CN106147524A - A kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating and preparation method thereof - Google Patents
A kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating and preparation method thereof Download PDFInfo
- Publication number
- CN106147524A CN106147524A CN201610532593.5A CN201610532593A CN106147524A CN 106147524 A CN106147524 A CN 106147524A CN 201610532593 A CN201610532593 A CN 201610532593A CN 106147524 A CN106147524 A CN 106147524A
- Authority
- CN
- China
- Prior art keywords
- montmorillonite
- epoxy resin
- modification
- yellowing
- weather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
nullThe invention discloses a kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating,Montmorillonite dilute hydrochloric acid solution acidification is carried out organically-modified again,Weaken the adhesion between cheating engaging layer,Interlayer lattice is made to split,Change the highly polar of surface,Interlayer is made to be changed into lipophile by hydrophilic,Reduce its surface energy,Interlamellar spacing is made to expand,Specific surface area and absorbability dramatically increase,Finally it is added at twice,Make montmorillonite in the epoxy resin modification stage by abundant intercalation and stripping,The lamella peeled off forms chemical bond with epoxy resin and is stably scattered in resin system,Modified epoxy is made to have superior high-temperature stability、Hot storage stability and ageing resistance,Improve water boiling resistance and the antikathode stripping performance of coating,The present invention goes back the composite modified filler of compatibility and other effective auxiliary agents simultaneously,It is good that the powdery paints prepared has pliability、The combination properties such as weather-proof yellowing-resistant,It is up to service life out of doors 15 years.
Description
Technical field
The present invention relates to powder coating technology field, particularly relate to a kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification
Epoxy resin based powder coating and preparation method thereof.
Background technology
Along with the enhancing of mankind's environmental consciousness, solvent based coating is gradually restricted, and development meets the coating of environmental requirement
Being trend of the times, Water-borne modification and solvent free coating are the directions of paint field development from now on.Powdery paints is a kind of novel
Without solvent 100% solid powdery coating, there is the advantages such as high usage, easy application, corrosion-resistant, environmental protection, the modern times spray
It is widely applied with in corrosion-resistant field.
Epoxy powder coating is a kind of important new coating that development in recent years is got up, with the material profit that it is higher
Heavier status is occupied with rate, stronger adhesive force and antiseptic property coating industry the most at home.In recent years, nanometer material
The development of material opens the frontier of material science, and nanometer particle-modified corrosion-resistant epoxy paint also has vast potential for future development.
Montmorillonite belongs to phyllosilicate, has the lattice arrangement of high-sequential.Utilize montmorillonite and the asphalt mixtures modified by epoxy resin with layer structure
Fat intercalation synthesis is prepared the research of a kind of high-performance epoxy resin based powder coatings and is received much concern, and epoxy resin based powder coating passes
System modification is that modifying agent montmorillonite is disposably joined the twin-screw extrusion stage, when hot setting, makes limellar stripping, this side
Method montmorillonite intercalation in the epoxy and peel off insufficient, the antikathode affecting powdery paints is peeled off and water boiling resistance performance.
The research of epoxy resin and performance powder coating thereof " the montmorillonite intercalation polymerization prepare " utilizes low molecular weight epoxy tree
Fat (E-51) inserts stratiform organo montmorillonite (OMMT), by intercalation polymeric and bisphenol-A and the 3rd component 2,6-di-t-butyl
P-methyl phenol (BHT) reacts, and obtains a kind of powder coating epoxy resin.The test of X x ray diffraction shows, stratiform is received
Rice montmorillonite layer is stripped completely, is dispersed in resin matrix.Control montmorillonite and add total amount and twice additional proportion,
The antikathode that can be obviously improved this coating is peeled off and water boiling resistance performance.
But, montmorillonite belongs to inorganic mineral, by adding montmorillonite at twice, makes montmorillonite prepare rank at epoxy resin
Section is by abundant intercalation and stripping, but both poor compatibility, the levelability of film certainly will be affected, meanwhile, in literary composition, method of modifying is single,
The powdery paints prepared only is peeled off at antikathode and makes moderate progress in water boiling resistance performance, and its comprcssive strength, scratch resistance, anti-corrosive properties
Etc. aspect improved, accordingly, it would be desirable to existing technique and formula are improved.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of weather-proof anti-yellowing modification montmorillonite intercalation gathers
Close modified epoxy based powder coatings and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating, by the raw material system of following weight portion
Become: fluorinated epoxy resin 63-65, montmorillonite 2.6-2.9, cetyl trimethylammonium bromide 0.7-0.9, humic acids 1-2, second two
Alcohol monobutyl ether 8-10, flyash 18-20, Herba thymi vulgaris 14-16, ESCALOL 567 1.3-1.7, phenyl three second
TMOS 2.7-3.4, fluorocarbon resin emulsion 14-16, firming agent 2-4, pigment 7-9.
