CN106189119A - A kind of computer power communication switch board electric power cable material - Google Patents
A kind of computer power communication switch board electric power cable material Download PDFInfo
- Publication number
- CN106189119A CN106189119A CN201610656627.1A CN201610656627A CN106189119A CN 106189119 A CN106189119 A CN 106189119A CN 201610656627 A CN201610656627 A CN 201610656627A CN 106189119 A CN106189119 A CN 106189119A
- Authority
- CN
- China
- Prior art keywords
- parts
- copper sulphate
- electric power
- cable material
- power cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of computer power communication switch board electric power cable material, composed of the following components: polyethylene terephthalate, styrene butadiene styrene block copolymer, poly (propylene carbonate), polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, dichloroisocyanuric acid sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder, lignocellulose, copper sulphate pentahydrate, nano-titanium oxide, TDE, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresyl phosphate, sulfenamide type accelerators, hexadecyltri-n-butylphosp, disproportionated rosin acid soap, Benzoinum, triethylene glycol, fumaric acid.Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Description
Technical field
The present invention relates to a kind of computer power communication switch board electric power cable material, belong to computer power communication skill
Art field.
Background technology
Electrical control cabinet is as the term suggests being exactly the electric cabinet as electrical control effect.Electrical control cabinet has traditional relay
With PLC control.Fairly simple control relay controls, and complicated control typically uses PLC control.PLC can compile exactly
Procedure logical control system.Electrical control cabinet, according to different needs, uses different control.According to the number of controlled device, greatly
The different electrical equipment of little selection is combined into a cabinet.The simplest electrical control cabinet controlling a motor exactly, one
Chopper, a catalyst, a thermal protective element, a start button, a stop button, two display lamps.Electric power leads to
Letter switch board must use power cable, in order to realize communication and the use of data, therefore, it is necessary to provide suitable electric power
Cable material.
Summary of the invention
It is an object of the invention to provide a kind of computer power communication switch board electric power cable material, in order to preferably
Realize the use function of computer power communication switch board electric power cable material, make product have fire-retardant, acid and alkali-resistance, anti-mildew
Anti-microbial property, improves product serviceability.
To achieve these goals, technical scheme is as follows.
A kind of computer power communication switch board electric power cable material, is made up of the component of following mass fraction: poly-right
Diethyl phthalate 26~30 parts, styrene butadiene styrene block copolymer (SBS) 24~28 parts, poly (propylene carbonate) 24
~28 parts, polyacrylate emulsion 22~26 parts, HMPA 24~28 parts, essence of Niobe 24~28 parts, acetic acid second
Ester 22~26 parts, bobbin oil 24~28 parts, calcium propionate 24~28 parts, dichloroisocyanuric acid sodium 22~26 parts, piperine 22~26
Part, hibitane 22~26 parts, copper sulphate powder 24~28 parts, calcium sulfate crystal whiskers 22~26 parts, basic lead chromate silicate 20~24 parts,
Paraffin 24~28 parts, molybdenum silicide powder 22~26 parts, lignocellulose 20~24 parts, copper sulphate pentahydrate 22~26 parts, nanometer
Titanium oxide 20~24 parts, TDE 20~24 parts, zinc phosphate 22~26 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 22~26 parts,
Tricresyl phosphate 22~26 parts, sulfenamide type accelerators 22~26 parts, hexadecyltri-n-butylphosp 22~26 parts, discrimination
Change RA rosin acid 22~26 parts, Benzoinum 22~26 parts, triethylene glycol 22~26 parts, fumaric acid 20~24 parts.
Further, above computer power communication switch board electric power cable material, by the component of following mass fraction
Composition: polyethylene terephthalate 26 parts, styrene butadiene styrene block copolymer (SBS) 24 parts, poly (propylene carbonate) 24
Part, polyacrylate emulsion 22 parts, HMPA 24 parts, essence of Niobe 24 parts, ethyl acetate 22 parts, bobbin oil 24
Part, calcium propionate 24 parts, dichloroisocyanuric acid sodium 22 parts, piperine 22 parts, hibitane 22 parts, copper sulphate powder 24 parts, calcium sulfate
Whisker 22 parts, basic lead chromate silicate 20 parts, 24 parts of paraffin, molybdenum silicide powder 22 parts, lignocellulose 20 parts, copper sulphate pentahydrate
22 parts, nano-titanium oxide 20 parts, TDE 20 parts, zinc phosphate 22 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 22 parts, tripotassium phosphate
Phenolic ester 22 parts, sulfenamide type accelerators 22 parts, hexadecyltri-n-butylphosp 22 parts, disproportionated rosin acid soap 22 parts, rest in peace
Perfume 22 parts, triethylene glycol 22 parts, fumaric acid 20 parts.
