CN106213635B - The production method of polyester-cotton blend adhered by double sided plaster lining - Google Patents

The production method of polyester-cotton blend adhered by double sided plaster lining Download PDF

Info

Publication number
CN106213635B
CN106213635B CN201610618104.8A CN201610618104A CN106213635B CN 106213635 B CN106213635 B CN 106213635B CN 201610618104 A CN201610618104 A CN 201610618104A CN 106213635 B CN106213635 B CN 106213635B
Authority
CN
China
Prior art keywords
polyester
cotton blend
double sided
lining
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610618104.8A
Other languages
Chinese (zh)
Other versions
CN106213635A (en
Inventor
曹平
李南南
朱红耀
黄�俊
曾燕
姜伟
黄新华
吴亮亮
杨静新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Original Assignee
NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd filed Critical NANTONG HAIHUI GARMENT ACCESSORIES Co Ltd
Priority to CN201610618104.8A priority Critical patent/CN106213635B/en
Priority to CN201810086503.3A priority patent/CN108185552B/en
Priority to CN201810086479.3A priority patent/CN108308770B/en
Publication of CN106213635A publication Critical patent/CN106213635A/en
Application granted granted Critical
Publication of CN106213635B publication Critical patent/CN106213635B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention discloses a kind of polyester-cotton blend adhered by double sided plaster lining and its production method, and production procedure includes turning over the seam → shrinkproof hard finishing of pre-treatment → heat setting → chemistry → front powder point coating or applying coating → reverse side applying coating → sanforized.Adhesive lining tow sides have adhesive layer, two pieces of fabrics of the same race or not of the same race can be bonded together, obtain harder feel, higher separation strength and other performances.Through the xeothermic size changing rate 0.8%~+0.5% of broadwise；Free and hydrolysis formaldehyde≤40mg/kg；It is 1.0%~+0.5% through broadwise washing size changing rate.Production technology operation of the present invention is easy, to eco-friendly, excellent product performance.

Description

The production method of polyester-cotton blend adhered by double sided plaster lining
Technical field
The present invention relates to a kind of polyester-cotton blend adhered by double sided plaster lining and its production method.
Background technology
There is adhesive layer in one face of conventional binder lining, can be bonded together with one piece of fabric.There are some special kinds clothes Or have particular/special requirement clothes, it is desirable to adhesive lining can be bonded together two pieces of fabrics, obtain harder feel, higher separation strength and Other performances.Therefore, the polyester-cotton blend adhered by double sided plaster that research and development and production tow sides have adhesive layer serves as a contrast, meet apparel industry need Ask.
The content of the invention
Present invention aims at provide a kind of excellent performance, prepare easy polyester-cotton blend adhered by double sided plaster lining and its producer Method.
The present invention technical solution be：
A kind of polyester-cotton blend adhered by double sided plaster lining, it is characterized in that：There is adhesive layer in the tow sides of polyester-cotton blend base fabric；Done through broadwise Hot size changing rate -0.8%~+0.5%；Free and hydrolysis formaldehyde≤40mg/kg；It is -1.0% through broadwise washing size changing rate ~+0.5%.
The fabric specification of polyester-cotton blend lining cloth is one kind in following two kinds：The first width is 48.5 inches, yarn count is 21s × 21s, density are 60 × 58 pieces/inch, and second width is 48.5 inches, yarn count is 16 s × 16s, density is 50 × 45 pieces/inch.
A kind of production method of polyester-cotton blend adhered by double sided plaster lining, it is shrinkproof including turning over seam → pre-treatment → heat setting → chemistry successively Hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.It is characterized in that：Heat setting When, by open width cloth feeding, needle plate on overfeeding -0.5%~0%, the setting of eight lattice hot blasts, wherein 180 DEG C of first and second lattice temperature, the 3rd, 190 DEG C of four lattice temperature, the five~eight 200 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 30~35m/ min。
During chemical shrinkproof hard finishing, the composition of shrinkproof hard finishing liquid is：
The fabric g/L of resin finishing agent KH-1 60~80
The g/L of auxiliary agent STN 150~200
MgCl2·6H2The g/L of O 9~12
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8~4.2 with citric acid.
During applying coating, HDPE PURs are after 155-160 DEG C of melting tank melting of temperature, by spout liquid hot melt adhesive Coated on cloth cover, the g/L of coated weight 70~90.
Polyester-cotton blend adhered by double sided plaster lining of the present invention, can be bonded together two pieces of fabrics, to obtain harder feel, higher stripping Strength and other performances, the xeothermic dimensional contraction rate of adhesive lining is low, and adhesive lining is low through broadwise washing shrinkage, dissociates and hydrolysis formaldehyde is small, To eco-friendly, production technology operation is easy.There is adhesive layer in the tow sides of polyester-cotton blend base fabric, can be of the same race or not Two pieces of fabrics of the same race are bonded together, to obtain harder feel, higher separation strength and other performances, through the xeothermic size of broadwise Rate of change -0.8%~+0.5%；Free and hydrolysis formaldehyde≤40mg/kg；Through broadwise washing size changing rate be -1.0%~+ 0.5%。
With reference to embodiment, the invention will be further described.
Embodiment
Embodiment 1：
Polyester-cotton blend（65/35）The fabric specification of lining cloth is：Door width is 48.5 inches, yarn count is 21s × 21s, density is 60 × 58 pieces/inch.
A kind of production method of polyester-cotton blend adhered by double sided plaster lining, it is shrinkproof including turning over seam → pre-treatment → heat setting → chemistry successively Hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.During heat setting, by flat Width cloth feeding, needle plate on overfeeding -0.5%~0%, eight lattice hot blasts setting, wherein 180 DEG C of first and second lattice temperature, third and fourth lattice temperature 190 DEG C of degree, the five~eight 200 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 33~35m/min.
During chemical shrinkproof hard finishing, the composition of shrinkproof hard finishing liquid is：
The fabric g/L of resin finishing agent KH-1 60~70（The g/L of example 60,65 g/L, 70 g/L）
The g/L of auxiliary agent STN 170~200（The g/L of example 170,180 g/L, 200 g/L）
MgCl2·6H2The g/L of O 9~10.5（The g/L of example 9,10 g/L, 10.5g/L）
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8~4.2 with citric acid.
By open width cloth feeding during chemical shrinkproof hard finishing, shrinkproof hard finishing liquid is rolled in two leachings two, and liquid carrying rate 65%~ 70%, 110~130 DEG C of loose formula dryings, needle plate on overfeeding -0.5%~0%, eight lattice hot blasts bake, wherein the first lattice temperature 150 DEG C, the second 160 DEG C of lattice temperature, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping steps, and speed is 35~ 40m/min.During applying coating, HDPE PURs are after 155-160 DEG C of melting tank melting of temperature, by spout liquid hot melt adhesive Coated on cloth cover, the g/L of coated weight 70~80.
Embodiment 2：
Polyester-cotton blend（65/35）The fabric specification of lining cloth is：Door width is 48.5 inches, yarn count is 16 s × 16s, density is 50 × 45 pieces/inch.
A kind of production method of polyester-cotton blend adhered by double sided plaster lining, it is shrinkproof including turning over seam → pre-treatment → heat setting → chemistry successively Hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.During heat setting, by flat Width cloth feeding, needle plate on overfeeding -0.5%~0%, eight lattice hot blasts setting, wherein 180 DEG C of first and second lattice temperature, third and fourth lattice temperature 190 DEG C of degree, the five~eight 200 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 30~32m/min.
During chemical shrinkproof hard finishing, the composition of shrinkproof hard finishing liquid is：
The fabric g/L of resin finishing agent KH-1 70~80（The g/L of example 70,75 g/L, 80 g/L）
The g/L of auxiliary agent STN 150~180（The g/L of example 150,165 g/L, 180 g/L）
MgCl2·6H2The g/L of O 10.5~12（The g/L of example 10.5,11g/L, 12 g/L）
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8~4.2 with citric acid.
By open width cloth feeding during chemical shrinkproof hard finishing, shrinkproof hard finishing liquid is rolled in two leachings two, and liquid carrying rate 65%~ 70%, 110~130 DEG C of loose formula dryings, needle plate on overfeeding -0.5%~0%, eight lattice hot blasts bake, wherein the first lattice temperature 150 DEG C, the second 160 DEG C of lattice temperature, the three~eight 170 DEG C of lattice temperature, two cylinders cool down cropping steps, and speed is 30~ 35m/min.During applying coating, HDPE PURs are after 155-160 DEG C of melting tank melting of temperature, by spout liquid hot melt adhesive Coated on cloth cover, the g/L of coated weight 75~90.

