CN106147341A - A kind of environment-friendly water-based Wood putty - Google Patents
A kind of environment-friendly water-based Wood putty Download PDFInfo
- Publication number
- CN106147341A CN106147341A CN201610618361.1A CN201610618361A CN106147341A CN 106147341 A CN106147341 A CN 106147341A CN 201610618361 A CN201610618361 A CN 201610618361A CN 106147341 A CN106147341 A CN 106147341A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- water
- based wood
- friendly water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of environment-friendly water-based Wood putty, and the raw material including following parts by weight forms: water-base resin 30 ~ 75 parts；Zinc stearate emulsion 10 ~ 30 parts；Filler 10 ~ 20 parts；Defoamer 1 ~ 3 part；PH regulator 0.5 ~ 1.5 part；Coalescents 0.5 ~ 2 part；Thickening agent 0.5 ~ 2.5 part and deionized water 15 ~ 25 parts.Wood putty proposed by the invention has good water resistance; simultaneously; there is the antibacterial effect of excellence, improve the protective effect to wood furniture, effectively extend its service life; and; ultraviolet irradiation is had certain adsorption, improves the service life of putty layer, and; stability is high, and the feature of environmental protection is strong.
Description
Technical field
The present invention relates to functional architectural decoration coating material technical field, be specifically related to a kind of environment-friendly water-based Wood putty.
Background technology
Along with improving constantly of people's living standard and quality of the life, people are more and more heavier with style to the layout in room
Depending on, and room interior wall and furniture play the effect on basis, especially coating and the popularization of paint in whole decoration link and answer
With, make metope and the color of furniture and texture more and more colourful.As the main coating process of wood furniture decoration, woodenware
Paint is possible not only to beautify living environment, additionally it is possible to woodenware rises good protective effect, and extends the service life of wood furniture.
Owing to being affected by seasonal variations and rainfall and air regime, especially at the area that humidity is rainy, furniture
Putty layer and the microorganism such as the easy breed bacteria of dope layer, mycete, it is attractive in appearance but also can seriously damage people that this not only affects furniture
Body is healthy.Simultaneously as putty layer normal phase and air and light contacts, putty layer poor adhesive force, closure can be caused for a long time
Close, the shortcoming such as easy to fall off, and affect its aesthetic property, its resistance to water also can be made to be substantially reduced, stability declines, and can cause ring
The pollution in border.
Therefore, for the problems referred to above, the present invention proposes a kind of new technical scheme.
Summary of the invention
It is an object of the invention to provide a kind of water-tolerant, stablize epistasis, there is the environment-friendly water-based of excellent antibacterial effect
Wood putty.
The present invention is achieved through the following technical solutions:
A kind of environment-friendly water-based Wood putty, the raw material including following parts by weight forms:
Water-base resin 30 ~ 75 parts；
Zinc stearate emulsion 10 ~ 30 parts；
Filler 10 ~ 20 parts；
Defoamer 1 ~ 3 part；
PH regulator 0.5 ~ 1.5 part；
Coalescents 0.5 ~ 2 part；
Thickening agent 0.5 ~ 2.5 part；
Deionized water 15 ~ 25 parts.
Further, also include that the raw material of following parts by weight forms:
Antibacterial 0.3 ~ 1 part；
UV absorbent 0.15 ~ 0.8 part.
Further, described filler includes titanium dioxide, precipitated calcium carbonate and hydroxyethyl cellulose, described titanium dioxide, lightweight
The mass ratio of calcium carbonate and hydroxyethyl cellulose is: 2:1 ~ 1.5:0.8 ~ 1.
Further, described defoamer silicone oil and the mixture of surfactant.
Further, described PH actuator is ammonia or sodium hydroxide solution or hydrochloric acid solution.
Further, described antibacterial is tourmaline powder.
The invention has the beneficial effects as follows: Wood putty proposed by the invention has good water resistance, has meanwhile
Excellent antibacterial effect, improves the protective effect to wood furniture of knowing clearly, effectively extends its service life, and, to purple
The irradiation of outside line has certain adsorption, improves the service life of putty layer, and, stability is high, and the feature of environmental protection is strong.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
A kind of environment-friendly water-based Wood putty, the raw material including following parts by weight forms:
Water-base resin 30 parts；
Zinc stearate emulsion 10 parts；
Filler 10 parts；
Defoamer 1 part；
PH regulator 0.5 part；
Coalescents 0.5 part；
Thickening agent 0.5 part；
Deionized water 15 parts；
Tourmaline powder 0.3 part；
UV absorbent 0.15 part.
