CN106186915A - Thin layer motar and construction method are directly scraped in modification - Google Patents
Thin layer motar and construction method are directly scraped in modification Download PDFInfo
- Publication number
- CN106186915A CN106186915A CN201610514568.4A CN201610514568A CN106186915A CN 106186915 A CN106186915 A CN 106186915A CN 201610514568 A CN201610514568 A CN 201610514568A CN 106186915 A CN106186915 A CN 106186915A
- Authority
- CN
- China
- Prior art keywords
- powder
- thin layer
- modification
- directly
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of modification and directly scrape thin layer motar and construction method, including following component: cement is 150 200 parts；Sand is 700 820 parts；Mineral micro powder is 60 90 parts；Polymer dispersion powder is 0.5 1.2 parts；Thickening agent is 0.5 1 parts；Alkali proof fiber is 0.2 0.6 parts；Thixotroping lubrication powder is 0.1 0.5 parts；Multi-functional powder is 0.5 2 parts；150 170 parts of water；Described part is in parts by weight.Mortar material of the present invention construction consumption is few, and technique is simple, and cohesive force and cracking resistance are excellent, are difficult to hollowing and cracking, and efficiency is substantially improved, cost-effective.
Description
Technical field
The present invention relates to a kind of structure material, directly scrape thin layer motar and construction method particularly to a kind of modification.
Background technology
Motar be spread upon the wall of building, top, on the surface such as post, directly make the decorative engineering of finish coat,
It both can protect basic unit, increase attractive in appearance, can be again that building provides special function.Common premixing motar construction technology
Flow process be base treatment, linked network, levelling, plaster and maintenance etc..Owing to tradition mortar bonding power is the highest, interface is the most treated directly
Hanging, screed is thin, and mortar easily comes off and ftractures, therefore to screed has more preferable adhesive property, base treatment mistake
Journey needs surface of wall is carried out moistening and in basic unit brushing polymer cement mortar or other interfacial agents make hair
Face.For ensure the mortar later stage do not fall off, hollowing and generation crack, link of plastering be divided into the end, in, table tri-level construction require respectively to smear
Must cohere between Ceng and between coat of plaster and basic unit firmly.Therefore, this working procedure is complicated, and the engineering time is longer, screed
Integral thickness is relatively big, and engineering cost is of a relatively high.
Summary of the invention
An object of the present invention is that directly scrapes thin layer by interpolation water conservation, enhancing, a kind of modification of adhesion-promoting material preparation
Motar, it can promote the adhesive property of mortar and matrix so that mortar and matrix are without carrying out conventional process basic unit, smearing
Bottom is grey, smear the interface processing such as middle level ash, finishing mortar, it is achieved disposable hanging.This not only reduces the thickness of screed, also reduces
Mortar hollowing and cracking situation produce.
Technical scheme is: a kind of modification directly scrapes thin layer motar, including following component:
Cement is 150-200 part；
Sand is 700-820 part；
Mineral micro powder is 60-90 part；
Polymer dispersion powder is 0.5-1.2 part；
Thickening agent is 0.5-1 part；
Alkali proof fiber is 0.2-0.6 part；
Thixotroping lubrication powder is 0.1-0.5 part；
Multi-functional powder is 0.5-2 part；With
Water 150-170 part；
Described part is in parts by weight.
As preferably, described multi-functional powder be the one in water-proofing powder, extender, retarder, early strength agent etc. or its
Mixture.
As preferably, described mineral micro powder be the one in flyash, slag powders, metakaolin, dicalcium powder, wollastonite powder or
Its mixture.
As preferably, described polymer dispersion powder is vinylacetate and ethylene copolymer rubber powder, acrylate and styrene
Copolymerization rubber powder, vinylacetate homopolymerization rubber powder, maleic acid and styrene copolymerized rubber powder, polyoxyethylene ether and acrylate copolymer glue
Powder；The molecular weight of described maleic acid-styrol copolymer or polyoxyethylene ether-acrylic copolymer preferably 80,000-12 ten thousand.
As preferably, described thickening agent is hydroxypropyl first class cellulose, sodium carboxymethyl cellulose, starch ether, guar gum, hat
One in wheel glue or its mixture.
As preferably, described alkali proof fiber is in polypropylene fibre, alkali-resistant glass fibre, mineral wool fiber, rock wool fibers
One or its mixture；Described alkali proof fiber preferred length is the long and short fiber mixture of 2-4mm and 10-14mm.
As preferably, described thixotroping lubrication powder is vermiculite power, bentonite, sepiolite powder, attapulgite, Kaolin, cunning
One in stone powder or its mixture.
As preferably, described cement is portland cement, Portland cement, white portland cement, calcium aluminate water
Mud or composite Portland cement.
The two of the purpose of the present invention are the construction method providing a kind of modification directly to scrape thin layer motar.
