CN106192410A - A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth - Google Patents
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth Download PDFInfo
- Publication number
- CN106192410A CN106192410A CN201610615945.3A CN201610615945A CN106192410A CN 106192410 A CN106192410 A CN 106192410A CN 201610615945 A CN201610615945 A CN 201610615945A CN 106192410 A CN106192410 A CN 106192410A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- dispensing
- impregnation liquid
- hgh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth, it is made up of following raw material, by weight: dispensing a: natural emulsion 20 25 parts, polyvinyl alcohol 68 parts, penetrating agent 24 parts, PH regulator 12 parts, antioxidant 0.4 0.8 parts, 55 65 parts of water；Dispensing b: styrene-butadiene latex 15 20 parts, alcohol ether 12 16 parts, antibacterial 46 parts, defoamer 0.5 0.8 parts, preservative 0.1 0.5 parts, 35 45 parts of water；Dispensing c: polyacrylamide 35 40 parts, cross-linking agent 25 parts, precipitated calcium carbonate 15 20 parts, dispersant 13 parts, silicone oil 12 parts, 40 50 parts of water.The present invention adds natural emulsion and penetrating agent, makes the immersion surface being immersed on industry cloth quickly form thin film, it is ensured that immersion and the bond properties on industry cloth surface；The present invention has high temperature resistance, antiacid alkali, the advantage of high abrasion.
Description
Technical field
The invention belongs to industrial cloth technical field, relate to a kind of hgh-performance emulsified obstruct dipping being applicable to industrial cloth
Liquid, is used for being coated in industry cloth surface, has high temperature resistance, antiacid alkali, high abrasion feature.
Background technology
In recent years, industry cloth uses in a large number, promotes the lifting of industry cloth product quality.Industry cloth is carried out dipping make
Industry, is an up an important ring of industry cloth product quality.Tradition impregnation liquid system uses RFL dipping solution, i.e. resorcinol
Formaldehyde latex impregnating system.Owing to resorcinol is the most volatile, not only reduce the concentration of impregnation liquid, make
RFL dipping solution reduces with the bond properties on industry cloth surface, also shop worker is caused harm.
Chinese Patent Application No. 201410000732.0 discloses a kind of industrial cloth dipping solution formula and preparation technology thereof,
This invention is applied to industry cloth impregnation, but its formula material is more, complicated process of preparation.Processing in small-scale enterprise
In, the method need to take longer working time, more cost of labor, is difficult to be suitable for.Therefore in small enterprise's impregnation processor, urgently
Dispensing is less, preparation technology is simple and convenient to need one, is not take up the dipping solution of more manpower and time.In order to overcome above-mentioned asking
Topic, and keep the stable performance of product, a kind of new technical scheme is now provided.
Summary of the invention
It is an object of the invention to provide a kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth, this impregnation liquid is made up of following raw material, by weight
Amount part meter:
Dispensing a: natural emulsion 20-25 part, polyvinyl alcohol 6-8 part, penetrating agent 2-4 part, PH regulator 1-2 part, antioxidation
Agent 0.4-0.8 part, water 55-65 part；
Dispensing b: styrene-butadiene latex 15-20 part, alcohol ether 12-16 part, antibacterial 4-6 part, defoamer 0.5-0.8 part, preservative
0.1-0.5 part, water 35-45 part；
Dispensing c: polyacrylamide 35-40 part, cross-linking agent 2-5 part, precipitated calcium carbonate 15-20 part, dispersant 1-3 part, silicon
Oil 1-2 part, water 40-50 part.
In described dispensing a: natural emulsion 22 parts, polyvinyl alcohol 7 parts, penetrating agent 3 parts, PH regulator 1.5 parts, antioxidation
Agent 0.6 part, 60 parts of water.
In described dispensing b: styrene-butadiene latex 18 parts, alcohol ether 14 parts, antibacterial 5 parts, defoamer 0.6 part, preservative 0.3
Part, 40 parts of water.
In described dispensing c: polyacrylamide 38 parts, cross-linking agent 4 parts, precipitated calcium carbonate 18 parts, dispersant 2 parts, silicone oil
1.5 parts, 45 parts of water.
Natural emulsion has good filming performance, and wet gel strength is high, good mechanical properties, nonrubber component content
Few, mechanical stability is high, and color is pure white, and foam stability is good.
Styrene-butadiene latex is through the stable emulsion of low temperature polymerization with butadiene and styrene.
Penetrating agent has fabulous adhesive force, the fluent material that penetration is extremely strong, fast drying, and wearability is strong, and has well
Chemical resistance and resistance to water.Penetrating agent is generally divided into nonionic and anion two class.Non-ionic have JFC, JFC-1, JFC-2,
JFC-E etc.；Anion have fast penetrant T, alkali-resistant penetrant OEP-70, alkali-resistant penetrant AEP, seeping at high temperature agent JFC-M.
Penetrating agent type is not limited by the present invention.
