CN106188438A - A kind of PVC communication tubing and preparation method thereof - Google Patents
A kind of PVC communication tubing and preparation method thereof Download PDFInfo
- Publication number
- CN106188438A CN106188438A CN201610555963.7A CN201610555963A CN106188438A CN 106188438 A CN106188438 A CN 106188438A CN 201610555963 A CN201610555963 A CN 201610555963A CN 106188438 A CN106188438 A CN 106188438A
- Authority
- CN
- China
- Prior art keywords
- parts
- mesh
- pvc
- powder
- tubing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe present invention relates to a kind of PVC communication tubing,It is made up of the component of following mass fraction: alumina silicate fibre 12~16 parts、Antimony oxide 14~18 parts、The titanium dioxide 10 of rutile-type~14 parts、Polyvinyl butyral resin 8~12 parts、Nano tin dioxide 14~18 parts、Boiled wood oil 10~14 parts、Butyl methacrylate 8~12 parts、Diisocyanate 14~18 parts、Diphenyl methane 10~14 parts、Linoleic acid 8~12 parts、Attapulgite powder 14~18 parts、Ammonium molybdate 10~14 parts、Phthalic anhydride 10~14 parts、Lead sulfate tribasic 8~12 parts、HMPA 14~18 parts、Polyvinyl chloride resin 10~14 parts、Poly-4 methyl 1 amylenes 8~12 parts、Glyceryl monostearate 14~18 parts、Methyl methacrylate 10~14 parts、Triethyl citrate 8~12 parts、Nanometer aluminium silicate sodium 14~18 parts、Dioctyl phthalate 10~14 parts、Tangerine oil 8~12 parts、Glass fiber powder 14~18 parts.The present invention has preferable combination property, and using effect is good.
Description
Technical field
The present invention relates to a kind of PVC communication tubing and preparation method thereof, belong to communication tubing technical field.
Background technology
The flexible pipe of PVC is inexpensive, is to generally acknowledge it is also to apply most outdoor pipe materials at present, but existing
There are some defects in the flexible pipe that PVC hose tubing is made, such as exposes to the weather for a long time, aging than very fast, radioprotective
Poor performance, overcoming the way of this defect at present is to add antioxidant with UV absorbent, but the material added is costly,
Cause PVC hose production cost higher.
Summary of the invention
It is an object of the invention to provide a kind of PVC communication tubing and preparation method thereof, in order to PVC communication is better achieved
The function of tubing.
To achieve these goals, technical scheme is as follows.
A kind of PVC communication tubing, is made up of the component of following mass fraction: alumina silicate fibre 12~16 parts, three oxidations two
Antimony 14~18 parts, the titanium dioxide 10 of rutile-type~14 parts, polyvinyl butyral resin 8~12 parts, nano tin dioxide 14~18 parts,
Boiled wood oil 10~14 parts, butyl methacrylate 8~12 parts, diisocyanate 14~18 parts, diphenyl methane 10~14 parts, Asia
Oleic acid 8~12 parts, attapulgite powder 14~18 parts, ammonium molybdate 10~14 parts, phthalic anhydride 10~14 parts, tribasic sulphuric acid
Lead 8~12 parts, HMPA 14~18 parts, polyvinyl chloride resin 10~14 parts, poly-4-methyl-1-pentene 8~12 parts, glycerol
Monostearate 14~18 parts, methyl methacrylate 10~14 parts, triethyl citrate 8~12 parts, nanometer aluminium silicate sodium 14
~18 parts, dioctyl phthalate 10~14 parts, tangerine oil 8~12 parts, glass fiber powder 14~18 parts.
Further, above-mentioned PVC communicates tubing, is made up of the component of following mass fraction: alumina silicate fibre 12 parts, three oxygen
Change 14 parts of two antimony, the titanium dioxide 10 parts of rutile-type, polyvinyl butyral resin 8 parts, nano tin dioxide 14 parts, boiled wood oil 10 parts,
Butyl methacrylate 8 parts, diisocyanate 14 parts, diphenyl methane 10 parts, linoleic acid 8 parts, attapulgite powder 14 parts, molybdic acid
Ammonium 10 parts, phthalic anhydride 10 parts, lead sulfate tribasic 8 parts, HMPA 14 parts, polyvinyl chloride resin 10 parts, poly-4-
Methyl-1-pentene 8 parts, glyceryl monostearate 14 parts, methyl methacrylate 10 parts, triethyl citrate 8 parts, nanometer silicic acid
14 parts of aluminum sodium, dioctyl phthalate 10 parts, tangerine oil 8 parts, glass fiber powder 14 parts.
