CN106192481A - A kind of leatherware coloring dyestuff binders - Google Patents
A kind of leatherware coloring dyestuff binders Download PDFInfo
- Publication number
- CN106192481A CN106192481A CN201610653246.8A CN201610653246A CN106192481A CN 106192481 A CN106192481 A CN 106192481A CN 201610653246 A CN201610653246 A CN 201610653246A CN 106192481 A CN106192481 A CN 106192481A
- Authority
- CN
- China
- Prior art keywords
- parts
- dyestuff
- leatherware
- heated
- adds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of leatherware coloring dyestuff binders, relate to leatherware processing technique field, it is made up of the raw material of following parts by weight: terpene resin 15 20 parts, active hargil 10 15 parts, microwax 8 13 parts, linear low density polyethylene 6 11 parts, water-soluble chitosan 59 parts, hydrogenated rosin 48 parts, methoxy poly (ethylene glycol) 48 parts, petroleum coke 36 parts, ceramic 36 parts, adhesion promoter 24 parts, polyvinylpyrrolidone 24 parts, nanometer rubber powder 24 parts, polyacrylamide 12 parts, oleamide 12 parts, Borax 0.5 1 parts, butyl acetate 25 30 parts.Invention adhesives is not only good with remaining component compatibility of dyestuff, is effectively improved the dyestuff uniformity, and can significantly improve color firmness, resistance to water and the resistant of high or low temperature of dyestuff, thus expands dyestuff range in field of leather.
Description
Technical field:
The present invention relates to leatherware processing technique field, be specifically related to a kind of leatherware coloring dyestuff binders.
Background technology:
In leather processing procedure, it usually needs leather is dyeed, leather is made to present various chromatic colour, with
The color adapting to consumer uses demand.The tone that during leather coloring, leather to be given is bright-coloured and pure, also requires color and luster
Uniformity, color firmness is high.But the color firmness of presently commercially available leather dye is general, this is mainly by dyestuff on leather
Cohesive determines.For this problem, we develop a kind of leatherware coloring dyestuff binders, and the feature of environmental protection is strong, will
It can significantly improve the color firmness of dyestuff after adding in dyestuff, thus the outward appearance improving leatherware uses quality.
Summary of the invention:
The technical problem to be solved is to provide a kind of resistance to water and resistant of high or low temperature is good and is conducive to improving
The leatherware coloring dyestuff binders of dyestuff color firmness.
The technical problem to be solved uses following technical scheme to realize:
A kind of leatherware coloring dyestuff binders, is made up of the raw material of following parts by weight:
Terpene resin 15-20 part, active hargil 10-15 part, microwax 8-13 part, linear low density polyethylene 6-11 part,
Water-soluble chitosan 5-9 part, hydrogenated rosin 4-8 part, methoxy poly (ethylene glycol) 4-8 part, petroleum coke 3-6 part, ceramic 3-6
Part, adhesion promoter 2-4 part, polyvinylpyrrolidone 2-4 part, nanometer rubber powder 2-4 part, polyacrylamide 1-2 part, oleic acid acyl
Amine 1-2 part, Borax 0.5-1 part, butyl acetate 25-30 part;
Its preparation method comprises the steps:
(1) in butyl acetate, add terpene resin and linear low density polyethylene, be stirred continuously down and be heated to the shape that refluxes
State isothermal holding 15min, adds hydrogenated rosin and petroleum coke, continues isothermal holding 15min, obtains material I;
(2) microwax is heated to 80-90 DEG C of insulation mixing 5min, is subsequently adding active hargil, ceramic and nanometer
Rubber powder, continues to be heated to 120-130 DEG C of insulation mixing 10min, obtains material II;
(3) in material I, add material II, methoxy poly (ethylene glycol), adhesion promoter and polyacrylamide, then add
Heat is to reflux state isothermal holding 10min, and process terminates the cooling of rear natural cooling, adds water-soluble after temperature is down to 50-60 DEG C
Property chitosan, polyvinylpyrrolidone, oleamide and Borax, be sufficiently mixed uniformly.
Described adhesion promoter is made up of the raw material of following parts by weight: epoxide coal bituminous 10-15 part, C9 Petropols
7-12 part, polyethylene glycol oxide 5-8 part, rubber powder 5-8 part, super fine magnesia 4-7 part, polyoxylethylene abietate 4-7 part, hydrophobic
Type nano silicon 3-5 part, glycerol trioleate 2-3 part, asbestos wool 1-2 part, glass powder 1-2 part, carbamide 0.5-1 part, receive
Rice zinc oxide 0.5-1 part, its preparation method is: first to epoxide coal bituminous middle addition C9 Petropols, polyethylene glycol oxide and nanometer
Zinc oxide, and it is heated to 120-130 DEG C of insulation mixing 15min, add rubber powder, polyoxylethylene abietate and hydrophobic type and receive
Rice silicon dioxide, continues insulation mixing 10min, then lowers the temperature with 10 DEG C/min under ice-water bath, after temperature is down to 50-60 DEG C
Add super fine magnesia, glycerol trioleate, asbestos wool, glass powder and carbamide, be sufficiently mixed uniformly.
