CN106117688B - Tire made from a kind of reclaimed rubber and the rubber - Google Patents
Tire made from a kind of reclaimed rubber and the rubber Download PDFInfo
- Publication number
- CN106117688B CN106117688B CN201610464222.8A CN201610464222A CN106117688B CN 106117688 B CN106117688 B CN 106117688B CN 201610464222 A CN201610464222 A CN 201610464222A CN 106117688 B CN106117688 B CN 106117688B
- Authority
- CN
- China
- Prior art keywords
- tire
- wind
- block
- pattern block
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Tire made from a kind of present invention reclaimed rubber of offer and the rubber, include the material of following parts by weight：Waste tyre rubber powder, glass fibre, nylon fiber, acroleic acid polyurethane, polyamide, styrenated phenol, 3 diphenylguanidine, polystyrene resin, composition epoxy resin, resin acid, rosin acid anhydrides, carbon black, aromatic disulfides, zinc salt.Tire made from reclaimed rubber, including tire body, tire body include two tire sides and the tire side face between two tire sides, wherein, wind-guiding block is distributed with least one tire side, wind guide tank is formed between adjacent two wind-guidings block；Tire side face is provided with polycyclic braking pattern block, and braking pattern block forms guiding gutter, wind guide tank is connected with guiding gutter with the center line symmetrical setting of tire side face on same ring between adjacent two brakings pattern block.The reclaimed rubber of the present invention, high mechanical strength, elastic strong, ageing-resistant, cold-resistant, high temperature resistant, while reduce power consumption, braking ability and driveability are strong.
Description
Technical field
The present invention relates to field of rubber technology, more particularly to tire made from a kind of reclaimed rubber and the rubber.
Background technology
With developing rapidly for auto industry, the rubber scrapped is more and more, and according to statistics, the whole world will scrap every year
More than 1000 ten thousand tons of tires, the key subjects of various countries' rubber industry circle concern how are effectively turned into using these discarded rubber.
Waste-tyre rubber-powder is as a kind of regenerated resources, and its application is quite varied, and more and more common, for producing
Reclaimed rubber, and then various rubbers are produced, such as retread, for construction material, such as it is used to lay highway, fortune
Dynamic field, floor, carpet etc., suitable for the home for the aged, kindergarten, ward, court, playground, gymnasium and various recreation grounds.It
The characteristics of be that elasticity is good, anti-aging is good, anti-skidding, impact resistance, fire-retardant and insulation effect are good, it is durable in use etc..But current city
On face all there is very big rubber taste, arene content height and the problems such as changing colour of easily turning blue, its reason master in rubber on sale
If reclaimed rubber contained in rubber is common reclaimed rubber, it is dense rubber taste to be inherently present in this reclaimed rubber, aromatic hydrocarbons
The problems such as content is high, therefore a kind of environment-friendly type regenerated rubber of market in urgent need.
As Chinese patent CN103570968A discloses environment-friendly type high intensity power tyre reclaimed rubber manufacturing method and combinations thereof
The formula of material, described combination material include the material of following parts by weight：Rubber powder：100 parts；Environment-friendly rubber softening agent：7-10
Part；Tackifier：1-2 parts, rubber powder therein are at least 20 of waste radial tire tyre surface through crushing, sieve, being obtained after magnetic separation
Rubber powder more than mesh；Environment-friendly rubber softening agent include the young oil one kind therein of tall oil, dish；Tackifier include rosin, increased
Viscosity resin one kind therein.Technical scheme disclosed by the invention, processing characteristics is good, and no rubber taste, arene content is low, non-discolouring,
Meet EU criteria.And the present invention, as primary raw material, environmental protection and energy saving, is that the recovery of junked tire is comprehensive using steel wire tire rubber powder
Close to utilize and provide a good approach.But the rubber in technical scheme disclosed by the invention, its intensity is relatively low, meanwhile,
Its is elastic, ageing-resistant, cold tolerance is relatively low.
