CN106189001A - A kind of field use cable core insulating layer material - Google Patents
A kind of field use cable core insulating layer material Download PDFInfo
- Publication number
- CN106189001A CN106189001A CN201610643068.0A CN201610643068A CN106189001A CN 106189001 A CN106189001 A CN 106189001A CN 201610643068 A CN201610643068 A CN 201610643068A CN 106189001 A CN106189001 A CN 106189001A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- insulating layer
- layer material
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of field use cable core insulating layer material, relate to cable material technical field, be made up of the raw material of following parts by weight: politef 30 40 parts, rubber powder 15 20 parts, polyethylene glycol oxide 10 15 parts, disproportionated rosin 10 15 parts, volcanic ash 8 12 parts, melamine resin 6 10 parts, sepiolite powder 58 parts, 58 parts of straw dry powder, ceramic 46 parts, stearic acid 46 parts, carbomer 35 parts, Brazil wax 35 parts, nanometer rubber powder 23 parts, 23 parts of carbamide, sulfated castor oil 12 parts, nanometer aluminium powder 12 parts.Insulating layer material of the present invention can be used directly to wrap up core, plays insulation blocking effect, and its insulating properties is strong, and has anti-flammability, wearability, corrosion resistance and the ageing resistance of excellence, service life length and safety high.
Description
Technical field:
The present invention relates to cable material technical field, be specifically related to a kind of field use cable core insulating layer material.
Background technology:
Cable, typically by triple line composition described above, has insulating barrier, between phase and phase i.e. at core outer wrapping one layer insulation material
Material, isolates core with external environment condition with adjacent core and core, protects cables from extraneous damage simultaneously.This insulating barrier institute
With material in addition to must having higher insulation resistance, dieletric strength and low dielectric loss, also to take into account good physics
Mechanical performance, such as stretch-proof, counter-bending, anti-vibration and antitorque and high-low temperature resistant, oil resistant, weather-proof etc..At present, field use
The research of cable focuses primarily upon the exploitation of sheath material, and the research for the directly insulating layer material of contact core is little, therefore
Our company develops a kind of field use cable core insulating layer material, has physical and mechanical properties and the high-low temperature resistant of excellence
Property, anti-flammability, insulating properties and wearability.
Summary of the invention:
The technical problem to be solved is to provide one to have excellent physical mechanical performance and high-low temperature resistant
Property, anti-flammability, insulating properties and the field use cable core insulating layer material of wearability.
The technical problem to be solved uses following technical scheme to realize:
A kind of field use cable core insulating layer material, is made up of the raw material of following parts by weight:
Politef 30-40 part, rubber powder 15-20 part, polyethylene glycol oxide 10-15 part, disproportionated rosin 10-15 part, fire
Mountain ash 8-12 part, melamine resin 6-10 part, sepiolite powder 5-8 part, straw dry powder 5-8 part, ceramic 4-6 part,
Stearic acid 4-6 part, carbomer 3-5 part, Brazil wax 3-5 part, nanometer rubber powder 2-3 part, carbamide 2-3 part, sulphation Semen Ricini
Oil 1-2 part, nanometer aluminium powder 1-2 part;
Its preparation method comprises the steps:
(1) politef, disproportionated rosin and melamine resin are added in banbury, prior to 70-80 DEG C at
Mixing 2-3min, mixing 3-5min at 110-120 DEG C, obtain compound I;
(2) rubber powder, polyethylene glycol oxide and nanometer aluminium powder are added in banbury, mixing 2-3min at 120-130 DEG C,
Add stearic acid, Brazil wax and nanometer rubber powder, continue mixing 3-4min, obtain compound II;
(3) by compound I, compound II, volcanic ash, sepiolite powder, straw dry powder, ceramic, carbomer, carbamide
Add after being sufficiently mixed with sulfated castor oil in mill, mill 3-5min at 120-130 DEG C, obtain insulating layer material.
The invention has the beneficial effects as follows: the present invention, with politef as primary raw material, is aided with rubber powder and polyoxyethylene
Alkene and multiple auxiliary agent prepare field use cable core insulating layer material, and this insulating layer material can be used directly to wrap up core,
Playing insulation blocking effect, its insulating properties is strong, and has anti-flammability, wearability, corrosion resistance and the ageing resistance of excellence, uses
Life-span length and safety are high.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below knot
Close specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) 30 parts of politef, 15 parts of disproportionated rosins and 6 parts of melamine resins are added in banbury, first
Mixing 2min at 70-80 DEG C, mixing 3min at 110-120 DEG C, obtain compound I;
(2) 20 parts of rubber powders, 10 parts of polyethylene glycol oxides and 1 part of nanometer aluminium powder are added in banbury, at 120-130 DEG C
Mixing 3min, adds 5 parts of stearic acid, 3 parts of Brazil waxs and 2 parts of nanometer rubber powders, continues mixing 3min, obtain compound
II;
(3) by compound I, compound II, 8 parts of volcanic ash, 6 parts of sepiolite powders, 6 parts of straw dry powder, 4 parts of ceramics, 3
Part carbomer, 2 parts of carbamide and 2 parts of sulfated castor oils add in mill after being sufficiently mixed, mill at 120-130 DEG C
5min, obtains insulating layer material.
Embodiment 2
(1) 35 parts of politef, 10 parts of disproportionated rosins and 8 parts of melamine resins are added in banbury, first
Mixing 2min at 70-80 DEG C, mixing 3min at 110-120 DEG C, obtain compound I;
(2) 15 parts of rubber powders, 10 parts of polyethylene glycol oxides and 2 parts of nanometer aluminium powders are added in banbury, at 120-130 DEG C
Mixing 3min, adds 4 parts of stearic acid, 5 parts of Brazil waxs and 3 parts of nanometer rubber powders, continues mixing 3min, obtain compound
II;
(3) by compound I, compound II, 10 parts of volcanic ash, 5 parts of sepiolite powders, 8 parts of straw dry powder, 5 parts of ceramics,
3 parts of carbomers, 2 parts of carbamide and 1 part of sulfated castor oil add in mill after being sufficiently mixed, mill at 120-130 DEG C
5min, obtains insulating layer material.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (2)
1. a field use cable core insulating layer material, it is characterised in that be made up of the raw material of following parts by weight:
Politef 30-40 part, rubber powder 15-20 part, polyethylene glycol oxide 10-15 part, disproportionated rosin 10-15 part, volcanic ash
8-12 part, melamine resin 6-10 part, sepiolite powder 5-8 part, straw dry powder 5-8 part, ceramic 4-6 part, tristearin
Acid 4-6 part, carbomer 3-5 part, Brazil wax 3-5 part, nanometer rubber powder 2-3 part, carbamide 2-3 part, sulfated castor oil 1-2
Part, nanometer aluminium powder 1-2 part.
Field use cable core insulating layer material the most according to claim 1, it is characterised in that its preparation method include as
Lower step:
(1) politef, disproportionated rosin and melamine resin are added in banbury, prior to 70-80 DEG C at mixing
2-3min, mixing 3-5min at 110-120 DEG C, obtain compound I;
(2) rubber powder, polyethylene glycol oxide and nanometer aluminium powder are added in banbury, mixing 2-3min at 120-130 DEG C, then add
Enter stearic acid, Brazil wax and nanometer rubber powder, continue mixing 3-4min, obtain compound II;
(3) by compound I, compound II, volcanic ash, sepiolite powder, straw dry powder, ceramic, carbomer, carbamide and sulfur
Acidifying Oleum Ricini adds in mill after being sufficiently mixed, and mill 3-5min at 120-130 DEG C obtains insulating layer material.