CN106013683A - Decorative layer for brown high-strength concrete decorative hanging plate - Google Patents

Decorative layer for brown high-strength concrete decorative hanging plate Download PDF

Info

Publication number
CN106013683A
CN106013683A CN201610541605.0A CN201610541605A CN106013683A CN 106013683 A CN106013683 A CN 106013683A CN 201610541605 A CN201610541605 A CN 201610541605A CN 106013683 A CN106013683 A CN 106013683A
Authority
CN
China
Prior art keywords
parts
particle diameter
mesh
sand
brown
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610541605.0A
Other languages
Chinese (zh)
Inventor
周全
王术华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Mingsheng Drawin Technology Investment Co Ltd
Original Assignee
China Mingsheng Drawin Technology Investment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Mingsheng Drawin Technology Investment Co Ltd filed Critical China Mingsheng Drawin Technology Investment Co Ltd
Priority to CN201610541605.0A priority Critical patent/CN106013683A/en
Publication of CN106013683A publication Critical patent/CN106013683A/en
Pending legal-status Critical Current

Abstract

The invention relates to external wall decoration of a building and specifically relates to a decorative layer for a brown high-strength concrete decorative hanging plate. According to the scheme, the decorative layer is prepared from the following raw materials in parts by weight: 400-800 parts of cement, 710-950 parts of 10-40-mesh sand, 160-240 parts of 70-140-mesh sand, 110-260 parts of 325-mesh sand, 45-110 parts of a water reducer, 120-160 parts of water and 0-4 parts of pigment iron oxide brown. On the basis of the prior part, the matching form of cement base stock and multi-level specific sand is adopted, and the decorative layer can be tightly connected with the structural layer of an external wall hanging plate, so that the connecting strength can be greatly increased and the stripping can be avoided.

