 12mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.5um, spinning voltage is 23KV, prepares anti-leakage layer;
Wherein, hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, i.e. can be made into
Novel hydrophilic antiseep absorbable medical film.
Wherein, in above-mentioned novel hydrophilic antiseep absorbable medical film, described spinning liquid be acetone, ethyl acetate, six
Fluorine isopropanol, dichloromethane, N, one or both in N-dimethylformamide, aqueous acetic acid and chloroform.
Wherein, in above-mentioned preparation method, described hydrophilic layer is Polyethylene Glycol, chitosan, gelatin and polylactic acid-glycolic base second
One in acid.
Wherein, in above-mentioned preparation method, described absorbed layer is in polylactic acid, the lactide of lactide-and poly-own ester
A kind of.
Wherein, in above-mentioned preparation method, described absorbed layer is the electrostatic spinning nano fiber film of fiber fluffy.
Wherein, in above-mentioned preparation method, described anti-leakage layer is in polylactic acid, the lactide of lactide-and poly-own ester
One.
Wherein, in above-mentioned preparation method, described anti-leakage layer is the electrostatic spinning nano fiber film that fiber is fine and close.
Have employed technique scheme, the invention have the benefit that
Compared with prior art, a kind of novel hydrophilic antiseep absorbable medical film of the present invention and preparation method thereof, tool
Standby hydrophilic layer, absorbed layer, anti-leakage layer so that while absorbed layer can be good at absorptive tissue sepage and ensure tissue sepage
Surrounding tissue will not be leaked into, improve the sticking nature of product, absorbability, leakproof, bring pole to surgical field
Big facility, especially has great prospect repairing of cerebral dura mater (spinal meninges) defect in the application replaced.
Accompanying drawing explanation
Fig. 1 is the structural representation of the novel hydrophilic antiseep absorbable medical film of the present invention;
In figure: 1 is hydrophilic layer;2 is absorbed layer;3 is anti-leakage layer.
Detailed description of the invention
Below in conjunction with the accompanying drawings and embodiment, the detailed description of the invention of the present invention is described in further detail.Hereinafter implement
Example is used for illustrating the present invention, but can not be used for limiting the scope of the present invention.
As it is shown in figure 1, the novel hydrophilic antiseep absorbable medical film of the present invention includes: hydrophilic layer 1, absorbed layer 2 and anti-
Seepage floor 3.This hydrophilic layer 1, absorbed layer 2 and anti-leakage layer 3 laminated structure successively, form hydrophilic antiseep absorbable medical film.
Hydrophilic layer 1, absorbed layer 2 and anti-leakage layer 3 pass sequentially through layer upon layer electrostatic spinning laminated structure, and electrostatic spinning is third
Ketone, ethyl acetate, hexafluoroisopropanol, dichloromethane, N, one in N-dimethylformamide, aqueous acetic acid and chloroform or
Two kinds so that hydrophilic layer 1, absorbed layer 2 and antiseep 3 are fitted by layer upon layer electrostatic spinning successively.
Specifically, hydrophilic layer 1 for and damage tissue docile, this hydrophilic layer 1 be Polyethylene Glycol, chitosan, gelatin and
One in poly lactic-co-glycolic acid, has absorbable structure.
Absorbed layer 2 is for the tissue hydrops of absorptive tissue seepage, and this absorbed layer 2 be polylactic acid, the lactide of lactide-and gathers
One in own ester, is formed as the electrostatic spinning nano fiber film of fiber fluffy, has the water absorption for fiber fluffy and can absorb
Structural material.
Anti-leakage layer 3 is for preventing the seepage of tissue fluid, and this anti-leakage layer 3 be polylactic acid, the lactide of lactide-and poly-own
One in ester, this anti-leakage layer 3 is the electrostatic spinning nano fiber film that fiber is fine and close, has the densification preventing tissue fluid seepage
Property can absorb structural material.