Technical scheme is: the construction method of thin layer motar is directly scraped in a kind of modification, comprises the following steps:
1. directly scrape thin layer motar formula feeding by above-mentioned modification, composition in addition to water is mixed, stirring
Uniformly become powder stand-by；
The most at the construction field (site), add water to powder, be stirred for mortar；
3. need the wall of building of construction, top, the linked network directly on a surface such as post；
4. the mortar 2. prepared disposably is spread upon the wall of building, top, on the surface such as post；
5. maintenance.
As preferably, described step 4. in smear after smear layer thickness be 0.3-1.0cm.
Beneficial effect:
The present invention, by improving the water-retaining property of mortar, rheological characteristic, compensation Mortar shrinkage, suppression mortar cracking, improves mortar
With the cohesive force of matrix, thus interface processing operation can be saved, directly mortar is hung on matrix, and once smears.Meanwhile,
Mortar is without hollowing, cracking, it is not necessary to does over again, reprocess.And smearing thickness is little, it is effectively increased the standard width of a room in an old-style house distance of building structure, improves
Space utilization rate.
Mortar material of the present invention construction consumption is few, and technique is simple, and cohesive force and cracking resistance are excellent, is difficult to hollowing and opens
Split, efficiency is substantially improved, cost-effective.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment 1
1) a kind of interior wall strength grade is that thin layer motar is directly scraped in the modification of M5.0, and its component and weight portion be:
By P.O42.5R cement 160 parts, 760 parts of sand, slag powders 80 parts, 160 parts of water, vinylacetate and ethylene copolymer rubber powder 0.8 part,
Sodium carboxymethyl cellulose 0.6 part, alkali-resistant glass fibre 0.4 part, vermiculite power 0.2 part, 0.7 part of multi-functional powder includes: stearic acid
Calcium waterproofing agent 0.2 part, sodium citrate 0.3 part, aluminium sulfate expanding agent 0.2 part.2) thin layer motar is directly scraped in a kind of modification
Preparation and construction:
1. press formula feeding in 1, composition in addition to water is mixed, is stirred into powder A stand-by.
The most at the construction field (site), adding water to powder A, be stirred for mortar A1, water addition is the water yield in 1.
3. need the wall of building of construction, top, linked network (not the carrying out base treatment) directly on a surface such as post.
4. mortar A1 is disposably spread upon the wall of building, top, on the surface such as post, smearing thickness be 0.8cm (no
Carry out secondary to smear).
5. maintenance.
With reference to the test method of " building mortar basic performance tests method " JGJT 70-2009, its main performance test knot
Fruit is as shown in table 1:
Thin layer motar main performance is directly scraped in table 1M5.0 interior wall modification
Institute's test index is satisfied by the technology requirement of thin layer motar in " premixing mortar " GB/T25181-2010.
Case study on implementation 2
1) a kind of exterior wall strength grade is that thin layer motar is directly scraped in the modification of M10, and its component and weight portion be:
P.C52.5R cement 170 parts, 760 parts of sand, dicalcium powder 70 parts, 165 parts of water, vinylacetate homopolymerization rubber powder 0.9 part, hydroxypropyl first
Level cellulose 0.5 part, starch ether 0.2 part, polypropylene fibre 0.3 part, bentonite 0.2 part, 1 part of multi-functional powder includes: organic
Silicon water-proofing powder 0.2 part, citric acid 0.2 part, extender 0.3 part, early strength agent 0.3 part.2) thin layer plastering sand is directly scraped in a kind of modification
The preparation of slurry and construction:
1. press formula feeding in 1, composition in addition to water is mixed, is stirred into powder A stand-by.
The most at the construction field (site), adding water to powder A, be stirred for mortar A1, water addition is the water yield in 1.
3. need the wall of building of construction, top, linked network (not the carrying out base treatment) directly on a surface such as post.
4. mortar A1 is disposably spread upon the wall of building, top, on the surface such as post, smearing thickness is 1.0cm.(no
Carry out secondary to smear)
5. maintenance.
With reference to the test method of " building mortar basic performance tests method " JGJT 70-2009, its main performance test knot
Fruit is as shown in table 2
Thin layer motar main performance is directly scraped in table 2M10 exterior wall modification
| Project | Test result |
| Setting time (h) | 9.5 |
| Water retention (%) | 99.4 |
| 14d tensile bond strength (MPa) | 0.38 |
| 28d comprcssive strength (MPa) | 12.7 |
| 28d shrinkage factor (%) | 0.09 |
Institute's test index is satisfied by the technology requirement of thin layer motar in " premixing mortar " GB/T25181-2010.