Further, above computer power communication switch board electric power cable material, by the component of following mass fraction
Composition: polyethylene terephthalate 28 parts, styrene butadiene styrene block copolymer (SBS) 26 parts, poly (propylene carbonate) 26
Part, polyacrylate emulsion 24 parts, HMPA 26 parts, essence of Niobe 26 parts, ethyl acetate 24 parts, bobbin oil 26
Part, calcium propionate 26 parts, dichloroisocyanuric acid sodium 24 parts, piperine 24 parts, hibitane 24 parts, copper sulphate powder 26 parts, calcium sulfate
Whisker 24 parts, basic lead chromate silicate 22 parts, 26 parts of paraffin, molybdenum silicide powder 24 parts, lignocellulose 22 parts, copper sulphate pentahydrate
24 parts, nano-titanium oxide 22 parts, TDE 22 parts, zinc phosphate 24 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 24 parts, tripotassium phosphate
Phenolic ester 24 parts, sulfenamide type accelerators 24 parts, hexadecyltri-n-butylphosp 24 parts, disproportionated rosin acid soap 24 parts, rest in peace
Perfume 24 parts, triethylene glycol 24 parts, fumaric acid 22 parts.
Further, above computer power communication switch board electric power cable material, by the component of following mass fraction
Composition: polyethylene terephthalate 30 parts, styrene butadiene styrene block copolymer (SBS) 28 parts, poly (propylene carbonate) 28
Part, polyacrylate emulsion 26 parts, HMPA 28 parts, essence of Niobe 28 parts, ethyl acetate 26 parts, bobbin oil 28
Part, calcium propionate 28 parts, dichloroisocyanuric acid sodium 26 parts, piperine 26 parts, hibitane 26 parts, copper sulphate powder 28 parts, calcium sulfate
Whisker 26 parts, basic lead chromate silicate 24 parts, 28 parts of paraffin, molybdenum silicide powder 26 parts, lignocellulose 24 parts, copper sulphate pentahydrate
26 parts, nano-titanium oxide 24 parts, TDE 24 parts, zinc phosphate 26 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 26 parts, tripotassium phosphate
Phenolic ester 26 parts, sulfenamide type accelerators 26 parts, hexadecyltri-n-butylphosp 26 parts, disproportionated rosin acid soap 26 parts, rest in peace
Perfume 26 parts, triethylene glycol 26 parts, fumaric acid 24 parts.
Further, above computer power communication switch board electric power cable material preparation method step is as follows:
(1) by the polyethylene terephthalate of described mass fraction, styrene butadiene styrene block copolymer (SBS),
Poly (propylene carbonate), polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, two
Chlorine isocyanuric acid sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder
End, lignocellulose, copper sulphate pentahydrate, nano-titanium oxide are mixed, ultrasonic high speed dispersion, ultrasonic frequency be 20~
40KHz, rate of dispersion 5000~about 5400r/min, jitter time is 30~60min;
(2) TDE of described mass fraction, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresol phosphate are added
Ester, sulfenamide type accelerators, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, rate of dispersion 4800~5200r/
About min, jitter time is 30~50min;
(3) hexadecyltri-n-butylphosp of described mass fraction, disproportionated rosin acid soap, Benzoinum, three second two are added
Alcohol, fumaric acid, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, rate of dispersion 4600~about 4800r/min,
Jitter time is 20~40min;This product is prepared after mix homogeneously.
This beneficial effect of the invention is: the computer power communication switch board electric power cable material in the present invention, by
Following components form: polyethylene terephthalate, styrene butadiene styrene block copolymer (SBS), poly (propylene carbonate),
Polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, dichloroisocyanuric acid sodium,
Piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder, wood fibre
Element, copper sulphate pentahydrate, nano-titanium oxide, TDE, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresyl phosphate, secondary
Sulfonamides accelerator, hexadecyltri-n-butylphosp, disproportionated rosin acid soap, Benzoinum, triethylene glycol, fumaric acid.
