CN106212205A - Douche that a kind of anti-biological film sticks and preparation method thereof - Google Patents
Douche that a kind of anti-biological film sticks and preparation method thereof Download PDFInfo
- Publication number
- CN106212205A CN106212205A CN201610613163.6A CN201610613163A CN106212205A CN 106212205 A CN106212205 A CN 106212205A CN 201610613163 A CN201610613163 A CN 201610613163A CN 106212205 A CN106212205 A CN 106212205A
- Authority
- CN
- China
- Prior art keywords
- douche
- dimethyl
- preparation
- sticks
- biological film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The douche that a kind of anti-biological film sticks is made up of base layer, transition zone and gel layer;Pass through UV-curing technology, under the effect of cross-linking agent and initiator, by amphion gel layer together with transition zone crosslinking curing at douche water passage surface, douche water passage surface is made to possess the anti-biological function sticked, can effectively reduce the douche in drip irrigation technique because microorganism is adhered at the wall of runner limit and forms biomembrane, solid suspended particle at flow path boundary due to relatively low speed, under biomembranous adhesion, particle builds up, and reduces runner valid circulation area and the situation of block water irrigator.
Description
Technical field
The present invention relates to drip irrigation technique field, be specifically related to douche that a kind of anti-biological film sticks and preparation method thereof.
Background technology
Douche as the critical component of drip irrigation system, the quality of its performance directly reflect the whole drip irrigation system life-span,
Water saving ability and uniformity of pouring water.The Main Bottleneck of the blockage problem of runner always suppression drip irrigation technique development, and along with regeneration
Developing rapidly of the technology such as water droplet filling, brackish water drip irrigation, rainwater drip irrigation, it is also proposed higher to the anti-blockage capability of drip irrigation system
Requirement, blockage problem has become the focus that drip irrigation technique is studied.Current result of study both domestic and external shows, overwhelming majority water dropper
Blocking composition is the inorganic particle that biomembrane sticks, after microbial film is formed, and the gelatinous agglomerate formed with fine grained, once
Enrichment will be difficult to peel off at short notice.Under sewage irrigation, drip emitter blocking material is mainly particle diameter > 0.06mm suspension
Granule (physical clogging), but particle is not the startup factor causing blocking process, and the accumulative of granule is as runner table
Biomembrane and the formation of flora mucus on face and start, for labyrinth runner, impurity particle is easily at microbial growth environment
Best sawtooth root concentrates deposition.Along with increasing of correlational study, the startup that emitter clogging is occurred by increasing scholar
The microorganism that factor is attributed in current forms biomembranous adhesion at runner limit wall.
Amphoteric ion polymer has hydrophilic anions and canons group, it is possible to higher by the hydration of electrostatic induction
Bound Water Molecules face, ground forms hydrophilic interface, at molecular level, it was demonstrated that the hydrone of surface adsorbed close is to confer to material and resists
The main cause of bio-adhesive properties, this discovery makes design antibiont adhesion characteristics material be possibly realized.
Summary of the invention
For the problems referred to above, it is an object of the invention to provide a kind of anti-biological film and stick the preparation method of douche, pass through
Photocuring technology, constructs amphion gel layer at douche water passage surface, makes douche water passage surface possess anti-biological sticking
Function, improve douche anti-blockage capability.
