CN106147539A - A kind of nanometer priming paint of resistance to marine anticorrosion - Google Patents
A kind of nanometer priming paint of resistance to marine anticorrosion Download PDFInfo
- Publication number
- CN106147539A CN106147539A CN201510186603.XA CN201510186603A CN106147539A CN 106147539 A CN106147539 A CN 106147539A CN 201510186603 A CN201510186603 A CN 201510186603A CN 106147539 A CN106147539 A CN 106147539A
- Authority
- CN
- China
- Prior art keywords
- nanometer
- marine
- resistance
- priming paint
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of nanometer priming paint of resistance to marine anticorrosion, it is characterized in that, be made up of the raw material of following parts by weight: linear phenolic epoxy resin 20-30 part, glyceryl tristearate 2-4 part, pnenolic aldehyde amine hardener 5-7 part, polyamide curing agent 4-6 part, titanium dioxide 2-4 part, nickel alloy powder 8-12 part, nano biological anti-fouling agent 3-5 part, zinc oxide 1-3 part, acetone 15-18 part, filler 12-14 part, acetic acid 2-5 part.The present invention has can application property and storage stability, solidification is rapid, even film layer, the addition of nickel alloy powder solves engineering component marine corrosion problem, there is good anticorrosion, wear-resisting, water-fast and chemical resistance, nanometer capsicim in nano biological anti-fouling agent, P-cinnamic acid sulfuric ester have very strong suppression adhewsive action to marine bacteria and barnacle, nanometer homarine is possible to prevent the attachment of marine benthic diatom and barnacle, avoidance effect is had to marine organisms, destroying halobiontic adhesive ability thus reaching the purpose prevented and remedied pollution, the feature of environmental protection is good.
Description
Technical field
The invention belongs to marine anticorrosion paint vehicle technical field, be specifically related to a kind of nanometer priming paint of resistance to marine anticorrosion.
Background technology
Sea marine corrosion is mainly chloride ion corrosion, and ocean chlorion can destroy metal oxide film protective layer, forms spot corrosion or pitting corrosion, there will be intercrystalline corrosion to metal.Engineer equipment local environment air in coastal waters and ocean is rainy, high temperature, many salt fogs and high wind stream, and its service condition is pressed ISO9225 environmental evaluation Standard General > C5 level, belonged to extreme environment.The comprehensive function that exposed part will be corroded by strong atmospheric corrosion, electrochemical corrosion and airflow scouring, is far below general inland outdoor environment the service life of various steel constructions.Metal is under the effect of tensile stress, and the destroyed region of passivating film will crack, and becomes the anode region of corrosion cell, and continuously electrochemical corrosion may finally cause the fracture of metal.Owing to ocean platform different parts (such as spud leg, exposing deck, ballast tank, upper chunk etc.) has different performance requirements to coating, during current Offshore Platform Construction, applying assembling platform and typically using more than 5 kinds different priming paint, supporting complexity, construction is also inconvenient.At present priming paint exist bad with the overcoatability of other producers, ask the bonding interface such as zinc coat and aluminium is good etc., erosion resistance not by force, application yet suffers from limit greatly.
Content of the invention
For problems of the prior art, it is an object of the invention to provide a kind of nanometer priming paint of resistance to marine anticorrosion.
The technical scheme that the present invention takes is:
A kind of nanometer priming paint of resistance to marine anticorrosion, it is characterised in that be made up of the raw material of following parts by weight:
Linear phenolic epoxy resin 20-30 part, glyceryl tristearate 2-4 part, pnenolic aldehyde amine hardener 5-7 part, polyamide curing agent 4-6 part, titanium dioxide 2-4 part, nickel alloy powder 8-12 part, nano biological anti-fouling agent 3-5 part, zinc oxide 1-3 part, acetone 15-18 part, filler 12-14 part, acetic acid 2-5 part.
Further, described nickel alloy powder is added with the iron oxide red of 0.5-0.7% and the trbasic zinc phosphate of 0.4-0.6%.
Further, described filler is the mixture that kaolin, wollastonite in powder, SiO 2 powder form than 3:2:2 according to weight.
Further, described nano biological anti-fouling agent is the mixture that nanometer capsicim, P-cinnamic acid sulfuric ester and nanometer homarine form than 1:2:5 according to weight.
The invention have the benefit that
It is primary raw material that the marine anticorrosion priming paint of the present invention uses linear phenolic epoxy resin and glyceryl tristearate, having can application property and storage stability, solidification is rapidly, even film layer, the addition of nickel alloy powder solves engineering component marine corrosion problem, there is good anticorrosion, wear-resisting, water-fast and chemical resistance, nanometer capsicim in nano biological anti-fouling agent, P-cinnamic acid sulfuric ester has very strong suppression adhewsive action to marine bacteria and barnacle, nanometer homarine is possible to prevent the attachment of marine benthic diatom and barnacle, avoidance effect is had to marine organisms, destroy halobiontic adhesive ability thus reach the purpose prevented and remedied pollution, the feature of environmental protection is good.
