CN106192426A - A kind of polyester-cotton fabric and thermal dye sublimation transfer printing technique thereof - Google Patents
A kind of polyester-cotton fabric and thermal dye sublimation transfer printing technique thereof Download PDFInfo
- Publication number
- CN106192426A CN106192426A CN201610649892.7A CN201610649892A CN106192426A CN 106192426 A CN106192426 A CN 106192426A CN 201610649892 A CN201610649892 A CN 201610649892A CN 106192426 A CN106192426 A CN 106192426A
- Authority
- CN
- China
- Prior art keywords
- polyester
- cotton
- cotton fabric
- nexine
- top layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of textile, a kind of polyester-cotton fabric and thermal dye sublimation transfer printing technique thereof.Including nexine, top layer, it is characterized in that: the lower section on described top layer is provided with nexine, being provided with adhesive linkage between top layer and nexine, described top layer is made up of terylene, and described nexine is made up of polyester fibre cotton, offers the micropore of some upward and downwards in described adhesive linkage.The present invention is compared with the existing technology, both comfortable as cotton, retains the advantage that terylene is quick-drying, wrinkle resistant, the most next to the skin simultaneously;Light compared with ordinary polyester volume weight by about 25%, can wear lighter, more comfortable;Conformality is good, can dry with machine washing, be unlikely to deform;The most outstanding ordinary polyester of quick-drying performance needs 32 minutes, and thread water absorben perspiring shell fabric only needs 20 minutes, is greatly improved drying time.
Description
Technical field
The present invention relates to field of textile, a kind of polyester-cotton fabric and thermal dye sublimation transfer printing technique thereof.
Background technology
It is poor that terylene has hygroscopicity, and dress has feeling of oppression and heat, and the most easily static electrification, contamination dust, affect attractive in appearance and comfortableness.
Current thread water absorben perspiring shell fabric of entirely washing carries out distilling printing the technique that the fabric processed has been maturation after antistatic treatment again,
But the moisture absorption sweat discharging functions of this fabric is the most limited, for garment market, merge the cotton and advantage of terylene, overcome again two simultaneously
The shortcoming of person, both comfortable as cotton, retain the advantage that terylene is quick-drying, wrinkle resistant, the most next to the skin simultaneously, become new grinding
Study carefully problem.
Summary of the invention
The present invention is for overcoming the deficiencies in the prior art, and design one is both comfortable as cotton, retains terylene quick-drying, no simultaneously
Thread water absorben perspiring shell fabric a little wrinkling, the most next to the skin.
For achieving the above object, a kind of polyester-cotton fabric of design, including nexine, top layer, it is characterized in that: the lower section on described top layer
Being provided with nexine, be provided with adhesive linkage between top layer and nexine, described top layer is made up of terylene, and described nexine is made up of polyester fibre cotton, institute
The micropore of some upward and downwards is offered in stating adhesive linkage.
The polyester-cotton blend ratio of described polyester fibre cotton is 81.8:18.2.
Described micro-pore diameter is 0.05~0.1 micron.
In described top layer, the longitude and latitude specification of terylene is respectively 100D/96F and 75D/48F.
In described nexine polyester fibre cotton, the specification of terylene is 100D/36F.
The thermal dye sublimation transfer printing technique of a kind of polyester-cotton fabric, it is characterised in that comprise the steps:
(1) step 1: pure terylene and polyester fibre cotton are made polyester-cotton fabric, through erosion hair ENZYME WASH, when washing, pH value is 9-10, simultaneously
It is warming up to 85 °, and retains a period of time;
(2) step 2: washed polyester-cotton fabric put into and print in printer, uses disperse dyes and water-solubility carrier thereof
Printing according to desirable pattern, during printing, the precision setting of printer is two-way 4PASS;
(3) step 3: the polyester-cotton fabric printed is put into pressing machine, pressing temperature is 220-230 °, and pressing machine rotating speed is per minute
12 turns, continue the 25-30 second.
In described step 2, the molecular weight of disperse dyes is 250-400, and particle diameter is 0.2-2 micron, and disperse dyes include
One or whole in disperse red, disperse yellow, disperse blue etc.;Described water-solubility carrier includes in water, glycerol, Polyethylene Glycol etc.
A kind of or whole.
The present invention is compared with the existing technology, both comfortable as cotton, retains terylene quick-drying simultaneously, wrinkle resistant, the most next to the skin
Advantage;Light compared with ordinary polyester volume weight by about 25%, can wear lighter, more comfortable;Conformality is good, can wash with machine
Dry, be unlikely to deform;The most outstanding ordinary polyester of quick-drying performance needs 32 minutes, and thread water absorben perspiring shell fabric only needs 20 points
Clock, is greatly improved drying time.
Accompanying drawing explanation
Fig. 1 is the structural representation of the present invention.
Seeing Fig. 1, wherein, 1 is top layer, and 2 is adhesive linkage, and 3 is nexine, and 4 is micropore.
Detailed description of the invention
Below according to accompanying drawing, the present invention is described further.
As it is shown in figure 1, the lower section of described top layer (1) is provided with nexine (3), between top layer (3) and nexine (1), it is provided with adhesive linkage
(2), described top layer (1) is made up of terylene, and described nexine (3) is made up of polyester fibre cotton, and described adhesive linkage offers on some in (2)
Lower to micropore (4).