And for example Chinese patent CN 104070934A disclose a kind of tire construction, including：One tire body, it is vehicle wheel
Tire；And several guidings are soon, the guiding block is incorporated at least one side around tire body in a manner of forward and backward serial arrangement, should
Guiding block is located at the one side of tire body advance rotation direction, provided with an at least guiding incline, the guiding incline and adjacent guiding
Formed respectively between block to help wind groove, make the tire body under direction of advance state, with the guiding incline of guiding block with helping wind recessed
Groove increase air conducting, reduce windage and sound of the wind noise and produce walk help power, also, the guiding incline of the guiding block is with helping wind groove
In tire body lower half circumferential position, produce the boosting power for guiding of taking advantage of a situation and stablize traveling effect.Technical side disclosed by the invention
Case, oil consumption when vehicle travels and power consumption is greatly lowered, reaches the optimum efficiency of fuel-efficient energy-conservation.But except power-assisted ability
Outside, other performances of tire are equally very important, i.e. braking ability and maneuvering performance, are only improved braking ability and maneuvering performance
It just can guarantee that the security of driving.
The content of the invention
To overcome problems of the prior art, the invention provides wheel made from a kind of reclaimed rubber and the rubber
Tire, a kind of reclaimed rubber provided by the invention is green, and with higher-strength and higher elasticity, resistance to ag(e)ing and resists cold
Property, tire made from a kind of reclaimed rubber provided by the invention, it can not only use separation to be used as boosting power, be provided simultaneously with preferably
Braking ability and maneuvering performance.
The invention provides a kind of reclaimed rubber, include the material of following parts by weight:
In some embodiments, the composition epoxy resin includes the material of following percentage by weight：
In some embodiments, the aromatic disulfides are one in pentachlorothiophenol, zinc salt of pentachlorothiophenol, thionaphthol
Kind or a variety of mixtures.
The invention discloses tire made from a kind of reclaimed rubber, including tire body, the tire body includes two-wheeled
Sidewall face and the tire side face between two tire side, wherein, it is distributed with and leads at least one tire side
Pomphus, wind guide tank is formed between adjacent two wind-guidings block；The tire side face is provided with polycyclic braking pattern block, the braking decorative pattern
Block forms guiding gutter with the center line symmetrical setting of the tire side face on same ring between the adjacent two braking pattern block,
The wind guide tank is connected with the guiding gutter.
In some embodiments, the section triangle at a right angle of the wind-guiding block, wherein the one of the right angled triangle
Right-angle side is located on the tire side edge of the tire body, the triangle base and right-angle side of the two neighboring wind-guiding block
Form the wind guide tank.
In some embodiments, the triangle base of the wind-guiding block of the right triangular shape is curved.
In some embodiments, the plane where the side side wall of the wind guide tank and putting down where the tire side
Face shape has angle, and the opposite side side wall of the wind guide tank is perpendicular to the plane where the tire side.
In some embodiments, the wind-guiding groove sidewall is flat where the side of the triangle base of the wind-guiding block
Face has angle with the planar shaped where the tire side, and the angular range is 30 ° -45 °.
In some embodiments, including described at least two rings pattern block is braked, and the number of rings of the braking pattern block is
Even number, an annular groove is formed between pattern block described in adjacent two ring；Using the center line of the tire side face as boundary, the institute of homonymy
It is consistent to state braking decorative pattern Block direction, and the guiding gutter is not orthogonal to the center line of the tire side face, the guiding gutter and institute
It is consistent to state wind guide tank direction.
In some embodiments, it is provided with along the tire body axis and sets positioned at the braking pattern block surface in outside
The breaker slot put, it is provided with positioned at the braking pattern block surface of inner side along the circumferentially disposed drag reduction groove of the tire body.
Compared with prior art, the beneficial effect of tire made from a kind of reclaimed rubber and its rubber provided by the invention
It is：
1st, a kind of reclaimed rubber provided by the invention, processing characteristics is good, no rubber taste, environmental protection and energy saving, meanwhile, it possess compared with
High tensile strength, elongation and mechanical strength, elasticity is strong, ageing-resistant, possesses cold-resistant, resistant to elevated temperatures performance, improves its use
Life-span.