Art finishes, and is placed in by medical films at wound, open and flat, flicking docile, is sewed up by wound.Specifically, medical films is placed in
At tissue injury so that hydrophilic layer 1 and the good docile of wound tissue, the tissue fluid at wound will be deep into polylactic acid layers, logical
Crossing absorbed layer 2 and suck tissue fluid in fluffy fibre structure, anti-leakage layer 3 prevents the tissue fluid seepage that absorbed layer 2 sucks.Cause
This, this novel medical films can be widely used in surgery and various surgical operation wound, and sticking nature is good, the green peace of material
Entirely, easy and simple to handle, can be by Matrix absorption, it is not necessary to second operation take out, expand the scope of application of this class absorbable medical film, especially
It is repairing and the replacement of cerebral dura mater (spinal meninges) defect.
The preparation method of the novel hydrophilic antiseep absorbable medical film of the present invention, comprises the steps:
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 18mL/h, receiving range 23cm, and spinning syringe needle footpath is
1.07um, spinning voltage is 19KV, prepares hydrophilic layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 15mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.67um, spinning voltage is 21KV, prepares absorbed layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 12mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.5um, spinning voltage is 23KV, prepares anti-leakage layer;
Wherein, hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, i.e. can be made into
Novel hydrophilic antiseep absorbable medical film.
This preparation method is specifically introduced below by several embodiments.
[embodiment one]
Preparation of spinning solution: take a certain amount of poly lactic-co-glycolic acid and join for 6%-15% with mass ratio with hexafluoroisopropanol
Spinning liquid A processed, its optimal proportioning is poly lactic-co-glycolic acid 50 grams with hexafluoroisopropanol with mass ratio is 8% to be configured to spin
Silk liquid A;Taking a certain amount of polylactic acid and prepare spinning liquid B with mass ratio for 10%-18% with acetone, its optimal proportioning is poly-breast
Acid 50 grams and acetone are 16% to be configured to spinning liquid B with mass ratio;Taking a certain amount of polylactic acid and N, N-dimethylformamide is with matter
Amount prepares spinning liquid B than for 9%-16%, and its optimal proportioning is polylactic acid 50 grams and N, and N-dimethylformamide with mass ratio is
13% is configured to spinning liquid from C;
The preparation of hydrophilic layer: draw each 20mL of spinning liquid A with disposable injection injection device 4, spinning parameter is fltting speed
18mL/h, receiving range 23cm, spinning syringe needle footpath is 1.07um, and spinning voltage is 19KV;
The preparation of water accepting layer: draw each 40mL of spinning liquid B with disposable injection injection device 4, spinning parameter is fltting speed
15mL/h, receiving range 23cm, spinning syringe needle footpath is 0.67um, and spinning voltage is 21KV;
The preparation of anti-leakage layer: draw each 30mL of spinning liquid C with disposable injection injection device 4, spinning parameter is for advancing speed
Degree 12mL/h, receiving range 23cm, spinning syringe needle footpath is 0.5um, and spinning voltage is 23KV;
Its hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, make hydrophilic antiseepage
Leakage absorbable medical film I.
[embodiment two]
Preparation of spinning solution: take a certain amount of chitosan and prepare spinning liquid A with mass ratio for 6%-15% with aqueous acetic acid,
Its optimal proportioning be poly-50 grams of shell be 8% to be configured to spinning liquid A with aqueous acetic acid with mass ratio;Take a certain amount of poly-(third
The lactide of lactide-) prepare spinning liquid B with mass ratio for 8%-18% with chloroform, its optimal proportioning be poly-(lactide-
Lactide) 50 grams be 9% to be configured to spinning liquid B with chloroform with mass ratio;Take a certain amount of polylactic acid and chloroform with
Mass ratio is that 6%-16% prepares spinning liquid B, and its optimal proportioning is polylactic acid 50 grams with chloroform with mass ratio is 8% to join
Make spinning liquid from C;
The preparation of hydrophilic layer: draw each 20mL of spinning liquid A with disposable injection injection device 4, spinning parameter is fltting speed
18mL/h, receiving range 23cm, spinning syringe needle footpath is 1.07um, and spinning voltage is 19KV;
The preparation of water accepting layer: draw each 40mL of spinning liquid B with disposable injection injection device 4, spinning parameter is fltting speed
15mL/h, receiving range 23cm, spinning syringe needle footpath is 0.67um, and spinning voltage is 21KV;
The preparation of anti-leakage layer: draw each 30mL of spinning liquid C with disposable injection injection device 4, spinning parameter is for advancing speed
Degree 12mL/h, receiving range 23cm, spinning syringe needle footpath is 0.5um, and spinning voltage is 23KV;
Its hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, make hydrophilic antiseepage
Leakage absorbable medical film II.