Further, above-mentioned PVC communicates tubing, is made up of the component of following mass fraction: alumina silicate fibre 14 parts, three oxygen
Change 16 parts of two antimony, the titanium dioxide 12 parts of rutile-type, polyvinyl butyral resin 10 parts, nano tin dioxide 16 parts, boiled wood oil 12 parts,
Butyl methacrylate 10 parts, diisocyanate 16 parts, diphenyl methane 12 parts, linoleic acid 10 parts, attapulgite powder 16 parts, molybdenum
Acid ammonium 12 parts, phthalic anhydride 12 parts, lead sulfate tribasic 10 parts, HMPA 16 parts, polyvinyl chloride resin 12 parts, poly-
4-methyl-1-pentene 10 parts, glyceryl monostearate 16 parts, methyl methacrylate 12 parts, triethyl citrate 10 parts, nanometer
Lagoriolite 16 parts, dioctyl phthalate 12 parts, tangerine oil 10 parts, glass fiber powder 16 parts.
Further, above-mentioned PVC communicates tubing, is made up of the component of following mass fraction: alumina silicate fibre 16 parts, three oxygen
Change 18 parts of two antimony, the titanium dioxide 14 parts of rutile-type, polyvinyl butyral resin 12 parts, nano tin dioxide 18 parts, boiled wood oil 14 parts,
Butyl methacrylate 12 parts, diisocyanate 18 parts, diphenyl methane 14 parts, linoleic acid 12 parts, attapulgite powder 18 parts, molybdenum
Acid ammonium 14 parts, phthalic anhydride 14 parts, lead sulfate tribasic 12 parts, HMPA 18 parts, polyvinyl chloride resin 14 parts, poly-
4-methyl-1-pentene 12 parts, glyceryl monostearate 18 parts, methyl methacrylate 14 parts, triethyl citrate 12 parts, nanometer
Lagoriolite 18 parts, dioctyl phthalate 14 parts, tangerine oil 12 parts, glass fiber powder 18 parts.
Further, the titanium dioxide of described rutile-type is made up of the powder body of three kinds of particle diameter mesh numbers, and its particle diameter mesh number is respectively
Being 30~50 mesh, 50~80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 3~7:4~8:1.
Further, described attapulgite powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 30~
50 mesh, 50~80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 3~8:2~8:1.
Further, the viscosity of described boiled wood oil is 12000~14000mpa.s at 25 DEG C.
Further, described glass fiber powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 20~
50 mesh, 50~70 mesh, 70~90 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 2~4:3~5:1.
Further, described Citrus oil viscosity is 8000~10000mpa.s at 25 DEG C.
Further, above-mentioned PVC communication tubing preparation method step is as follows:
(1) by the alumina silicate fibre of described mass fraction, antimony oxide, the titanium dioxide of rutile-type, polyvinyl alcohol contracting
Butyraldehyde, nano tin dioxide, boiled wood oil, butyl methacrylate, diisocyanate, diphenyl methane, linoleic acid, attapulgite
Powder, ammonium molybdate, polyvinyl chloride resin, triethyl citrate, nanometer aluminium silicate sodium, dioctyl phthalate, tangerine oil, glass fibre
Powder is mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20~40KHz, rate of dispersion 5000~about 5400r/min, point
The scattered time is 30~60min;
(2) phthalic anhydride of described mass fraction, lead sulfate tribasic, HMPA are added, ultrasonic height
Speed dispersion, ultrasonic frequency is 20~35KHz, rate of dispersion 4800~about 5200r/min, and jitter time is 30~50min;
(3) the poly-4-methyl-1-pentene of described mass fraction, glyceryl monostearate, methyl methacrylate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20~30KHz, rate of dispersion 4600~about 4800r/min, jitter time be 20~
40min;Mixture is prepared after mix homogeneously;Add mixture to again and double screw extruder carries out melting mixing, further
Obtain desired mixt;(4) mixture that step (3) obtains is extruded in an extruder, it is thus achieved that finished product, wherein, extrusion condition
For: barrel temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6~0.9m/
Min, engine speed: 25~30 revs/min.