The present invention solves the system of the douche that above-mentioned technical problem be the technical scheme is that a kind of anti-biological film sticks
Preparation Method, it is characterised in that: douche is made up of base layer, transition zone and gel layer;
Described base layer is prepared by injection molding process;
The preparation of described transition zone:
1. the configuration of solution: add 30-70% presoma, 10-60% solvent and 2%-the most by mass percentage
40% water, stirs under the conditions of 20-80 DEG C, and drips the hydrochloric acid of 0.1-1%, and 20 DEG C of constant temperature are placed 24 hours, then add
The light trigger of 0.1-5%, obtains hybrid inorganic-organic transition zone solution;
2. prepared by transition zone: at the hybrid inorganic-organic that one layer of above-mentioned configuration of runner side surface spraying of douche is good
Transition zone solution, is dried 5-20s at 80-100 DEG C, obtains transition zone;
The preparation of described gel layer:
1. the configuration of solution: add 30-60% zwitterionic monomer, vinyl monomer 0-the most by mass percentage
5%, 5-40% solvent, 0.1-5% light trigger, 10-60% water and 1-5% polyene cross-linking agent, stirring and dissolving obtains the most afterwards
Amphion gel solution;
2. prepared by gel layer: the douche runner side of complete for above-mentioned spraying transition zone is sprayed last layer amphion again and coagulates
Sol solution, through ultraviolet light treatment with irradiation 10-30s at 60-80 DEG C, the anti-biological film obtaining having amphion gel coat sticks
Douche.
Being preferably, described presoma is VTES, vinyltrimethoxy silane, vinyl three (2-
Methoxy ethoxy) silane one or more.
Being preferably, described vinyl monomer is acrylamide, NIPA, acrylic acid, methacrylic acid, first
One or more in base 2-(Acryloyloxy)ethanol, 2-HPMA, NVP.
Being preferably, described polyene cross-linking agent is BDO double methacrylate, neopentyl glycol double methacrylate, three hydroxyl first
Base propane triacrylate, pentaerythritol triacrylate, tetramethylol methane tetraacrylate, ethoxylated trimethylolpropane three
Acrylate, two contracting trimethylolpropane tetra-acrylate, double pentaerythritol C5 methacrylate and Bis(pentaerythritol) six acrylic acid
Ester, ethylene glycol diacrylate, Ethylene glycol dimethacrylate, 1, one or more in 6-hexanediol double methacrylate.
Be preferably, described zwitterionic monomer be N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salt,
N, N-dimethyl-N-methacryiamidopropyl-N, N-dimethyl-N-propane sulfonic acid inner salt, 1-carboxy-N, N-dimethyl-
N acrylamide propyl group inner salt, 2-carboxy-N, N-dimethyl-N-acrylamide propyl inner salt, 3-carboxy-N, N-dimethyl-N-
Acrylamide propyl inner salt, 4-carboxy-N, N-dimethyl-N-acrylamide propyl inner salt, 1-carboxy-N, N-dimethyl-N-third
E pioic acid methyl ester propyl group inner salt, 2-carboxy-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt, 3-carboxy-N, N-dimethyl-N-
Acrylic acid methyl ester. propyl group inner salt, 4-carboxy-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt and 2-(methacryloxy)
In ethyl-2-(trimethylamino) ethyl phosphonic acid ester any one or more.
Being preferably, described light trigger is diphenylethan, benzophenone, 2,4 dihydroxy benaophenonels, Michler's keton, α,
Alpha, alpha-dimethyl epoxide-α-phenyl acetophenone, α, α-diethoxy acetophenone, alpha-hydroxyalkyl benzophenone, α-amine alkyl phenones, double benzoyl
Base phenyl phosphine oxide, sulfur for propoxyl group thioxanthone, isopropyl thioxanthone, 2,4-diethyl thioxanthone, 2-ethyl-anthraquinone
One or more.
Being preferably, described solvent is methanol, ethanol, propanol, ethylene glycol, toluene, dimethylbenzene, benzene, ether, epoxy second
One or more in alkane, oxolane, acetone.
Being preferably, described transition region thickness is 100 μm;Thickness 100 μm of described gel layer.
It is preferably, a length of 300-400nm of described ultraviolet light wave.
The douche that a kind of anti-biological film sticks, it is characterised in that: obtained by the preparation method of above-mentioned any one.
It is an advantage of the current invention that: the present invention passes through UV-curing technology, under the effect of cross-linking agent and initiator, will
Amphion gel layer crosslinking curing together with transition zone, at douche water passage surface, makes douche water passage surface possess anti-biological
The function sticked, it is possible to effectively reduce the douche in drip irrigation technique because microorganism is adhered at the wall of runner limit and forms biology
Film, solid suspended particle is due to relatively low speed at flow path boundary, and under biomembranous adhesion, particle gradually tires out
Long-pending, reduce runner valid circulation area and the situation of block water irrigator.