2nd, tire made from a kind of reclaimed rubber provided by the invention, its tire side are provided with wind-guiding block, between wind-guiding block
It provided with wind guide tank, can be acted on by wind-force, booster action is played to tire, reduce power consumption；Tire side face is provided with braking simultaneously
Decorative pattern, and decorative pattern is braked with the center line symmetrical setting of the tire side face, using the center line of the tire side face as boundary, homonymy
The braking decorative pattern Block direction it is consistent, and the guiding gutter is not orthogonal to the center line of the tire side face, makes braking decorative pattern
Flechette-type is integrally formed, therefore, is not only that tire provides good braking ability in motion, also improves good driven nature
Energy；In addition, the breaker slot set along the tire body axis is provided with positioned at the braking pattern block surface in outside, positioned at interior
The braking pattern block surface of side is provided with along the circumferentially disposed drag reduction groove of the tire body, is not only improved tire and is laterally hindered
Power, while reduce tire drag.
Brief description of the drawings
A kind of structure structural representation of Fig. 1 positions tire provided by the invention.
Embodiment
Below in conjunction with the drawings and specific embodiments, the present invention will be described in further detail.It should be appreciated that this place is retouched
The specific embodiment stated only to explain the present invention, is not intended to limit the present invention.
The present invention discloses a kind of reclaimed rubber.
Embodiment 1：
A kind of reclaimed rubber of present disclosure, include the material of following parts by weight：80 parts of waste tyre rubber powder, glass fibre
10 parts, 40 parts of nylon fiber, 3 parts of acroleic acid polyurethane, 4 parts of polyamide, 8 parts of styrenated phenol, 6 parts of 3- diphenylguanidine, polyphenyl
20 parts of vinyl, 20 parts of composition epoxy resin, 5 parts of resin acid, 5 parts of rosin acid anhydrides, 20 parts of carbon black, aromatic disulfides
5 parts, 5 parts of zinc salt.
As preferable, composition epoxy resin includes the material of following percentage by weight：Epoxy resin 60%, even benzene three
Phenol-divinyl benzene polycondensate：20%th, silica 6%, '-diphenylmethane diisocyanate 14%.
The preparation method of above-mentioned composition epoxy resin is：Above-mentioned epoxy resin is taken to be heated to 50 in vacuum reaction kettle
DEG C, stirred with 200r/min mixing speed, while silica is added with 3g/min speed, 1h is reacted,；Benzene three will be connected
Phenol-divinyl benzene polycondensate adds reactor and maintains the temperature at 60 DEG C, is stirred with 200r/min mixing speed, then
Above-mentioned '-diphenylmethane diisocyanate is added in reactor with 5g/min speed, and controls maximum temperature to be no more than 80 DEG C,
1h is reacted, insulation reaction 2h is made.
As preferable, aromatic disulfides are pentachlorothiophenol.
A kind of preparation method of above-mentioned reclaimed rubber is：Damaged tire tyre surface is crushed, and by sieving, magnetic separation
Journey, as preferable, sieving processing is carried out using 500 eye mesh screens, above-mentioned waste tyre rubber powder is made by sieving, magnetic separation, selected
The waste tyre rubber powder of mass parts in above-described embodiment mode, while according to the glass of above-described embodiment addition respective quality number
Fiber, nylon fiber, acroleic acid polyurethane, polyamide, styrenated phenol, 3- diphenylguanidine, polystyrene resin, epoxy resin
Composition, resin acid, rosin acid anhydrides, carbon black, aromatic disulfides, zinc salt and water, above-mentioned material is inserted in digester
Row desulfurization process, material is constantly stirred, while be heated to 250 DEG C, when pressure reaches 1.5MPa, stop adding
Heat, after standing 6 minutes, exhaust pressure relief discharging, complete desulfurization operations.Slightly refined by extraction, rubber mixing machine again, scrape refining, refining, filtering
The step of, finally shaping obtains product.
