CN106189857A - A kind of metal thickness slurry heavy anti-corrosion antirust paint - Google Patents
A kind of metal thickness slurry heavy anti-corrosion antirust paint Download PDFInfo
- Publication number
- CN106189857A CN106189857A CN201610575954.4A CN201610575954A CN106189857A CN 106189857 A CN106189857 A CN 106189857A CN 201610575954 A CN201610575954 A CN 201610575954A CN 106189857 A CN106189857 A CN 106189857A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal
- antirust paint
- heavy anti
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of metal thick slurry heavy anti-corrosion antirust paint, raw material is: coal tar pitch, epoxy resin, polyamide, potassium silicate, aluminium silicate, BTA, strontium sulfate, dimethylbenzene, polyphosphoric acids aluminum and chromic oxide；Antirust for metal surface, surface strength is high, viscosity 60 80s, fineness 30 50 μm, has good adhesive force to metal；Antiseptic property is good, impact 60 80cm, and resistance to salt water 20 60d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying 6 10h, does solid work 18 22h, covering power 90 110g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for current material.
Description
Technical field
The present invention relates to metal field of material technology, particularly relate to a kind of metal thick slurry heavy anti-corrosion antirust paint.
Background technology
Antirust paint is a kind of chemistry protecting metal surfaces from air, sea water etc. or the coating of electrochemical corrosion.Main
Physical property to be divided into and the big class of chemically antirust paint two.The former is by the suitable cooperation of pigment and paint vehicle, formed fine and close paint film with
Stop the intrusion of corrosive substance, such as thickness slurry heavy antisepsis, thick slurry heavy antisepsis, graphite antirust paint etc.；The latter is by the change of rust resisting pigment
Press down rust effect, such as coal tar pitch, zinc chromate anti-rust paint etc..Antirust for metals such as bridge, boats and ships, pipelines.Coal tar pitch antirust paint
It is the paint that mixes with drying oil of a kind of coal tar pitch.Its permeability, wettability are good, and paint film is soft, attachment is strong, but is dried
Slower.Great additionally, due to coal tar pitch ratio, easily precipitate, and stored for a long time can be thickening, brushability is the most poor.
The antirust paint substantially oiliness used and aqueous two kinds.Oily antirust varniss makes the greasy difficulty of removing of material surface,
It is rarely employed.Oily antirust varniss is easy to use, cheap, but because of containing the noxious substance such as nitrite, chromate, to operation
Personnel's harm is relatively big, and country has limited use, and these type of properties of product are single, it is impossible to meets the antirust of magnetic alloy material and wants
Ask.Epoxy anti-rust paint is used for polyamide as firming agent, and polymer with bis phenol A amide is adhesive, and film is good to substrate adhesion, executes
Work is functional, and paint film flexibility is good, water-fast, oil resistant chemicals-resistant is good.Add different rust resisting pigments, difference can be configured to
Antirust paint, mostly be priming paint.
Water-based metal antirust paint selects metal strength chelating agen inositol six polyesteramide to be main component, with other several water
Property additive compound forms.Inositol six polyesteramide is the Nantural non-toxic Organic chemical products extracted from cereal crops, when it is made
When using for magnetic material antirust agent, can chelate rapidly with metal on surface, form one layer of fine and close unimolecule complex protection
Film, can effectively suppress corrosion of metal.Material surface after this product treatment keeps primary colors, it is not necessary to washing can enter application
Deng next procedure.Conventional epoxy anti-rust paint has epoxy thickness slurry heavy anti-corrosion antirust paint, epoxy thickness slurry heavy anti-corrosion antirust paint, epoxy silicon
Acid aluminum antirust paint, epoxy thickness slurry heavy anti-corrosion antirust paint and epoxy zinc rich primer etc..
Rust resisting pigment is the important component part of antirust paint. physics rust resisting pigment is that an own chemical property of class is relatively stable
Pigment, they are the physical properties by itself, and stable chemical performance, quality is hard, and granule is trickle, excellent fillibility, carries
The consistency of high paint film, reduces the permeable of paint film thus plays antirust effect. and oxidation thickness slurry heavy antisepsis just belongs to this kind of material.
And the rust-preventing characteristic of metal thickness slurry heavy antisepsis is to have sclay texture due to thickness slurry heavy antisepsis, form paint film tight, also have stronger
The ability of uv reflectance light, paint film aging-resistant ability can be improved.Epoxy thickness slurry heavy antisepsis, epoxy thickness slurry heavy antisepsis and ring
Oxygen aluminium silicate antirust paint oxidation thickness slurry heavy antisepsis is the rust resisting pigment that epoxy anti-rust paint is conventional, if adding thickness slurry heavy antisepsis, then
Its rustless property can be strengthened, starch the epoxy aluminium silicate antirust paint of heavy anti-corrosion antirust pigment containing aluminium silicate and oxidation thickness, except
Antirust for steel surface, is also especially possible for the antirust of galvanized part.Should be noted that and be, owing to aluminium silicate is slightly soluble in water,
Although so the antirust paint rustless property containing aluminium silicate pigment is better than the antirust paint comprising only thick slurry heavy antisepsis, but it is not
Recommend long-term for underwater sites, otherwise can produce the problems such as foaming.
