CN106129179A - A kind of production technology of hydrolysis solar energy backboard - Google Patents
A kind of production technology of hydrolysis solar energy backboard Download PDFInfo
- Publication number
- CN106129179A CN106129179A CN201610608844.3A CN201610608844A CN106129179A CN 106129179 A CN106129179 A CN 106129179A CN 201610608844 A CN201610608844 A CN 201610608844A CN 106129179 A CN106129179 A CN 106129179A
- Authority
- CN
- China
- Prior art keywords
- base material
- pet base
- backboard
- hydrolysis
- solar energy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production technology of a kind of hydrolysis solar energy backboard; the solar energy backboard utilizing present invention process to produce is made up of PET base material, fluoro-containing coating protective layer and coat; the hydrolytic resistance of solar energy backboard and adhesive force is made to be greatly improved by the surface configuration fluoro-containing coating protective layer at weathering layer; this fluoro-containing coating protective layer has resistant to hydrolysis, anti-oxidation function; extend service life, save Financial cost.
Description
Technical field
The present invention relates to solar components field, particularly relate to the production technology of a kind of hydrolysis solar energy backboard.
Background technology
Solar energy, as a kind of environmental protection, the inexhaustible energy, replaces the optimal choosing of tradition thermal power generation beyond doubt
Select, owing to solaode needs to be chronically exposed to outdoor practicality, so the cell piece in photovoltaic module needs to be protected by, come
Prevent impact and the vertical view of the environmental factorss such as the steam in air, oxygen, ultraviolet.Solar energy backboard is whole solaode
One of accessory, act primarily as mechanical support and effect that protection cell piece permeates from environmental factors, current existing solar energy
Backboard anti-hydrolytic performance is poor, the most oxidizable, affect service life.
Summary of the invention
The applicant, for above-mentioned existing existing issue, has carried out Improvement, it is provided that a kind of hydrolysis solar energy backboard
Production technology, it has, and adhesive force is strong, hydrolytic resistance and the advantage of good in oxidation resistance.
The technical solution adopted in the present invention is as follows:
The production technology of a kind of hydrolysis solar energy backboard, comprises the following steps:
The first step: carried out PET base material for volume by unreeling machine;
Second step: binding agent good for proportioning is coated on uniformly by double roller coating rollers a side surface of PET base material;
3rd step: the pet substrate of band application of adhesive in second step is delivered in drying room carry out baking and curing, dries temperature
Degree is 100~120 DEG C, and drying time is 7~8 minutes;
4th step: at the one layer of fluoro-containing coating protective layer of PET base material material surface recombination with binding agent, described fluoro-containing coating
Protective layer is the resistant to hydrolysis containing polyester urethane resin material, oxidation resistant protective layer;
5th step: the PET base material of fluoro-containing coating protective layer compound in the 4th step is rolled up formation semi-finished product on refill and carries out
Hanging, open assembly time is 1~5 day;
6th step: utilize the binding agent that proportioning is good to be coated on the 5th step gained PET base material uniformly by double roller coating rollers
Opposite side surface;
7th step: the pet substrate of band application of adhesive in the 6th step is delivered in drying room carry out baking and curing, dries temperature
Degree is 130~190 DEG C, and drying time is 7~12 minutes;
8th step: at the one layer of coat of PET base material material surface recombination with binding agent;Described coat is polytetrafluoroethyl-ne
The coating material that the molecule of alkene or Kynoar and base resin are mixed to form;
9th step: the 8th step gained PET base material being rolled up formation finished product backboard on refill and hangs, open assembly time is 1
~5 days;
Tenth step: the 9th step gained backboard is carried out trimming, bundling according to customer demand;
11st step: the tenth step gained backboard is sampled detection, the performance of detection backboard and credit rating.
Its further technical scheme is:
The thickness of described PET base material is 26~60 microns.
Beneficial effects of the present invention is as follows:
The solar energy back board structure utilizing present invention process to produce is simple, by the surface configuration fluoro-containing coating at weathering layer
Protective layer makes the hydrolytic resistance of solar energy backboard and adhesive force be greatly improved, and this fluoro-containing coating protective layer has resistant to hydrolysis, antioxygen
Change function, extend service life, save Financial cost.
