CN106120340A - A kind of cotton anti-corrosive pulp containing nm-class boron nitride of flame-proof antibiotic - Google Patents
A kind of cotton anti-corrosive pulp containing nm-class boron nitride of flame-proof antibiotic Download PDFInfo
- Publication number
- CN106120340A CN106120340A CN201610475552.7A CN201610475552A CN106120340A CN 106120340 A CN106120340 A CN 106120340A CN 201610475552 A CN201610475552 A CN 201610475552A CN 106120340 A CN106120340 A CN 106120340A
- Authority
- CN
- China
- Prior art keywords
- boron nitride
- minute
- stirring
- cotton
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the cotton anti-corrosive pulp containing nm-class boron nitride of a kind of flame-proof antibiotic, it is made up of the raw material of following weight portion: boron nitride nanosheet 56, 18-amine. 78, dehydrated alcohol is appropriate, dodecylbenzene sodium sulfonate 2.5 3, alkylphenol polyoxyethylene 0.8 1, Ammonium persulfate. 0.5 0.55, acrylic acid 20 22, ethyl acrylate 50 53, methyl methacrylate 28 30, volution phosphinylidyne imidazate 78, phosphoric acid 0.5 0.6, pure water is appropriate, hydroxy terminated fluorosilicone oil 1 1.2, organic silicon emulsion 67, penetrating agent JFC 2 2.5, nano zine oxide 45, polyvinyl alcohol 23.The product treatment cotton made by the present invention, not only antiseptic property is excellent, and fire-retardant, antibacterial, resistance to water, free from extraneous odour, technique is easy to Industry Control, is worthy to be popularized.
Description
Technical field
The present invention relates to textile technology field, particularly relate to the slurry of the cotton anticorrosion containing nm-class boron nitride of a kind of flame-proof antibiotic
Material.
Background technology
Cotton have wear soft comfortable, warming, moisture absorption, breathability is strong, be prone to the features such as dyeing and finishing processing, due to it this
A little natural characteristics, are liked by people already, become indispensable basic articles for use in life.Cotton is in people's daily life
Necessary, the aspect such as it is taken in the dress of people, bedding, indoor article, interior decoration has purposes widely,
Additionally also it is widely used at packaging, the aspect such as industrial, medical, military.But cotton deficiency the most acidproof, elastic, easily rises
Wrinkle, easy moldy metamorphism, cotton often runs into antiseptical problem after making ready-made clothes, and this is accomplished by many cottons and carries out preservative treatment,
But time traditional preservative not only affect the chemical characteristic of linen-cotton, also affect the naturality of garment products simultaneously, and have tight
The abnormal flavour of weight.In patent documentation " a kind of for linen-cotton antiseptical environment protection additive ", utilize the Cortex Eucommiae, Herba thymi vulgaris, meson etc.
The additive that composition is made is in the making of linen-cotton, although solve the question-and-answer problems such as the abnormal flavour of anticorrosive additive, environmental protection, but
Owing to being the effective ingredient using plant, inherently antiseptic effect is had a greatly reduced quality after repeatedly washing.For this problem,
It is accomplished by developing a kind of impregnating fluid processing cotton, not only there is safe antiseptic property, simultaneously can be antibacterial, crease-resistant etc..
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of flame-proof antibiotic containing nm-class boron nitride
Cotton anti-corrosive pulp.
The present invention is achieved by the following technical solutions:
The cotton anti-corrosive pulp containing nm-class boron nitride of a kind of flame-proof antibiotic, is made up of the raw material of following weight portion: nitridation
Boron nanometer sheet 5-6,18-amine. 7-8, dehydrated alcohol are appropriate, dodecylbenzene sodium sulfonate 2.5-3, alkylphenol polyoxyethylene 0.8-
1, Ammonium persulfate. 0.5-0.55, acrylic acid 20-22, ethyl acrylate 50-53, methyl methacrylate 28-30, volution phosphinylidyne miaow
Azoles ester 7-8, phosphoric acid 0.5-0.6, pure water are appropriate, hydroxy terminated fluorosilicone oil 1-1.2, organic silicon emulsion 6-7, penetrating agent JFC 2-2.5, receive
Rice zinc oxide 4-5, polyvinyl alcohol 2-3.