The main component of antirust paint is rust resisting pigment and film forming matter.Generally name with the title of rust resisting pigment, such as: coal
Colophonium anticorrosive paint, thick slurry heavy anti-corrosion antirust paint etc..If divided with its rust inhibition, it is broadly divided into four big classes:
Physical action anticorrosive paint, chemical action anticorrosive paint, electrochemical action anticorrosive paint, comprehensive function anticorrosive paint.Coal tar pitch
Antirust paint forms: by compositions such as modified alkyd resin, rust resisting pigment, extender pigment, drier, organic solvents.Characteristic: adhesive force
Good, rustless property is high, and resistance to water is strong, and natural drying is fast at normal temperatures.Some anticorrosive paints are based on trickle flakey material
Want pigment.Conversion and prevention paint of rust is transformant solvent bottom paint, has the rust cleaning of excellence, rustless property, can directly brush and have rust
The metal surface of (thickness≤100 μm), simplifies rust cleaning operation, improves work efficiency, reduces cost.This paint is at rustless metal
Surface also can use；Can support the use with multiple finish paint；Can construct under the conditions of-20 DEG C.
Coat of metal mainly carries out bonderizing, oxidation processes, Passivation Treatment to coated metal；On-metallic protective coating
Mainly the coatings such as paint of coating, plastics, enamel, mineral oils and fats are formed protective layer on the metal surface.Both is protected
The purpose of layer is all to play isolation base material and contact with sea water, replaces base material to react with sea water, thus forms protection.
Summary of the invention
The present invention provides the metal thick slurry heavy anti-corrosion antirust paint that a kind of fast drying, anti-corrosive properties are good, solves existing metal and uses
Material is dried the technical problems such as slow and antiseptic property is poor.
The present invention is by the following technical solutions: a kind of metal thickness slurry heavy anti-corrosion antirust paint, its raw material is joined by mass fraction
Ratio is as follows: coal tar pitch 100 parts, epoxy resin 15-35 part, polyamide 5-25 part, potassium silicate 10-30 part, aluminium silicate 5-25 part, benzene
And triazole 4-16 part, strontium sulfate 0.1-0.5 part, dimethylbenzene 50-90 part, polyphosphoric acids aluminum 8-12 part, chromic oxide 1-20
Part.
As a preferred technical solution of the present invention: the raw material of described metal thick slurry heavy anti-corrosion antirust paint is by mass parts
Number proportioning is as follows: coal tar pitch 100 parts, epoxy resin 20-30 part, polyamide 10-20 part, potassium silicate 15-25 part, aluminium silicate 10-
20 parts, BTA 6-12 part, strontium sulfate 0.2-0.4 part, dimethylbenzene 60-80 part, polyphosphoric acids aluminum 9-11 part, three oxidations two
Chromium 5-15 part.
As a preferred technical solution of the present invention: the raw material of described metal thick slurry heavy anti-corrosion antirust paint is by mass parts
Number proportioning is as follows: coal tar pitch 100 parts, epoxy resin 20 parts, polyamide 10 parts, potassium silicate 15 parts, aluminium silicate 10 parts, benzo three nitrogen
Azoles 6 parts, strontium sulfate 0.2 part, dimethylbenzene 60 parts, 9 parts of polyphosphoric acids aluminum, chromic oxide 5 parts.
As a preferred technical solution of the present invention: the raw material of described metal thick slurry heavy anti-corrosion antirust paint is by mass parts
Number proportioning is as follows: coal tar pitch 100 parts, epoxy resin 30 parts, polyamide 20 parts, potassium silicate 25 parts, aluminium silicate 20 parts, benzo three nitrogen
Azoles 12 parts, strontium sulfate 0.4 part, dimethylbenzene 80 parts, 11 parts of polyphosphoric acids aluminum, chromic oxide 15 parts.
As a preferred technical solution of the present invention: the raw material of described metal thick slurry heavy anti-corrosion antirust paint is by mass parts
Number proportioning is as follows: coal tar pitch 100 parts, epoxy resin 25 parts, polyamide 15 parts, potassium silicate 20 parts, aluminium silicate 15 parts, benzo three nitrogen
Azoles 9 parts, strontium sulfate 0.3 part, dimethylbenzene 70 parts, 10 parts of polyphosphoric acids aluminum, chromic oxide 10 parts.
