CN106145852A - A kind of high-performance cement for building mortar - Google Patents
A kind of high-performance cement for building mortar Download PDFInfo
- Publication number
- CN106145852A CN106145852A CN201610509792.4A CN201610509792A CN106145852A CN 106145852 A CN106145852 A CN 106145852A CN 201610509792 A CN201610509792 A CN 201610509792A CN 106145852 A CN106145852 A CN 106145852A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- mortar
- building mortar
- performance cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high-performance cement for building mortar, it is made up of the raw material of following parts by weight: cement 30 45 parts, Lauxite 15 20 parts, antimony oxide 8 17 parts, butanone 12 16 parts, 8 12 parts of firming agent, polyethylene glycol monooleate 6 13 parts, diethanol monoisopropanolamine 9 13 parts, limestone 46 parts, powdered cement additive 37 parts, ground calcium carbonate 20 26 parts, hexylene glycol 47 parts, 1.5 2.5 parts of tartaric acid, anhydrite 14 22 parts, vinylacetate 2.5 5.2 parts, polyamide urea formaldehyde resin 2 4.2 parts, sodium silicate 36 parts, dodecyl sodium sulfate 2.5 4.2 parts.The invention has the beneficial effects as follows: the high-performance cement for building mortar of the present invention have the water-impervious of excellence, wear-resisting, antifreezing function, difficult drop-off ftractures, and improves the workability of mortar, and low cost, technique are simple.
Description
Technical field
The present invention relates to a kind of high-performance cement for building mortar.
Background technology
Mortar is formulated by proper proportion by Binder Materials, fine aggregate and water.Building mortar presses gelling material used
The difference of material, can be divided into cement mortar, cement mixing mortar, lime mortar and gypsum mortar etc..In house decoration, floor tile,
Wall brick stickup and building by laying bricks or stones etc. will use cement mortar, and it is possible not only to the absorbability of enhancing face material and basic unit, but also
Internal structure can be protected, can simultaneously serve as building the screed-coat of hair side, so in fitting-out work, cement mortar is must
Few material.Cement is the major gelled material of masonry mortar, but the traditional cement mortar built by laying bricks or stones, between mortar and bulk
Adhesive property is poor, causes occurring more cracking of building body and leakage scenarios, reduction of service life in engineering.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of high-performance cement for building mortar, has
Excellent water-impervious, wear-resisting, antifreezing function, difficult drop-off ftractures, and improves the workability of mortar, and low cost, technique are simple.
For solving prior art problem, the technical scheme that the present invention provides is, a kind of high-performance cement for building mortar, its
It is made up of the raw material of following parts by weight:
Cement 30-45 part, Lauxite 15-20 part, antimony oxide 8-17 part, butanone 12-16 part, firming agent 8-12 part,
Polyethylene glycol monooleate 6-13 part, diethanol monoisopropanolamine 9-13 part, limestone 4-6 part, powdered cement additive 3-7
Part, ground calcium carbonate 20-26 part, hexylene glycol 4-7 part, tartaric acid 1.5-2.5 part, anhydrite 14-22 part, vinylacetate 2.5-
5.2 parts, polyamide urea formaldehyde resin 2-4.2 part, sodium silicate 3-6 part, dodecyl sodium sulfate 2.5-4.2 part.
The invention has the beneficial effects as follows: the high-performance cement for building mortar of the present invention that there is the water-impervious, resistance to of excellence
Mill, antifreezing function, difficult drop-off ftractures, and improves the workability of mortar, and low cost, technique are simple.
Detailed description of the invention
Embodiment 1
A kind of high-performance cement for building mortar, it is made up of the raw material of following parts by weight:
Cement 30 parts, Lauxite 15 parts, antimony oxide 8 parts, butanone 12 parts, 8 parts of firming agent, polyethylene glycol monooleate
6 parts, diethanol monoisopropanolamine 9 parts, limestone 4 parts, powdered cement additive 3 parts, ground calcium carbonate 20 parts, hexylene glycol 4 parts,
1.5 parts of tartaric acid, anhydrite 14 parts, vinylacetate 2.5 parts, polyamide urea formaldehyde resin 2 parts, sodium silicate 3 parts, dodecyl
Sodium sulfonate 2.5 parts.
Embodiment 2
A kind of high-performance cement for building mortar, it is made up of the raw material of following parts by weight:
Cement 45 parts, Lauxite 20 parts, antimony oxide 17 parts, butanone 16 parts, 12 parts of firming agent, polyethyleneglycol oleic acid
Ester 13 parts, diethanol monoisopropanolamine 13 parts, limestone 6 parts, powdered cement additive 7 parts, ground calcium carbonate 26 parts, hexylene glycol
7 parts, 2.5 parts of tartaric acid, anhydrite 22 parts, vinylacetate 5.2 parts, polyamide urea formaldehyde resin 4.2 parts, sodium silicate 6 parts, ten
Dialkyl sulfonates 4.2 parts.
Claims (1)
1. a high-performance cement for building mortar, it is characterised in that: it is made up of the raw material of following parts by weight:
Cement 30-45 part, Lauxite 15-20 part, antimony oxide 8-17 part, butanone 12-16 part, firming agent 8-12 part,
Polyethylene glycol monooleate 6-13 part, diethanol monoisopropanolamine 9-13 part, limestone 4-6 part, powdered cement additive 3-7
Part, ground calcium carbonate 20-26 part, hexylene glycol 4-7 part, tartaric acid 1.5-2.5 part, anhydrite 14-22 part, vinylacetate 2.5-
5.2 parts, polyamide urea formaldehyde resin 2-4.2 part, sodium silicate 3-6 part, dodecyl sodium sulfate 2.5-4.2 part.