CN106187310A - The preparation method of heat preservation environment protection aerated bricks - Google Patents
The preparation method of heat preservation environment protection aerated bricks Download PDFInfo
- Publication number
- CN106187310A CN106187310A CN201610609880.1A CN201610609880A CN106187310A CN 106187310 A CN106187310 A CN 106187310A CN 201610609880 A CN201610609880 A CN 201610609880A CN 106187310 A CN106187310 A CN 106187310A
- Authority
- CN
- China
- Prior art keywords
- weight
- foaming agent
- water reducer
- preparation
- heat preservation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of heat preservation environment protection aerated bricks, raw material includes by weight: dolomite 17 59, powder of lacquer putty for use on 2 10, ammonium pyrophosphate 57, polyacrylamide 0.5 0.7, sodium benzoate 1 1.5, potassium hydroxide 36, Lithium metasilicate 4 12, calcium nitrate 29, water 30 36, water reducer 1.2 1.7, foaming agent 1.5 2.2.The present invention is coordinated with foaming agent can be foamed faster by dolomite, powder of lacquer putty for use on, red mud, and obtained block weight is light.In raw material, the dissolubility of solvent is good, can preferably be polymerized guarantee strength of wall body with water reducer.Na-alginate, dalcium biphosphate coordinate with xanthan gum can play preferable heat-insulating property, and extend body of wall use time, body of wall the most easy to crack.
Description
Technical field
The present invention relates to the preparation method of heat preservation environment protection aerated bricks.
Background technology
Aerated bricks is also referred to as air-entrained concrete building block, it has also become the leading products of building material industry, and application is the widest
General, produce lightweight, thermal and insulating performance good and shock resistance is strong.In order to save material and turn waste into wealth, some aerating
Concrete segment utilizes mine tailing, sea mud, flyash etc. to make as raw material, along with the development of building trade, the property to aerated bricks
Can require to improve the most therewith, but and heat-insulating property one general relative to the aerated bricks comprcssive strength that traditional raw material is made
As.
Summary of the invention
Present invention aim to address the problem that aerated bricks comprcssive strength is general and heat-insulating property is general.
The technical solution used in the present invention is: the preparation method of heat preservation environment protection aerated bricks, and raw material includes by weight: white
Marble 17-59, powder of lacquer putty for use on 2-10, ammonium pyrophosphate 5-7, polyacrylamide 0.5-0.7, sodium benzoate 1-1.5, potassium hydroxide 3-6,
Lithium metasilicate 4-12, calcium nitrate 2-9, water 30-36, water reducer 1.2-1.7, foaming agent 1.5-2.2;
Described foaming agent includes by weight: red mud 2-6, florfenicol sodium succinate 9-18, normal-butyl tri-phenyl-phosphorus bromide
4.2-6.7, monobutyl itaconate 3.1-3.9, xanthan gum 3.9-4.6, cocos nucifera oil acyl diethanolamine 0.5-1.2, N-isopropylhydroxyla
2.5-7.2, resveratrol 5-12;
Described water reducer includes by weight: isobutene. triethoxysilane 2.4-2.8, Na-alginate 2-4, tert-dodecyl mercaptan 3-
7, allyl glycidyl ether 0.7-1.4, N-Methyl pyrrolidone 2.3-2.6, dalcium biphosphate 5.8-8.8, acrylic acid hydroxyl second
Ester 2.3-4.1.
The invention has the beneficial effects as follows: the present invention passes through dolomite, powder of lacquer putty for use on, red mud coordinates with foaming agent can be faster
Foaming, obtained block weight is light.In raw material, the dissolubility of solvent is good, can preferably be polymerized guarantee body of wall with water reducer strong
Degree.Na-alginate, dalcium biphosphate coordinate with xanthan gum can play preferable heat-insulating property, and extend body of wall use time
Between, body of wall the most easy to crack.
Detailed description of the invention
The present invention is described further below.
