CN106117874A - Cabinet material and preparation method thereof moulded by a kind of wood - Google Patents
Cabinet material and preparation method thereof moulded by a kind of wood Download PDFInfo
- Publication number
- CN106117874A CN106117874A CN201610502193.XA CN201610502193A CN106117874A CN 106117874 A CN106117874 A CN 106117874A CN 201610502193 A CN201610502193 A CN 201610502193A CN 106117874 A CN106117874 A CN 106117874A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- cabinet
- preparation
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of wood and mould cabinet material and preparation method thereof, mainly include that following raw material is made: PVC resin powder 100 parts, sisal fiber 40 55 parts, Al (OH)350 60 parts, silane coupler 68 parts, calcium stearate 58 parts, Firebrake ZB 46 parts, antioxidant CA 0.5 1 parts, acrylic acid amides 0.3 0.8 parts, coloring agent 0.2 0.5, ethylene bis stearic acid amide (EBS) 2 parts, present invention also offers this wood and mould the preparation method of cabinet material, above-mentioned formula combines preparation method and can solve the problem that current cabinet material, the problems such as moisture-sensitive is gone mouldy, breed bacteria, harm Element release (formaldehyde etc.), and the environmental protection of material own, elegant in appearance.
Description
Technical field
The present invention relates to a kind of cabinet material, particularly relate to a kind of wood and mould cabinet material and preparation method thereof.
Background technology
Cabinet refers to storing kitchen tool in kitchen and the platform of operation of cooking, its material select to have solid wood, stainless,
PLASTIC LAMINATED, melamine plate, plastics sucking plate, poly (methyl methacrylate) plate, paint plate etc., due to the specific use environment of cabinet, cause it
Moisture-sensitive, easily cause mycete, require again cabinet composition material environmental protection, elegant in appearance, non-hazardous Element release (formaldehyde simultaneously
Deng), above-mentioned material all exists such or such defect.
Summary of the invention
The technical problem to be solved is to provide a kind of wood to mould cabinet material and preparation method thereof, it is possible to solve
At present cabinet material, the problem such as moisture-sensitive is gone mouldy, breed bacteria, harm Element release (formaldehyde etc.), and material green itself
Environmental protection, elegant in appearance.
In the present invention, " consumption ", " part " are all quality criterias, and the amount of each component is all on the basis of 100 parts of polyvinyl chloride resin.
For solving above-mentioned existing technical problem, the present invention uses following scheme:
Cabinet material moulded by a kind of wood, mainly includes that following raw material is made: PVC resin powder 100 parts, sisal fiber 40-55 part,
Al(OH)350-60 part, silane coupler 6-8 part, calcium stearate 5-8 part, Firebrake ZB 4-6 part, antioxidant CA 0.5-1 part, third
Enoic 0.3-0.8 part, coloring agent 0.2-0.5, ethylene bis stearic acid amide (EBS) 2 parts.
As preferably, described coloring agent is selected according to required color: (1) red mainly phthalocyanine is red；(2) yellow mainly has
Chrome yellow；(3) green predominantly phthalocyanine green；(4) white mainly uses titanium dioxide；(5) purple is mainly permanent violet RL.
The preparation method of cabinet material moulded by this wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, and the Plant fiber after broken is crossed 100 mesh sieves, dry for standby, water content ＜
2wt%；
(2) according to proportioning raw materials, PVC resin powder, step (1) are obtained sisal fiber, silane coupler, calcium stearate add and stir
Mixing in machine and mix, rotating speed is 500 revs/min, and the time is 8-11 minute, and temperature is 95 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Al (OH)3, Firebrake ZB, antioxidant CA, acrylic acid amides, coloring agent, second
The double stearic amide (EBS) of support continues stirring, and rotating speed is 1200 revs/min, and the time is 25-30 minute, and temperature is 115 DEG C,
Standby to mixture；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 135 DEG C, the granulate cooling that will obtain
After, obtain a kind of wood and mould cabinet material former material granule；
(5) granular Wood-plastic material step (4) obtained makes all kinds of model cabinet plate by extruding production line or injection moulding technology
Or the technique of cabinet door makes requirement, produced by extruding or die cast.
The invention have benefit that: the present invention uses technique scheme to provide a kind of wood to mould cabinet material and system thereof
Preparation Method, it is possible to solve current cabinet material, the problem such as moisture-sensitive is gone mouldy, breed bacteria, harm Element release (formaldehyde etc.), and
And it is the environmental protection of material own, elegant in appearance.
Detailed description of the invention
The present invention is described in detail, in illustrative examples and the explanation of this present invention below in conjunction with specific embodiment
It is used for explaining the present invention, but not as a limitation of the invention.
Embodiment 1
Cabinet material moulded by a kind of wood, mainly includes that following raw material is made: PVC resin powder 100 parts, sisal fiber 40 parts, Al
(OH)350 parts, silane coupler 6 parts, calcium stearate 5 parts, Firebrake ZB 4 parts, antioxidant CA 0.5 part, acrylic acid amides 0.3
Part, phthalocyanine green 0.2, ethylene bis stearic acid amide (EBS) 2 parts.
The preparation method of cabinet material moulded by this wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, and the Plant fiber after broken is crossed 100 mesh sieves, dry for standby, water content ＜
2wt%；
(2) according to proportioning raw materials, PVC resin powder, step (1) are obtained sisal fiber, silane coupler, calcium stearate add and stir
Mixing in machine and mix, rotating speed is 500 revs/min, and the time is 8 minutes, and temperature is 95 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Al (OH)3, Firebrake ZB, antioxidant CA, acrylic acid amides, phthalocyanine green, second
The double stearic amide (EBS) of support continues stirring, and rotating speed is 1200 revs/min, and the time is 25 minutes, and temperature is 115 DEG C, is mixed
Compound is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 135 DEG C, the granulate cooling that will obtain
After, obtain a kind of wood and mould cabinet material former material granule；
(5) granular Wood-plastic material step (4) obtained makes all kinds of model cabinet plate by extruding production line or injection moulding technology
Or the technique of cabinet door makes requirement, produced by extruding or die cast.
