CN106085141A - Montmorillonite intercalation polymeric modification epoxy resin based powder coating that a kind of spun cast pipe is special and preparation method thereof - Google Patents
Montmorillonite intercalation polymeric modification epoxy resin based powder coating that a kind of spun cast pipe is special and preparation method thereof Download PDFInfo
- Publication number
- CN106085141A CN106085141A CN201610532686.8A CN201610532686A CN106085141A CN 106085141 A CN106085141 A CN 106085141A CN 201610532686 A CN201610532686 A CN 201610532686A CN 106085141 A CN106085141 A CN 106085141A
- Authority
- CN
- China
- Prior art keywords
- montmorillonite
- epoxy resin
- modified
- cast pipe
- special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
nullThe invention discloses the montmorillonite intercalation polymeric modification epoxy resin based powder coating that a kind of spun cast pipe is special，Montmorillonite calcium sulphate soln acidification is carried out organically-modified again，Weaken the adhesion between cheating engaging layer，Interlayer lattice is made to split，Change the highly polar of surface，Interlayer is made to be changed into lipophile by hydrophilic，Reduce its surface energy，Interlamellar spacing is made to expand，Specific surface area and absorbability dramatically increase，Finally it is added at twice，Make montmorillonite in the epoxy resin modification stage by abundant intercalation and stripping，The lamella peeled off forms chemical bond with epoxy resin and is stably scattered in resin system，Modified epoxy is made to have superior high-temperature stability、Hot storage stability and ageing resistance，Improve water boiling resistance and the antikathode stripping performance of coating，The present invention goes back the composite modified filler of compatibility and other effective auxiliary agents simultaneously，The powdery paints prepared film mechanical strength when spun cast pipe application is high、Antiseptic property is good.
Description
Technical field
The present invention relates to powder coating technology field, the montmorillonite intercalation polymerization particularly relating to a kind of spun cast pipe special changes
Property epoxy resin based powder coating and preparation method thereof.
Background technology
Along with the enhancing of mankind's environmental consciousness, solvent based coating is gradually restricted, and development meets the coating of environmental requirement
Being trend of the times, Water-borne modification and solvent free coating are the directions of paint field development from now on.Powdery paints is a kind of novel
Without solvent 100% solid powdery coating, there is the advantages such as high usage, easy application, corrosion-resistant, environmental protection, the modern times spray
It is widely applied with in corrosion-resistant field.
Epoxy powder coating is a kind of important new coating that development in recent years is got up, with the material profit that it is higher
Heavier status is occupied with rate, stronger adhesive force and antiseptic property coating industry the most at home.In recent years, nanometer material
The development of material opens the frontier of material science, and nanometer particle-modified corrosion-resistant epoxy paint also has vast potential for future development.
Montmorillonite belongs to phyllosilicate, has the lattice arrangement of high-sequential.Utilize montmorillonite and the asphalt mixtures modified by epoxy resin with layer structure
Fat intercalation synthesis is prepared the research of a kind of high-performance epoxy resin based powder coatings and is received much concern, and epoxy resin based powder coating passes
System modification is that modifying agent montmorillonite is disposably joined the twin-screw extrusion stage, when hot setting, makes limellar stripping, this side
Method montmorillonite intercalation in the epoxy and peel off insufficient, the antikathode affecting powdery paints is peeled off and water boiling resistance performance.
The research of epoxy resin and performance powder coating thereof " the montmorillonite intercalation polymerization prepare " utilizes low molecular weight epoxy tree
Fat (E-51) inserts stratiform organo montmorillonite (OMMT), by intercalation polymeric and bisphenol-A and the 3rd component 2,6-di-t-butyl
P-methyl phenol (BHT) reacts, and obtains a kind of powder coating epoxy resin.The test of X x ray diffraction shows, stratiform is received
Rice montmorillonite layer is stripped completely, is dispersed in resin matrix.Control montmorillonite and add total amount and twice additional proportion,
The antikathode that can be obviously improved this coating is peeled off and water boiling resistance performance.
But, montmorillonite belongs to inorganic mineral, by adding montmorillonite at twice, makes montmorillonite prepare rank at epoxy resin
Section is by abundant intercalation and stripping, but both poor compatibility, the levelability of film certainly will be affected, meanwhile, in literary composition, method of modifying is single,
The powdery paints prepared only is peeled off at antikathode and makes moderate progress in water boiling resistance performance, and its comprcssive strength, scratch resistance, anti-corrosive properties
Etc. aspect improved, accordingly, it would be desirable to existing technique and formula are improved.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that the montmorillonite intercalation that a kind of spun cast pipe is special
Polymeric modification epoxy resin based powder coating and preparation method thereof.
The present invention is achieved by the following technical solutions:
The montmorillonite intercalation polymeric modification epoxy resin based powder coating that a kind of spun cast pipe is special, by the raw material of following weight portion
Make: novolac epoxy resin 63-65, montmorillonite 2.8-3.4, dodecyl sodium sulfate 1.1-1.4, polycaprolactone 1.3-
1.6, ehtylene acetate 11-12, blanc fixe 18-20, nano aluminum nitride 1.4-1.7, calcium sulfate 0.6-0.8, chlorinated paraffin 4-
6, non-bleached hardwood pulp 17-19, phenyltrimethoxysila,e 2.2-2.5, firming agent 5-7, pigment 6-8.