Embodiment 2：
A kind of reclaimed rubber of present disclosure, include the material of following parts by weight:100 parts of waste tyre rubber powder, glass fibers
Dimension 20 parts, 80 parts of nylon fiber, 7 parts of acroleic acid polyurethane, 8 parts of polyamide, 12 parts of styrenated phenol, 10 parts of 3- diphenylguanidine,
30 parts of polystyrene resin, 25 parts of composition epoxy resin, 6 parts of resin acid, 6 parts of rosin acid anhydrides, 25 parts of carbon black, the sulphur of aromatic series two
7 parts of compound, 8 parts of zinc salt part.
As preferable, composition epoxy resin includes the material of following percentage by weight：Epoxy resin 10%, even benzene three
Phenol-divinyl benzene polycondensate：60%th, silica 5%, '-diphenylmethane diisocyanate 25%.As preferable, fragrance
Race's disulphide is the mixture of zinc salt of pentachlorothiophenol and thionaphthol, as it is further preferred that zinc salt of pentachlorothiophenol and naphthalene sulphur
The mass ratio of phenol is 6：4.
The preparation method of above-mentioned composition epoxy resin is：Above-mentioned epoxy resin is taken to be heated to 80 in vacuum reaction kettle
DEG C, stirred with 400r/min mixing speed, while silica is added with 6g/min speed, 3h is reacted,；Benzene three will be connected
Phenol-divinyl benzene polycondensate adds reactor and maintains the temperature at 80 DEG C, is stirred with 400r/min mixing speed, then
Above-mentioned '-diphenylmethane diisocyanate is added in reactor with 20g/min speed, and controls maximum temperature to be no more than 80 DEG C,
3h is reacted, insulation reaction 4h is made.
A kind of preparation method of above-mentioned reclaimed rubber is：Damaged tire tyre surface is crushed, and by sieving, magnetic separation
Journey, as preferable, sieving processing is carried out using 600 eye mesh screens, above-mentioned waste tyre rubber powder is made by sieving, magnetic separation, selected
The waste tyre rubber powder of mass parts in above-described embodiment mode, while according to the glass of above-described embodiment addition respective quality number
Fiber, nylon fiber, acroleic acid polyurethane, polyamide, styrenated phenol, 3- diphenylguanidine, polystyrene resin, epoxy resin
Composition, resin acid, rosin acid anhydrides, carbon black, aromatic disulfides, zinc salt and water, above-mentioned material is inserted in digester
Row desulfurization process, material is constantly stirred, while be heated to 300 DEG C, when pressure reaches 2.9MPa, stop adding
Heat, after standing 12 minutes, exhaust pressure relief discharging, complete desulfurization operations.Slightly refined by extraction, rubber mixing machine again, scrape refining, refining, mistake
The step of filter, finally shaping obtain product.
Embodiment 3：
A kind of reclaimed rubber of present disclosure, include the material of following parts by weight:90 parts of waste tyre rubber powder, glass fibre
15 parts, 60 parts of nylon fiber, 5 parts of acroleic acid polyurethane, polyamide 6 part, 10 parts of styrenated phenol, 8 parts of 3- diphenylguanidine, polyphenyl
25 parts of vinyl, 22 parts of composition epoxy resin, 5 parts of resin acid, 5 parts of rosin acid anhydrides, 22 parts of carbon black, aromatic disulfides
6 parts, 7 parts of zinc salt part.
As preferable, composition epoxy resin includes the material of following percentage by weight：Epoxy resin 30%, even benzene three
Phenol-divinyl benzene polycondensate：40%th, silica 1 0%, '-diphenylmethane diisocyanate 20%.
The preparation method of above-mentioned composition epoxy resin is：Above-mentioned epoxy resin is taken to be heated to 70 in vacuum reaction kettle
DEG C, stirred with 300r/min mixing speed, while silica is added with 4g/min speed, 2h is reacted,；Benzene three will be connected
Phenol-divinyl benzene polycondensate adds reactor and maintains the temperature at 70 DEG C, is stirred with 300r/min mixing speed, then
Above-mentioned '-diphenylmethane diisocyanate is added in reactor with 14g/min speed, and controls maximum temperature to be no more than 80 DEG C,
2h is reacted, insulation reaction 3h is made.
As preferable, aromatic disulfides are zinc salt of pentachlorothiophenol.