This beneficial effect of the invention is: the multiple dispensing of the present invention is mutually mixed, and forms novel composite toughening reinforcement
System, toughness, rigidity, elastic modelling quantity performance indications are preferable, are greatly improved ageing resistace and the serviceability of product, have preferably
Anticorrosion effect.The present invention has preferable combination property, and using effect is good.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
PVC communication tubing in the present embodiment, is made up of the component of following mass fraction: alumina silicate fibre 12 parts, three oxygen
Change 14 parts of two antimony, the titanium dioxide 10 parts of rutile-type, polyvinyl butyral resin 8 parts, nano tin dioxide 14 parts, boiled wood oil 10 parts,
Butyl methacrylate 8 parts, diisocyanate 14 parts, diphenyl methane 10 parts, linoleic acid 8 parts, attapulgite powder 14 parts, molybdic acid
Ammonium 10 parts, phthalic anhydride 10 parts, lead sulfate tribasic 8 parts, HMPA 14 parts, polyvinyl chloride resin 10 parts, poly-4-
Methyl-1-pentene 8 parts, glyceryl monostearate 14 parts, methyl methacrylate 10 parts, triethyl citrate 8 parts, nanometer silicic acid
14 parts of aluminum sodium, dioctyl phthalate 10 parts, tangerine oil 8 parts, glass fiber powder 14 parts.
The titanium dioxide of described rutile-type is made up of the powder body of three kinds of particle diameter mesh numbers, and its particle diameter mesh number is respectively 30~50
Mesh, 50~80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 3:4:1.
Described attapulgite powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 30~50 mesh, 50~
80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 3:2:1.
The viscosity of described boiled wood oil is 12000mpa.s at 25 DEG C.
Described glass fiber powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 20~50 mesh, 50~
70 mesh, 70~90 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 2:3:1.
Described Citrus oil viscosity is 8000mpa.s at 25 DEG C.
Above-mentioned PVC communication tubing preparation method step is as follows:
(1) by the alumina silicate fibre of described mass fraction, antimony oxide, the titanium dioxide of rutile-type, polyvinyl alcohol contracting
Butyraldehyde, nano tin dioxide, boiled wood oil, butyl methacrylate, diisocyanate, diphenyl methane, linoleic acid, attapulgite
Powder, ammonium molybdate, polyvinyl chloride resin, triethyl citrate, nanometer aluminium silicate sodium, dioctyl phthalate, tangerine oil, glass fibre
Powder is mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, and jitter time is
60min;
(2) phthalic anhydride of described mass fraction, lead sulfate tribasic, HMPA are added, ultrasonic height
Speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) the poly-4-methyl-1-pentene of described mass fraction, glyceryl monostearate, methyl methacrylate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min;Mix homogeneously
Rear prepared mixture;Add mixture to again and double screw extruder carries out melting mixing, obtain desired mixt further;
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: barrel
Temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6~0.9m/min, main frame turns
Speed: 25~30 revs/min.
Embodiment 2
PVC communication tubing in the present embodiment, is made up of the component of following mass fraction: alumina silicate fibre 14 parts, three oxygen
Change 16 parts of two antimony, the titanium dioxide 12 parts of rutile-type, polyvinyl butyral resin 10 parts, nano tin dioxide 16 parts, boiled wood oil 12 parts,
Butyl methacrylate 10 parts, diisocyanate 16 parts, diphenyl methane 12 parts, linoleic acid 10 parts, attapulgite powder 16 parts, molybdenum
Acid ammonium 12 parts, phthalic anhydride 12 parts, lead sulfate tribasic 10 parts, HMPA 16 parts, polyvinyl chloride resin 12 parts, poly-
4-methyl-1-pentene 10 parts, glyceryl monostearate 16 parts, methyl methacrylate 12 parts, triethyl citrate 10 parts, nanometer
Lagoriolite 16 parts, dioctyl phthalate 12 parts, tangerine oil 10 parts, glass fiber powder 16 parts.