Product of the present invention has the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improves properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Computer power communication switch board electric power cable material in the present embodiment, by the component group of following mass fraction
Become: polyethylene terephthalate 26 parts, styrene butadiene styrene block copolymer (SBS) 24 parts, poly (propylene carbonate) 24
Part, polyacrylate emulsion 22 parts, HMPA 24 parts, essence of Niobe 24 parts, ethyl acetate 22 parts, bobbin oil 24
Part, calcium propionate 24 parts, dichloroisocyanuric acid sodium 22 parts, piperine 22 parts, hibitane 22 parts, copper sulphate powder 24 parts, calcium sulfate
Whisker 22 parts, basic lead chromate silicate 20 parts, 24 parts of paraffin, molybdenum silicide powder 22 parts, lignocellulose 20 parts, copper sulphate pentahydrate
22 parts, nano-titanium oxide 20 parts, TDE 20 parts, zinc phosphate 22 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 22 parts, tripotassium phosphate
Phenolic ester 22 parts, sulfenamide type accelerators 22 parts, hexadecyltri-n-butylphosp 22 parts, disproportionated rosin acid soap 22 parts, rest in peace
Perfume 22 parts, triethylene glycol 22 parts, fumaric acid 20 parts.
Above computer power communication switch board electric power cable material preparation method step is as follows:
(1) by the polyethylene terephthalate of described mass fraction, styrene butadiene styrene block copolymer (SBS),
Poly (propylene carbonate), polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, two
Chlorine isocyanuric acid sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder
End, lignocellulose, copper sulphate pentahydrate, nano-titanium oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, point
Dissipating about speed 5400r/min, jitter time is 60min;
(2) TDE of described mass fraction, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresol phosphate are added
Ester, sulfenamide type accelerators, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, dispersion
Time is 50min;
(3) hexadecyltri-n-butylphosp of described mass fraction, disproportionated rosin acid soap, Benzoinum, three second two are added
Alcohol, fumaric acid, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is
40min;This product is prepared after mix homogeneously.
Embodiment 2
Computer power communication switch board electric power cable material in the present embodiment, by the component group of following mass fraction
Become: polyethylene terephthalate 28 parts, styrene butadiene styrene block copolymer (SBS) 26 parts, poly (propylene carbonate) 26
Part, polyacrylate emulsion 24 parts, HMPA 26 parts, essence of Niobe 26 parts, ethyl acetate 24 parts, bobbin oil 26
Part, calcium propionate 26 parts, dichloroisocyanuric acid sodium 24 parts, piperine 24 parts, hibitane 24 parts, copper sulphate powder 26 parts, calcium sulfate
Whisker 24 parts, basic lead chromate silicate 22 parts, 26 parts of paraffin, molybdenum silicide powder 24 parts, lignocellulose 22 parts, copper sulphate pentahydrate
24 parts, nano-titanium oxide 22 parts, TDE 22 parts, zinc phosphate 24 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 24 parts, tripotassium phosphate
Phenolic ester 24 parts, sulfenamide type accelerators 24 parts, hexadecyltri-n-butylphosp 24 parts, disproportionated rosin acid soap 24 parts, rest in peace
Perfume 24 parts, triethylene glycol 24 parts, fumaric acid 22 parts.
Above computer power communication switch board electric power cable material preparation method step is as follows:
(1) by the polyethylene terephthalate of described mass fraction, styrene butadiene styrene block copolymer (SBS),
Poly (propylene carbonate), polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, two
Chlorine isocyanuric acid sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder
End, lignocellulose, copper sulphate pentahydrate, nano-titanium oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, point
Dissipating about speed 5200r/min, jitter time is 45min;
(2) TDE of described mass fraction, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresol phosphate are added
Ester, sulfenamide type accelerators, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, dispersion
Time is 40min;
(3) hexadecyltri-n-butylphosp of described mass fraction, disproportionated rosin acid soap, Benzoinum, three second two are added
Alcohol, fumaric acid, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is
30min;This product is prepared after mix homogeneously.