The cotton anti-corrosive pulp containing nm-class boron nitride of described a kind of flame-proof antibiotic, is made up of step in detail below:
(1) mix with 18-amine. after boron nitride nanosheet being vacuum dried 3-4 hour at 80-90 DEG C, under nitrogen protection,
Stir process 2-3 hour under the oil bath of 170-180 DEG C, is subsequently adding the dehydrated alcohol of reactant 2-2.5 times amount, after stirring
Supersound process 30-40 minute, continues to be heated to 80-90 DEG C, evaporates dehydrated alcohol, continues to be heated to 170-180 DEG C, and stirring is anti-
It is cooled to room temperature after answering 24 hours, filters to isolate solid particle, rinse 2-3 time with dehydrated alcohol, be finally putting into vacuum drying oven
In, it is dried to constant weight at 80-90 DEG C, obtains surface modification boron nitride;
(2) being mixed homogeneously with alkylphenol polyoxyethylene by dodecylbenzene sodium sulfonate, be divided into two parts, a copy of it is dissolved in 10-
In the pure water of 12 times amount, the modified boron nitride made with step (1) after stirring mixes, and stirs 30-40 minute and forms dispersion
Liquid is stand-by;Another part mixes with acrylic acid, ethyl acrylate, methyl methacrylate, stirs with the speed of 150-200 rev/min
Add above-mentioned dispersion liquid after 20-30 minute, after continuing stirring 10-15 minute, be slowly added dropwise Ammonium persulfate., completion of dropwise addition post-heating
To 80-85 DEG C and isothermal reaction 90-120 minute, being cooled to room temperature, regulation pH, to neutral, obtains nano silicon nitride boron modification poly-third
Olefin(e) acid slurry;
(3) by adding the pure water of 20-30 times amount in polyvinyl alcohol, being heated to 90-100 DEG C, stirring, to being completely dissolved, is subsequently adding
Volution phosphinylidyne imidazate, phosphoric acid, add the nanometer that step (2) obtains with the speed of 150-200 rev/min after stirring 15-20 minute
Boron nitride modified polyacrylic acid slurry, after continuing stirring 60-90 minute, adds remaining residual components, raise speed to 300-400 turn/
Divide stirring 10-12 minute and get final product.
The invention have the advantage that boron nitride nanosheet is carried out surface modification by a series of technique and adds to by the present invention
In the preparation of polyacrylic acid size, improve boron nitride nanosheet dispersibility in polyacrylic acid size, improve boron nitride
Nanometer sheet and the compatibility of slurry, improve the high-temperature stability of slurry, corrosion resistance, it is possible to reduces heat and glues phenomenon again;Well
Greasy property, be conducive to protect serous coat integrity, and contribute to increase serous coat obdurability;Anticorrosion of the present invention is utilized to starch
Cotton after material processes not only has good decay resistance, simultaneously cloth good hand touch, resistance to water.
The present invention also with the addition of volution phosphinylidyne imidazate, phosphoric acid, synergism in preparation process, it is possible to is processing cotton
It expand into charcoal when surface is heated, form protective layer, stop heat inwardly to transmit, reduce the thermal decomposition rate of material, reduce flammable
The release of property material, thus reach fire-retardant purpose;Add nano zine oxide and organic silicon emulsion complex role, slurry can be significantly improved
The multiple performance such as antibacterial, washable of material;The product treatment cotton made by the present invention, not only antiseptic property is excellent, and fire-retardant,
Antibacterial, resistance to water, free from extraneous odour, technique is easy to Industry Control, is worthy to be popularized.
Detailed description of the invention
The cotton anti-corrosive pulp containing nm-class boron nitride of a kind of flame-proof antibiotic, is prepared by the raw material of following weight portion (kilogram)
Make: boron nitride nanosheet 5,18-amine. 7, dehydrated alcohol are appropriate, dodecylbenzene sodium sulfonate 2.5, alkylphenol polyoxyethylene
0.8, Ammonium persulfate. 0.5, acrylic acid 20, ethyl acrylate 50, methyl methacrylate 28, volution phosphinylidyne imidazate 7, phosphoric acid
0.5, pure water is appropriate, hydroxy terminated fluorosilicone oil 1, organic silicon emulsion 6, penetrating agent JFC 2, nano zine oxide 4, polyvinyl alcohol 2.