Embodiment 1: the preparation method of heat preservation environment protection aerated bricks, raw material includes by weight: dolomite 59, powder of lacquer putty for use on 2,
Ammonium pyrophosphate 5, polyacrylamide 0.7, sodium benzoate 1, potassium hydroxide 3, Lithium metasilicate 12, calcium nitrate 2, water 36, water reducer 1.7,
Foaming agent 2.2;
Described foaming agent includes by weight: red mud 6, florfenicol sodium succinate 9, normal-butyl tri-phenyl-phosphorus bromide 6.7, clothing health
Acid mono-n-butylester 3.9, xanthan gum 4.6, cocos nucifera oil acyl diethanolamine 0.5, N-isopropylhydroxyla 2.5, resveratrol 12;
Described water reducer includes by weight: isobutene. triethoxysilane 2.8, Na-alginate 2, tert-dodecyl mercaptan 7, pi-allyl
Glycidyl ether 1.4, N-Methyl pyrrolidone 2.3, dalcium biphosphate 5.8,2-(Acryloyloxy)ethanol 4.1.
Embodiment 2: the preparation method of heat preservation environment protection aerated bricks, raw material includes by weight: dolomite 17, powder of lacquer putty for use on 10,
Ammonium pyrophosphate 7, polyacrylamide 0.5, sodium benzoate 1.5, potassium hydroxide 6, Lithium metasilicate 4, calcium nitrate 9, water 30, water reducer 1.2,
Foaming agent 1.5;
Described foaming agent includes by weight: red mud 2, florfenicol sodium succinate 18, normal-butyl tri-phenyl-phosphorus bromide 4.2, clothing
Health acid mono-n-butylester 3.1, xanthan gum 3.9, cocos nucifera oil acyl diethanolamine 1.2, N-isopropylhydroxyla 7.2, resveratrol 5;
Described water reducer includes by weight: isobutene. triethoxysilane 2.4, Na-alginate 4, tert-dodecyl mercaptan 3, pi-allyl
Glycidyl ether 0.7, N-Methyl pyrrolidone 2.6, dalcium biphosphate 8.8,2-(Acryloyloxy)ethanol 2.3.
Embodiment 3: the preparation method of heat preservation environment protection aerated bricks, raw material includes by weight: dolomite 37, powder of lacquer putty for use on 7,
Ammonium pyrophosphate 6, polyacrylamide 0.7, sodium benzoate 1.3, potassium hydroxide 4, Lithium metasilicate 9, calcium nitrate 5, water 33, water reducer 1.6,
Foaming agent 1.9;
Described foaming agent includes by weight: red mud 4, florfenicol sodium succinate 15, normal-butyl tri-phenyl-phosphorus bromide 5.9, clothing
Health acid mono-n-butylester 3.7, xanthan gum 4.2, cocos nucifera oil acyl diethanolamine 0.7, N-isopropylhydroxyla 4.5, resveratrol 7;
Described water reducer includes by weight: isobutene. triethoxysilane 2.5, Na-alginate 3, tert-dodecyl mercaptan 5, pi-allyl
Glycidyl ether 1.2, N-Methyl pyrrolidone 2.4, dalcium biphosphate 6.4,2-(Acryloyloxy)ethanol 3.1.
Those skilled in the art are it is to be understood that the protection scheme of the present invention is not limited only to the above embodiments, it is also possible to
Various permutation and combination and conversion is carried out, on the premise of spirit of the present invention, to the present invention on the basis of above-described embodiment
The various conversion carried out all fall within protection scope of the present invention.
Claims (1)
1. the preparation method of heat preservation environment protection aerated bricks, it is characterised in that raw material includes by weight: dolomite 17-59, powder of lacquer putty for use on
2-10, ammonium pyrophosphate 5-7, polyacrylamide 0.5-0.7, sodium benzoate 1-1.5, potassium hydroxide 3-6, Lithium metasilicate 4-12, nitric acid
Calcium 2-9, water 30-36, water reducer 1.2-1.7, foaming agent 1.5-2.2;
Described foaming agent includes by weight: red mud 2-6, florfenicol sodium succinate 9-18, normal-butyl tri-phenyl-phosphorus bromide
4.2-6.7, monobutyl itaconate 3.1-3.9, xanthan gum 3.9-4.6, cocos nucifera oil acyl diethanolamine 0.5-1.2, N-isopropylhydroxyla
2.5-7.2, resveratrol 5-12;
Described water reducer includes by weight: isobutene. triethoxysilane 2.4-2.8, Na-alginate 2-4, tert-dodecyl mercaptan 3-
7, allyl glycidyl ether 0.7-1.4, N-Methyl pyrrolidone 2.3-2.6, dalcium biphosphate 5.8-8.8, acrylic acid hydroxyl second
Ester 2.3-4.1.