Embodiment 3
Computer power communication switch board electric power cable material in the present embodiment, by the component group of following mass fraction
Become: polyethylene terephthalate 30 parts, styrene butadiene styrene block copolymer (SBS) 28 parts, poly (propylene carbonate) 28
Part, polyacrylate emulsion 26 parts, HMPA 28 parts, essence of Niobe 28 parts, ethyl acetate 26 parts, bobbin oil 28
Part, calcium propionate 28 parts, dichloroisocyanuric acid sodium 26 parts, piperine 26 parts, hibitane 26 parts, copper sulphate powder 28 parts, calcium sulfate
Whisker 26 parts, basic lead chromate silicate 24 parts, 28 parts of paraffin, molybdenum silicide powder 26 parts, lignocellulose 24 parts, copper sulphate pentahydrate
26 parts, nano-titanium oxide 24 parts, TDE 24 parts, zinc phosphate 26 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 26 parts, tripotassium phosphate
Phenolic ester 26 parts, sulfenamide type accelerators 26 parts, hexadecyltri-n-butylphosp 26 parts, disproportionated rosin acid soap 26 parts, rest in peace
Perfume 26 parts, triethylene glycol 26 parts, fumaric acid 24 parts.
Above computer power communication switch board electric power cable material preparation method step is as follows:
(1) by the polyethylene terephthalate of described mass fraction, styrene butadiene styrene block copolymer (SBS),
Poly (propylene carbonate), polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, two
Chlorine isocyanuric acid sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder
End, lignocellulose, copper sulphate pentahydrate, nano-titanium oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, point
Dissipating speed 5000r/min, jitter time is 30min;
(2) TDE of described mass fraction, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresol phosphate are added
Ester, sulfenamide type accelerators, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, jitter time
For 30min;
(3) hexadecyltri-n-butylphosp of described mass fraction, disproportionated rosin acid soap, Benzoinum, three second two are added
Alcohol, fumaric acid, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is
20min;This product is prepared after mix homogeneously.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured
Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a computer power communication switch board electric power cable material, it is characterised in that: by the component of following mass fraction
Composition: polyethylene terephthalate 26~30 parts, styrene butadiene styrene block copolymer (SBS) 24~28 parts, poly-carbonic acid
Sub-propyl ester 24~28 parts, polyacrylate emulsion 22~26 parts, HMPA 24~28 parts, essence of Niobe 24~28
Part, ethyl acetate 22~26 parts, bobbin oil 24~28 parts, calcium propionate 24~28 parts, dichloroisocyanuric acid sodium 22~26 parts, Fructus Piperis
Alkali 22~26 parts, hibitane 22~26 parts, copper sulphate powder 24~28 parts, calcium sulfate crystal whiskers 22~26 parts, basic lead chromate silicate
20~24 parts, paraffin 24~28 parts, molybdenum silicide powder 22~26 parts, lignocellulose 20~24 parts, copper sulphate pentahydrate 22~
26 parts, nano-titanium oxide 20~24 parts, TDE 20~24 parts, zinc phosphate 22~26 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate
22~26 parts, tricresyl phosphate 22~26 parts, sulfenamide type accelerators 22~26 parts, hexadecyltri-n-butylphosp 22
~26 parts, disproportionated rosin acid soap 22~26 parts, Benzoinum 22~26 parts, triethylene glycol 22~26 parts, fumaric acid 20~24
Part.
Computer power communication switch board electric power cable material the most according to claim 1, it is characterised in that: described meter
Calculate electro-mechanical force Control on Communication cabinet electric power cable material to be made up of the component of following mass fraction: polyethylene terephthalate 26
Part, styrene butadiene styrene block copolymer (SBS) 24 parts, poly (propylene carbonate) 24 parts, polyacrylate emulsion 22 parts, pregnancy
Base phosphoric triamide 24 parts, essence of Niobe 24 parts, ethyl acetate 22 parts, 24 parts of bobbin oil, calcium propionate 24 parts, DCCA
22 parts of sodium, piperine 22 parts, hibitane 22 parts, copper sulphate powder 24 parts, calcium sulfate crystal whiskers 22 parts, basic lead chromate silicate 20 parts,
24 parts of paraffin, molybdenum silicide powder 22 parts, lignocellulose 20 parts, copper sulphate pentahydrate 22 parts, nano-titanium oxide 20 parts, ten bromines two
Vinylbenzene 20 parts, zinc phosphate 22 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 22 parts, tricresyl phosphate 22 parts, sulfenamide type accelerators
22 parts, hexadecyltri-n-butylphosp 22 parts, disproportionated rosin acid soap 22 parts, Benzoinum 22 parts, triethylene glycol 22 parts, anti-butylene
Diacid 20 parts.