Accompanying drawing explanation
Fig. 1 is the structural representation of douche of the present invention.
Fig. 2 carries out anti-clogging experiment schematic diagram for using the present invention.
Detailed description of the invention
Below in conjunction with accompanying drawing, technical scheme is clearly and completely described, it is clear that described enforcement
Example is a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill
The every other embodiment that personnel are obtained under not making creative work premise, broadly falls into the scope of protection of the invention.
Embodiment 1
Adding 30 parts of VTESs, 30 parts of ethanol, 30 parts of water in a reservoir, at 40 DEG C, stirring is the most slowly
Dripping the hydrochloric acid of 0.5 part, after at 20 DEG C, constant temperature is placed 24 hours, in system, 2 parts of benzophenone of addition are as light trigger, mixed
Close uniformly, i.e. can get hybrid inorganic-organic transition zone solution, prepared hybrid inorganic-organic transition zone solution spraying is arrived
Douche runner one side surface that injection obtains, is dried 10s at 80 DEG C, obtains transition zone;
30 parts of N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salts of addition in a reservoir, 2 parts of ethanol, 30
Part water, 1 part of BDO double methacrylate, 1 part of light trigger 2,4 dihydroxy benaophenonel, stirring and dissolving obtains the most afterwards
Amphion gel solution, sprays to above-mentioned douche runner one side surface, warp at 80 DEG C by amphion gel solution
300nm ultraviolet light treatment with irradiation 5s, the anti-biological film obtaining having amphion gel coat sticks douche.
Embodiment 2
Adding 30 parts of vinyltrimethoxy silanes, 30 parts of ethanol, 30 parts of water in a reservoir, at 40 DEG C, stirring is the most slowly
Dripping the hydrochloric acid of 0.5 part, after at 20 DEG C, constant temperature is placed 24 hours, in system, 2 parts of benzophenone of addition are as light trigger, mixed
Close uniformly, i.e. can get hybrid inorganic-organic transition zone solution, prepared hybrid inorganic-organic transition zone solution spraying is arrived
Douche runner one side surface that injection obtains, is dried 10s at 80 DEG C, obtains transition zone;
30 parts of N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salts of addition in a reservoir, 2 parts of ethanol, 30
Part water, 1 part of BDO double methacrylate, 1 part of light trigger 2,4 dihydroxy benaophenonel, stirring and dissolving obtains the most afterwards
Amphion gel solution, sprays to above-mentioned douche runner one side surface, warp at 80 DEG C by amphion gel solution
300nm ultraviolet light treatment with irradiation 5s, the anti-biological film obtaining having amphion gel coat sticks douche.
Embodiment 3
Adding 50 parts of vinyltrimethoxy silanes, 30 parts of ethanol, 10 parts of water in a reservoir, at 40 DEG C, stirring is the most slowly
Dripping the hydrochloric acid of 0.5 part, after constant temperature is placed 24 hours at 20 DEG C, add 2 part 2 in system, 4 dihydroxy benaophenonels are as light
Initiator, mix homogeneously, i.e. can get hybrid inorganic-organic transition zone solution, by molten for prepared hybrid inorganic-organic transition zone
Liquid sprays to be molded douche runner one side surface obtained, and is dried 10s, obtains transition zone at 80 DEG C;
Add 30 parts of N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salts and 10 parts of N, N-in a reservoir
Dimethyl-N-methacryiamidopropyl-N, N-dimethyl-N-propane sulfonic acid inner salt, 20 parts of ethanol, 50 parts of water, 3 parts new penta
Diol acrylate, 1 part of light trigger 2,4 dihydroxy benaophenonel, it is molten that stirring and dissolving obtains amphion gel the most afterwards
Liquid, sprays to above-mentioned douche runner one side surface, at 80 DEG C at 300nm ultraviolet light irradiation by amphion gel solution
Reason 5s, the anti-biological film obtaining having amphion gel coat sticks douche.