The titanium dioxide of described rutile-type is made up of the powder body of three kinds of particle diameter mesh numbers, and its particle diameter mesh number is respectively 30~50
Mesh, 50~80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 5:6:1.
Described attapulgite powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 30~50 mesh, 50~
80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 5:5:1.
The viscosity of described boiled wood oil is 13000mpa.s at 25 DEG C.
Described glass fiber powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 20~50 mesh, 50~
70 mesh, 70~90 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 3:4:1.
Described Citrus oil viscosity is 9000mpa.s at 25 DEG C.
Above-mentioned PVC communication tubing preparation method step is as follows:
(1) by the alumina silicate fibre of described mass fraction, antimony oxide, the titanium dioxide of rutile-type, polyvinyl alcohol contracting
Butyraldehyde, nano tin dioxide, boiled wood oil, butyl methacrylate, diisocyanate, diphenyl methane, linoleic acid, attapulgite
Powder, ammonium molybdate, polyvinyl chloride resin, triethyl citrate, nanometer aluminium silicate sodium, dioctyl phthalate, tangerine oil, glass fibre
Powder is mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, and jitter time is
45min;
(2) phthalic anhydride of described mass fraction, lead sulfate tribasic, HMPA are added, ultrasonic height
Speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) the poly-4-methyl-1-pentene of described mass fraction, glyceryl monostearate, methyl methacrylate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min;Mix homogeneously
Rear prepared mixture;Add mixture to again and double screw extruder carries out melting mixing, obtain desired mixt further;
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: barrel
Temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6~0.9m/min, main frame turns
Speed: 25~30 revs/min.
Embodiment 3
PVC communication tubing in the present embodiment, is made up of the component of following mass fraction: alumina silicate fibre 16 parts, three oxygen
Change 18 parts of two antimony, the titanium dioxide 14 parts of rutile-type, polyvinyl butyral resin 12 parts, nano tin dioxide 18 parts, boiled wood oil 14 parts,
Butyl methacrylate 12 parts, diisocyanate 18 parts, diphenyl methane 14 parts, linoleic acid 12 parts, attapulgite powder 18 parts, molybdenum
Acid ammonium 14 parts, phthalic anhydride 14 parts, lead sulfate tribasic 12 parts, HMPA 18 parts, polyvinyl chloride resin 14 parts, poly-
4-methyl-1-pentene 12 parts, glyceryl monostearate 18 parts, methyl methacrylate 14 parts, triethyl citrate 12 parts, nanometer
Lagoriolite 18 parts, dioctyl phthalate 14 parts, tangerine oil 12 parts, glass fiber powder 18 parts.
The titanium dioxide of described rutile-type is made up of the powder body of three kinds of particle diameter mesh numbers, and its particle diameter mesh number is respectively 30~50
Mesh, 50~80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 7:8:1.
Described attapulgite powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 30~50 mesh, 50~
80 mesh, 80~100 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 8:8:1.
The viscosity of described boiled wood oil is 14000mpa.s at 25 DEG C.
Described glass fiber powder is made up of the powder body of three kinds of particle diameter mesh numbers, its particle diameter mesh number be respectively 20~50 mesh, 50~
70 mesh, 70~90 mesh, the mixing quality ratio of above-mentioned three kinds of powder body is 4:5:1.
Described Citrus oil viscosity is 10000mpa.s at 25 DEG C.
Above-mentioned PVC communication tubing preparation method step is as follows:
(1) by the alumina silicate fibre of described mass fraction, antimony oxide, the titanium dioxide of rutile-type, polyvinyl alcohol contracting
Butyraldehyde, nano tin dioxide, boiled wood oil, butyl methacrylate, diisocyanate, diphenyl methane, linoleic acid, attapulgite
Powder, ammonium molybdate, polyvinyl chloride resin, triethyl citrate, nanometer aluminium silicate sodium, dioctyl phthalate, tangerine oil, glass fibre
Powder is mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, and jitter time is 30min;
(2) phthalic anhydride of described mass fraction, lead sulfate tribasic, HMPA are added, ultrasonic height
Speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) the poly-4-methyl-1-pentene of described mass fraction, glyceryl monostearate, methyl methacrylate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min;Mix homogeneously
Rear prepared mixture;Add mixture to again and double screw extruder carries out melting mixing, obtain desired mixt further;
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: barrel
Temperature: 184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6~0.9m/min, main frame turns
Speed: 25~30 revs/min.
