CN106192058A - A kind of polyester flame-retardant Dense mesh screen production technology - Google Patents
A kind of polyester flame-retardant Dense mesh screen production technology Download PDFInfo
- Publication number
- CN106192058A CN106192058A CN201610541831.9A CN201610541831A CN106192058A CN 106192058 A CN106192058 A CN 106192058A CN 201610541831 A CN201610541831 A CN 201610541831A CN 106192058 A CN106192058 A CN 106192058A
- Authority
- CN
- China
- Prior art keywords
- retardant
- polyester
- polyester flame
- mesh screen
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyester flame-retardant Dense mesh screen production technology, comprise the steps: polyester bottles pulverizing, HIGH TEMPERATURE PURGE, drying drying, spice, Screw Extrusion spray webbing, cold drawing-off, high-temperature shaping, warping, net machine molding, cut-parts block limit, finished product packing.The invention has the beneficial effects as follows, simple in construction, practical.
Description
Technical field
The present invention relates to the safe Dense mesh screen of flame retardant polyester for building and flame retardant polyester sunshade net, particularly a kind of polyester flame-retardant
Dense mesh screen production technology.
Background technology
Safe Dense mesh screen for building is non-antiflaming the earliest, and the later stage must be with resistance through national regulation flame-retardant fine mesh for building net
Combustion reaches fire-protection standard, and material used is pp and hdpe.Be currently used for flame-retarding Dense mesh screen material for building be pp and
Hdpe, the maximum shortcoming of Dense mesh screen that these 2 kinds of materials are made be fire retardant be that a kind of inorganic interpolation, aging resistance time are short, anti-impact
Power of hitting is weak, and fire retardant of exposing to the weather through the 3-6 outdoor of individual month separates out, and flame retardant effect weakens, the aging of product, and impulsive force is the biggest
Big reduction, brings invisible potential safety hazard to construction site.
Summary of the invention
The invention aims to solve the problems referred to above, devise a kind of polyester flame-retardant Dense mesh screen production technology.
Realizing above-mentioned purpose the technical scheme is that, a kind of polyester flame-retardant Dense mesh screen production technology, including walking as follows
Rapid:
(1) polyester bottles is pulverized-is used polyester bottles and renders to, in plastic crusher, be ground into polyester bottle slice;
(2) HIGH TEMPERATURE PURGE-by polyester bottle slice is rendered to HIGH TEMPERATURE PURGE machine and is carried out HIGH TEMPERATURE PURGE, removes microorganism bacterial parasite;
(3) centrifuge dripping drying unit is dried-utilized to drying by polyester bottle slice drying and dewatering;
(4) spice-by 85-92% polyester bottle slice, 1% age resister, 2% reinforcing agent, the fire retardant of 5%-12% is thrown in
In blender, uniform stirring, form recycled polyester flame retardant solution;
(5) that recycled polyester flame retardant solution carries out Screw Extrusion, spray webbing is anti-for Screw Extrusion, spray webbing-utilize wire drawing machine screw rod
Should, it is fabricated to polyester flame-retardant monofilament first product;
(6) hot and cold water drawing-off-polyester flame-retardant monofilament first product leads through a series of cold water drawing-off, hot water, is drawn into specification
Silk number;
(7) high-temperature shaping-again polyester flame-retardant monofilament first product is carried out high-temperature shaping;
(8) warping-utilize silk screen warping machine that polyester flame-retardant monofilament first product is carried out warping, is fabricated to the fire-retardant list of multi-end polyester
Silk;
(9) net machine molding-polyester flame-retardant monofilament is woven into sheet of polyester flame-retardant Dense mesh screen by netting machine:
(10) cut-parts-sheet of polyester flame-retardant Dense mesh screen is utilized slitter, are cut into polyester flame-retardant Dense mesh screen by specification;
(11) selvage is carried out edge sealing by edge banding machine by block limit-polyester flame-retardant Dense mesh screen;
(12) finished product packing-utilize finished product packing machine that the polyester flame-retardant Dense mesh screen after edge sealing is packaged into axle;
The time of described drying and dewatering is 25 minutes.
Described fire retardant is halogen-free environmental response type permanent fire retardant high molecular weight flame retardant.
Described cleaning high temperature is 100-120 degree Celsius.
Described drying temperature is 130-150 degree Celsius.
Described high-temperature shaping temperature is 210-260 degree Celsius.
Utilize the polyester flame-retardant Dense mesh screen production technology that technical scheme makes, increase the fire-retardant of safe Dense mesh screen
Permanent, increase the aging resistance time of this product, increase the impulsive force of this product, society can be increased with recycling simultaneously
And economic benefit.
