CN106167392A - A kind of antidetonation domestic ceramics - Google Patents
A kind of antidetonation domestic ceramics Download PDFInfo
- Publication number
- CN106167392A CN106167392A CN201610499463.6A CN201610499463A CN106167392A CN 106167392 A CN106167392 A CN 106167392A CN 201610499463 A CN201610499463 A CN 201610499463A CN 106167392 A CN106167392 A CN 106167392A
- Authority
- CN
- China
- Prior art keywords
- parts
- antidetonation
- domestic ceramics
- spodumene
- wollastonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antidetonation domestic ceramics, by forming according to the raw material of weight portion as follows: Kaolin 55 ~ 80 parts, potassium feldspar 15 ~ 30 parts, 15 ~ 30 parts of this base mud, wollastonite in powder 15 ~ 25 parts, spodumene 5 ~ 15 parts, Red Stone Ware 5 ~ 10 parts, bentonite 2 ~ 12 parts, silane coupler 6 ~ 12 parts, zinc oxide 1 ~ 3 part, titanium dioxide 0.4 ~ 2.8 part, hydroxypropyl methyl cellulose 3 ~ 10 parts, polyvinyl alcohol 10 ~ 15 parts, anti-wear agent 2 ~ 8 parts and active catalyst 3 ~ 9 parts.This kind of antidetonation domestic ceramics has good anti-seismic performance and impact resistance, intensity height, good toughness, resistance to greasy dirt, and production cost is relatively low, and between its granule, caking property is preferable, effectively reduces pottery breakage in transportation.
Description
Technical field
The present invention relates to ceramic ware for daily use, be specifically related to a kind of antidetonation domestic ceramics.
Background technology
Ceramic has a wide range of applications in worldwide, and domestic ceramics has become as in people's daily life not
The part that can or lack, crockery has greasy dirt elegant in appearance, resistance to, is prone to washing, durable in use, better heat stability, biography
The advantages such as heat is slow, but, existing crockery is easily chapped in transportation, and intensity is poor, accordingly, it would be desirable to it
Performance improves.
Summary of the invention
Present invention aim at solving the problems referred to above, it is provided that a kind of antidetonation domestic ceramics.
For achieving the above object, the invention provides a kind of antidetonation domestic ceramics, by as follows according to the raw material group of weight portion
Become: Kaolin 55 ~ 80 parts, potassium feldspar 15 ~ 30 parts, 15 ~ 30 parts of this base mud, wollastonite in powder 15 ~ 25 parts, spodumene 5 ~ 15 parts, purple
Sand 5 ~ 10 parts, bentonite 2 ~ 12 parts, silane coupler 6 ~ 12 parts, zinc oxide 1 ~ 3 part, titanium dioxide 0.4 ~ 2.8 part, hydroxypropyl
Methylcellulose 3 ~ 10 parts, polyvinyl alcohol 10 ~ 15 parts, anti-wear agent 2 ~ 8 parts and active catalyst 3 ~ 9 parts.
Described antidetonation domestic ceramics, by forming according to the raw material of weight portion as follows: Kaolin 60 ~ 75 parts, potassium feldspar 18 ~ 26
Part, 19 ~ 24 parts of this base mud, wollastonite in powder 18 ~ 22 parts, spodumene 6 ~ 13 parts, Red Stone Ware 6 ~ 8 parts, bentonite 4 ~ 11 parts, silane are occasionally
Connection agent 8 ~ 10 parts, zinc oxide 1 ~ 2 part, titanium dioxide 0.8 ~ 1.6 part, hydroxypropyl methyl cellulose 5 ~ 9 parts, polyvinyl alcohol 12 ~ 14
Part, anti-wear agent 3 ~ 6 parts and active catalyst 4 ~ 7 parts.
Described antidetonation domestic ceramics, by forming according to the raw material of weight portion as follows: Kaolin 65 parts, potassium feldspar 24 part,
22 parts of base mud, wollastonite in powder 20 parts, spodumene 8 parts, Red Stone Ware 7 parts, bentonite 10 parts, silane coupler 8.8 parts, zinc oxide
1.4 parts, titanium dioxide 1.2 parts, hydroxypropyl methyl cellulose 7 parts, polyvinyl alcohol 12.5 parts, anti-wear agent 5 parts and active catalyst 5
Part.
Beneficial effects of the present invention: this kind of antidetonation domestic ceramics has good anti-seismic performance and impact resistance, intensity
Height, good toughness, resistance to greasy dirt, production cost is relatively low, and between its granule, caking property is preferable, effectively reduces pottery in transportation
Damaged.