Beneficial effect
A kind of metal of the present invention thick slurry heavy anti-corrosion antirust paint uses above technical scheme compared with prior art, tool
Have a techniques below effect: 1, antirust for metal surface, surface strength is high, viscosity 60-80s, fineness 30-50 μm, metal is had
Good adhesive force；2, antiseptic property is good, impact 60-80cm, and resistance to salt water 20-60d is non-foaming, do not fall off, and film smooths
Light；3, coating drying property is good, surface drying 6-10h, does solid work 18-22h, covering power 90-110g/cm2, preparation method is simple, raw material
Simple and easy to get, can be with the widespread production not division of history into periods for current material.
Detailed description of the invention
Below in conjunction with example, the invention will be further described, and embodiment is only used for that the present invention will be described, not
Constituting the restriction to right, other alternative means that it may occur to persons skilled in the art that, all in right of the present invention
In claimed range.
Embodiment 1:
The first step: weigh coal tar pitch 100 parts, epoxy resin 15 parts, polyamide 5 parts, potassium silicate according to mass fraction proportioning
10 parts, aluminium silicate 5 parts, BTA 4 parts, strontium sulfate 0.1 part, dimethylbenzene 50 parts, 8 parts of polyphosphoric acids aluminum, chromic oxide 1
Part.
Second step: coal tar pitch, epoxy resin, polyamide, potassium silicate and BTA are put in reactor, is heated to
125 DEG C, stir 35min with 240r/min speed.
3rd step: the liquid after stirring stands 90min, adds aluminium silicate, strontium sulfate, dimethylbenzene, polyphosphoric acids
Aluminum and chromic oxide, put into grinder after 160 DEG C of mix homogeneously and grind 12h, pack after filtration.
Antirust for metal surface, surface strength is high, viscosity 60s, fineness 50 μm, has good adhesive force to metal；Anti-
Rotten performance is good, impact 60cm, and resistance to salt water 20d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying
10h, does solid work 22h, covering power 90g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for existing
There is material.
Embodiment 2:
The first step: weigh coal tar pitch 100 parts, epoxy resin 35 parts, polyamide 25 parts, potassium silicate according to mass fraction proportioning
30 parts, aluminium silicate 25 parts, BTA 16 parts, strontium sulfate 0.5 part, dimethylbenzene 90 parts, 12 parts of polyphosphoric acids aluminum, three oxidations two
Chromium 20 parts.
Second step: coal tar pitch, epoxy resin, polyamide, potassium silicate and BTA are put in reactor, is heated to
145 DEG C, stir 55min with 280r/min speed.
3rd step: the liquid after stirring stands 100min, adds aluminium silicate, strontium sulfate, dimethylbenzene, polyphosphoric acids
Aluminum and chromic oxide, put into grinder after 180 DEG C of mix homogeneously and grind 14h, pack after filtration.
Antirust for metal surface, surface strength is high, viscosity 65s, fineness 45 μm, has good adhesive force to metal；Anti-
Rotten performance is good, impact 65cm, and resistance to salt water 30d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying
9h, does solid work 21h, covering power 95g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for existing
Material.
Embodiment 3:
The first step: weigh coal tar pitch 100 parts, epoxy resin 20 parts, polyamide 10 parts, potassium silicate according to mass fraction proportioning
15 parts, aluminium silicate 10 parts, BTA 6 parts, strontium sulfate 0.2 part, dimethylbenzene 60 parts, 9 parts of polyphosphoric acids aluminum, chromic oxide
5 parts.
Second step: coal tar pitch, epoxy resin, polyamide, potassium silicate and BTA are put in reactor, is heated to
125 DEG C, stir 35min with 240r/min speed.
3rd step: the liquid after stirring stands 90min, adds aluminium silicate, strontium sulfate, dimethylbenzene, polyphosphoric acids
Aluminum and chromic oxide, put into grinder after 160 DEG C of mix homogeneously and grind 12h, pack after filtration.
Antirust for metal surface, surface strength is high, viscosity 70s, fineness 40 μm, has good adhesive force to metal；Anti-
Rotten performance is good, impact 70cm, and resistance to salt water 40d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying
8h, does solid work 20h, covering power 100g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for existing
There is material.
Embodiment 4:
The first step: weigh coal tar pitch 100 parts, epoxy resin 30 parts, polyamide 20 parts, potassium silicate according to mass fraction proportioning
25 parts, aluminium silicate 20 parts, BTA 12 parts, strontium sulfate 0.4 part, dimethylbenzene 80 parts, 11 parts of polyphosphoric acids aluminum, three oxidations two
Chromium 15 parts.