Accompanying drawing explanation
Fig. 1 is the flow chart of polyester flame-retardant Dense mesh screen production technology of the present invention;
Detailed description of the invention
Below in conjunction with the accompanying drawings the present invention is specifically described, as it is shown in figure 1, a kind of polyester flame-retardant Dense mesh screen produces work
Skill, comprises the steps:
(1) polyester bottles is pulverized-is used polyester bottles and renders to, in plastic crusher, be ground into polyester bottle slice;
(2) HIGH TEMPERATURE PURGE-by polyester bottle slice is rendered to HIGH TEMPERATURE PURGE machine and is carried out HIGH TEMPERATURE PURGE, removes microorganism bacterial parasite;
(3) centrifuge dripping drying unit is dried-utilized to drying by polyester bottle slice drying and dewatering;
(4) spice-by 85-92% polyester bottle slice, 1% age resister, 2% reinforcing agent, the fire retardant of 5%-12% is thrown in
In blender, uniform stirring, form recycled polyester flame retardant solution;
(5) that recycled polyester flame retardant solution carries out Screw Extrusion, spray webbing is anti-for Screw Extrusion spray webbing-utilize wire drawing machine screw rod
Should, it is fabricated to polyester flame-retardant monofilament first product;
(6) hot and cold water drawing-off-polyester flame-retardant monofilament first product leads through a series of cold water drawing-off, hot water, is drawn into specification
Silk number;
(7) high-temperature shaping-again polyester flame-retardant monofilament first product is carried out high-temperature shaping;
(8) warping-utilize silk screen warping machine that polyester flame-retardant monofilament first product is carried out warping, is fabricated to the fire-retardant list of multi-end polyester
Silk;
(9) net machine molding-polyester flame-retardant monofilament is woven into sheet of polyester flame-retardant Dense mesh screen by netting machine:
(10) cut-parts-sheet of polyester flame-retardant Dense mesh screen is utilized slitter, are cut into polyester flame-retardant Dense mesh screen by specification;
(11) selvage is carried out edge sealing by edge banding machine by block limit-polyester flame-retardant Dense mesh screen;
(12) finished product packing-utilize finished product packing machine that the polyester flame-retardant Dense mesh screen after edge sealing is packaged into axle;Described drying
The time of dehydration is 25 minutes;Described fire retardant is halogen-free environmental response type permanent fire retardant high molecular weight flame retardant;Described cleaning height
Temperature is 100-120 degree Celsius;Described drying temperature is 130-150 degree Celsius;Described high-temperature shaping temperature is that 210-260 is Celsius
Degree.
The feature of the present embodiment is, comprises the steps: that (1) polyester bottles is pulverized-used polyester bottles and renders to molding powder
In broken machine, it is ground into polyester bottle slice;(2) HIGH TEMPERATURE PURGE-polyester bottle slice is rendered to HIGH TEMPERATURE PURGE machine carries out HIGH TEMPERATURE PURGE,
Remove microorganism bacterial parasite;(3) centrifuge dripping drying unit is dried-utilized to drying by polyester bottle slice drying and dewatering;(4) spice-
By 85-92% polyester bottle slice, 1% age resister, 2% reinforcing agent, the fire retardant of 5%-12% is rendered to, in blender, uniformly stir
Mix, form recycled polyester flame retardant solution;(5) Screw Extrusion spray webbing-utilize wire drawing machine screw rod to be carried out by recycled polyester flame retardant solution
Screw Extrusion, spray webbing react, and are fabricated to polyester flame-retardant monofilament first product;(6) hot and cold water drawing-off-polyester flame-retardant monofilament first product is through one
The cold water drawing-off of series, hot water lead, and are drawn into specification silk number;(7) high-temperature shaping-again polyester flame-retardant monofilament first product is carried out high temperature
Sizing;(8) warping-utilize silk screen warping machine that polyester flame-retardant monofilament first product is carried out warping, is fabricated to polyester flame-retardant monofilament;(9)
Net machine molding-polyester flame-retardant monofilament is woven into sheet of polyester flame-retardant Dense mesh screen by netting machine: (10) cut-parts-by sheet of
Polyester flame-retardant Dense mesh screen utilizes slitter, is cut into polyester flame-retardant Dense mesh screen by specification;(11) block limit-polyester flame-retardant Dense mesh screen
By edge banding machine, selvage is carried out edge sealing;(12) finished product packing-utilize finished product packing machine by the polyester flame-retardant Dense mesh screen after edge sealing
It is packaged into axle, increases the fire-retardant permanent of safe Dense mesh screen, increase the aging resistance time of this product, increase the impact of this product
Power, can increase society and economic benefit with recycling simultaneously.