Detailed description of the invention
The present invention takes techniques below scheme to realize: this kind of antidetonation domestic ceramics, by as follows according to the raw material of weight portion
Composition: Kaolin 55 ~ 80 parts, potassium feldspar 15 ~ 30 parts, 15 ~ 30 parts of this base mud, wollastonite in powder 15 ~ 25 parts, spodumene 5 ~ 15 parts,
Red Stone Ware 5 ~ 10 parts, bentonite 2 ~ 12 parts, silane coupler 6 ~ 12 parts, zinc oxide 1 ~ 3 part, titanium dioxide 0.4 ~ 2.8 part, hydroxypropyl
Ylmethyl cellulose 3 ~ 10 parts, polyvinyl alcohol 10 ~ 15 parts, anti-wear agent 2 ~ 8 parts and active catalyst 3 ~ 9 parts.
As the preferred version of the present invention, antidetonation domestic ceramics is by forming according to the raw material of weight portion as follows: Kaolin 60 ~
75 parts, potassium feldspar 18 ~ 26 parts, 19 ~ 24 parts of this base mud, wollastonite in powder 18 ~ 22 parts, spodumene 6 ~ 13 parts, Red Stone Ware 6 ~ 8 parts, swollen
4 ~ 11 parts of profit soil, silane coupler 8 ~ 10 parts, zinc oxide 1 ~ 2 part, titanium dioxide 0.8 ~ 1.6 part, hydroxypropyl methyl cellulose 5 ~ 9
Part, polyvinyl alcohol 12 ~ 14 parts, anti-wear agent 3 ~ 6 parts and active catalyst 4 ~ 7 parts.
As the preferred version of the present invention, antidetonation domestic ceramics is by forming according to the raw material of weight portion as follows: Kaolin 65
Part, potassium feldspar 24 parts, 22 parts of this base mud, wollastonite in powder 20 parts, spodumene 8 parts, Red Stone Ware 7 parts, bentonite 10 parts, silane coupled
Agent 8.8 parts, zinc oxide 1.4 parts, titanium dioxide 1.2 parts, hydroxypropyl methyl cellulose 7 parts, polyvinyl alcohol 12.5 parts, anti-wear agent 5
Part and active catalyst 5 parts.
This kind of antidetonation domestic ceramics has good anti-seismic performance and an impact resistance, intensity height, good toughness, resistance to greasy dirt,
Production cost is relatively low, and between its granule, caking property is preferable, effectively reduces pottery breakage in transportation.
The preferred embodiment of the present invention described in detail above.Should be appreciated that those of ordinary skill in the art without
Need creative work just can make many modifications and variations according to the design of the present invention.Therefore, all technology in the art
Personnel are available by logical analysis, reasoning, or a limited experiment the most on the basis of existing technology
Technical scheme, all should be in the protection domain being defined in the patent claims.
Claims (3)
1. an antidetonation domestic ceramics, it is characterised in that by forming according to the raw material of weight portion as follows: Kaolin 55 ~ 80 parts, potassium
Anhydrite 15 ~ 30 parts, 15 ~ 30 parts of this base mud, wollastonite in powder 15 ~ 25 parts, spodumene 5 ~ 15 parts, Red Stone Ware 5 ~ 10 parts, bentonite 2 ~
12 parts, silane coupler 6 ~ 12 parts, zinc oxide 1 ~ 3 part, titanium dioxide 0.4 ~ 2.8 part, hydroxypropyl methyl cellulose 3 ~ 10 parts, poly-
Vinyl alcohol 10 ~ 15 parts, anti-wear agent 2 ~ 8 parts and active catalyst 3 ~ 9 parts.
Antidetonation domestic ceramics the most according to claim 1, it is characterised in that by forming according to the raw material of weight portion as follows:
Kaolin 60 ~ 75 parts, potassium feldspar 18 ~ 26 parts, 19 ~ 24 parts of this base mud, wollastonite in powder 18 ~ 22 parts, spodumene 6 ~ 13 parts, Red Stone Ware
6 ~ 8 parts, bentonite 4 ~ 11 parts, silane coupler 8 ~ 10 parts, zinc oxide 1 ~ 2 part, titanium dioxide 0.8 ~ 1.6 part, hydroxypropyl methyl
Cellulose 5 ~ 9 parts, polyvinyl alcohol 12 ~ 14 parts, anti-wear agent 3 ~ 6 parts and active catalyst 4 ~ 7 parts.
Antidetonation domestic ceramics the most according to claim 1, it is characterised in that by forming according to the raw material of weight portion as follows:
Kaolin 65 parts, potassium feldspar 24 parts, 22 parts of this base mud, wollastonite in powder 20 parts, spodumene 8 parts, Red Stone Ware 7 parts, bentonite 10 parts,
Silane coupler 8.8 parts, zinc oxide 1.4 parts, titanium dioxide 1.2 parts, hydroxypropyl methyl cellulose 7 parts, polyvinyl alcohol 12.5 parts,
Anti-wear agent 5 parts and active catalyst 5 parts.