CN106193509A - A kind of decorative layer of red color tone high-strength concrete Decorative hanging board - Google Patents
A kind of decorative layer of red color tone high-strength concrete Decorative hanging board Download PDFInfo
- Publication number
- CN106193509A CN106193509A CN201610541935.XA CN201610541935A CN106193509A CN 106193509 A CN106193509 A CN 106193509A CN 201610541935 A CN201610541935 A CN 201610541935A CN 106193509 A CN106193509 A CN 106193509A
- Authority
- CN
- China
- Prior art keywords
- parts
- sand
- particle diameter
- mesh
- strength concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to decorating outer wall of building, be specifically related to the decorative layer of a kind of red color tone high-strength concrete Decorative hanging board.The solution of the present invention is: prepared by the raw material including following weight: cement 400～800 parts, particle diameter 10～40 mesh sand 700～1000 parts, particle diameter 70～140 mesh sand 150～250 parts, particle diameter 325 mesh sand 80～240 parts, water reducer 40～120 parts, water 120～175 parts, pigment 0～4 parts.The present invention on the basis of existing technology, uses cement base material and the form of multistage specific sand cooperation, can be completely embedded with the structure sheaf of exterior wall cladding, thus be greatly improved bonding strength, it is to avoid peel off.
Description
Technical field
The present invention relates to decorating outer wall of building, be specifically related to the decorative layer of a kind of red color tone high-strength concrete Decorative hanging board.
Background technology
In existing building exposed wall decorative hangig panel, stone decoration link plate occupies quite a few market share.But stone material
Take, transport, processing etc. more difficult, complicated process of preparation, cost is high；And stone material is a kind of non-renewable resources, mining is tight
Heavily destroy ecological environment.Along with people are ecological, the lifting of environmental protection ideas, and to resources conservation and the enhancing of protective awareness, because of
This, imitative stone decoration link plate based on concrete also becomes the primary study object of current field of decorative, and develops
Various products.But the color and luster of cement, admixture, sand and stone is required and granular-grade by Concrete decorated hanging board
Join be desirable that the highest, simultaneously in additive water reducer select be also intended to ask high, must colourless, water-reducing rate is high, the slump
Losing little and cement adaptability strong etc., so Concrete decorated hanging board easily produces, color and luster is the best, the problem of stripping easy to crack.
The Chinese invention patent application of Publication No. CN1045964A discloses the decorative panel of a kind of cement sintering, color use
No. 425 white cements, quartz sand and inorganic pigment mix in proportion, are formed with multicolour pattern such as animal, scenery with hills and waters, birds and flowers and large-scale
Decorative pattern combination pattern.But the decorative panel that the program is formed easily collapses, and inferior suitability, and easy to crack.China
Patent of invention " CN102493617B " discloses a kind of imitative stone decoration panel, and its structure is divided into three layers, and panel layer is thin-walled tradition
Stone material, basic unit is cement-based material, is connected with polymer mortar and makes a kind of imitative stone decoration panel between surface layer with basic unit.This
The consumption of stone material is greatly reduced by the method for kind, greatly reduces the dependence to stone material.But, the method for attachment that the method uses is also
Unreliable, cement basic layer is easily peeled off in the presence of a harsh environment with the connection of slabstone surface layer, and layers of material composition differs greatly, it
Thermal coefficient of expansion differ, easily ftracture under thermal environment, peel off.Meanwhile, in the installation in later stage, need the works such as boring
Sequence, not only increases cost, and increases the percent defective of stone material.
Summary of the invention
For the decorative layer overcoming existing exposed wall decorative hangig panel stripping easy to crack and the best problem of color and luster, the present invention carries
Decorative layer for a kind of novel red color tone high-strength concrete Decorative hanging board.
The implementation of the present invention is: the decorative layer of a kind of red color tone high-strength concrete Decorative hanging board, by including following weight
The raw material of amount part proportioning prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 700～1000 parts, particle diameter 70～140 mesh sand 150～250 part,
Footpath 325 mesh sand 80～240 parts, water reducer 40～120 parts, water 120～175 parts, pigment 0～4 parts.
Another preferred version of the present invention is, on the basis of such scheme, by the raw material system including following weight
:
Cement 400～800 parts, particle diameter 10～40 mesh sand 750～850 parts, particle diameter 70～140 mesh sand 200～240 part,
Footpath 325 mesh sand 180～230 parts, water reducer 45～90 parts, water 120～140 parts, pigment iron oxide red 1.8～3.0 parts.
Another preferred version of the present invention is, on the basis of such scheme, described cement is white cement, its whiteness be 75 with
On.