Beneficial effects of the present invention:
1) present invention is by adding natural emulsion in the feed, makes the immersion surface being immersed on industry cloth quickly form one
Layer film, this layer film can stop the volatilization of raw material effectively, it is ensured that immersion and the bond properties on industry cloth surface；Meanwhile,
The addition of penetrating agent makes the present invention have high temperature resistance, antiacid alkali, the advantage of high abrasion, improves the performance of dipping solution；
2) preparation method of the present invention is simple to operation, is not required to take the longer working time, reduces cost of labor, is suitable for
Processing in small-scale enterprise；
3) present invention is with polyacrylamide and polyvinyl alcohol as primary raw material so that impregnation liquid has good barrier
Energy；
4) present invention has stronger suds, defoaming capacity, stability in hard water is good, cleaning is good；Impregnation liquid is the most steady
Fixed, increase the service life.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.Raw material Jun Neng city used in the present invention
Face is commercially available.
Embodiment 1
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth, by weight: in dispensing a: natural emulsion
22 parts, polyvinyl alcohol 7 parts, penetrating agent 3 parts, PH regulator 1.5 parts, antioxidant 0.6 part, 60 parts of water；By PH regulator and water
Ratio in 1: 4 mixes at 60 DEG C, and stirring, to being completely dissolved, is cooled to room temperature, adds natural emulsion mix homogeneously, adds
Polyvinyl alcohol, mix homogeneously, make mixed liquor stand-by；Utilizing remaining water purification to dilute antioxidant, penetrating agent, stirring is all
Even, make latex A stand-by；
In dispensing b: styrene-butadiene latex 18 parts, alcohol ether 14 parts, antibacterial 5 parts, defoamer 0.6 part, preservative 0.3 part, water 40
Part；Antibacterial, defoamer, preservative being mixed at 60 DEG C in the ratio of 1: 4 with water, stirring, to being completely dissolved, is cooled to room
Temperature, adds remaining water, styrene-butadiene latex mix homogeneously, adds alcohol ether, mix homogeneously, make mixed liquid B stand-by；
In dispensing c: polyacrylamide 38 parts, cross-linking agent 4 parts, precipitated calcium carbonate 18 parts, dispersant 2 parts, silicone oil 1.5 parts,
45 parts of water；Cross-linking agent, dispersant being mixed at 60 DEG C in the ratio of 1: 4 with water, stirring, to being completely dissolved, is cooled to room temperature,
Add remaining water, precipitated calcium carbonate mix homogeneously, add polyacrylamide, silicone oil, mix homogeneously, make mixed liquor C and treat
With；
Finally latex A is added rapidly in mixed liquid B, then with in mixed liquor C, uniform stirring, make impregnation liquid.
Embodiment 2
Dispensing a: natural emulsion 25 parts, polyvinyl alcohol 6 parts, penetrating agent 4 parts, PH regulator 1 part, antioxidant 0.8 part, water
55 parts；
Dispensing b: styrene-butadiene latex 20 parts, alcohol ether 12 parts, antibacterial 6 parts, defoamer 0.5 part, preservative 0.5 part, 35 parts of water；
Dispensing c: polyacrylamide 40 parts, cross-linking agent 2 parts, precipitated calcium carbonate 20 parts, dispersant 1 part, silicone oil 2 parts, water 40
Part.
Preparation method such as embodiment 1.
Embodiment 3
Dispensing a: natural emulsion 20 parts, polyvinyl alcohol 8 parts, penetrating agent 2 parts, PH regulator 2 parts, antioxidant 0.4 part, water
65 parts；
Dispensing b: styrene-butadiene latex 15 parts, alcohol ether 16 parts, antibacterial 4 parts, defoamer 0.8 part, preservative 0.1 part, 45 parts of water；
Dispensing c: polyacrylamide 35 parts, cross-linking agent 5 parts, precipitated calcium carbonate 15 parts, dispersant 3 parts, silicone oil 1 part, water 50
Part.
Preparation method such as embodiment 1.
Above content is only citing made for the present invention and explanation, and affiliated those skilled in the art are to being retouched
The specific embodiment stated makes various amendment or supplements or use similar mode to substitute, without departing from inventing or super
More scope defined in the claims, all should belong to protection scope of the present invention.
Claims (4)
1. the hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth, it is characterised in that this impregnation liquid is by following raw material
Composition, by weight:
Dispensing a: natural emulsion 20-25 part, polyvinyl alcohol 6-8 part, penetrating agent 2-4 part, PH regulator 1-2 part, antioxidant
0.4-0.8 part, water 55-65 part；
Dispensing b: styrene-butadiene latex 15-20 part, alcohol ether 12-16 part, antibacterial 4-6 part, defoamer 0.5-0.8 part, preservative 0.1-
0.5 part, water 35-45 part；
Dispensing c: polyacrylamide 35-40 part, cross-linking agent 2-5 part, precipitated calcium carbonate 15-20 part, dispersant 1-3 part, silicone oil 1-2
Part, water 40-50 part.
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth the most according to claim 1, it is characterised in that
In described dispensing a: natural emulsion 22 parts, polyvinyl alcohol 7 parts, penetrating agent 3 parts, PH regulator 1.5 parts, antioxidant 0.6 part,
60 parts of water.
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth the most according to claim 1, it is characterised in that
In described dispensing b: styrene-butadiene latex 18 parts, alcohol ether 14 parts, antibacterial 5 parts, defoamer 0.6 part, preservative 0.3 part, 40 parts of water.
A kind of hgh-performance emulsified obstruct impregnation liquid being applicable to industrial cloth the most according to claim 1, it is characterised in that
In described dispensing c: polyacrylamide 38 parts, cross-linking agent 4 parts, precipitated calcium carbonate 18 parts, dispersant 2 parts, silicone oil 1.5 parts, water
45 parts.