Description

A kind of brown heightens the decorative layer of reinforced concrete Decorative hanging board
Technical field
The present invention relates to decorating outer wall of building, be specifically related to a kind of brown and heighten reinforced concrete Decorative hanging board Decorative layer.
Background technology
In existing building exposed wall decorative hangig panel, stone decoration link plate occupies quite a few market share. But the taking of stone material, transport, processing etc. more difficult, complicated process of preparation, cost is high；And stone material It is a kind of non-renewable resources, heavy damage ecological environment of digging up mine.Along with people are ecological, environmental protection ideas Lifting, and to resources conservation and the enhancing of protective awareness, therefore, imitative stone material based on concrete Decorative hanging board also becomes the primary study object of current field of decorative, and have developed various respectively The product of sample.But the color and luster requirement that Concrete decorated hanging board is to cement, admixture, sand and stone It is desirable that the highest with grain composition, selects to be also intended to ask high to the water reducer in additive simultaneously, Must colourless, water-reducing rate is high, little loss of slump and cement adaptability are strong, so concrete decoration Link plate easily produces that color and luster is the best, the problem of stripping easy to crack.
The Chinese invention patent application of Publication No. CN1045964A discloses the dress of a kind of cement sintering Plaque, coloured silk mixes in proportion with No. 425 white cements, quartz sand and inorganic pigment, forms band chromatic colour Pattern such as animal, scenery with hills and waters, birds and flowers and large-scale decorative pattern combination pattern.But the decoration that the program is formed Plate easily collapses, and inferior suitability, and easy to crack.Chinese invention patent " CN102493617B " Disclosing a kind of imitative stone decoration panel, its structure is divided into three layers, and panel layer is thin-walled Bartlit, base Layer is cement-based material, is connected with polymer mortar and makes a kind of imitative stone decoration between surface layer with basic unit Panel.The consumption of stone material is greatly reduced by this kind of method, greatly reduces the dependence to stone material.But, The method of attachment unreliable that the method uses, cement basic layer is connected to adverse circumstances with slabstone surface layer Under be easily peeled off, and layers of material composition differ greatly, their thermal coefficient of expansion differs, at hot ring Easily ftracture under border, peel off.Meanwhile, in the installation in later stage, need the operations such as boring, not only increase Add cost, and increase the percent defective of stone material.
Summary of the invention
For the decorative layer overcoming existing exposed wall decorative hangig panel stripping easy to crack and the best the asking of color and luster Topic, the present invention provides a kind of novel brown to heighten the decorative layer of reinforced concrete Decorative hanging board.
The implementation of the present invention is: a kind of brown heightens the decorative layer of reinforced concrete Decorative hanging board, by Raw material including following weight prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 710～950 parts, particle diameter 70～140 mesh sand 160～240 parts, particle diameter 325 mesh sand 110～260 parts, water reducer 45～110 parts, water 120～160 Part, pigment iron oxide brown 0～4 parts.
Another preferred version of the present invention is, on the basis of such scheme, by including that following weight portion is joined The raw material of ratio prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 760～850 parts, particle diameter 70～140 mesh sand 200～240 parts, particle diameter 325 mesh sand 160～220 parts, water reducer 45～90 parts, water 120～140 Part, pigment iron oxide brown 0.2～3.7 parts.
Another preferred version of the present invention is, on the basis of such scheme, described cement is white cement, Its whiteness is more than 75.
Another preferred version of the present invention is, on the basis of such scheme, and described particle diameter 10～40 mesh sand For the mixing of one or more in quartz sand, river sand.
Another preferred version of the present invention is, on the basis of such scheme, and described particle diameter 70～140 mesh Sand is the mixing of the one or both in quartz sand or river sand；
Another preferred version of the present invention is, on the basis of such scheme, described particle diameter 325 mesh sand is The mixing of the one or both in quartz sand or river sand.
Another preferred version of the present invention is, on the basis of such scheme, and described particle diameter 10～40 mesh sand Mixture for color sand with quartz sand；Or the mixture of color sand and river sand；Or color sand and quartz sand and river Husky mixture.
Another preferred version of the present invention is, on the basis of such scheme, the volume of color sand is less than footpath The 30% of 10～40 mesh sand.
Another preferred version of the present invention is, on the basis of such scheme, color sand can be sphalerite, Tourmaline, calcite, cassiterite, bornite, garnet, crocoite, Chalkopyrite, colorful pebble, hero Huangshi, goethitum, pyrite, serpentine, chlorite, diopside, villiersite, malachite, red Iron mine, dravite, galena, Talcum, granite, Iceland spar, griotte, pyroxene, brightness molybdenum Ore deposit, illite, sandstone, Anhydrite, manganite, ilmenite, magnetic iron ore, tantalite, pyrolusite, The mixing of one or more in tetrahedrite.