Another preferred version of the present invention is, on the basis of such scheme, described particle diameter 70～140 mesh sand be quartz sand or
The mixing of the one or both in river sand；
Another preferred version of the present invention is, on the basis of such scheme, described particle diameter 325 mesh sand is quartz sand or river sand
In the mixing of one or both.
Another preferred version of the present invention is, on the basis of such scheme, described particle diameter 10～40 mesh sand is quartz sand, river
The mixing of one or more in sand.
Another preferred version of the present invention is, on the basis of such scheme, described particle diameter 10～40 mesh sand is color sand and stone
The mixture of sand；Or the mixture of color sand and river sand；Or color sand and quartz sand and the mixture of river sand.
Another preferred version of the present invention is, on the basis of such scheme, the volume of color sand is less than particle diameter 10～40 mesh
The 30% of sand.
Another preferred version of the present invention is, on the basis of such scheme, color sand can be sphalerite, tourmaline, Fang Xie
Stone, cassiterite, bornite, garnet, crocoite, Chalkopyrite, colorful pebble, realgar stone, goethitum, pyrite, serpentine, green mud
Stone, diopside, villiersite, malachite, bloodstone, dravite, galena, Talcum, granite, Iceland spar, griotte, brightness
One in stone, molybdenite, illite, sandstone, Anhydrite, manganite, ilmenite, magnetic iron ore, tantalite, pyrolusite, tetrahedrite
Or several mixing.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand is by following weight portion
Material composition mixture: fluvial sand 200 parts, garnet 200 parts, cassiterite 360 parts, bloodstone 70 parts.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand is by following weight portion
Material composition mixture: 410 parts of particle diameter 20～40 mesh calcite, 200 parts of particle diameter 20～40 mesh bornite, particle diameter 10～20
Mesh garnet 110 parts.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand is by following weight portion
Material composition mixture: quartz sand 400 parts, 300 parts of sphalerite stone, 60 parts of granite.
The present invention on the basis of existing technology, uses the form that cement base material and multistage specific sand coordinate, and research is sent out
Existing, use the formula design of the present invention, prepared decorative layer, can be completely embedded with the structure sheaf of exterior wall cladding, with structure
Layer is between the layers under cement aquation, and hydrolysis product of cement is interweaved, and makes layer inconspicuous with the demarcation line of layer, from
And it is greatly improved bonding strength, it is to avoid peel off.The present invention devises the water reducer of suitable consumption, the addition of cement water reducing agent, subtracts
Hydrophilic polyether lateral chain in water preparation structure is stretched in solution, thus can form one at the cement particle surface adsorbed
Determine the hydrophilic solid adsorption layer of thickness.When cement granules near time, adsorption layer starts overlap, thus can between cement granules
To produce sterically hindered effect, overlap is the most, and power that is this sterically hindered and that repel is the biggest, namely condenses between cement granules
The obstruction power of effect is the biggest so that the slump of concrete component keeps good.The present invention uses suitable pigment iron oxide red,
Good dispersion and stable under the system of the present invention, in the case of being not required to add surfactant, still can keep dispersion
Stability, thus form the outward appearance of uniform in color.
The decorative layer of the present invention can one-shot forming, it is achieved clear water decorative effect, also can pass through pickling, slow setting, ball blast, water mill
Realizing undisguisedly expecting texture etc. technique, being also with mould and turn over and make art veins effect, its decoration is flexible and changeable, can meet difference
Client's requirement to building skin pattern, is a kind of ideal construction exterior exterior material.It can be used for shear wall, framework or
The decorating outer wall of building of the structural systems such as low layer.
Detailed description of the invention:
The preferred embodiment of the present invention presented below, to help being further appreciated by the present invention, but the protection model of the present invention
Enclose and be not limited in these embodiments.
Embodiment 1
Decorative layer formula: road cement 600 parts, particle diameter 20～40 mesh quartz sand 820 parts, particle diameter 70～140 mesh fluvial sand 230
Part, particle diameter 325 mesh fluvial sand 210 parts, water reducer 50 parts, 140 parts of water, pigment iron oxide red 1.8 parts.