Above-described embodiment 1, embodiment 2 can be measured with the tubing Progressive symmetric erythrokeratodermia that communicates obtained by embodiment 3, and commercially available with certain
As a control group, measured performance is as shown in table 1 for communication tubing, the performance that the performance of embodiment of the present invention product is more excellent.
The tubing performance parameter that communicates of table 1 embodiment and matched group
Performance measurement | Embodiment 1 | Embodiment 2 | Embodiment 3 | Matched group |
Yield strength (MPa) | 35 | 46 | 39 | 25 |
Tensile modulus of elasticity (MPa) | 2775 | 2948 | 2675 | 1350 |
The modulus of elasticity in static bending (GPa) | 2.6 | 2.8 | 2.5 | 1.5 |
Comprcssive strength (MPa) | 115 | 132 | 128 | 38 |
Longitudinal extension rate (%) | 1.8 | 1.9 | 1.8 | 9.9 |
Tracheid shape properties (μm) | 90 | 85 | 89 | 151 |
Heat conductivity λ (W/m k) | 0.15 | 0.18 | 0.16 | 0.12 |
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (10)
1. a PVC communicates tubing, it is characterised in that: it is made up of the component of following mass fraction: alumina silicate fibre 12~16 parts,
Antimony oxide 14~18 parts, the titanium dioxide 10 of rutile-type~14 parts, polyvinyl butyral resin 8~12 parts, nano tin dioxide
14~18 parts, boiled wood oil 10~14 parts, butyl methacrylate 8~12 parts, diisocyanate 14~18 parts, diphenyl methane 10
~14 parts, linoleic acid 8~12 parts, attapulgite powder 14~18 parts, ammonium molybdate 10~14 parts, phthalic anhydride 10~14 parts,
Lead sulfate tribasic 8~12 parts, HMPA 14~18 parts, polyvinyl chloride resin 10~14 parts, poly-4-methyl-1-pentene 8
~12 parts, glyceryl monostearate 14~18 parts, methyl methacrylate 10~14 parts, triethyl citrate 8~12 parts, nanometer
Lagoriolite 14~18 parts, dioctyl phthalate 10~14 parts, tangerine oil 8~12 parts, glass fiber powder 14~18 parts.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described PVC communication tubing is by following mass fraction
Component composition: alumina silicate fibre 12 parts, antimony oxide 14 parts, the titanium dioxide 10 parts of rutile-type, polyvinyl butyral resin 8
Part, nano tin dioxide 14 parts, boiled wood oil 10 parts, butyl methacrylate 8 parts, diisocyanate 14 parts, diphenyl methane 10 parts,
Linoleic acid 8 parts, attapulgite powder 14 parts, ammonium molybdate 10 parts, phthalic anhydride 10 parts, lead sulfate tribasic 8 parts, hempa
Acyl triamine 14 parts, polyvinyl chloride resin 10 parts, poly-4-methyl-1-pentene 8 parts, glyceryl monostearate 14 parts, methyl methacrylate
10 parts, triethyl citrate 8 parts, 14 parts of nanometer aluminium silicate sodium, dioctyl phthalate 10 parts, tangerine oil 8 parts, glass fibre
14 parts of powder.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described PVC communication tubing is by following mass fraction
Component composition: alumina silicate fibre 14 parts, antimony oxide 16 parts, the titanium dioxide 12 parts of rutile-type, polyvinyl butyral resin
10 parts, nano tin dioxide 16 parts, boiled wood oil 12 parts, butyl methacrylate 10 parts, diisocyanate 16 parts, diphenyl methane 12
Part, linoleic acid 10 parts, attapulgite powder 16 parts, ammonium molybdate 12 parts, phthalic anhydride 12 parts, lead sulfate tribasic 10 parts, six
Methyl phosphoric triamide 16 parts, polyvinyl chloride resin 12 parts, poly-4-methyl-1-pentene 10 parts, glyceryl monostearate 16 parts, metering system
Acid methyl ester 12 parts, triethyl citrate 10 parts, 16 parts of nanometer aluminium silicate sodium, dioctyl phthalate 12 parts, tangerine oil 10 parts,
Glass fiber powder 16 parts.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described PVC communication tubing is by following mass fraction
Component composition: alumina silicate fibre 16 parts, antimony oxide 18 parts, the titanium dioxide 14 parts of rutile-type, polyvinyl butyral resin
12 parts, nano tin dioxide 18 parts, boiled wood oil 14 parts, butyl methacrylate 12 parts, diisocyanate 18 parts, diphenyl methane 14
Part, linoleic acid 12 parts, attapulgite powder 18 parts, ammonium molybdate 14 parts, phthalic anhydride 14 parts, lead sulfate tribasic 12 parts, six
Methyl phosphoric triamide 18 parts, polyvinyl chloride resin 14 parts, poly-4-methyl-1-pentene 12 parts, glyceryl monostearate 18 parts, metering system
Acid methyl ester 14 parts, triethyl citrate 12 parts, 18 parts of nanometer aluminium silicate sodium, dioctyl phthalate 14 parts, tangerine oil 12 parts,
Glass fiber powder 18 parts.