3. according to the computer power communication switch board electric power cable material described in claim 1 to 2, it is characterised in that: institute
State computer power communication switch board electric power cable material to be made up of the component of following mass fraction: poly terephthalic acid diethyl
Ester 28 parts, styrene butadiene styrene block copolymer (SBS) 26 parts, poly (propylene carbonate) 26 parts, polyacrylate emulsion 24 parts,
HMPA 26 parts, essence of Niobe 26 parts, ethyl acetate 24 parts, 26 parts of bobbin oil, calcium propionate 26 parts, dichloro isocyanide
24 parts of urea acid sodium, piperine 24 parts, hibitane 24 parts, copper sulphate powder 26 parts, calcium sulfate crystal whiskers 24 parts, basic lead chromate silicate 22
Part, 26 parts of paraffin, molybdenum silicide powder 24 parts, lignocellulose 22 parts, copper sulphate pentahydrate 24 parts, nano-titanium oxide 22 parts, ten
Bromine diphenylethane 22 parts, zinc phosphate 24 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 24 parts, tricresyl phosphate 24 parts, sulfenamide promote
Enter agent 24 parts, hexadecyltri-n-butylphosp 24 parts, disproportionated rosin acid soap 24 parts, Benzoinum 24 parts, triethylene glycol 24 parts, anti-
Butene dioic acid 22 parts.
4. according to the computer power communication switch board electric power cable material described in claims 1 to 3, it is characterised in that: institute
State computer power communication switch board electric power cable material to be made up of the component of following mass fraction: poly terephthalic acid diethyl
Ester 30 parts, styrene butadiene styrene block copolymer (SBS) 28 parts, poly (propylene carbonate) 28 parts, polyacrylate emulsion 26 parts,
HMPA 28 parts, essence of Niobe 28 parts, ethyl acetate 26 parts, 28 parts of bobbin oil, calcium propionate 28 parts, dichloro isocyanide
26 parts of urea acid sodium, piperine 26 parts, hibitane 26 parts, copper sulphate powder 28 parts, calcium sulfate crystal whiskers 26 parts, basic lead chromate silicate 24
Part, 28 parts of paraffin, molybdenum silicide powder 26 parts, lignocellulose 24 parts, copper sulphate pentahydrate 26 parts, nano-titanium oxide 24 parts, ten
Bromine diphenylethane 24 parts, zinc phosphate 26 parts, 2,2'-ethylenedioxybis(ethanol). two tricaprylate 26 parts, tricresyl phosphate 26 parts, sulfenamide promote
Enter agent 26 parts, hexadecyltri-n-butylphosp 26 parts, disproportionated rosin acid soap 26 parts, Benzoinum 26 parts, triethylene glycol 26 parts, anti-
Butene dioic acid 24 parts.
Computer power communication switch board electric power cable material the most according to claim 1, it is characterised in that: described meter
Calculate electro-mechanical force Control on Communication cabinet electric power cable material preparation method step as follows:
(1) by the polyethylene terephthalate of described mass fraction, styrene butadiene styrene block copolymer (SBS), poly-carbon
The sub-propyl ester of acid, polyacrylate emulsion, HMPA, essence of Niobe, ethyl acetate, bobbin oil, calcium propionate, dichloro are different
Cyanurate sodium, piperine, hibitane, copper sulphate powder, calcium sulfate crystal whiskers, basic lead chromate silicate, paraffin, molybdenum silicide powder,
Lignocellulose, copper sulphate pentahydrate, nano-titanium oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20~40KHz,
Rate of dispersion about 5000~5400r/min, jitter time is 30~about 60min;
(2) TDE of described mass fraction, zinc phosphate, 2,2'-ethylenedioxybis(ethanol). two tricaprylate, tricresyl phosphate, secondary is added
Sulfonamides accelerator, ultrasonic high speed dispersion, ultrasonic frequency is 20~35KHz, and rate of dispersion is about 4800~5200r/
Min, jitter time is 30~about 50min;
(3) hexadecyltri-n-butylphosp of described mass fraction, disproportionated rosin acid soap, Benzoinum, triethylene glycol, anti-is added
Butene dioic acid, ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, and rate of dispersion is about 4600~4800r/min, dispersion
Time is 20~about 40min;This product is prepared after mix homogeneously.