CN106145897A - Anticracking floor tile preparation method - Google Patents
Anticracking floor tile preparation method Download PDFInfo
- Publication number
- CN106145897A CN106145897A CN201610678445.4A CN201610678445A CN106145897A CN 106145897 A CN106145897 A CN 106145897A CN 201610678445 A CN201610678445 A CN 201610678445A CN 106145897 A CN106145897 A CN 106145897A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- bentonite
- compound
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anticracking floor tile preparation method, relate to building material technical field, the method comprises the steps: that barite, limestone, bentonite and clay are ground to the powder of 70 mesh by A. respectively;B. blanc fixe, pulverized limestone, bentonite in powder and clay powder step A prepared and POLY-karaya powder, glass fibre, wood fibre are put in blender, stir 8 minutes with the speed of 3000 revs/min, obtain compound;C. adding water in the compound that step B prepares, stir 6 minutes with the speed of 4600 revs/min, wherein compound is 12:1 with the weight ratio of water, old standby;D. the compound that step C prepares is put into mould and be pressed into germule;Pressure 1.6 megapascal (MPa), bulk density is 480 kilograms per cubic meter;E, germule is inserted in the machine of baking bricks and fires, to obtain final product.The present invention provides a kind of natural environmental-protective, high intensity, can bear weight and the floor tile being not easily broken.
Description
Technical field
The present invention relates to building material technical field, especially a kind of anticracking floor tile preparation method.
Background technology
For convenience of people's trip with keep the people attractive in appearance in city that footpath carries out cure process, existing road hard
Change is that it is laid floor tile, and existing floor tile is usually and is mixed by limestone and sand, but this floor tile also exists table
Face intensity is the highest, easily by the problem of weight pressure break, therefore, how to produce a kind of high intensity, can bear weight, be not easily broken
Floor tile be the new problem that those skilled in the art constantly solve.
Summary of the invention
It is an object of the invention to provide a kind of natural environmental-protective, high intensity, weight and the floor tile being not easily broken can be born.
In order to solve the problems referred to above, the technical scheme is that this anticracking floor tile preparation method, use following weight
The raw material of part is made:
Bentonite: 16 parts~19 parts, limestone: 25 parts~35 parts, clay: 12 parts~14 parts, barite: 5 parts~10 parts, stings Chinese parasol tree
Paulownia rubber powder: 2 parts~5 parts, glass fibre: 2 parts~5 parts, wood fibre: 1 part~3 parts;
Comprise the steps:
A. barite, limestone, bentonite and clay are ground respectively, then with the screen filtration that mesh is 70 mesh, obtain barite
Powder, pulverized limestone, bentonite in powder and clay powder, standby;
B. blanc fixe, pulverized limestone, bentonite in powder and the clay powder and the POLY-karaya powder that step A are prepared, glass fibre, wooden
Fiber is put in blender, stirs 8 minutes with the speed of 3000 revs/min, obtains compound;
C. in the compound that step B prepares, add water, stir 6 minutes with the speed of 4600 revs/min, wherein compound and water
Weight ratio be 12:1, old standby;
D. the compound that step C prepares is put into mould and be pressed into germule;Pressure 1.6 megapascal (MPa), bulk density is 480,000
Gram/cubic metre;
E, germule is inserted in the machine of baking bricks and fires, to obtain final product.
In technique scheme, more specifically scheme is it may also is that bentonite: 17 parts, limestone: 30 parts, clay: 13
Part, barite: 8 parts, POLY-karaya powder: 3 parts, glass fibre: 4 parts, wood fibre: 2 parts.
The limestone of the present invention, is a kind of air-setting inorganic coagulation material with calcium oxide as main component, and it has good
Good uniformly dispersed and hydrophilic, in the blank of floor tile, plays skeleton function.
The bentonite of the present invention, is the nonmetallic minerals with montmorillonite as main mineral constituent, its have good bonding,
Suspend and stability, in the blank of floor tile, play filler effect.
The clay of the present invention, is the soil having stickiness, predominantly silicon oxide and aluminium oxide, has preferable plasticity;
The barite of the present invention, also known as blanc fixe, has good radiation protection.
