CN106189073A - Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method and product - Google Patents
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method and product Download PDFInfo
- Publication number
- CN106189073A CN106189073A CN201610591043.0A CN201610591043A CN106189073A CN 106189073 A CN106189073 A CN 106189073A CN 201610591043 A CN201610591043 A CN 201610591043A CN 106189073 A CN106189073 A CN 106189073A
- Authority
- CN
- China
- Prior art keywords
- bamboo fibre
- tea packaging
- fibre reinforced
- carbon
- packaging apparatus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method, comprises the technical steps that: mass ratio is (4.5~6.5) by (1): (0.6~1.5): (2.5~4.5): the powdered carbon of (0.05~0.5), starch, urea-formaldehyde resin powder or melmac powder, bamboo fibre raw material mix homogeneously;(2) mixing material is added in heating die cavity, thermocompression forming under the conditions of temperature 140~150 DEG C, pressure 25~35MPa, obtain the carbon bamboo fibre reinforced tea packaging thick embryo of apparatus;(3) surface to the described carbon bamboo fibre reinforced tea packaging thick embryo of apparatus carries out grinding process or mechanism processing obtains carbon bamboo fibre reinforced tea packaging apparatus finished product.Carbon bamboo fibre reinforced tea packaging apparatus product, uses above-mentioned manufacturing technique method to make.
Description
Technical field
The present invention relates to tea packaging apparatus, more specifically refer to that the carbon bamboo fibre with carbon as material of main part adds
Strong type tea packaging apparatus manufacturing technique method and product.
Background technology
The manufacture material of existing tea packaging apparatus is metal, synthetic paper, glass, timber, pottery etc., and these materials are all
It it not preferable tea packaging material.
Summary of the invention
It is an object of the invention to provide a kind of use Carbon Materials to produce tea-processing packing appliance tea packaging use
Tool manufacturing technique method and product, i.e. carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method and product.Use
Technical scheme be:
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method, comprises the technical steps that: mass ratio is by (1)
(4.5~6.5): (0.6~1.5): (2.5~4.5): powdered carbon, starch, urea-formaldehyde resin powder or the melamine resin of (0.05~0.5)
Powder, bamboo fibre raw material mix homogeneously;(2) mixing material is added in heating die cavity, temperature 140~150 DEG C, pressure 25~
Thermocompression forming under the conditions of 35MPa, obtains the carbon bamboo fibre reinforced tea packaging thick embryo of apparatus;(3) to described carbon bamboo
The surface of the fiber reinforced thick embryo of tea packaging apparatus carries out grinding process or mechanism processing, and to obtain carbon bamboo fibre reinforced
Tea packaging apparatus finished product.
For enhancing product performance, can be selected for modified urea-formaldehyde resin powder or melamine resin powder, improve the resistance to water of goods.Such as choosing
It is used in synthesis Lauxite or during melamine resin, adds a small amount of tripolycyanamide, phenol, resorcinol, alkylamine, alditol etc. all
The resistance to water of resin can be effectively improved.Add aluminum sulfate, aluminum phosphate etc. as cross-linking agent, it is possible to significantly improve resistance to water.From
And obtain the goods of water-tolerant.
Carbon bamboo fibre reinforced tea packaging apparatus, uses above-mentioned manufacturing technique method to make.
The technological progress that technique scheme acquirement is the most positive:
1, owing to using charcoal to manufacture tea packaging apparatus for the main material that manufactures, it is achieved that the tea packaging of a kind of novel concept
Apparatus.Charcoal has moisture absorption, filters the function of various miscellaneous taste, carrys out packaging tealeaves with described apparatus, it is possible to maintain the product of Folium Camelliae sinensis very well
Matter.
2, the intensity using the described tea packaging apparatus of increase of bamboo fibre.
3, charcoal applies in tea packaging first, has innovated tea packaging theory, has abundant tea culture and propagates succession
Characteristic element, especially for the packaging of all kinds of high-end tea, can be welcome by market.
Embodiment
It is exemplified below:
Embodiment 1:
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method, comprises the technical steps that: mass ratio is by (1)
Powdered carbon, starch, urea-formaldehyde resin powder or the melamine resin powder of 4.5: 0.6: 2.5:0.05, bamboo fibre raw material mix homogeneously;(2) mixed
Even material adds in heating die cavity, and thermocompression forming under the conditions of temperature 140 DEG C, pressure 25MPa obtains carbon bamboo fibre and strengthens
The thick embryo of type tea packaging apparatus;(3) is polished in the surface of the described carbon bamboo fibre reinforced tea packaging thick embryo of apparatus
Process or mechanism processing obtains carbon bamboo fibre reinforced tea packaging apparatus finished product.
Carbon bamboo fibre reinforced tea packaging apparatus, uses above-mentioned manufacturing technique method to make.
Embodiment 2:
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method, comprises the technical steps that: mass ratio is by (1)
Powdered carbon, starch, urea-formaldehyde resin powder or the melmac powder of 5.0: 0.9: 3.5:0.10, bamboo fibre raw material mix homogeneously;(2)
Mixing material is added in heating die cavity, thermocompression forming under the conditions of temperature 145 DEG C, pressure 30MPa, obtain carbon bamboo fibre
The reinforced thick embryo of tea packaging apparatus;(3) surface of the described carbon bamboo fibre reinforced tea packaging thick embryo of apparatus is carried out
Grinding process or mechanism processing obtain carbon bamboo fibre reinforced tea packaging apparatus finished product.
Carbon bamboo fibre reinforced tea packaging apparatus, uses above-mentioned manufacturing technique method to make.
Embodiment 3:
Carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method, comprises the technical steps that: mass ratio is by (1)
Powdered carbon, starch, urea-formaldehyde resin powder or the melamine resin powder of 6.5: 1.5: 4.5:0.5, bamboo fibre raw material mix homogeneously;(2) mixed
Even material adds in heating die cavity, and thermocompression forming under the conditions of temperature 150 DEG C, pressure 35MPa obtains carbon bamboo fibre and strengthens
The thick embryo of type tea packaging apparatus;(3) is polished in the surface of the described carbon bamboo fibre reinforced tea packaging thick embryo of apparatus
Process or mechanism processing obtains carbon bamboo fibre reinforced tea packaging apparatus finished product.
Carbon bamboo fibre reinforced tea packaging apparatus, uses above-mentioned manufacturing technique method to make.
Claims (2)
1. carbon bamboo fibre reinforced tea packaging apparatus manufacturing technique method and product, its technology is characterized in that include as follows
Processing step: mass ratio is (4.5~6.5) by (1): (0.6~1.5): (2.5~4.5): the powdered carbon of (0.05~0.5), shallow lake
Powder, urea-formaldehyde resin powder or melmac powder, bamboo fibre raw material mix homogeneously;(2) mixing material is added in heating die cavity,
Thermocompression forming under the conditions of temperature 140~150 DEG C, pressure 25~35MPa, obtains the reinforced tea packaging of carbon bamboo fibre and uses
Has thick embryo;(3) surface of the described carbon bamboo fibre reinforced tea packaging thick embryo of apparatus is carried out grinding process or mechanism adds
Work obtains carbon bamboo fibre reinforced tea packaging apparatus finished product.
2. carbon bamboo fibre reinforced tea packaging apparatus product, it technology is characterized in that and produces work described in employing claim 1
Process is made.