Another preferred version of the present invention is, on the basis of such scheme, in color sand containing sphalerite, Tourmaline, calcite, cassiterite, bornite, garnet, bloodstone, dravite, goethitum, One or more in serpentine, pyroxene, and account for more than the 20% of color sand total amount.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand be by The mixture of the material composition of following weight portion: particle diameter 20～40 mesh quartz sand 400 parts, particle diameter 20～ 40 280 parts of mesh pyroxenes, 68 parts of particle diameter 10～20 mesh calcite.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand be by The mixture of the material composition of following weight portion: particle diameter 20～40 mesh fluvial sand 100 parts, particle diameter 20～ 40 mesh serpentine 415 parts, 160 parts of particle diameter 20～40 mesh granite, particle diameter 10～20 conjunctival congestion iron mine 110 parts of stone.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand be by The mixture of the material composition of following weight portion: particle diameter 20～40 mesh fluvial sand 200 parts, particle diameter 20～ 40 mesh cassiterites 210 parts, 350 parts of particle diameter 20～40 conjunctival congestion iron mine, particle diameter 20～40 mesh serpentine 70 Part.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand be by The mixture of the material composition of following weight portion: particle diameter 20～40 mesh quartz sand 100 parts, particle diameter 20～ 40 mesh dravites 490 parts, particle diameter 20～40 mesh garnet 200 parts, particle diameter 20～40 mesh Magnet 78 parts of ore deposit.
Another preferred version of the present invention is, on the basis of such scheme, particle diameter 10～40 mesh sand be by The mixture of the material composition of following weight portion: particle diameter 20～40 mesh fluvial sand 400 parts, particle diameter 20～ 40 280 parts of mesh pyroxenes, particle diameter 20～40 mesh Anhydrite 120 parts.
The present invention on the basis of existing technology, uses the shape that cement base material and multistage specific sand coordinate Formula, research finds, uses the formula design of the present invention, prepared decorative layer, can hang with exterior wall The structure sheaf of plate is completely embedded, with structure sheaf between the layers under cement aquation, and cement water Change product to be interweaved, make layer inconspicuous with the demarcation line of layer, thus be greatly improved bonding strength, keep away Exempt to peel off.The present invention devises the water reducer of suitable consumption, the addition of cement water reducing agent, and water reducer is tied Hydrophilic polyether lateral chain in structure is stretched in solution, thus can at the cement particle surface adsorbed To form certain thickness hydrophilic solid adsorption layer.When cement granules near time, adsorption layer start weight Folded, thus sterically hindered effect can be produced between cement granules, overlap is the most, this space bit Resistance and the power repelled are the biggest namely the biggest to the obstruction power of cohesion between cement granules so that The slump of concrete component keeps good.The present invention uses suitable pigment iron oxide brown, at this Good dispersion and stable under bright system, in the case of being not required to add surfactant, still can keep The stability of dispersion, thus form the outward appearance of uniform in color.
The decorative layer of the present invention can one-shot forming, it is achieved clear water decorative effect, also can pass through pickling, slow The techniques such as solidifying, ball blast, water mill realize undisguisedly expecting texture, are also with mould and turn over and make art veins effect Really, its decoration is flexible and changeable, can meet the different client requirement to building skin pattern, is a kind of non- The most preferably construction exterior exterior material.It can be used for building of the structural systems such as shear wall, framework or low layer Build decoration of exterior wall.
Detailed description of the invention:
The preferred embodiment of the present invention presented below, to help being further appreciated by the present invention, but this Bright protection domain is not limited in these embodiments.
Embodiment 1
Decorative layer formula: road cement 600 parts, particle diameter 20～40 mesh quartz sand 820 parts, particle diameter 70～140 mesh fluvial sand 230 parts, particle diameter 325 mesh fluvial sand 210 parts, water reducer 50 parts, 140 parts of water, Pigment iron oxide brown 1.9 parts.
Preparation: after decorative layer formula uniform stirring is mixed on mould cloth, after uniform distribution i.e. For decorative layer；
Application: the decorative layer good at cloth lays boundary layer grid cloth, then by strong for structure sheaf superelevation coagulation Soil (its main component is close more preferably with decorative layer) is evenly distributed on grid cloth, slight vibration 5～15s Placing pre-buried back of the body bolt after paving, cloth is complete carries out maintenance, carries out the demoulding after maintenance to demoulding strength, Can be prepared by band brown and adjust the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 2
Decorative layer formula: road cement 580 parts, particle diameter 20～40 mesh quartz sand 780 parts, particle diameter 70～140 mesh fluvial sand 248 parts, particle diameter 325 mesh fluvial sand 220 parts, water reducer 60 parts, 130 parts of water, Pigment iron oxide brown 2.3 parts；
Preparation: after decorative layer formula uniform stirring is mixed on mould cloth, after uniform distribution i.e. For decorative layer；
Application: the decorative layer good at cloth lays boundary layer grid cloth, then by strong for structure sheaf superelevation coagulation Soil (its main component is close with decoration more preferably) is evenly distributed on grid cloth, and slight vibration 5～15s spreads Placing pre-buried back of the body bolt after Ping, cloth is complete carries out maintenance, carries out the demoulding after maintenance to demoulding strength, Can be prepared by band brown and adjust the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 3
Decorative layer formula: Sheng Dehan white cement 560 parts, particle diameter 20～40 mesh quartz sand 400 parts, grain 280 parts of footpath 20～40 mesh pyroxene, 68 parts of particle diameter 10～20 mesh calcite, particle diameter 70～140 mesh river 220 parts of sand, particle diameter 325 mesh fluvial sand 215 parts, water reducer 50 parts, 138 parts of water, pigment ferrum oxide Palm fibre 0.23 part；