The POLY-karaya powder of the present invention, is the glue of thorn phoenix tree, has good thickening, Stabilization.
The metallic fiber of the present invention, as toughener, its crack resistance not only adding floor tile and wearability, also makes floor tile
There is good electric conductivity.
The wood fibre of the present invention, adds crack resistance and the wearability of floor tile.
Owing to using technique scheme, there is advantages that
The present invention uses natural material to make, and its scientific formulation is reasonable, with low cost, to human non-toxic's evil, safe and reliable;
Not only intensity is high, can bear weight, be not easily broken but also have good shielding property.
Detailed description of the invention
By embodiment, the present invention is described in further detail below:
Embodiment 1:
This anticracking floor tile preparation method, uses the raw material of following weight to make:
Bentonite: 16 kilograms, limestone: 25 kilograms, clay: 12 kilograms, barite: 5 kilograms, POLY-karaya powder: 2 kilograms, glass
Glass fiber: 2 kilograms, wood fibre: 1 kilogram;
Comprise the steps:
A. barite, limestone, bentonite and clay are ground respectively, then with the screen filtration that mesh is 70 mesh, obtain barite
Powder, pulverized limestone, bentonite in powder and clay powder, standby;
B. blanc fixe, pulverized limestone, bentonite in powder and the clay powder and the POLY-karaya powder that step A are prepared, glass fibre, wooden
Fiber is put in blender, stirs 8 minutes with the speed of 3000 revs/min, obtains compound;
C. in the compound that step B prepares, add water, stir 6 minutes with the speed of 4600 revs/min, wherein compound and water
Weight ratio be 12:1, old standby;
D. the compound that step C prepares is put into mould and be pressed into germule;Pressure 1.6 megapascal (MPa), bulk density is 480,000
Gram/cubic metre;
E, germule is inserted in the machine of baking bricks and fires, to obtain final product.
Embodiment 2:
This anticracking floor tile preparation method, uses the raw material of following weight to make:
Bentonite: 19 kilograms, limestone: 35 kilograms, clay: 14 kilograms, barite: 10 kilograms, POLY-karaya powder: 5 kilograms, glass
Glass fiber: 5 kilograms, wood fibre: 3 kilograms;
Remaining is identical with embodiment one.
Embodiment 3:
This anticracking floor tile preparation method, uses the raw material of following weight to make:
Bentonite: 17 kilograms, limestone: 30 kilograms, clay: 13 kilograms, barite: 8 kilograms, POLY-karaya powder: 3 kilograms, glass
Glass fiber: 4 kilograms, wood fibre: 2 kilograms;
Remaining is identical with embodiment one.
Claims (2)
1. an anticracking floor tile preparation method, it is characterised in that: use the raw material of following weight portion to make:
Bentonite: 16 parts~19 parts, limestone: 25 parts~35 parts, clay: 12 parts~14 parts, barite: 5 parts~10 parts, stings Chinese parasol tree
Paulownia rubber powder: 2 parts~5 parts, glass fibre: 2 parts~5 parts, wood fibre: 1 part~3 parts;
Comprise the steps:
A. barite, limestone, bentonite and clay are ground respectively, then with the screen filtration that mesh is 70 mesh, obtain barite
Powder, pulverized limestone, bentonite in powder and clay powder, standby;
B. blanc fixe, pulverized limestone, bentonite in powder and the clay powder and the POLY-karaya powder that step A are prepared, glass fibre, wooden
Fiber is put in blender, stirs 8 minutes with the speed of 3000 revs/min, obtains compound;
C. in the compound that step B prepares, add water, stir 6 minutes with the speed of 4600 revs/min, wherein compound and water
Weight ratio be 12:1, old standby;
D. the compound that step C prepares is put into mould and be pressed into germule;Pressure 1.6 megapascal (MPa), bulk density is 480,000
Gram/cubic metre;
E, germule is inserted in the machine of baking bricks and fires, to obtain final product.
Anticracking floor tile preparation method the most according to claim 1, it is characterised in that: bentonite: 17 parts, limestone: 30 parts,
Clay: 13 parts, barite: 8 parts, POLY-karaya powder: 3 parts, glass fibre: 4 parts, wood fibre: 2 parts.