[embodiment three]
Preparation of spinning solution: take a certain amount of poly lactic-co-glycolic acid and join for 6%-15% with mass ratio with hexafluoroisopropanol
Spinning liquid A processed, its optimal proportioning is poly lactic-co-glycolic acid 50 grams with hexafluoroisopropanol with mass ratio is 10% to be configured to spin
Silk liquid A;Taking a certain amount of poly-(lactide-lactide) and prepare spinning liquid B with mass ratio for 8%-18% with chloroform, it is
Good proportioning is poly-(lactide-lactide) 50 grams with chloroform with mass ratio is 9% to be configured to spinning liquid B;Take a certain amount of
Polylactic acid and chloroform prepare spinning liquid B with mass ratio for 6%-16%, its optimal proportioning is polylactic acid 50 grams and three
Chloromethanes is 10% to be configured to spinning liquid from C with mass ratio;
The preparation of hydrophilic layer: draw each 20mL of spinning liquid A with disposable injection injection device 4, spinning parameter is fltting speed
18mL/h, receiving range 23cm, spinning syringe needle footpath is 1.07um, and spinning voltage is 19KV;
The preparation of water accepting layer: draw each 40mL of spinning liquid B with disposable injection injection device 4, spinning parameter is fltting speed
15mL/h, receiving range 23cm, spinning syringe needle footpath is 0.67um, and spinning voltage is 21KV;
The preparation of anti-leakage layer: draw each 30mL of spinning liquid C with disposable injection injection device 4, spinning parameter is for advancing speed
Degree 12mL/h, receiving range 23cm, spinning syringe needle footpath is 0.5um, and spinning voltage is 23KV;
Its hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, make hydrophilic antiseepage
Leakage absorbable medical film III.
The performance test of hydrophilic antiseep absorbable medical film
1, hydrophilic test
2, antiseep test
The animal experiment of hydrophilic antiseep absorbable medical film:
Laboratory animal is local beasle dog, and unification is provided by The 2nd Army Medical College.To newly purchased dog breeders 2 weeks, observe
Experiment is entered after their health, growth promoter situation and nursing custom.Specific embodiments is to be shaved by dog after intravenous anesthesia
Capillus, is placed in animal on special-purpose operating table, ventricumbent position.The crown hits exactly, longitudinally slit scalp, uses Single-pole electric knife after entering scalp
Along sagittal suture, side opens about 0.5 centimetre, is individually separated bilateral top muscle group, with detacher separation periosteum, exposes Double Tops portion skull
The skull plate of 4cm × 3cm, opens skull with High speed drill mill, and High speed drill mill Double Tops portion skull, it is left that Double Tops portion forms 1cm × 2cm
Right dura defect.First test sample is taken out from packaging bag, be trimmed to the size of 1.5cm × 2.5cm, just to cover
Living the defect after excision cerebral dura mater, 3/0 not damaged wire discontinuous sewing, test sample four limit is respectively sewed up a pin, is tied a knot during stitching
Being close to i.e. stop, make artificial dura mater and primary dura mater not stay lacuna as far as possible, involutory smooth, needle gage is uniform.After having closed cerebral dura mater,
The most uniformly it is sprinkled into wound with penicillin sodium powder, strengthens prevention anastomotic stoma and infect.With round needle, No. 1 silk suture muscle, epidural is double
Film drainage strip is put in side, and scalp is with No. 4 wire discontinuous sewings.