The polyester-cotton blend ratio of described polyester fibre cotton is 81.8:18.2.
A diameter of 0.05~0.1 micron of described micropore (4).
In described top layer (1), the longitude and latitude specification of terylene is respectively 100D/96F and 75D/48F.
In described nexine (3) polyester fibre cotton, the specification of terylene is 100D/36F.
The thermal dye sublimation transfer printing technique of a kind of polyester-cotton fabric, it is characterised in that comprise the steps:
(1) step 1: pure terylene and polyester fibre cotton are made polyester-cotton fabric, through erosion hair ENZYME WASH, when washing, pH value is 9-10, simultaneously
It is warming up to 85 °, and retains a period of time;
(2) step 2: washed polyester-cotton fabric put into and print in printer, uses disperse dyes and water-solubility carrier thereof
Printing according to desirable pattern, during printing, the precision setting of printer is two-way 4PASS;
(3) step 3: the polyester-cotton fabric printed is put into pressing machine, pressing temperature is 220-230 °, and pressing machine rotating speed is per minute
12 turns, continue the 25-30 second.
In described step 2, the molecular weight of disperse dyes is 250-400, and particle diameter is 0.2-2 micron, and disperse dyes include
One or whole in disperse red, disperse yellow, disperse blue etc.;Described water-solubility carrier includes in water, glycerol, Polyethylene Glycol etc.
A kind of or whole.
Embodiment:
Polyester-cotton blend is made polyester fibre cotton according to the ratio blending of 81.8 to 18.2, purer terylene is bonded together with polyester fibre cotton makes
Polyester-cotton fabric, in the purest terylene, the longitude and latitude specification of terylene is respectively the longitude and latitude specification of terylene and is respectively 100D/96F and 75D/
48F, in polyester fibre cotton, the specification of terylene is 100D/36F.Polyester-cotton fabric passes through erosion hair ferment under the temperature conditions that temperature is 85 °
Washing, wherein the pH value of erosion hair ferment is 9, and retains 5 minutes.
Configuration dyestuff, the pigment such as color proportioning disperse red as required, disperse yellow, disperse blue, wherein disperse dyes
Molecular weight is 300, particle diameter 0.5 micron, adds appropriate water, glycerol, is configured to disperse dyes, by washed polyester-cotton blend face
Printer put into by material, printer printed according to required figure by the dyestuff configured, and wherein printer is set to two-way
4PASS.Print complete after polyester-cotton fabric is put in pressing machine, pressing temperature is set to 220 °, and pressing machine rotating speed is set to every point
12 turns of clock, and after carrying out pressing 30 seconds, take out after the cooling of band polyester-cotton fabric, i.e. can obtain washing by thermal dye sublimation transfer printing fabrication techniques
Cotton face fabric.
Claims (7)
1. a polyester-cotton fabric, including nexine, top layer, is characterized in that: the lower section of described top layer (1) is provided with nexine (3), top layer
And be provided with adhesive linkage (2) between nexine (1) (3), described top layer (1) is made up of terylene, and described nexine (3) is made up of polyester fibre cotton,
The micropore (4) of some upward and downwards is offered in described adhesive linkage (2).
The polyester-cotton fabric of a kind of moisture absorbing and sweat releasing the most as claimed in claim 1, is characterized in that: the polyester-cotton blend ratio of described polyester fibre cotton is
81.8:18.2。
The polyester-cotton fabric of a kind of moisture absorbing and sweat releasing the most as claimed in claim 1, is characterized in that: described micropore (4) a diameter of 0.05
~0.1 micron.
The polyester-cotton fabric of a kind of moisture absorbing and sweat releasing the most as claimed in claim 1, is characterized in that: the warp of terylene in described top layer (1)
Latitude specification is respectively 100D/96F and 75D/48F.
The polyester-cotton fabric of a kind of moisture absorbing and sweat releasing the most as claimed in claim 1, is characterized in that: wash in described nexine (3) polyester fibre cotton
The specification of synthetic fibre is 100D/36F.
6. the thermal dye sublimation transfer printing technique of a polyester-cotton fabric, it is characterised in that comprise the steps:
Step 1: pure terylene and polyester fibre cotton are made polyester-cotton fabric, through erosion hair ENZYME WASH, when washing, pH value is 9-10, heats up simultaneously
To 85 °, and retain a period of time;
Step 2: washed polyester-cotton fabric is put in printer and prints, use disperse dyes and water-solubility carrier thereof according to
Desirable pattern prints, and during printing, the precision setting of printer is two-way 4PASS;
Step 3: the polyester-cotton fabric printed is put into pressing machine, pressing temperature is 220-230 °, pressing machine rotating speed per minute 12
Turn, continue the 25-30 second.
The thermal dye sublimation transfer printing technique of a kind of polyester-cotton fabric the most as claimed in claim 6, is characterized in that: disperse in described step 2
The molecular weight of dyestuff is 250-400, and particle diameter is 0.2-2 micron, and disperse dyes include disperse red, disperse yellow, disperse blue etc.
In one or all;Described water-solubility carrier includes the one in water, glycerol, Polyethylene Glycol etc. or whole.