The preparation method of described hydrophobic nano silicon dioxide is: 15 parts of tetraethyl orthosilicates add equivalent with volume ratio
In the mixed solvent of 1:1 second alcohol and water preparation, stirring is micro-under microwave frequency 2450MHz, power 700W after forming homogeneous solution
Ripple processes 5min, adds 1 part of polyoxyethylene lauryl ether, 0.5 part of beta-schardinger dextrin-and 0.5 part of titanate coupling agent, and mixing is all
Continuing microwave treatment 5min after even, then stand 30min, and be dried 8h at 100-105 DEG C, gained solid abrasive becomes powder,
Last roasting 3h at 550-600 DEG C.
The invention has the beneficial effects as follows: the present invention, with terpene resin as primary raw material, is aided with multiple auxiliary agent and prepares leather system
Product coloring dyestuff binders, this binding agent is directly appended in dyestuff when using, not only good with remaining component compatibility of dyestuff,
It is effectively improved the dyestuff uniformity, and color firmness, resistance to water and the resistant of high or low temperature of dyestuff can be significantly improved, thus expand
Dyestuff range in field of leather.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) in 30 parts of butyl acetates, add 15 parts of terpene resins and 6 parts of linear low density polyethylene, be stirred continuously down and add
Heat, to reflux state isothermal holding 15min, adds 4 parts of hydrogenated rosins and 3 parts of petroleum cokes, continues isothermal holding 15min, to obtain final product
Material I;
(2) 10 parts of microwaxes are heated to 80-90 DEG C of insulation mixing 5min, are subsequently adding 10 parts of active hargil, 5 parts of potteries
Micropowder and 2 parts of nanometer rubber powders, continue to be heated to 120-130 DEG C of insulation mixing 10min, obtain material II;
(3) in material I, material II, 4 parts of methoxy poly (ethylene glycol)s, 4 parts of adhesion promoters and 1 part of polyacrylamide are added
Amine, is then heated to reflux state isothermal holding 10min, and process terminates the cooling of rear natural cooling, after temperature is down to 50-60 DEG C
Add 6 parts of water-soluble chitosans, 3 parts of polyvinylpyrrolidones, 1 part of oleamide and 0.5 part of Borax, be sufficiently mixed uniformly.
Adhesion promoter is made up of the raw material of following parts by weight: first to 15 parts of epoxide coal bituminous 9 parts of C9 stones of middle addition
Oleoresin, 5 parts of polyethylene glycol oxides and 0.5 part of nano zine oxide, and it is heated to 120-130 DEG C of insulation mixing 15min, add 5
Part rubber powder, 4 parts of polyoxylethylene abietate and 3 parts of hydrophobic nano silicon dioxide, continue insulation mixing 10min, then exist
Lower the temperature with 10 DEG C/min under ice-water bath, add after temperature is down to 50-60 DEG C 4 parts of super fine magnesias, 2 parts of glycerol trioleate, 1
Part asbestos wool, 1 part of glass powder and 0.5 part of carbamide, be sufficiently mixed uniformly.
The preparation of hydrophobic nano silicon dioxide: 15 parts of tetraethyl orthosilicates are added equivalent with volume ratio 1:1 ethanol and
In the mixed solvent of water preparation, stirring forms after homogeneous solution microwave treatment under microwave frequency 2450MHz, power 700W
5min, adds 1 part of polyoxyethylene lauryl ether, 0.5 part of beta-schardinger dextrin-and 0.5 part of titanate coupling agent, and mix homogeneously is follow-up
Continuous microwave treatment 5min, then stands 30min, and is dried 8h at 100-105 DEG C, and gained solid abrasive becomes powder, finally in
Roasting 3h at 550-600 DEG C.
Embodiment 2
(1) in 30 parts of butyl acetates, add 20 parts of terpene resins and 8 parts of linear low density polyethylene, be stirred continuously down and add
Heat, to reflux state isothermal holding 15min, adds 6 parts of hydrogenated rosins and 3 parts of petroleum cokes, continues isothermal holding 15min, to obtain final product
Material I;
(2) 8 parts of microwaxes are heated to 80-90 DEG C of insulation mixing 5min, are subsequently adding 10 parts of active hargil, 3 parts of potteries
Micropowder and 2 parts of nanometer rubber powders, continue to be heated to 120-130 DEG C of insulation mixing 10min, obtain material II;
(3) in material I, material II, 5 parts of methoxy poly (ethylene glycol)s, 3 parts of adhesion promoters and 2 parts of polyacrylamides are added
Amine, is then heated to reflux state isothermal holding 10min, and process terminates the cooling of rear natural cooling, after temperature is down to 50-60 DEG C
Add 8 parts of water-soluble chitosans, 2 parts of polyvinylpyrrolidones, 1 part of oleamide and 0.5 part of Borax, be sufficiently mixed uniformly.