The cotton anti-corrosive pulp containing nm-class boron nitride of described a kind of flame-proof antibiotic, is made up of step in detail below:
(1) mix with 18-amine. after boron nitride nanosheet being vacuum dried 3 hours at 80 DEG C, under nitrogen protection, 170 DEG C
Stir process 2 hours under oil bath, are subsequently adding the dehydrated alcohol of reactant 2 times amount, and after stirring, supersound process 30 minutes, continue
Continuing and be heated to 80 DEG C, evaporate dehydrated alcohol, continue to be heated to 170 DEG C, stirring reaction was cooled to room temperature after 24 hours, filters and divides
Separate out solid particle, rinse 2 times with dehydrated alcohol, be finally putting in vacuum drying oven, be dried to constant weight at 80 DEG C, obtain surface
Modified boron nitride;
(2) being mixed homogeneously with alkylphenol polyoxyethylene by dodecylbenzene sodium sulfonate, be divided into two parts, a copy of it is dissolved in 10 times
In the pure water of amount, the modified boron nitride made with step (1) after stirring mixes, and stirs 30 minutes formation dispersion liquids stand-by;
Another part mixes with acrylic acid, ethyl acrylate, methyl methacrylate, adds after stirring 20 minutes with the speed of 150 revs/min
Above-mentioned dispersion liquid, is slowly added dropwise Ammonium persulfate. after continuing stirring 10 minutes, completion of dropwise addition post-heating to 80 DEG C isothermal reaction 90
Minute, it being cooled to room temperature, regulation pH, to neutral, obtains nm-class boron nitride modified polyacrylic acid slurry;
(3) will add the pure water of 20 times amount in polyvinyl alcohol, be heated to 90 DEG C, stirring, to being completely dissolved, is subsequently adding volution phosphorus
Acyl imidazate, phosphoric acid, add the nano silicon nitride boron modification poly-third that step (2) obtains with the speed of 150 revs/min after stirring 15 minutes
Olefin(e) acid slurry, after continuing stirring 60 minutes, adds remaining residual components, raises speed to 300 revs/min and stirs 10 minutes and get final product.
Utilize product of the present invention that cotton is processed, use two leachings two to roll (pick-up 80%), the mode dried, warp
Cotton after measurement processing is dry/and hygrometric state creasy recovery angle promoted, and soft, breaking strength retention warp-wise is
83.8%, broadwise is 84.1%, and Tear strength retention rate warp-wise is 86.2%, and broadwise is 88.4%, hence it is evident that be better than untreated cotton.
Claims (2)
1. the cotton anti-corrosive pulp containing nm-class boron nitride of a flame-proof antibiotic, it is characterised in that by the raw material of following weight portion
Preparation is made: boron nitride nanosheet 5-6,18-amine. 7-8, dehydrated alcohol are appropriate, dodecylbenzene sodium sulfonate 2.5-3, alkyl phenol
Polyoxyethylene ether 0.8-1, Ammonium persulfate. 0.5-0.55, acrylic acid 20-22, ethyl acrylate 50-53, methyl methacrylate
28-30, volution phosphinylidyne imidazate 7-8, phosphoric acid 0.5-0.6, pure water are appropriate, hydroxy terminated fluorosilicone oil 1-1.2, organic silicon emulsion 6-7, ooze
Agent JFC2-2.5, nano zine oxide 4-5, polyvinyl alcohol 2-3 thoroughly.
A kind of cotton anti-corrosive pulp containing nm-class boron nitride of flame-proof antibiotic, it is characterised in that by
Step is made in detail below:
(1) mix with 18-amine. after boron nitride nanosheet being vacuum dried 3-4 hour at 80-90 DEG C, under nitrogen protection,
Stir process 2-3 hour under the oil bath of 170-180 DEG C, is subsequently adding the dehydrated alcohol of reactant 2-2.5 times amount, after stirring
Supersound process 30-40 minute, continues to be heated to 80-90 DEG C, evaporates dehydrated alcohol, continues to be heated to 170-180 DEG C, and stirring is anti-
It is cooled to room temperature after answering 24 hours, filters to isolate solid particle, rinse 2-3 time with dehydrated alcohol, be finally putting into vacuum drying oven
In, it is dried to constant weight at 80-90 DEG C, obtains surface modification boron nitride;
(2) being mixed homogeneously with alkylphenol polyoxyethylene by dodecylbenzene sodium sulfonate, be divided into two parts, a copy of it is dissolved in 10-
In the pure water of 12 times amount, the modified boron nitride made with step (1) after stirring mixes, and stirs 30-40 minute and forms dispersion
Liquid is stand-by;Another part mixes with acrylic acid, ethyl acrylate, methyl methacrylate, stirs with the speed of 150-200 rev/min
Add above-mentioned dispersion liquid after 20-30 minute, after continuing stirring 10-15 minute, be slowly added dropwise Ammonium persulfate., completion of dropwise addition post-heating
To 80-85 DEG C and isothermal reaction 90-120 minute, being cooled to room temperature, regulation pH, to neutral, obtains nano silicon nitride boron modification poly-third
Olefin(e) acid slurry;
(3) by adding the pure water of 20-30 times amount in polyvinyl alcohol, being heated to 90-100 DEG C, stirring, to being completely dissolved, is subsequently adding
Volution phosphinylidyne imidazate, phosphoric acid, add the nanometer that step (2) obtains with the speed of 150-200 rev/min after stirring 15-20 minute
Boron nitride modified polyacrylic acid slurry, after continuing stirring 60-90 minute, adds remaining residual components, raise speed to 300-400 turn/
Divide stirring 10-12 minute and get final product.