Described filler includes titanium dioxide, precipitated calcium carbonate and hydroxyethyl cellulose, described titanium dioxide, precipitated calcium carbonate and hydroxyl
The mass ratio of ethyl cellulose is: 2:1.2:0.8；Described defoamer silicone oil and the mixture of surfactant；Described PH regulates
Device is ammonia or sodium hydroxide solution or hydrochloric acid solution.
Embodiment 2
A kind of environment-friendly water-based Wood putty, the raw material including following parts by weight forms:
Water-base resin 50 parts；
Zinc stearate emulsion 20 parts；
Filler 15 parts；
Defoamer 2 parts；
PH regulator 1 part；
Coalescents 1 part；
Thickening agent 1.5 parts；
Deionized water 20 parts；
Tourmaline powder 0.8 part；
UV absorbent 0.4 part.
Described filler includes titanium dioxide, precipitated calcium carbonate and hydroxyethyl cellulose, described titanium dioxide, precipitated calcium carbonate and hydroxyl
The mass ratio of ethyl cellulose is: 2:1.2:0.8；Described defoamer silicone oil and the mixture of surfactant；Described PH regulates
Device is ammonia or sodium hydroxide solution or hydrochloric acid solution.
Embodiment 3
A kind of environment-friendly water-based Wood putty, the raw material including following parts by weight forms:
Water-base resin 75 parts；
Zinc stearate emulsion 30 parts；
Filler 20 parts；
Defoamer 3 parts；
PH regulator 1.5 parts；
Coalescents 2 parts；
Thickening agent 2.5 parts；
Deionized water 25 parts；
Tourmaline powder 1 part；
UV absorbent 0.8 part.
Described filler includes titanium dioxide, precipitated calcium carbonate and hydroxyethyl cellulose, described titanium dioxide, precipitated calcium carbonate and hydroxyl
The mass ratio of ethyl cellulose is: 2:1.2:0.8；Described defoamer silicone oil and the mixture of surfactant；Described PH regulates
Device is ammonia or sodium hydroxide solution or hydrochloric acid solution.
Wood putty proposed by the invention has good water resistance, meanwhile, has the antibacterial effect of excellence, improves
Know clearly the protective effect to wood furniture, effectively extend its service life, and, ultraviolet irradiation is had certain
Adsorption, improves the service life of putty layer, and, stability is high, and the feature of environmental protection is strong.
The above, be only embodiments of the invention, is not the restriction that the present invention makees any other form, and
Any amendment made according to the technical spirit of the present invention or equivalent variations, still fall within scope of the present invention.
Claims (6)
1. an environment-friendly water-based Wood putty, it is characterised in that: include that the raw material of following parts by weight forms:
Water-base resin 30 ~ 75 parts；
Zinc stearate emulsion 10 ~ 30 parts；
Filler 10 ~ 20 parts；
Defoamer 1 ~ 3 part；
PH regulator 0.5 ~ 1.5 part；
Coalescents 0.5 ~ 2 part；
Thickening agent 0.5 ~ 2.5 part；
Deionized water 15 ~ 25 parts.
A kind of environment-friendly water-based Wood putty, it is characterised in that: also include the former of following parts by weight
Material composition:
Antibacterial 0.3 ~ 1 part；
UV absorbent 0.15 ~ 0.8 part.
A kind of environment-friendly water-based Wood putty, it is characterised in that: described filler includes titanium dioxide, light
Matter calcium carbonate and hydroxyethyl cellulose, the mass ratio of described titanium dioxide, precipitated calcium carbonate and hydroxyethyl cellulose is: 2:1 ~ 1.5:
0.8~1。
A kind of environment-friendly water-based Wood putty, it is characterised in that: live in described defoamer silicone oil and surface
The mixture of property agent.
A kind of environment-friendly water-based Wood putty, it is characterised in that: described PH actuator is ammonia or hydrogen
Sodium hydroxide solution or hydrochloric acid solution.
A kind of environment-friendly water-based Wood putty, it is characterised in that: described antibacterial is tourmaline powder.