CN106187076A - Fred salts is utilized to prepare fired brick technology - Google Patents
Fred salts is utilized to prepare fired brick technology Download PDFInfo
- Publication number
- CN106187076A CN106187076A CN201610553048.4A CN201610553048A CN106187076A CN 106187076 A CN106187076 A CN 106187076A CN 201610553048 A CN201610553048 A CN 201610553048A CN 106187076 A CN106187076 A CN 106187076A
- Authority
- CN
- China
- Prior art keywords
- fred salts
- technology
- fred
- fired brick
- salts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses and utilize Fred salts to prepare fired brick technology, specially utilize Fred salts prepare fired brick technology for by Fred salts and folding, hundred clays the most fully mixs after, use traditional clay to bake brick technology production fired brick.The Fred salts that utilizes that the present invention uses prepares fired brick technology, make use of calcination process technology to reclaim Fred salts, makes Fred salts adequately and reasonably resource, turn waste into wealth, decrease clay usage amount, protects land resource；The green compact using the technology of the present invention to generate directly are exposed to the sun under the sun and will not crack, and are unlikely to deform, have saved adjuvant and mat shelter, reduced production cost.
Description
Technical field
The present invention relates to solid waste recovery and reuse technology field, particularly relate to the recovery and utilization technology of Fred salts, belong to
Civil construction Material Field.
Background technology
After Fred salts adsorption treatment waste water, containing a small amount of organic impurities, it is mainly composed of aluminum and calcium, and these are solid
The useless waste water that can not again process, and regenerative process is complicated, long-term for this type of solid waste air storage or the degree of depth can only be filled out by current factory
It is embedded in improvement soil, wastes substantial amounts of resource.Fred salts after processing waste water applies to fired brick technology and has no report.
The green compact produced due to unselected clay fired brick technology are directly exposed to the sun under the sun and can crack, yielding, waste a large amount of
Adjuvant, improve production cost, and the common brick natural drying time that prior art produces be about 25 days, produces effect
Rate is the highest.
Summary of the invention
It is an object of the invention to the defect for solving above-mentioned prior art, it is provided that utilize Fred salts to prepare fired brick skill
Art.
What the present invention used utilizes Fred salts to prepare the technical scheme of fired brick technology for being glued with folding hundred by Fred salts
After soil the most fully mixes, use traditional clay to bake brick technology and produce fired brick.
Described Fred salts is Fred salts with the ratio of folding hundred clays: roll over hundred clay=2～8:1～5.
Described Fred salts is Fred salts with the ratio of folding hundred clays: roll over hundred clays=2:4.
Calcic and aluminum in described Fred salts, the ratio of described calcium and aluminum is Ca:Al=5～8:1.
In described Fred salts, the ratio of calcium and aluminum is Ca:Al=6:1.
Beneficial effect: the Fred salts that utilizes that the present invention uses prepares fired brick technology, make use of calcination process technology to return
Receive Fred salts, make Fred salts adequately and reasonably resource, turn waste into wealth, decrease clay usage amount, protect land resource；
The green compact using the technology of the present invention to generate directly are exposed to the sun under the sun and will not crack, and are unlikely to deform, and have saved adjuvant and cool
Canopy, reduces production cost；Green compact Fred salts fired brick natural drying time under the effect of calcium hydroxide is 7～8 days, and
The common brick natural drying time is about 25 days, hence it is evident that shortens the natural drying cycle of green compact than common brick, has
Effect improves productivity ratio.
Detailed description of the invention
Following enforcement row can make those skilled in the art be more completely understood by the present invention, but the most therefore by the present invention
It is limited among described scope of embodiments.
Embodiment 1
By Fred salts and clay (folding hundred) in Fred salts: the ratio of clay (folding hundred)=2:4 is sufficiently stirred for mixing, biography
System method makes adobe, natural drying 17 days, and neat pile is inserted in porous brick calcining kiln, and control sintering temperature is at 900 DEG C, even
Continuous roasting two days, kiln discharge of lowering the temperature.After kiln discharge detecting Fred block salt, smooth in appearance is smooth, and color is dark red, and radioactivity reaches
To A level, meet GB/T5101-98 requirement.
Claims (5)
1. utilize Fred salts to prepare fired brick technology, it is characterised in that: described fired brick technology of preparing is for by Fred salts
With roll over after hundred clays the most fully mix, use traditional clay to bake brick technology and produce fired brick.
The most according to claim 1 Fred salts is utilized to prepare fired brick technology, it is characterised in that: described Fred salts
It is Fred salts with rolling over the ratio of hundred clays: roll over hundred clay=2～8:1～5.
The most according to claim 1 Fred salts is utilized to prepare fired brick technology, it is characterised in that: described Fred salts
It is Fred salts with rolling over the ratio of hundred clays: roll over hundred clays=2:4.
The most according to claim 1 Fred salts is utilized to prepare fired brick technology, it is characterised in that: described Fred salts
Middle calcic and aluminum, the ratio of described calcium and aluminum is Ca:Al=5～8:1.
The most according to claim 4 utilizing Fred salts to prepare fired brick technology, its spy detects and is: described Fred salts
The ratio of middle calcium and aluminum is Ca:Al=6:1.