A kind of preparation method of above-mentioned reclaimed rubber is：Damaged tire tyre surface is crushed, and by sieving, magnetic separation
Journey, as preferable, sieving processing is carried out using 600 eye mesh screens, above-mentioned waste tyre rubber powder is made by sieving, magnetic separation, selected
The waste tyre rubber powder of mass parts in above-described embodiment mode, while according to the glass of above-described embodiment addition respective quality number
Fiber, nylon fiber, acroleic acid polyurethane, polyamide, styrenated phenol, 3- diphenylguanidine, polystyrene resin, epoxy resin
Composition, resin acid, rosin acid anhydrides, carbon black, aromatic disulfides, zinc salt and water, above-mentioned material is inserted in digester
Row desulfurization process, material is constantly stirred, while be heated to 275 DEG C, when pressure reaches 2.4MPa, stop adding
Heat, it is quiet
After putting 10 minutes, exhaust pressure relief discharging, desulfurization operations are completed.Again by extraction, rubber mixing machine slightly refine, scrape refining,
Refining, the step of filtering, finally shaping obtains product.
Table 1 schematically shows embodiment 1 to the performance for implementing different reclaimed rubbers again in 3.
Therefore, a kind of reclaimed rubber provided by the invention, processing characteristics is good, no rubber taste, environmental protection and energy saving, meanwhile, it has
Standby higher tensile strength, tearing strength, elongation, hardness, elasticity is strong, ageing-resistant, possesses cold-resistant, resistant to elevated temperatures performance, carries
Its high service life.
As shown in figure 1, invention further discloses using tire made from above-mentioned reclaimed rubber.
As shown in figure 1, tire made from the above-mentioned reclaimed rubber of the use of present disclosure, including tire body 1, tire sheet
Body 1 includes two tire sides 11 and the tire side face 12 between two tire sides 11.
As shown in figure 1, it is carved with wind-guiding block 111, wind-guiding block 111 and tire at least one tire side 11 of tire body 1
Body 1 is integral.As preferable, in a preferred embodiment of the invention, in the tire side 11 of the both sides of tire body 1
Wind-guiding block 111 is distributed with, wind-guiding block 111 is uniformly distributed, and wind guide tank 112 is formed between adjacent two wind-guidings block 111, adjacent two lead
The distance between pomphus 111 is 3mm-5mm, in this embodiment of the present invention, as preferred embodiment, and adjacent two wind-guiding
The distance between block 111 is 4mm, without with sufficient amount of wind guide tank 112, while can ensure wind and each wind guide tank
112 faying face, wind-force boosting power is improved, effectively utilizes natural energy resources.As it is further preferred that wind-guiding block 111 along tire
The section triangle at a right angle of plane where side 11, and be non-right-isosceles triangle, the wind-guiding block of right triangular shape
111 wherein long right-angle side is located on the edge of tire side 11 of tire body 1, i.e., positioned at the tire side 11 of tire body 1 with
The junction of tire side face 12, triangle base and the short right-angle side of two neighboring wind-guiding block 111 form above-mentioned wind guide tank 112.
As still more preferably, the triangle base of the wind-guiding block 111 of right triangular shape is arc-shaped side, base arcuate edge design,
Streamline sense is improved, is easy to wind-force to assemble, improves wind-force boosting power, as still further preferably, the side wall of wind guide tank 112 is wind-guiding
Plane where the side of the triangle base of block 111 has angle with the planar shaped where tire side 11, and angular range is
30 ° -45 °, in this embodiment of the present invention, in order to preferably utilize wind-force, the utilization rate of boosting power is improved, its angle is adopted
With 35 °, i.e., the side wall of wind guide tank 112 is the side of the triangle base of wind-guiding block 111 without wall height.