Embodiment 4
30 parts of VTESs of addition and 5 parts of vinyltrimethoxy silanes in a reservoir, 20 parts of methanol, 30
Part water, stirs and is slowly added dropwise the hydrochloric acid of 1 part at 40 DEG C, after constant temperature is placed 24 hours at 20 DEG C, adds 4 part 2 in system,
4 dihydroxy benaophenonels, as light trigger, mix homogeneously, i.e. can get hybrid inorganic-organic transition zone solution, by prepared
Douche runner one side surface that hybrid inorganic-organic transition zone solution spraying obtains to injection, is dried 10s, i.e. at 80 DEG C
Obtain transition zone;
Add 30 parts of N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salts and 30 parts of N, N-in a reservoir
Dimethyl-N-methacryiamidopropyl-N, N-dimethyl-N-propane sulfonic acid inner salt, 10 parts of acetone, 50 parts of water, 4 parts new penta
Diol acrylate, 2 parts of light trigger 2,4 dihydroxy benaophenonels, it is molten that stirring and dissolving obtains amphion gel the most afterwards
Liquid, douche runner one side surface obtained to injection by prepared hybrid inorganic-organic transition zone solution spraying, at 80 DEG C
It is dried 10s, obtains transition zone.
Embodiment 5
Adding 50 parts of vinyl three (2-methoxy ethoxy) silane in a reservoir, 30 parts of methanol, 30 parts of water, at 40 DEG C
Stir and be slowly added dropwise the hydrochloric acid of 1 part, after constant temperature is placed 24 hours at 20 DEG C, system adds 3 parts of double benzoylphenyls
Phosphine oxide, as light trigger, mix homogeneously, i.e. can get hybrid inorganic-organic transition zone solution, by prepared organic and inorganic
Douche runner one side surface that hydridization transition zone solution spraying obtains to injection, is dried 10s at 80 DEG C, obtains transition zone;
30 parts of N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salts of addition in a reservoir, 20 parts of methanol,
50 parts of water, 2 parts of trimethylolpropane trimethacrylates, 1 part of light trigger α, alpha, alpha-dimethyl epoxide-α-phenyl acetophenone, stirs molten
Obtain amphion gel solution after solving uniformly, prepared hybrid inorganic-organic transition zone solution spraying is obtained to injection
Douche runner one side surface, is dried 10s at 80 DEG C, obtains transition zone.
The anti-biological douche that sticks prepared by embodiment 1-5 is prepared as the internally-inlaid of Φ 16*0.2mm*300mm specification
Drip irrigation zone, is laid in earth's surface, alfalfa irrigation experimental plot, every drip irrigation belt length 10 meters, and it has 30 douches, douche flow
For 3L/h, irrigation water is pool water in a canal, and drip irrigation system stem uses the well strainer of single-stage 120 mesh, operating pressure position, drip irrigation zone
0.1Mpa, pours water 3 hours every day, and test period continues 90 days (as shown in Figure 2), and test result is as shown in table 1:
Table 1 anti-clogging experiment test result
Last it is noted that various embodiments above is only in order to illustrate technical scheme, it is not intended to limit;To the greatest extent
The present invention has been described in detail by pipe with reference to foregoing embodiments, it will be understood by those within the art that: it depends on
So the technical scheme described in foregoing embodiments can be modified, or the most some or all of technical characteristic is entered
Row equivalent;And these amendments or replacement, do not make the essence of appropriate technical solution depart from various embodiments of the present invention technology
The scope of scheme.