Preparation and the application on high-strength concrete Decorative hanging board:
Structure sheaf: use super high strength concrete；
Boundary layer: use basalt grid cloth to lay；
Implement step as follows:
Retarder is sprayed on mould, after retarder dry tack free, carries out cloth.Decorative layer is joined Side concrete uniform stirring mix after on mould cloth, after uniform distribution lay boundary layer grid Cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, after slight vibration 5～15s is paved Placing pre-buried back of the body bolt, cloth is complete carries out maintenance, carries out the demoulding, the demoulding after maintenance to demoulding strength Afterwards decor surface water is rinsed so that it is expose aggregate, after drying moisture, can be prepared by The high-strength concrete Decorative hanging board of decorative layer is adjusted with brown.
Embodiment 4
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali-resisting glass fiber three dimensional fabric to lay；
Decorative layer: Sheng Dehan cement 410 parts, particle diameter 20～40 mesh fluvial sand 100 parts, particle diameter 20～ 40 mesh serpentine 415 parts, particle diameter 20～40 mesh granite 160 parts, particle diameter 10～20 conjunctival congestion iron mine 110 parts of stone, particle diameter 70～140 mesh quartz sand 225 parts, particle diameter 325 mesh fluvial sand 180 parts, diminishing Agent 48 parts, 128 parts of water, pigment iron oxide yellow 3.65 parts；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary Surface layer grid cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～ 15s places pre-buried back of the body bolt after paving, cloth is complete carries out maintenance, carries out after maintenance to demoulding strength The demoulding, scrubs decor surface with mordant after the demoulding, washes away with clear water after question response is complete Surface slurry, i.e. prepares band brown and adjusts the high-strength concrete Decorative hanging board of decorative layer after drying moisture.
Embodiment 5
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali resistant glass fibre open weave cloth to lay；
Decorative layer: road cement 780 parts, particle diameter 20～40 mesh fluvial sand 200 parts, particle diameter 20～40 Mesh cassiterite 200 parts, particle diameter 20～40 conjunctival congestion iron ore 350 parts, particle diameter 20～40 mesh serpentine 70 Part, particle diameter 70～140 mesh fluvial sand 210 parts, particle diameter 325 mesh quartz sand 210 parts, water reducer 90 parts, 125 parts of water；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary Surface layer grid cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～ 15s places pre-buried back of the body bolt after paving, cloth is complete carries out maintenance, carries out after maintenance to demoulding strength The demoulding, sends into shot-blasting machine and carries out ball blast, carry out its surface after surface slurry is uniformly thrown and removed after the demoulding Steel gray and scrub process, band brown adjusts the high-strength concrete Decorative hanging board of decorative layer.
Embodiment 6
Structure sheaf: use super high strength concrete；
Boundary layer: use bar-mat reinforcement to lay；
Decorative layer: Sheng Dehan cement 600 parts, particle diameter 20～40 mesh quartz sand 100 parts, particle diameter 20～ 40 mesh dravites 490 parts, particle diameter 20～40 mesh garnet 200 parts, particle diameter 20～40 mesh Magnet 78 parts of stone, particle diameter 70～140 mesh fluvial sand 170 parts, particle diameter 325 mesh fluvial sand 160 parts, water reducer 100 parts, 90 parts of water；
Implement step as follows:
After decorative layer concrete uniform stirring is mixed on mould cloth, after uniform distribution lay boundary Surface layer grid cloth, then structure sheaf super high strength concrete is evenly distributed on grid cloth, slight vibration 5～ 15s places pre-buried back of the body bolt after paving, cloth is complete carries out maintenance, carries out after maintenance to demoulding strength The demoulding, sends into buffing machine and carries out surface finish process, treat that surface finish is to exposing bone clearly after the demoulding Material and smooth surface uniformly after complete polishing process, can be prepared by band brown and adjust the high-strength coagulation of decorative layer Soil Decorative hanging board.
Embodiment 7
Structure sheaf: use super high strength concrete；
Boundary layer: use alkali-resisting glass fiber three dimensional fabric to lay；
Decorative layer: road cement 600 parts, particle diameter 20～40 mesh fluvial sand 400 parts, particle diameter 20～40 280 parts of mesh pyroxene, particle diameter 20～40 mesh Anhydrite 120 parts, particle diameter 70～140 mesh fluvial sand 210 parts, Particle diameter 325 mesh quartz sand 200 parts, water reducer 59 parts, 121 parts of water；
Implement step as follows:
Retarder is sprayed on mould, after retarder dry tack free, carries out cloth.Decorative layer is mixed Solidifying soil uniform stirring mix after on mould cloth, lay boundary layer grid cloth after uniform distribution, then Being evenly distributed on grid cloth by structure sheaf super high strength concrete, slight vibration 5～15s is placed pre-after paving Burying back of the body bolt, cloth is complete carries out maintenance, carries out the demoulding, to dress after the demoulding after maintenance to demoulding strength Decorations layer surface water is rinsed so that it is exposes aggregate, after drying moisture, can be prepared by band brown Adjust the high-strength concrete Decorative hanging board of decorative layer.
The decorative layer thickness of the present invention is preferably 4～6mm, and the largest particles particle diameter of mortar is not more than 2mm；
Above-described embodiment is the present invention preferably embodiment, but embodiments of the present invention are not by upper Stating the restriction of embodiment, that is made under other any spirit without departing from the present invention and principle changes Become, modify, substitute, combine, simplify, all should be the substitute mode of equivalence, be included in the present invention Protection domain within.

