CN106189047A - A kind of high surface finish ABS material - Google Patents
A kind of high surface finish ABS material Download PDFInfo
- Publication number
- CN106189047A CN106189047A CN201610598958.4A CN201610598958A CN106189047A CN 106189047 A CN106189047 A CN 106189047A CN 201610598958 A CN201610598958 A CN 201610598958A CN 106189047 A CN106189047 A CN 106189047A
- Authority
- CN
- China
- Prior art keywords
- parts
- high surface
- surface finish
- abs
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high surface finish ABS material, be made up of the raw material of following weight parts: ABS resin 85 90 parts, styrene acrylonitrile copolymer 5 10 parts, toughener 36 parts, 0.3 0.8 parts of antioxidant, UV absorbent 0 0.5 parts.The present invention is by adding styrene acrylonitrile copolymer and improving former fineness in ABS resin, and both schemes are carried out simultaneously so that product glossiness is brought up to 95 100 by 85 90；Styrene acrylonitrile copolymer can be the most compatible with ABS, has been simultaneously introduced toughener, it is ensured that the toughness of material, still disclosure satisfy that the requirement of impact resistance and tensile property；There is excellent anti-ultraviolet property simultaneously, extend the service life of material.
Description
Technical field
The present invention relates to technical field of polymer materials, specifically a kind of high surface finish ABS material.
Background technology
ABS is acrylonitrile, 1,3-butadiene, the graft copolymer of three kinds of monomers of styrene, have high intensity, good toughness,
The feature that glossiness is high.For household electrical appliances, common ABS can meet the demand of product glossiness, but special for some
Parts, such as the surface of high-grade household electrical appliances, it is desirable to reach mirror effect, then cannot meet.ABS is improved glossiness difficulty relatively big, mesh
Before also there is no suitable method.
Summary of the invention
It is an object of the invention to provide a kind of high surface finish ABS material, to solve above-mentioned background technology proposes
Problem.
For achieving the above object, the present invention provides following technical scheme:
A kind of high surface finish ABS material, is made up of the raw material of following weight parts:
ABS resin 85-90 part, SAN 5-10 part, toughener 3-6 part, antioxidant 0.3-0.8 part,
UV absorbent 0-0.5 part.
Preferably, described UV absorbent is Ultraviolet Absorber UV-P.
Preferably, described toughener is butadiene type terpolymer.
Preferably, described antioxidant is 2, tri-grades of butyl-4-methylphenols of 6-.
Preferably, described a kind of high surface finish ABS material, it is made up of the raw material of following weight parts:
ABS resin 88 parts, SAN 6 parts, toughener 5.2 parts, 0.5 part of antioxidant, ultra-violet absorption
Agent 0.3 part
Compared with prior art, the invention has the beneficial effects as follows:
The present invention is by adding SAN and improving former fineness in ABS resin, and these are two years old
The scheme of kind is carried out simultaneously so that product glossiness is brought up to 95-100 by 85-90；SAN is permissible with ABS
The most compatible, it is simultaneously introduced toughener, it is ensured that the toughness of material, still disclosure satisfy that impact resistance and tensile property
Requirement；There is excellent anti-ultraviolet property simultaneously, extend the service life of material.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
One high surface finish ABS material of the present invention, is made up of the raw material of following weight parts:
ABS resin 85 parts, SAN 10 parts, toughener 4.6 parts, 0.3 part of antioxidant, ultraviolet is inhaled
Receive agent UV-P 0.1 part.
Described toughener is butadiene type terpolymer.
Described antioxidant is 2, tri-grades of butyl-4-methylphenols of 6-, can delay or suppress the carrying out of polymer oxidizing process,
Thus stop the aging of polymer and extend its service life.
UV absorbent can absorb ultraviolet (especially wavelength is 290-400nm) consumingly；Heat stability is good, even if
Work in-process also will not change because of heat, and hot volatility is little；Chemical stability is good, unfavorable instead with material component generation in goods
Should；Compatibility is good, may be uniformly dispersed in material, and no blooming does not oozes out；The photochemical stability of absorbent itself is good, no
Decompose, invariant color；Colourless, nontoxic, odorless；Resistance to embathe；Inexpensive, be easy to get.
A kind of high surface finish ABS material of the present invention, in preparation process, selects the product mold of corresponding requirements, will
Cavity-polishing grade brings up to essence and throws grade.
Embodiment 2
One high surface finish ABS material of the present invention, is made up of the raw material of following weight parts:
ABS resin 88 parts, SAN 6 parts, toughener 5.2 parts, 0.5 part of antioxidant, ultra-violet absorption
Agent UV-P 0.3 part.
Described toughener is butadiene type terpolymer.
Described antioxidant is 2, tri-grades of butyl-4-methylphenols of 6-, can delay or suppress the carrying out of polymer oxidizing process,
Thus stop the aging of polymer and extend its service life.
UV absorbent can absorb ultraviolet (especially wavelength is 290-400nm) consumingly；Heat stability is good, even if
Work in-process also will not change because of heat, and hot volatility is little；Chemical stability is good, unfavorable instead with material component generation in goods
Should；Compatibility is good, may be uniformly dispersed in material, and no blooming does not oozes out；The photochemical stability of absorbent itself is good, no
Decompose, invariant color；Colourless, nontoxic, odorless；Resistance to embathe；Inexpensive, be easy to get.
A kind of high surface finish ABS material of the present invention, in preparation process, selects the product mold of corresponding requirements, will
Cavity-polishing grade brings up to essence and throws grade.
Embodiment 3
One high surface finish ABS material of the present invention, is made up of the raw material of following weight parts:
ABS resin 90 parts, SAN 5 parts, toughener 3-5 part, 4.2 parts of antioxidant, ultra-violet absorption
Agent UV-P 0.5 part.
Described toughener is butadiene type terpolymer.
Described antioxidant is 2, tri-grades of butyl-4-methylphenols of 6-, can delay or suppress the carrying out of polymer oxidizing process,
Thus stop the aging of polymer and extend its service life.
UV absorbent can absorb ultraviolet (especially wavelength is 290-400nm) consumingly；Heat stability is good, even if
Work in-process also will not change because of heat, and hot volatility is little；Chemical stability is good, unfavorable instead with material component generation in goods
Should；Compatibility is good, may be uniformly dispersed in material, and no blooming does not oozes out；The photochemical stability of absorbent itself is good, no
Decompose, invariant color；Colourless, nontoxic, odorless；Resistance to embathe；Inexpensive, be easy to get.
A kind of high surface finish ABS material of the present invention, in preparation process, selects the product mold of corresponding requirements, will
Cavity-polishing grade brings up to essence and throws grade.
Claims (5)
1. a high surface finish ABS material, it is characterised in that be made up of the raw material of following weight parts:
ABS resin 85-90 part, SAN 5-10 part, toughener 3-6 part, antioxidant 0.3-0.8 part, ultraviolet
Light absorbers 0-0.5 part.
A kind of high surface finish ABS material the most according to claim 1, it is characterised in that described UV absorbent
For Ultraviolet Absorber UV-P.
A kind of high surface finish ABS material the most according to claim 1, it is characterised in that described toughener is fourth two
Alkenes terpolymer.
A kind of high surface finish ABS material the most according to claim 1, it is characterised in that described antioxidant is 2,6-
Three grades of butyl-4-methylphenols.
5. according to a kind of high surface finish ABS material described in any one of claim 1-4, it is characterised in that by following heavy
The raw material of amount part is made:
ABS resin 88 parts, SAN 6 parts, toughener 5.2 parts, 0.5 part of antioxidant, UV absorbent
0.3 part.