The manufacture method of described a kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating,
Comprise the following steps:
(1) montmorillonite is put in the dilute hydrochloric acid solution that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds humic acids, ESCALOL 567
In 60 DEG C of stirred in water bath 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, it is dried under vacuum to constant weight, grinds, sieve
Obtain modified nano montmorillonite;
(2) dried by Herba thymi vulgaris, attrition grinding crosses 200 mesh sieves, adds fluorocarbon resin emulsion, flyash stirring and evenly mixing standing 12-
14 hours, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl triethoxysilane and grind 20-
Within 30 minutes, obtain composite modified filler;
(3) by fluorinated epoxy resin, ethylene glycol monobutyl ether stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy;
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.
The invention have the advantage that montmorillonite dilute hydrochloric acid solution acidification is carried out organically-modified by the present invention again, weaken
Adhesion between cheating engaging layer, makes interlayer lattice split, changes the highly polar of surface, make interlayer be changed into parent by hydrophilic
Oiliness, reduces its surface energy, makes interlamellar spacing expand, and specific surface area and absorbability dramatically increase, and finally it are added at twice,
Make montmorillonite steady by abundant intercalation and stripping, the lamella of stripping and epoxy resin formation chemical bond in the epoxy resin modification stage
Surely it is scattered in resin system, makes modified epoxy have superior high-temperature stability, hot storage stability and aging resistance
Property, improve water boiling resistance and the antikathode stripping performance of coating, the present invention goes back the composite modified filler of compatibility and other have simultaneously
Effect auxiliary agent, prepared powdery paints proportioning is scientific and reasonable, has the combination properties such as good pliability, weather-proof yellowing-resistant, at family
Outer service life can reach 15 years.
Detailed description of the invention
A kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating, former by following weight portion
Material is made: fluorinated epoxy resin 63, montmorillonite 2.6, cetyl trimethylammonium bromide 0.7, humic acids 1, ethylene glycol monobutyl ether
8, flyash 18, Herba thymi vulgaris 14, ESCALOL 567 1.3, phenyl triethoxysilane 2.7, fluorocarbon resin breast
Liquid 14, firming agent 2, pigment 7.
The manufacture method of described a kind of weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating,
Comprise the following steps:
(1) montmorillonite is put in the dilute hydrochloric acid solution that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds humic acids, ESCALOL 567
In 60 DEG C of stirred in water bath 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, it is dried under vacuum to constant weight, grinds, sieve
Obtain modified nano montmorillonite;
(2) dried by Herba thymi vulgaris, attrition grinding crosses 200 mesh sieves, adds fluorocarbon resin emulsion, flyash stirring and evenly mixing standing 12-
14 hours, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl triethoxysilane and grind 20-
Within 30 minutes, obtain composite modified filler;
(3) by fluorinated epoxy resin, ethylene glycol monobutyl ether stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy;
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.
The decocting in water performance and the antikathode fissility that utilize the powdery paints that the present invention prepares all reach Primary plateaus;Shock resistance
Ability is 39.4kg cm.
Claims (2)
1. a weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating, it is characterised in that by following
The raw material of weight portion is made: fluorinated epoxy resin 63-65, montmorillonite 2.6-2.9, cetyl trimethylammonium bromide 0.7-0.9,
Humic acids 1-2, ethylene glycol monobutyl ether 8-10, flyash 18-20, Herba thymi vulgaris 14-16, ESCALOL 567
1.3-1.7, phenyl triethoxysilane 2.7-3.4, fluorocarbon resin emulsion 14-16, firming agent 2-4, pigment 7-9.
The weather-proof anti-yellowing modification montmorillonite intercalation polymeric modification epoxy resin based powder coating of one the most according to claim 1
Manufacture method, it is characterised in that comprise the following steps:
(1) montmorillonite is put in the dilute hydrochloric acid solution that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds humic acids, ESCALOL 567
In 60 DEG C of stirred in water bath 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, it is dried under vacuum to constant weight, grinds, sieve
Obtain modified nano montmorillonite;
(2) dried by Herba thymi vulgaris, attrition grinding crosses 200 mesh sieves, adds fluorocarbon resin emulsion, flyash stirring and evenly mixing standing 12-
14 hours, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl triethoxysilane and grind 20-
Within 30 minutes, obtain composite modified filler;
(3) by fluorinated epoxy resin, ethylene glycol monobutyl ether stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy;
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.