Embodiment 3
1) a kind of roof strength grade is that thin layer motar is directly scraped in the modification of M10, and its component and weight portion be:
P.O42.5 cement 180 parts, 750 parts of sand, wollastonite powder 60 parts, 170 parts of water, maleic acid and styrene copolymerized rubber powder 1 part, crown gear glue
0.7 part, starch ether 0.2 part, mineral wool fiber 0.5 part, attapulgite 0.5 part, 1.3 parts of multi-functional powder includes: organic silicon water-proofing
0.3 part of powder, sodium gluconate 0.3 part, MgO expansion agent 0.3 part, early strength agent 0.4 part.2) a kind of modification is directly scraped thin layer and is smeared
The preparation of lime and brick and construction:
1. press formula feeding in 1, composition in addition to water is mixed, is stirred into powder A stand-by.
The most at the construction field (site), adding water to powder A, be stirred for mortar A1, water addition is the water yield in 1.
3. need the wall of building of construction, top, linked network (not the carrying out base treatment) directly on a surface such as post.
4. mortar A1 is disposably spread upon the wall of building, top, on the surface such as post, smearing thickness is 1.5cm.(no
Carry out secondary to smear)
5. maintenance.
With reference to the test method of " building mortar basic performance tests method " JGJT 70-2009, its main performance, test
Result is as shown in table 3
Thin layer motar main performance is directly scraped in table 3M10 roof modification
| Project | Test result |
| Setting time (h) | 8 |
| Water retention (%) | 99.4 |
| 14d tensile bond strength (MPa) | 0.40 |
| 28d comprcssive strength | 12.9 |
| 28d shrinkage factor | 0.10 |
Institute's test index is satisfied by the technology requirement of thin layer motar in " premixing mortar " GB/T25181-2010.
Claims (10)
1. modification directly scrapes a thin layer motar, including following component:
Cement is 150-200 part；
Sand is 700-820 part；
Mineral micro powder is 60-90 part；
Polymer dispersion powder is 0.5-1.2 part；
Thickening agent is 0.5-1 part；
Alkali proof fiber is 0.2-0.6 part；
Thixotroping lubrication powder is 0.1-0.5 part；
Multi-functional powder is 0.5-2 part；With
Water 150-170 part；
Described part is in parts by weight.
Thin layer motar is directly scraped in modification the most according to claim 1, it is characterised in that: described multi-functional powder is waterproof
One in powder, extender, retarder, early strength agent etc. or its mixture.
3. directly scrape thin layer motar according to the modification described in claim 1-2 any claim, it is characterised in that: described ore deposit
Thing micropowder is the one in flyash, slag powders, metakaolin, dicalcium powder, wollastonite powder or its mixture.
4. directly scrape thin layer motar according to the modification described in claim 1-3 any claim, it is characterised in that: described can
Dispersed latex powder is vinylacetate and ethylene copolymer rubber powder, acrylate and styrene copolymerized rubber powder, vinylacetate homopolymerization
Rubber powder, maleic acid and styrene copolymerized rubber powder, polyoxyethylene ether and acrylate copolymer rubber powder；Described maleic acid-styrene is common
The molecular weight of polymers or polyoxyethylene ether-acrylic copolymer preferably 80,000-12 ten thousand.
Thin layer motar is directly scraped in modification the most according to claim 4, it is characterised in that: described thickening agent is hydroxypropyl first
One in level cellulose, sodium carboxymethyl cellulose, starch ether, guar gum, crown gear glue or its mixture.
6. directly scrape thin layer motar according to the modification described in claim 1-5 any claim, it is characterised in that: described resistance to
Alkali fiber is the one in polypropylene fibre, alkali-resistant glass fibre, mineral wool fiber, rock wool fibers or its mixture；Described alkaline-resisting
Fiber preferred length is the long and short fiber mixture of 2-4mm and 10-14mm.
7. directly scrape thin layer motar according to the modification described in claim 1-6 any claim, it is characterised in that: described tactile
Become lubrication powder be vermiculite power, one in bentonite, sepiolite powder, attapulgite, Kaolin, Pulvis Talci or its mixture.
8. directly scrape thin layer motar according to the modification described in claim 1-7 any claim, it is characterised in that: described water
Mud is portland cement, Portland cement, white portland cement, aluminous cement or composite Portland cement.
9. a construction method for thin layer motar is directly scraped in modification, comprises the following steps:
1. directly scrape thin layer motar formula feeding by the modification in claim 1-7, composition in addition to water mixed,
It is stirred into powder stand-by；
The most at the construction field (site), add water to powder, be stirred for mortar；
3. need the wall of building of construction, top, the linked network directly on a surface such as post；
4. the mortar 2. prepared disposably is spread upon the wall of building, top, on the surface such as post；
5. maintenance.
The construction method of thin layer motar is directly scraped in modification the most according to claim 11, it is characterised in that: described step
4. the smear layer thickness after smearing in is 0.3-1.0cm.