Preparation: after decorative layer formula uniform stirring is mixed on mould cloth, be decorative layer after uniform distribution；
Application: the decorative layer good at cloth lays boundary layer grid cloth, then (it mainly becomes by structure sheaf super high strength concrete
Point with decoration close more preferably) be evenly distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt after paving, cloth complete enter
Row maintenance, carries out the demoulding after maintenance to demoulding strength, can be prepared by adjusting redly the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 2
Decorative layer formula: road cement 580 parts, particle diameter 20～40 mesh quartz sand 780 parts, particle diameter 70～140 mesh fluvial sand 248
Part, particle diameter 325 mesh fluvial sand 220 parts, water reducer 60 parts, 130 parts of water, pigment iron oxide red 2.6 parts；
Preparation: after decorative layer formula uniform stirring is mixed on mould cloth, be decorative layer after uniform distribution；
Application: the decorative layer good at cloth lays boundary layer grid cloth, then (it mainly becomes by structure sheaf super high strength concrete
Point with decoration close more preferably) be evenly distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt after paving, cloth complete enter
Row maintenance, carries out the demoulding after maintenance to demoulding strength, can be prepared by adjusting redly the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 3
Decorative layer formula: Sheng Dehan white cement 560 parts, particle diameter 20～40 mesh quartz sand 400 parts, particle diameter 20～40 mesh dodges zinc
300 parts of Ore, 60 parts of particle diameter 10～20 mesh granite, particle diameter 70～140 mesh fluvial sand 220 parts, particle diameter 325 mesh fluvial sand 215 parts, subtract
50 parts of water preparation, 138 parts of water, pigment iron oxide red 0.2 part；
Preparation and the application on high-strength concrete Decorative hanging board:
Structure sheaf: use super high strength concrete；
Boundary layer: use basalt grid cloth to lay；
Implement step as follows:
Retarder is sprayed on mould, after retarder dry tack free, carries out cloth.Concrete by decorative layer formula
Uniform stirring mix after on mould cloth, lay boundary layer grid cloth after uniform distribution, then by strong for structure sheaf superelevation coagulation
Soil is evenly distributed on grid cloth, and slight vibration 5～15s places pre-buried back of the body bolt after paving, and cloth is complete carries out maintenance, treats that maintenance is extremely
Carry out the demoulding after demoulding strength, after the demoulding, decor surface water is rinsed so that it is expose aggregate, after drying moisture,
Can be prepared by adjusting redly the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 4
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali-resisting glass fiber three dimensional fabric to lay；
Decorative layer: Sheng Dehan cement 410 parts, particle diameter 20～40 mesh fluvial sand 100 parts, 410 parts of particle diameter 20～40 mesh calcite,
200 parts of particle diameter 20～40 mesh bornite, particle diameter 10～20 mesh garnet 110 parts, particle diameter 70～140 mesh quartz sand 225 parts, particle diameter
325 mesh fluvial sand 180 parts, water reducer 48 parts, 128 parts of water, pigment iron oxide red 3.3 parts；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary layer grid
Cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt, cloth after paving
Expect complete to carry out maintenance, after maintenance to demoulding strength, carry out the demoulding, with mordant, decor surface is scrubbed after the demoulding,
Wash away surface slurry with clear water after question response is complete, i.e. prepare after drying moisture and adjust the high-strength concrete of decorative layer to decorate redly
Link plate.
Embodiment 5
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali resistant glass fibre open weave cloth to lay；
Decorative layer: road cement 780 parts, particle diameter 20～40 mesh fluvial sand 200 parts, particle diameter 20～40 mesh garnet 200 parts, grain
Footpath 20～40 mesh cassiterite 360 parts, 70 parts of particle diameter 20～40 conjunctival congestion iron mine, particle diameter 70～140 mesh fluvial sand 210 parts, particle diameter 325 mesh stone
Sand 210 parts, water reducer 90 parts, 125 parts of water；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary layer grid
Cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt, cloth after paving
Expect complete to carry out maintenance, after maintenance to demoulding strength, carry out the demoulding, send into shot-blasting machine after the demoulding and carry out ball blast, treat surface slurry
Uniformly throw and its surface carried out steel gray except rear and scrub process, adjust the high-strength concrete decoration of decorative layer to hang redly
Plate.
Embodiment 6
Structure sheaf: use super high strength concrete；
Boundary layer: use bar-mat reinforcement to lay；
Decorative layer: Sheng Dehan cement 600 parts, particle diameter 20～40 mesh quartz sand 100 parts, particle diameter 20～40 mesh bornite 500
Part, particle diameter 20～40 mesh Anhydrite 200 parts, particle diameter 20～40 mesh Iceland spar 80 parts, particle diameter 70～140 mesh fluvial sand 170 parts, particle diameter
325 mesh fluvial sand 160 parts, water reducer 100 parts, 90 parts of water；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary layer grid
Cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt, cloth after paving
Expect complete to carry out maintenance, after maintenance to demoulding strength, carry out the demoulding, send into buffing machine after the demoulding and carry out surface finish process, treat
Surface finish to expose clearly aggregate and smooth surface uniformly after complete polishing process, can be prepared by adjusting redly decorative layer
High-strength concrete Decorative hanging board.