Claims (10)
1. the preparation method of the douche that an anti-biological film sticks, it is characterised in that: douche by base layer, transition zone and
Gel layer forms;
Described base layer is prepared by injection molding process;
The preparation of described transition zone:
1. the configuration of solution: add 30-70% presoma, 10-60% solvent and 2%-40% water the most by mass percentage,
Stirring under the conditions of 20-80 DEG C, and drip the hydrochloric acid of 0.1-1%, 20 DEG C of constant temperature are placed 24 hours, then add 0.1-5%
Light trigger, obtain hybrid inorganic-organic transition zone solution;
2. prepared by transition zone: in the hybrid inorganic-organic transition that one layer of above-mentioned configuration of runner side surface spraying of douche is good
Layer solution, is dried 5-20s at 80-100 DEG C, obtains transition zone;
The preparation of described gel layer:
1. the configuration of solution: add 30-60% zwitterionic monomer, 5-40% solvent, alkenes list the most by mass percentage
Body 0-5%, 0.1-5% light trigger, 10-60% water and 1-5% polyene cross-linking agent, stirring and dissolving obtains amphion gel the most afterwards
Solution;
2. prepared by gel layer: the douche runner side of complete for above-mentioned spraying transition zone is sprayed last layer amphion gel more molten
Liquid, through ultraviolet light treatment with irradiation 10-30s at 60-80 DEG C, obtains having the anti-biological film of amphion gel coat and sticks and pour water
Device.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: before described
Driving body is VTES, vinyltrimethoxy silane, vinyl three (2-methoxy ethoxy) silane one
Or it is several.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described
Vinyl monomer is acrylamide, NIPA, acrylic acid, methacrylic acid, hydroxyethyl methylacrylate, 2-hydroxypropyl
In methyl acrylate, NVP one or more (material of telling somebody what one's real intentions are is given, but claim 1
In be not directed to vinyl monomer, please inventor confirm).
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described many
Alkene cross-linking agent is BDO double methacrylate, neopentyl glycol double methacrylate, trimethylolpropane trimethacrylate, season penta
Tetrol triacrylate, tetramethylol methane tetraacrylate, ethoxylated trimethylolpropane triacrylate, two contracting trihydroxy methyls
Tetraacrylate, double pentaerythritol C5 methacrylate and double pentaerythritol methacrylate, ethylene glycol diacrylate, two
Methacrylic acid glycol ester, 1, one or more in 6-hexanediol double methacrylate.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described two
Property ion monomer is N, N-dimethyl (methylacryoyloxyethyl) aminopropanesulfonic acid inner salt, N, N-dimethyl-N-metering system
Amidopropyl-N, N-dimethyl-N-propane sulfonic acid inner salt, 1-carboxy-N, N-dimethyl-N-acrylamide propyl inner salt, 2-
Carboxy-N, N-dimethyl-N-acrylamide propyl inner salt, 3-carboxy-N, N-dimethyl-N-acrylamide propyl inner salt, 4-carboxylic
Base-N, N-dimethyl-N-acrylamide propyl inner salt, 1-carboxy-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt, 2-carboxylic
Base-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt, 3-carboxy-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt, 4-
Carboxy-N, N-dimethyl-N-acrylic acid methyl ester. propyl group inner salt and 2-(methacryloxy) ethyl-2-(trimethylamino) second
In base phosphate ester any one or more.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described light
Initiator is diphenylethan, benzophenone, 2,4 dihydroxy benaophenonels, Michler's keton, α, alpha, alpha-dimethyl epoxide-α-phenyl benzene second
Ketone, α, α-diethoxy acetophenone, alpha-hydroxyalkyl benzophenone, α-amine alkyl phenones, bis(benzoylphenyl) phosphine oxide, sulfur generation the third oxygen
Base thioxanthone, isopropyl thioxanthone, 2,4-diethyl thioxanthone, 2-ethyl-anthraquinone one or more.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described
Solvent is in methanol, ethanol, propanol, ethylene glycol, toluene, dimethylbenzene, benzene, ether, oxirane, oxolane, acetone
Plant or multiple.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described mistake
Crossing layer thickness is 100 μm;Thickness 100 μm of described gel layer.
The preparation method of the douche that a kind of anti-biological film the most according to claim 1 sticks, it is characterised in that: described purple
The a length of 300-400nm of outer light wave.
10. the douche that an anti-biological film sticks, it is characterised in that: obtained by the preparation method of claim 1 ~ 9 any one
Arrive.