Claims (10)

1. brown heightens a decorative layer for reinforced concrete Decorative hanging board, it is characterized in that, as follows by including The raw material of weight prepares:
Cement 400～800 parts, particle diameter 10～40 mesh sand 710～950 parts, particle diameter 70～140 mesh sand 160～240 parts, particle diameter 325 mesh sand 110～260 parts, water reducer 45～110 parts, water 120～160 Part, pigment iron oxide brown 0～4 parts.
The most according to claim 1, brown heightens the decorative layer of reinforced concrete Decorative hanging board, its feature It is to be prepared by the raw material including following weight:
Cement 400～800 parts, particle diameter 10～40 mesh sand 760～850 parts, particle diameter 70～140 mesh sand 200～240 parts, particle diameter 325 mesh sand 160～220 parts, water reducer 45～90 parts, water 120～140 Part, pigment iron oxide brown 0.2～3.7 parts.
Brown the most according to claim 1 or claim 2 heightens the decorative layer of reinforced concrete Decorative hanging board, its Feature is, described cement is white cement, and its whiteness is more than 75.
Brown the most according to claim 1 or claim 2 heightens the decorative layer of reinforced concrete Decorative hanging board, its Feature is, described particle diameter 10～40 mesh sand is the mixing of one or more in quartz sand, river sand.
Brown the most according to claim 1 or claim 2 heightens the decorative layer of reinforced concrete Decorative hanging board, its Feature is, described particle diameter 10～40 mesh sand is the mixture of color sand and quartz sand；Or color sand and river sand Mixture；Or color sand and quartz sand and the mixture of river sand.
The most according to claim 5, brown heightens the decorative layer of reinforced concrete Decorative hanging board, its feature It is that the volume of color sand is less than the 30% of particle diameter 10～40 mesh sand.
The most according to claim 5, brown heightens the decorative layer of reinforced concrete Decorative hanging board, its feature It is that color sand can be sphalerite, tourmaline, calcite, cassiterite, bornite, garnet, chromium lead Ore deposit, Chalkopyrite, colorful pebble, realgar stone, goethitum, pyrite, serpentine, chlorite, saturating brightness Stone, villiersite, malachite, bloodstone, dravite, galena, Talcum, granite, ice continent Stone, griotte, pyroxene, molybdenite, illite, sandstone, Anhydrite, manganite, ilmenite, magnetic The mixing of one or more in iron mine, tantalite, pyrolusite, tetrahedrite.
The most according to claim 5, brown heightens the decorative layer of reinforced concrete Decorative hanging board, its feature It is, containing sphalerite, tourmaline, calcite, cassiterite, bornite, garnet, red ferrum in color sand One or more in ore deposit, dravite, goethitum, serpentine, pyroxene, and account for color sand total amount More than 20%.
Brown the most according to claim 1 or claim 2 heightens the decorative layer of reinforced concrete Decorative hanging board, its Feature is, the mixture that particle diameter 10～40 mesh sand is made up of the material of following weight portion: particle diameter 20～ 40 mesh quartz sands 400 parts, 280 parts of particle diameter 20～40 mesh pyroxene, particle diameter 10～20 mesh calcite 68 Part.
Brown the most according to claim 1 or claim 2 heightens the decorative layer of reinforced concrete Decorative hanging board, It is characterized in that, the mixture that particle diameter 10～40 mesh sand is made up of the material of following weight portion: particle diameter 20～40 mesh fluvial sand 100 parts, particle diameter 20～40 mesh serpentine 415 parts, particle diameter 20～40 Mu Hua hilllock 160 parts of rock, particle diameter 10～20 conjunctival congestion iron ore 110 parts；Or described particle diameter 10～40 mesh sand is The mixture being made up of the material of following weight portion: particle diameter 20～40 mesh fluvial sand 200 parts, particle diameter 20～ 40 mesh cassiterites 210 parts, 350 parts of particle diameter 20～40 conjunctival congestion iron mine, particle diameter 20～40 mesh serpentine 70 Part；Or the mixture that described particle diameter 10～40 mesh sand is made up of the material of following weight portion: particle diameter 20～40 mesh quartz sands 100 parts, particle diameter 20～40 mesh dravite 490 parts, particle diameter 20～40 mesh Garnet 200 parts, particle diameter 20～40 mesh magnetic iron ore 78 parts；Or described particle diameter 10～40 mesh sand is The mixture being made up of the material of following weight portion: particle diameter 20～40 mesh fluvial sand 400 parts, particle diameter 20～ 40 280 parts of mesh pyroxenes, particle diameter 20～40 mesh Anhydrite 120 parts.
CN201610541605.0A 2016-07-11 2016-07-11 Decorative layer for brown high-strength concrete decorative hanging plate Pending CN106013683A (en)