Claims (3)

1. a kind of production method of polyester-cotton blend adhered by double sided plaster lining, shrinkproof including turning over seam → pre-treatment → heat setting → chemistry successively Hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized；It is characterized in that：It is described to wash Cotton adhered by double sided plaster lining has adhesive layer in the tow sides of polyester-cotton blend base fabric；Through the xeothermic size changing rate -0.8% of broadwise~+ 0.5%；Free and hydrolysis formaldehyde≤40mg/kg；It is -1.0%~+0.5% through broadwise washing size changing rate；During heat setting, lead to Cross open width cloth feeding, needle plate on overfeeding -0.5%~0%, the setting of eight lattice hot blasts, wherein 180 DEG C of first and second lattice temperature, third and fourth 190 DEG C of lattice temperature, the five~eight 200 DEG C of lattice temperature, two cylinders cool down cropping step, and speed is 30~35m/min；
During chemical shrinkproof hard finishing, the composition of shrinkproof hard finishing liquid is：
The fabric g/L of resin finishing agent KH-1 60~80
The g/L of auxiliary agent STN 150~200
MgCl2·6H2The g/L of O 9~12
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8~4.2 with citric acid.
2. the production method of the polyester-cotton blend adhered by double sided plaster lining according to claim 1, it is characterized in that：During applying coating, HDPE PURs are coated in liquid hot melt adhesive on cloth cover, coated weight after 155-160 DEG C of melting tank melting of temperature by spout 70~90 g/L.
3. the production method of the polyester-cotton blend adhered by double sided plaster lining according to claim 1, it is characterized in that：The fabric of polyester-cotton blend lining cloth Specification is one kind in following two kinds：The first width is 48.5 inches, yarn count is 21s × 21s, density is 60 × 58 Piece/inch, second width is 48.5 inches, yarn count is 16 s × 16s, density is 50 × 45 pieces/inch.
CN201610618104.8A 2016-08-01 2016-08-01 The production method of polyester-cotton blend adhered by double sided plaster lining Active CN106213635B (en)