Post operation sends Animal House back to after animal is completely clear-headed, stops fluid infusion, and full diet is raised.3d after animal surgery
In, 2 times/d of penicillin, 800,000 units/time intramuscular injection, 2 times/d of chloromycetin, 0.5g/ intramuscular injection;Post operation 4 6d, blue or green
1 time/d of mycin, 800,000 units/time intramuscular injection, 1 time/d, 0.5g/ intramuscular injection of chloromycetin.Simultaneously observe animal normal
The physiological activity of feed, drinking-water and other each side is normal, the dyskinesia simultaneously caused without central nervous system injury and other is different
Often.
The animal experiment tracking result of hydrophilic antiseep absorbable medical film:
As it has been described above, a kind of novel hydrophilic antiseep absorbable medical film of the present invention, possess hydrophilic layer, absorbed layer, prevent
Seepage floor so that while absorbed layer can be good at absorptive tissue sepage and ensure that tissue sepage will not leak into group around
Knit, improve the sticking nature of product, absorbability, leakproof, bring great convenience to surgical field, especially exist
Repairing of cerebral dura mater (spinal meninges) defect has great prospect in the application replaced.
The above-mentioned description to embodiment is to be understood that for ease of those skilled in the art and apply this
Bright.These embodiments obviously easily can be made various amendment by person skilled in the art, and described herein
General Principle is applied in other embodiments without through performing creative labour.Therefore, the invention is not restricted to enforcement here
Example, those skilled in the art should be the present invention's according to the announcement of the present invention, the improvement made for the present invention and amendment
Within protection domain.
Claims (8)
1. a novel hydrophilic antiseep absorbable medical film, it is characterised in that described medical films includes: hydrophilic layer (1), absorption
Layer (2) and anti-leakage layer (3);Described hydrophilic layer (1), absorbed layer (2) and anti-leakage layer (3) laminated structure successively, formed hydrophilic
Antiseep absorbable medical film;Described hydrophilic layer (1) is for organizing docile with damage, and described absorbed layer (2) is used for absorptive tissue
The tissue hydrops of seepage, described anti-leakage layer (3) is for preventing the seepage of tissue fluid.
2. the method preparing novel hydrophilic antiseep absorbable medical film as claimed in claim 1, it is characterised in that bag
Include following steps:
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 18mL/h, receiving range 23cm, and spinning syringe needle footpath is
1.07um, spinning voltage is 19KV, prepares hydrophilic layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 15mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.67um, spinning voltage is 21KV, prepares absorbed layer;
Taking a certain amount of spinning liquid, spinning parameter is fltting speed 12mL/h, receiving range 23cm, and spinning syringe needle footpath is
0.5um, spinning voltage is 23KV, prepares anti-leakage layer;
Wherein, hydrophilic layer, absorbed layer, anti-leakage layer are to spin successively to be sequentially overlapped on same reception paper, i.e. can be made into novel
Hydrophilic antiseep absorbable medical film.
Preparation method the most according to claim 2, it is characterised in that described spinning liquid is that acetone, ethyl acetate, hexafluoro are different
Propanol, dichloromethane, N, one or both in N-dimethylformamide, aqueous acetic acid and chloroform.
Preparation method the most according to claim 2, it is characterised in that described hydrophilic layer (1) be Polyethylene Glycol, chitosan,
One in gelatin and poly lactic-co-glycolic acid.
Preparation method the most according to claim 2, it is characterised in that described absorbed layer (2) is polylactic acid, lactide-
One in lactide and poly-own ester.
Preparation method the most according to claim 2, it is characterised in that described absorbed layer (2) is the Static Spinning of fiber fluffy
Nano fibrous membrane.
Preparation method the most according to claim 2, it is characterised in that described anti-leakage layer (3) be polylactic acid, lactide-
Lactide and the one in poly-own ester.
Preparation method the most according to claim 2, it is characterised in that described anti-leakage layer (3) is the electrostatic that fiber is fine and close
Spinning nanometer fiber membrane.