Second step: coal tar pitch, epoxy resin, polyamide, potassium silicate and BTA are put in reactor, is heated to
145 DEG C, stir 55min with 280r/min speed.
3rd step: the liquid after stirring stands 100min, adds aluminium silicate, strontium sulfate, dimethylbenzene, polyphosphoric acids
Aluminum and chromic oxide, put into grinder after 180 DEG C of mix homogeneously and grind 14h, pack after filtration.
Antirust for metal surface, surface strength is high, viscosity 75s, fineness 35 μm, has good adhesive force to metal；Anti-
Rotten performance is good, impact 75cm, and resistance to salt water 50d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying
7h, does solid work 19h, covering power 105g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for existing
There is material.
Embodiment 5:
The first step: weigh coal tar pitch 100 parts, epoxy resin 25 parts, polyamide 15 parts, potassium silicate according to mass fraction proportioning
20 parts, aluminium silicate 15 parts, BTA 9 parts, strontium sulfate 0.3 part, dimethylbenzene 70 parts, 10 parts of polyphosphoric acids aluminum, three oxidations two
Chromium 10 parts.
Second step: coal tar pitch, epoxy resin, polyamide, potassium silicate and BTA are put in reactor, is heated to
135 DEG C, stir 45min with 260r/min speed.
3rd step: the liquid after stirring stands 95min, adds aluminium silicate, strontium sulfate, dimethylbenzene, polyphosphoric acids
Aluminum and chromic oxide, put into grinder after 170 DEG C of mix homogeneously and grind 13h, pack after filtration.
Antirust for metal surface, surface strength is high, viscosity 80s, fineness 30 μm, has good adhesive force to metal；Anti-
Rotten performance is good, impact 80cm, and resistance to salt water 60d is non-foaming, do not fall off, the smooth light of film；Coating drying property is good, surface drying
6h, does solid work 18h, covering power 110g/cm2, preparation method is simple, and raw material is simple and easy to get, can be with the widespread production not division of history into periods for existing
There is material.
Claims (5)
1. a metal thickness slurry heavy anti-corrosion antirust paint, it is characterised in that the raw material of described metal thick slurry heavy anti-corrosion antirust paint
As follows by mass fraction proportioning: coal tar pitch 100 parts, epoxy resin 15-35 part, polyamide 5-25 part, potassium silicate 10-30 part, silicon
Acid aluminum 5-25 part, BTA 4-16 part, strontium sulfate 0.1-0.5 part, dimethylbenzene 50-90 part, polyphosphoric acids aluminum 8-12 part, three
Aoxidize two chromium 1-20 parts.
A kind of metal the most according to claim 1 thick slurry heavy anti-corrosion antirust paint, it is characterised in that the thick slurry of described metal
It is as follows that mass fraction proportioning pressed by the raw material of heavy anti-corrosion antirust paint: coal tar pitch 100 parts, epoxy resin 20-30 part, polyamide 10-20
Part, potassium silicate 15-25 part, aluminium silicate 10-20 part, BTA 6-12 part, strontium sulfate 0.2-0.4 part, dimethylbenzene 60-80
Part, polyphosphoric acids aluminum 9-11 part, chromic oxide 5-15 part.
A kind of metal the most according to claim 1 thick slurry heavy anti-corrosion antirust paint, it is characterised in that the thick slurry of described metal
It is as follows that mass fraction proportioning pressed by the raw material of heavy anti-corrosion antirust paint: coal tar pitch 100 parts, epoxy resin 20 parts, polyamide 10 parts, silicic acid
15 parts of potassium, aluminium silicate 10 parts, BTA 6 parts, strontium sulfate 0.2 part, dimethylbenzene 60 parts, 9 parts of polyphosphoric acids aluminum, three oxidations two
Chromium 5 parts.
A kind of metal the most according to claim 2 thick slurry heavy anti-corrosion antirust paint, it is characterised in that the thick slurry of described metal
It is as follows that mass fraction proportioning pressed by the raw material of heavy anti-corrosion antirust paint: coal tar pitch 100 parts, epoxy resin 30 parts, polyamide 20 parts, silicic acid
25 parts of potassium, aluminium silicate 20 parts, BTA 12 parts, strontium sulfate 0.4 part, dimethylbenzene 80 parts, 11 parts of polyphosphoric acids aluminum, three oxidations
Two chromium 15 parts.
A kind of metal the most according to claim 1 thick slurry heavy anti-corrosion antirust paint, it is characterised in that: the thick slurry of described metal
It is as follows that mass fraction proportioning pressed by the raw material of heavy anti-corrosion antirust paint: coal tar pitch 100 parts, epoxy resin 25 parts, polyamide 15 parts, silicic acid
20 parts of potassium, aluminium silicate 15 parts, BTA 9 parts, strontium sulfate 0.3 part, dimethylbenzene 70 parts, 10 parts of polyphosphoric acids aluminum, three oxidations
Two chromium 10 parts.