In the present embodiment,
Embodiment 1
The raw material of polyester flame-retardant Dense mesh screen is virgin plastics grained high density polyethylene or regrown material mineral water bottle
Bottle cap material, pulverizes raw material plastic crusher processing, and it is clear that the polyester bottle slice after pulverizing is put into high temperature in HIGH TEMPERATURE PURGE machine
Wash, by the bacterial micro-organism of polyester bottle slice, thus improve antiseptic power, after having sterilized, polyester bottles material is dried,
Dry with centrifugation apparatus, then dried by drying plant, after drying, by 85% polyester bottle slice, 1% aging resistance
Agent, 2% reinforcing agent, the fire retardant of 5% is rendered in blender, uniform stirring, forms recycled polyester flame retardant solution, utilizes wire drawing
Recycled polyester flame retardant solution is carried out Screw Extrusion by machine screw rod, through spray webbing consersion unit, is fabricated to polyester flame-retardant monofilament first product,
Polyester flame-retardant monofilament first product leads through a series of cold water drawing-off, hot water, is drawn into standard specifications silk number, will become the monofilament of specification
Carry out high-temperature shaping, utilize silk screen warping machine that polyester flame-retardant monofilament first product is carried out warping, be fabricated to polyester flame-retardant monofilament, pass through
Polyester flame-retardant monofilament is woven into sheet of polyester flame-retardant Dense mesh screen by netting machine, and polyester flame-retardant Dense mesh screen passes through edge banding machine by selvage
Carry out edge sealing, utilize finished product packing machine that the polyester flame-retardant Dense mesh screen after edge sealing is packaged into axle, increase the fire-retardant of safe Dense mesh screen
Permanent, increase the aging resistance time of this product, increase the impulsive force of this product, society can be increased with recycling simultaneously
And economic benefit.
Recycled polyester flame retardant solution distribution percentage ratio table
Embodiment 2
Embodiment 2 is substantially the same manner as Example 1, and unique difference is: the ratio that recycled polyester flame retardant solution is thrown in,
Throw in material according to recycled polyester flame retardant solution distribution percentage ratio table correspondence embodiment 2, utilize in blender, uniformly
Stirring, forms recycled polyester flame retardant solution.
Embodiment 3
Embodiment 3 is substantially the same manner as Example 1, and unique difference is: the ratio that recycled polyester flame retardant solution is thrown in,
Throw in material according to recycled polyester flame retardant solution distribution percentage ratio table correspondence embodiment 3, utilize in blender, uniformly
Stirring, forms recycled polyester flame retardant solution.
Technique scheme only embodies the optimal technical scheme of technical solution of the present invention, those skilled in the art
Some variations may made some of which part all embody the principle of the present invention, belong to protection scope of the present invention it
In.
Claims (6)
1. a polyester flame-retardant Dense mesh screen production technology, it is characterised in that comprise the steps:
(1) polyester bottles is pulverized-is used polyester bottles and renders to, in plastic crusher, be ground into polyester bottle slice;
(2) HIGH TEMPERATURE PURGE-by polyester bottle slice is rendered to HIGH TEMPERATURE PURGE machine and is carried out HIGH TEMPERATURE PURGE, removes microorganism bacterial parasite;
(3) centrifuge dripping drying unit is dried-utilized to drying by polyester bottle slice drying and dewatering;
(4) spice-by 85-92% polyester bottle slice, 1% age resister, 2% reinforcing agent, the fire retardant of 5%-12% is rendered to stir
Mix in machine, uniform stirring, form recycled polyester flame retardant solution;
(5) recycled polyester flame retardant solution is carried out Screw Extrusion, spray webbing reaction, system by Screw Extrusion spray webbing-utilize wire drawing machine screw rod
It is made polyester flame-retardant monofilament first product;
(6) hot and cold water drawing-off-polyester flame-retardant monofilament first product leads through a series of cold water drawing-off, hot water, is drawn into specification silk number;
(7) high-temperature shaping-again polyester flame-retardant monofilament first product is carried out high-temperature shaping;
(8) warping-utilize silk screen warping machine that polyester flame-retardant monofilament first product is carried out warping, is fabricated to multi-end polyester flame-proof monofilament;
(9) net machine molding-polyester flame-retardant monofilament is woven into sheet of polyester flame-retardant Dense mesh screen by netting machine:
(10) cut-parts-sheet of polyester flame-retardant Dense mesh screen is utilized slitter, are cut into multi-end polyester flame-retardant fine mesh net by specification;
(11) selvage is carried out edge sealing by edge banding machine by block limit-polyester flame-retardant Dense mesh screen;
(12) finished product packing-utilize finished product packing machine that the polyester flame-retardant Dense mesh screen after edge sealing is packaged into axle.
A kind of polyester flame-retardant Dense mesh screen production technology the most according to claim 1, it is characterised in that in step (3), described
The time of drying and dewatering is 25 minutes.
A kind of polyester flame-retardant Dense mesh screen production technology the most according to claim 1, it is characterised in that in step (4), described
Fire retardant is halogen-free environmental response type permanent fire retardant high molecular weight flame retardant.
A kind of polyester flame-retardant Dense mesh screen production technology the most according to claim 1, it is characterised in that in step (2), institute
State cleaning high temperature and be 100-120 degree Celsius.
A kind of polyester flame-retardant Dense mesh screen production technology the most according to claim 1, it is characterised in that in step (3), described
Dry temperature and be 130-150 degree Celsius.
A kind of polyester flame-retardant Dense mesh screen production technology the most according to claim 1, it is characterised in that in step (7), described
High-temperature shaping temperature is 210-260 degree Celsius.