Detailed description of the invention
The detailed description of the invention of the present invention is described below.
The production technology of a kind of hydrolysis solar energy backboard of the present invention comprises the following steps:
The first step: carried out PET base material for volume by unreeling machine;
Second step: binding agent good for proportioning is coated on uniformly by double roller coating rollers a side surface of PET base material;
The thickness of PET base material is 60 microns.
3rd step: the pet substrate of band application of adhesive in second step is delivered in drying room carry out baking and curing, dries temperature
Degree is 100 DEG C, and drying time is 7 minutes;
4th step: at the one layer of fluoro-containing coating protective layer of PET base material material surface recombination with binding agent, fluoro-containing coating is protected
Layer is the resistant to hydrolysis containing polyester urethane resin material, oxidation resistant protective layer.
5th step: the PET base material of fluoro-containing coating protective layer compound in the 4th step is rolled up formation semi-finished product on refill and carries out
Hanging, open assembly time is 1 day;
6th step: utilize the binding agent that proportioning is good to be coated on the 5th step gained PET base material uniformly by double roller coating rollers
Opposite side surface;
7th step: the pet substrate of band application of adhesive in the 6th step is delivered in drying room carry out baking and curing, dries temperature
Degree is 130 DEG C, and drying time is 7 minutes;
8th step: at the one layer of coat of PET base material material surface recombination with binding agent;Coat be politef or
The coating material that the molecule of Kynoar and base resin are mixed to form;
9th step: the 8th step gained PET base material being rolled up formation finished product backboard on refill and hangs, open assembly time is 1
My god;
Tenth step: the 9th step gained backboard is carried out trimming, bundling according to customer demand;
11st step: the tenth step gained backboard is sampled detection, the performance of detection backboard and credit rating.
The solar energy back board structure utilizing present invention process to produce is simple, by the surface configuration fluoro-containing coating at weathering layer
Protective layer makes the hydrolytic resistance of solar energy backboard and adhesive force be greatly improved, and this fluoro-containing coating protective layer has resistant to hydrolysis, antioxygen
Change function, extend service life, save Financial cost.
Above description is explanation of the invention, is not the restriction to invention, and limited range of the present invention sees right
Requirement, in the case of the basic structure of the present invention, the present invention can make any type of amendment.
Claims (2)
1. the production technology of a hydrolysis solar energy backboard, it is characterised in that comprise the following steps:
The first step: carried out PET base material for volume by unreeling machine;
Second step: binding agent good for proportioning is coated on uniformly by double roller coating rollers a side surface of PET base material;
3rd step: the pet substrate of band application of adhesive in second step is delivered in drying room carry out baking and curing, drying temperature is
100~120 DEG C, drying time is 7~8 minutes;
4th step: at the one layer of fluoro-containing coating protective layer of PET base material material surface recombination with binding agent, described fluoro-containing coating is protected
Layer is the resistant to hydrolysis containing polyester urethane resin material, oxidation resistant protective layer;
5th step: the PET base material of fluoro-containing coating protective layer compound in the 4th step is rolled up formation semi-finished product on refill and hangs,
Open assembly time is 1~5 day;
6th step: utilize the binding agent that proportioning is good to be coated on the another of the 5th step gained PET base material uniformly by double roller coating rollers
One side surface;
7th step: the pet substrate of band application of adhesive in the 6th step is delivered in drying room carry out baking and curing, drying temperature is
130~190 DEG C, drying time is 7~12 minutes;
8th step: at the one layer of coat of PET base material material surface recombination with binding agent;Described coat be politef or
The coating material that the molecule of Kynoar and base resin are mixed to form;
9th step: the 8th step gained PET base material being rolled up formation finished product backboard on refill and hangs, open assembly time is 1~5
My god;
Tenth step: the 9th step gained backboard is carried out trimming, bundling according to customer demand;
11st step: the tenth step gained backboard is sampled detection, the performance of detection backboard and credit rating.
The production technology of a kind of hydrolysis solar energy backboard the most as claimed in claim 1, it is characterised in that: described PET base material
Thickness be 26~60 microns.