Embodiment 2
Cabinet material moulded by a kind of wood, mainly includes that following raw material is made: PVC resin powder 100 parts, sisal fiber 45 parts, Al
(OH)355 parts, silane coupler 7 parts, calcium stearate 6 parts, Firebrake ZB 5 parts, antioxidant CA 0.7 part, acrylic acid amides 0.5
Part, titanium dioxide 0.3, ethylene bis stearic acid amide (EBS) 2 parts.
The preparation method of cabinet material moulded by wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, and the Plant fiber after broken is crossed 100 mesh sieves, dry for standby, water content ＜
2wt%；
(2) according to proportioning raw materials, PVC resin powder, step (1) are obtained sisal fiber, silane coupler, calcium stearate add and stir
Mixing in machine and mix, rotating speed is 500 revs/min, and the time is 9 minutes, and temperature is 95 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Al (OH)3, Firebrake ZB, antioxidant CA, acrylic acid amides, titanium dioxide, second
The double stearic amide (EBS) of support continues stirring, and rotating speed is 1200 revs/min, and the time is 27 minutes, and temperature is 115 DEG C, is mixed
Compound is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 135 DEG C, the granulate cooling that will obtain
After, obtain a kind of wood and mould cabinet material former material granule；
(5) granular Wood-plastic material step (4) obtained makes all kinds of model cabinet plate by extruding production line or injection moulding technology
Or the technique of cabinet door makes requirement, produced by extruding or die cast.
Embodiment 3
Cabinet material moulded by a kind of wood, mainly includes that following raw material is made: PVC resin powder 100 parts, sisal fiber 55 parts, Al
(OH)360 parts, silane coupler 8 parts, calcium stearate 8 parts, Firebrake ZB 6 parts, antioxidant CA 1 part, acrylic acid amides 0.8 part,
Permanent violet RL 0.5, ethylene bis stearic acid amide (EBS) 2 parts.
The preparation method of cabinet material moulded by wood, comprises the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, and the Plant fiber after broken is crossed 100 mesh sieves, dry for standby, water content ＜
2wt%；
(2) according to proportioning raw materials, PVC resin powder, step (1) are obtained sisal fiber, silane coupler, calcium stearate add and stir
Mixing in machine and mix, rotating speed is 500 revs/min, and the time is 11 minutes, and temperature is 95 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Al (OH)3, Firebrake ZB, antioxidant CA, acrylic acid amides, permanent violet RL,
Ethylene bis stearic acid amide (EBS) continues stirring, and rotating speed is 1200 revs/min, and the time is 30 minutes, and temperature is 115 DEG C, obtains
Mixture is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 135 DEG C, the granulate cooling that will obtain
After, obtain a kind of wood and mould cabinet material former material granule；
(5) granular Wood-plastic material step (4) obtained makes all kinds of model cabinet plate by extruding production line or injection moulding technology
Or the technique of cabinet door makes requirement, produced by extruding or die cast.
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting the present invention.Any ripe
Above-described embodiment all can be modified under the spirit and the scope of the present invention or change by the personage knowing this technology.Cause
This, have usually intellectual such as complete with institute under technological thought without departing from disclosed spirit in art
All equivalences become are modified or change, and must be contained by the claim of the present invention.
Claims (2)
1. cabinet material and preparation method thereof moulded by a wood, it is characterised in that mainly include that following raw material is made: PVC tree
100 parts of cosmetics, sisal fiber 40-55 part, Al (OH)350-60 part, silane coupler 6-8 part, calcium stearate 5-8 part, boric acid
Zinc 4-6 part, antioxidant CA 0.5-1 part, acrylic acid amides 0.3-0.8 part, coloring agent 0.2-0.5, ethylene bis stearic acid amide
(EBS) 2 parts；Described coloring agent is selected according to required color: (1) red mainly phthalocyanine is red；(2) yellow mainly has chrome yellow；(3)
Green predominantly phthalocyanine green；(4) white mainly uses titanium dioxide；(5) purple is mainly permanent violet RL.
The preparation method of cabinet material moulded by wood the most according to claim 1, it is characterised in that comprise the following steps:
(1) after sisal fiber being soaked 2 hours in water, using single screw extrusion machine, extrusion stripping obtains in an extruder
Plant fiber, places in fiber disintegrating machine broken, and the Plant fiber after broken is crossed 100 mesh sieves, dry for standby, water content ＜
2wt%；
(2) according to proportioning raw materials, PVC resin powder, step (1) are obtained sisal fiber, silane coupler, calcium stearate add and stir
Mixing in machine and mix, rotating speed is 500 revs/min, and the time is 8-11 minute, and temperature is 95 DEG C, obtains mixture standby；
(3) batch mixing step (2) obtained, adds Al (OH)3, Firebrake ZB, antioxidant CA, acrylic acid amides, coloring agent, ethylene
Double stearic amides (EBS) continue stirring, and rotating speed is 1200 revs/min, and the time is 25-30 minute, and temperature is 115 DEG C, obtains
Mixture is standby；
(4) pelletize is carried out at a temperature of the mixture that step (3) obtains being joined comminutor 135 DEG C, the granulate cooling that will obtain
After, obtain a kind of wood and mould cabinet material former material granule；
(5) granular Wood-plastic material step (4) obtained makes all kinds of model cabinet plate by extruding production line or injection moulding technology
Or the technique of cabinet door makes requirement, produced by extruding or die cast.