The making side of the montmorillonite intercalation polymeric modification epoxy resin based powder coating that described a kind of spun cast pipe is special
Method, comprises the following steps:
(1) montmorillonite is put in the calcium sulphate soln that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds dodecyl sodium sulfate, polycaprolactone at 60 DEG C of water
Bath is stirred 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, be dried under vacuum to constant weight, grind, sieve modified to receive
Rice montmorillonite；
(2) dried by non-bleached hardwood pulp, attrition grinding crosses 200 mesh sieves, adds ehtylene acetate, blanc fixe stirring and evenly mixing
Stand 12-14 hour, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl trimethoxy silicon
Alkane, nano aluminum nitride grind 20-30 minute to obtain composite modified filler；
(3) by novolac epoxy resin, chlorinated paraffin stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy；
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.
The invention have the advantage that montmorillonite calcium sulphate soln acidification is carried out organically-modified by the present invention again, weaken
Adhesion between cheating engaging layer, makes interlayer lattice split, changes the highly polar of surface, make interlayer be changed into parent by hydrophilic
Oiliness, reduces its surface energy, makes interlamellar spacing expand, and specific surface area and absorbability dramatically increase, and finally it are added at twice,
Make montmorillonite steady by abundant intercalation and stripping, the lamella of stripping and epoxy resin formation chemical bond in the epoxy resin modification stage
Surely it is scattered in resin system, makes modified epoxy have superior high-temperature stability, hot storage stability and aging resistance
Property, improve water boiling resistance and the antikathode stripping performance of coating, the present invention goes back the composite modified filler of compatibility and other have simultaneously
Effect auxiliary agent, prepared powdery paints has solvent-free, pollution-free, environmental protection, energy-conservation for spun cast pipe application, and film machinery is strong
The features such as degree is high, antiseptic property is good.
Detailed description of the invention
The montmorillonite intercalation polymeric modification epoxy resin based powder coating that a kind of spun cast pipe is special, by following weight portion
Raw material is made: novolac epoxy resin 63, montmorillonite 2.8, dodecyl sodium sulfate 1.1, polycaprolactone 1.3, acetic acid second two
Ester 11, blanc fixe 18, nano aluminum nitride 1.4, calcium sulfate 0.6, chlorinated paraffin 4, non-bleached hardwood pulp 17, phenyl trimethoxy
Base silane 2.2, firming agent 5, pigment 6.
The making side of the montmorillonite intercalation polymeric modification epoxy resin based powder coating that described a kind of spun cast pipe is special
Method, comprises the following steps:
(1) montmorillonite is put in the calcium sulphate soln that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds dodecyl sodium sulfate, polycaprolactone at 60 DEG C of water
Bath is stirred 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, be dried under vacuum to constant weight, grind, sieve modified to receive
Rice montmorillonite；
(2) dried by non-bleached hardwood pulp, attrition grinding crosses 200 mesh sieves, adds ehtylene acetate, blanc fixe stirring and evenly mixing
Stand 12-14 hour, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl trimethoxy silicon
Alkane, nano aluminum nitride grind 20-30 minute to obtain composite modified filler；
(3) by novolac epoxy resin, chlorinated paraffin stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy；
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.
The decocting in water performance and the antikathode fissility that utilize the powdery paints that the present invention prepares all reach Primary plateaus；Shock resistance
Ability is 38.5kg cm.
Claims (2)
1. the montmorillonite intercalation polymeric modification epoxy resin based powder coating that a spun cast pipe is special, it is characterised in that under by
The raw material of row weight portion is made: novolac epoxy resin 63-65, montmorillonite 2.8-3.4, dodecyl sodium sulfate 1.1-1.4,
Polycaprolactone 1.3-1.6, ehtylene acetate 11-12, blanc fixe 18-20, nano aluminum nitride 1.4-1.7, calcium sulfate 0.6-
0.8, chlorinated paraffin 4-6, non-bleached hardwood pulp 17-19, phenyltrimethoxysila,e 2.2-2.5, firming agent 5-7, pigment 6-
8。
The montmorillonite intercalation polymeric modification epoxy resin based powder painting that a kind of spun cast pipe the most according to claim 1 is special
The manufacture method of material, it is characterised in that comprise the following steps:
(1) montmorillonite is put in the calcium sulphate soln that mass fraction is 5-8% and stirs 3-5 hour at 50 DEG C-90 DEG C, filter,
Washing, to neutral, dried, is dispersed in EtOH-DI water solution, adds dodecyl sodium sulfate, polycaprolactone at 60 DEG C of water
Bath is stirred 2-4 hour, ultrasonic disperse 20-30 minute, sucking filtration, washing, be dried under vacuum to constant weight, grind, sieve modified to receive
Rice montmorillonite；
(2) dried by non-bleached hardwood pulp, attrition grinding crosses 200 mesh sieves, adds ehtylene acetate, blanc fixe stirring and evenly mixing
Stand 12-14 hour, pelletize, sinter 20-30 minute in 800-1000 DEG C under nitrogen protection, add phenyl trimethoxy silicon
Alkane, nano aluminum nitride grind 20-30 minute to obtain composite modified filler；
(3) by novolac epoxy resin, chlorinated paraffin stirring and evenly mixing, the modified nano montmorillonite of half quality is added, in
Take out after reacting by heating 2-3 hour at 130-150 DEG C, obtain modified epoxy；
(4) modified epoxy prepared for step (3), step (2) material, the modified Nano of second half quality remaining are covered de-
Soil and other residual componentss put into stirring and evenly mixing in high mixer, melt extrude through double screw extruder, cool down pulverizing, cross 250-
300 mesh sieves, discharging.