Embodiment 7
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali-resisting glass fiber three dimensional fabric to lay；
Decorative layer: road cement 600 parts, particle diameter 20～40 mesh fluvial sand 400 parts, 300 parts of particle diameter 20～40 mesh tourmaline, grain
Footpath 20～40 mesh malachite 100 parts, particle diameter 70～140 mesh fluvial sand 210 parts, particle diameter 325 mesh quartz sand 200 parts, water reducer 59 parts,
121 parts of water；
Implement step as follows:
Retarder is sprayed on mould, after retarder dry tack free, carries out cloth.Decorative layer concrete is uniformly stirred
Mix after mixing cloth on mould, after uniform distribution, lay boundary layer grid cloth, then by uniform for structure sheaf super high strength concrete
Being distributed on grid cloth, slight vibration 5～15s places pre-buried back of the body bolt after paving, and cloth is complete carries out maintenance, treats that maintenance is strong to the demoulding
Carry out the demoulding after degree, after the demoulding, decor surface water is rinsed so that it is expose aggregate, after drying moisture, can make
Obtain the high-strength concrete Decorative hanging board adjusting decorative layer redly.
The decorative layer thickness of the present invention is preferably 4～6mm, and the largest particles particle diameter of mortar is not more than 2mm；
Above-described embodiment is the present invention preferably embodiment, but embodiments of the present invention are not by above-described embodiment
Limit, the change made under other any spirit without departing from the present invention and principle, modify, substitute, combine, simplify,
All should be the substitute mode of equivalence, within being included in protection scope of the present invention.
Claims (10)
1. a decorative layer for red color tone high-strength concrete Decorative hanging board, is characterized in that, by including the former of following weight
Material prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 700～1000 parts, particle diameter 70～140 mesh sand 150～250 parts, particle diameter
325 mesh sand 80～240 parts, water reducer 40～120 parts, water 120～175 parts, pigment 0～4 parts.
The most according to claim 1, the decorative layer of red color tone high-strength concrete Decorative hanging board, is characterized in that, by including following weight
The raw material of amount part proportioning prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 750～850 parts, particle diameter 70～140 mesh sand 200～240 parts, particle diameter 325
Mesh sand 180～230 parts, water reducer 45～90 parts, water 120～140 parts, pigment iron oxide red 1.8～3.0 parts.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, described cement
For white cement, its whiteness is more than 75.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, described grain grain
Footpath 10～40 mesh sand is the mixing of one or more in quartz sand, river sand.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, described particle diameter
10～40 mesh sand are the mixture of color sand and quartz sand；Or the mixture of color sand and river sand；Or color sand and quartz sand and river sand
Mixture.
The most according to claim 5, the decorative layer of red color tone high-strength concrete Decorative hanging board, is characterized in that, the volume of color sand is not
Exceed the 30% of particle diameter 10～40 mesh sand.
The most according to claim 5, the decorative layer of red color tone high-strength concrete Decorative hanging board, is characterized in that, color sand can be to dodge
Zinc ore, tourmaline, calcite, cassiterite, bornite, garnet, crocoite, Chalkopyrite, colorful pebble, realgar stone, goethitum, Huang Tie
Ore deposit, serpentine, chlorite, diopside, villiersite, malachite, bloodstone, dravite, galena, Talcum, granite, ice continent
Stone, griotte, pyroxene, molybdenite, illite, sandstone, Anhydrite, manganite, ilmenite, magnetic iron ore, tantalite, pyrolusite, black
The mixing of one or more in copper mine.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, particle diameter 10～
The mixture that 40 mesh sand are made up of the material of following weight portion: fluvial sand 200 parts, garnet 200 parts, cassiterite 360 parts, bloodstone
70 parts.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, particle diameter 10～
The mixture that 40 mesh sand are made up of the material of following weight portion: 410 parts of particle diameter 20～40 mesh calcite, particle diameter 20～40 mesh speckle
Copper mine 200 parts, particle diameter 10～20 mesh garnet 110 parts.
The decorative layer of red color tone high-strength concrete Decorative hanging board the most according to claim 1 or claim 2, is characterized in that, particle diameter 10～
The mixture that 40 mesh sand are made up of the material of following weight portion: quartz sand 400 parts, 300 parts of sphalerite stone, 60 parts of granite.