Detailed description of the invention
Embodiment 1
A kind of nanometer priming paint of resistance to marine anticorrosion, it is characterised in that be made up of the raw material of following parts by weight:
Linear phenolic epoxy resin 20 parts, glyceryl tristearate 2 parts, pnenolic aldehyde amine hardener 5 parts, polyamide curing agent 4 parts, titanium dioxide 2 parts, nickel alloy powder 8 parts, nano biological anti-fouling agent 3 parts, 1 part of zinc oxide, 15 parts of acetone, filler 12 parts, acetic acid 2 parts.
Further, described nickel alloy powder is added with the iron oxide red of 0.5% and the trbasic zinc phosphate of 0.4%.
Further, described filler is the mixture that kaolin, wollastonite in powder, SiO 2 powder form than 3:2:2 according to weight.
Further, described nano biological anti-fouling agent is the mixture that nanometer capsicim, P-cinnamic acid sulfuric ester and nanometer homarine form than 1:2:5 according to weight.
Embodiment 2
A kind of nanometer priming paint of resistance to marine anticorrosion, it is characterised in that be made up of the raw material of following parts by weight:
Linear phenolic epoxy resin 25 parts, glyceryl tristearate 3 parts, pnenolic aldehyde amine hardener 6 parts, polyamide curing agent 5 parts, titanium dioxide 3 parts, nickel alloy powder 10 parts, nano biological anti-fouling agent 4 parts, 2 parts of zinc oxide, 16 parts of acetone, filler 13 parts, acetic acid 3 parts.
Further, described nickel alloy powder is added with the iron oxide red of 0.6% and the trbasic zinc phosphate of 0.5%.
Further, described filler is the mixture that kaolin, wollastonite in powder, SiO 2 powder form than 3:2:2 according to weight.
Further, described nano biological anti-fouling agent is the mixture that nanometer capsicim, P-cinnamic acid sulfuric ester and nanometer homarine form than 1:2:5 according to weight.
Embodiment 3
A kind of nanometer priming paint of resistance to marine anticorrosion, it is characterised in that be made up of the raw material of following parts by weight:
Linear phenolic epoxy resin 30 parts, glyceryl tristearate 4 parts, pnenolic aldehyde amine hardener 7 parts, polyamide curing agent 6 parts, titanium dioxide 4 parts, nickel alloy powder 12 parts, nano biological anti-fouling agent 5 parts, 3 parts of zinc oxide, 18 parts of acetone, filler 14 parts, acetic acid 5 parts.
Further, described nickel alloy powder is added with the iron oxide red of 0.7% and the trbasic zinc phosphate of 0.6%.
Further, described filler is the mixture that kaolin, wollastonite in powder, SiO 2 powder form than 3:2:2 according to weight.
Further, described nano biological anti-fouling agent is the mixture that nanometer capsicim, P-cinnamic acid sulfuric ester and nanometer homarine form than 1:2:5 according to weight.
The above is not limitation of the present invention; it is noted that, for those skilled in the art; on the premise of without departing from essential scope of the present invention, can also make some changes, remodeling, interpolation or replace, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (4)
1. the nanometer priming paint of resistance to marine anticorrosion, it is characterised in that be made up of the raw material of following parts by weight:
Linear phenolic epoxy resin 20-30 part, glyceryl tristearate 2-4 part, pnenolic aldehyde amine hardener 5-7 part, polyamide curing agent 4-6 part, titanium dioxide 2-4 part, nickel alloy powder 8-12 part, nano biological anti-fouling agent 3-5 part, zinc oxide 1-3 part, acetone 15-18 part, filler 12-14 part, acetic acid 2-5 part.
2. a kind of nanometer priming paint of resistance to marine anticorrosion according to claim 1, it is characterised in that be added with the iron oxide red of 0.5-0.7% and the trbasic zinc phosphate of 0.4-0.6% in described nickel alloy powder.
3. a kind of nanometer priming paint of resistance to marine anticorrosion according to claim 1, it is characterised in that described filler is the mixture that kaolin, wollastonite in powder, SiO 2 powder form than 3:2:2 according to weight.
4. a kind of nanometer priming paint of resistance to marine anticorrosion according to claim 1, it is characterised in that described nano biological anti-fouling agent is the mixture that nanometer capsicim, P-cinnamic acid sulfuric ester and nanometer homarine form than 1:2:5 according to weight.