Adhesion promoter is made up of the raw material of following parts by weight: first to 15 parts of epoxide coal bituminous 7 parts of C9 stones of middle addition
Oleoresin, 6 parts of polyethylene glycol oxides and 1 part of nano zine oxide, and it is heated to 120-130 DEG C of insulation mixing 15min, add 7 parts
Rubber powder, 4 parts of polyoxylethylene abietate and 3 parts of hydrophobic nano silicon dioxide, continue insulation mixing 10min, then at ice
Lower the temperature with 10 DEG C/min under water-bath, add after temperature is down to 50-60 DEG C 5 parts of super fine magnesias, 3 parts of glycerol trioleate, 1 part
Asbestos wool, 1 part of glass powder and 0.5 part of carbamide, be sufficiently mixed uniformly.
The preparation of hydrophobic nano silicon dioxide: 15 parts of tetraethyl orthosilicates are added equivalent with volume ratio 1:1 ethanol and
In the mixed solvent of water preparation, stirring forms after homogeneous solution microwave treatment under microwave frequency 2450MHz, power 700W
5min, adds 1 part of polyoxyethylene lauryl ether, 0.5 part of beta-schardinger dextrin-and 0.5 part of titanate coupling agent, and mix homogeneously is follow-up
Continuous microwave treatment 5min, then stands 30min, and is dried 8h at 100-105 DEG C, and gained solid abrasive becomes powder, finally in
Roasting 3h at 550-600 DEG C.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (3)
1. a leatherware coloring dyestuff binders, it is characterised in that be made up of the raw material of following parts by weight:
Terpene resin 15-20 part, active hargil 10-15 part, microwax 8-13 part, linear low density polyethylene 6-11 part, water-soluble
Property chitosan 5-9 part, hydrogenated rosin 4-8 part, methoxy poly (ethylene glycol) 4-8 part, petroleum coke 3-6 part, ceramic 3-6 part, attached
Adhesion promoter 2-4 part, polyvinylpyrrolidone 2-4 part, nanometer rubber powder 2-4 part, polyacrylamide 1-2 part, oleamide 1-2
Part, Borax 0.5-1 part, butyl acetate 25-30 part;
Its preparation method comprises the steps:
(1) in butyl acetate, add terpene resin and linear low density polyethylene, be stirred continuously down and be heated to reflux state guarantor
Temperature processes 15min, adds hydrogenated rosin and petroleum coke, continues isothermal holding 15min, obtains material I;
(2) microwax is heated to 80-90 DEG C of insulation mixing 5min, is subsequently adding active hargil, ceramic and nanometer rubber powder,
Continue to be heated to 120-130 DEG C of insulation mixing 10min, obtain material II;
(3) in material I, add material II, methoxy poly (ethylene glycol), adhesion promoter and polyacrylamide, be then heated to
Reflux state isothermal holding 10min, process terminates the cooling of rear natural cooling, adds water soluble shells after temperature is down to 50-60 DEG C
Polysaccharide, polyvinylpyrrolidone, oleamide and Borax, be sufficiently mixed uniformly.
Leatherware coloring dyestuff binders the most according to claim 1, it is characterised in that described adhesion promoter
Be made up of the raw material of following parts by weight: epoxide coal bituminous 10-15 part, C9 Petropols 7-12 part, polyethylene glycol oxide 5-8 part,
Rubber powder 5-8 part, super fine magnesia 4-7 part, polyoxylethylene abietate 4-7 part, hydrophobic nano silicon dioxide 3-5 part, three
Olein 2-3 part, asbestos wool 1-2 part, glass powder 1-2 part, carbamide 0.5-1 part, nano zine oxide 0.5-1 part, it is prepared
Method is: first to epoxide coal bituminous middle addition C9 Petropols, polyethylene glycol oxide and nano zine oxide, and be heated to 120-130
DEG C insulation mixing 15min, adds rubber powder, polyoxylethylene abietate and hydrophobic nano silicon dioxide, continues insulation mixed
Close 10min, then lower the temperature with 10 DEG C/min under ice-water bath, after temperature is down to 50-60 DEG C, adds super fine magnesia, three oleic acid
Glyceride, asbestos wool, glass powder and carbamide, be sufficiently mixed uniformly.
Leatherware coloring dyestuff binders the most according to claim 2, it is characterised in that described hydrophobic nano two
The preparation method of silicon oxide is: the mixing 15 parts of tetraethyl orthosilicates addition equivalent prepared with volume ratio 1:1 second alcohol and water is molten
In agent, stirring forms after homogeneous solution microwave treatment 5min under microwave frequency 2450MHz, power 700W, adds 1 portion of Laurel
Polyoxyethylenated alcohol, 0.5 part of beta-schardinger dextrin-and 0.5 part of titanate coupling agent, continue microwave treatment 5min, then after mix homogeneously
Standing 30min, and be dried 8h at 100-105 DEG C, gained solid abrasive becomes powder, finally roasting 3h at 550-600 DEG C.