PVC the most according to claim 1 communicates tubing, it is characterised in that: the titanium dioxide of described rutile-type is by three kinds of grains
The powder body composition of footpath mesh number, its particle diameter mesh number is respectively 30~50 mesh, 50~80 mesh, 80~100 mesh, above-mentioned three kinds of powder body mixed
Closing mass ratio is 3~7:4~8:1.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described attapulgite powder is by three kinds of particle diameter mesh numbers
Powder body composition, its particle diameter mesh number is respectively 30~50 mesh, 50~80 mesh, 80~100 mesh, the mixing quality of above-mentioned three kinds of powder body
Ratio is 3~8:2~8:1.
PVC the most according to claim 1 communicates tubing, it is characterised in that: the viscosity of described boiled wood oil is 12000 at 25 DEG C
~14000mpa.s.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described glass fiber powder is by three kinds of particle diameter mesh numbers
Powder body composition, its particle diameter mesh number is respectively 20~50 mesh, 50~70 mesh, 70~90 mesh, the mixing quality of above-mentioned three kinds of powder body
Ratio is 2~4:3~5:1.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described Citrus oil viscosity is 8000 at 25 DEG C
~10000mpa.s.
PVC the most according to claim 1 communicates tubing, it is characterised in that: described PVC communicates tubing preparation method step
As follows:
(1) by the alumina silicate fibre of described mass fraction, antimony oxide, the titanium dioxide of rutile-type, polyvinyl butyral resin,
Nano tin dioxide, boiled wood oil, butyl methacrylate, diisocyanate, diphenyl methane, linoleic acid, attapulgite powder, molybdic acid
Ammonium, polyvinyl chloride resin, triethyl citrate, nanometer aluminium silicate sodium, dioctyl phthalate, tangerine oil, glass fiber powder are mixed
Close, ultrasonic high speed dispersion, ultrasonic frequency is 20~40KHz, rate of dispersion 5000~5400r/min, jitter time be 30~
60min;
(2) adding the phthalic anhydride of described mass fraction, lead sulfate tribasic, HMPA, ultrasonic high speed is divided
Dissipating, ultrasonic frequency is 20~35KHz, rate of dispersion 4800~5200r/min, and jitter time is 30~50min;
(3) the poly-4-methyl-1-pentene of described mass fraction, glyceryl monostearate, methyl methacrylate are added, ultrasonic
High speed dispersion, ultrasonic frequency is 20~30KHz, rate of dispersion 4600~4800r/min, and jitter time is 20~40min;Mixed
Mixture is prepared after closing uniformly;Add mixture to again and double screw extruder carries out melting mixing, obtain required further
Mixture;
(4) being extruded in an extruder by the mixture that step (3) obtains, it is thus achieved that finished product, wherein, extrusion condition is: barrel temperature:
184 ± 2 DEG C, merging core temperature: 176 ± 2 DEG C, head temperature: 190 ± 5 DEG C, traction: 0.6~0.9m/min, engine speed: 25
~30 revs/min.