As shown in figure 1, tire side face 12 is provided with braking pattern block 121, as preferable, in this embodiment party of the present invention
In formula, there are 4 rings to brake pattern block 121 on tire side face 12, braking pattern block 121 is symmetrically set with the center line of tire side face 12
Put, the braking pattern block 121 on each ring is uniformly distributed, and the distance on each ring between adjacent two brakings pattern block 121 is 2mm-
5mm, in this embodiment of the present invention, as preferred embodiment, on each ring between adjacent two brakings pattern block 121
Distance be 3mm, without enough playing braking action, while inclusion particles can be prevented to be embedded, and therefore, adjacent two brake on same ring
Guiding gutter 122 is formed between pattern block 121, guiding gutter 122 is connected with wind guide tank 112, not only possesses drain function, while can
The boosting power of wind is more utilized, saves the energy.Meanwhile the distance between braking pattern block 121 is equal per ring, adjacent two rings braking flower
Distance between line block 121 is 3mm-5mm, in this embodiment of the present invention, as preferred embodiment, and adjacent two rings braking
Distance between pattern block 121 is 4mm, therefore, annular groove 123, annular groove 123 is formed between adjacent two rings pattern block 121
It is connected with guiding gutter 122, therefore not only acts as drainage, while reduce rolling resistance, improves lateral resistance.As preferred
, using the center line of tire side face 12 as boundary, the direction of braking pattern block 121 of center line homonymy is consistent, and guiding gutter 122 does not hang down
Directly in the center line of tire side face 12, while guiding gutter 122 is consistent with the direction of wind guide tank 112, therefore, on whole tire side face 12
Braking pattern block 121 into flechette-type, and the direction of arrow is consistent with tire rolling direction, when tire is run, is favorably improved wheel
The motive force on tire surface, therefore, driveability can be improved.
As still more preferably, in a preferred embodiment of the invention, guiding gutter 122, wind guide tank 112 and annular
The depth of groove 123 is 5mm-10mm, and in a preferred embodiment of the invention, its depth selection 8mm.
As still more preferably, it is provided with positioned at two rings braking pattern block 121 surface in outside along tire body 1 axis
The breaker slot 1211 of setting, it is provided with positioned at two rings braking pattern block 121 surface of inner side along the circumferentially disposed drag reduction of tire body 1
Groove 1212, therefore, tire lateral resistance is not only improved, while reduce tire drag.
The preferred embodiments of the present invention have shown and described in described above, as before, it should be understood that the present invention is not limited to
Form disclosed herein, the exclusion to other embodiment is not to be taken as, and can be used for various other combinations, modification and ring
Border, and can be modified in this paper invented the scope of the idea by the technology or knowledge of above-mentioned teaching or association area.And this
The change and change that field personnel are carried out do not depart from the spirit and scope of the present invention, then all should be in appended claims of the present invention
Protection domain in.
Claims (7)
1. one kind utilizes tire made from reclaimed rubber, the reclaimed rubber, include the material of following parts by weight:
The aromatic series monosulfide is a kind of in pentachlorothiophenol, zinc salt of pentachlorothiophenol or thionaphthol or any number of mixture；
The composition epoxy resin includes the material of following percentage by weight：
The tire includes tire body (1), and the tire body (1) includes two tire sides (11) and positioned at two tire
Tire side face (12) between side (11), it is characterised in that wind-guiding block is distributed with least one tire side (11)
(111) wind guide tank (112), is formed between adjacent two wind-guidings block (111)；The tire side face (12) is provided with polycyclic braking decorative pattern
Block (121), the braking pattern block (121) is with the center line symmetrical setting of the tire side face (12), adjacent two on same ring
Guiding gutter (122) is formed between the braking pattern block (121), the wind guide tank (112) is connected with the guiding gutter (122).
A kind of 2. tire according to claim 1, it is characterised in that the section triangle at a right angle of the wind-guiding block (111)
Shape, a wherein right-angle side for the right angled triangle are located on tire side (11) edge of the tire body (1), and adjacent two
The triangle base of the individual wind-guiding block (111) forms the wind guide tank (112) with right-angle side.
3. a kind of tire according to claim 2, it is characterised in that the wind-guiding block (111) of the right triangular shape
Triangle base is curved.
4. a kind of tire according to claim 3, it is characterised in that where the side side wall of the wind guide tank (112)
Plane has angle with the planar shaped where the tire side (11), the opposite side side wall of the wind guide tank (112) perpendicular to
Plane where the tire side (11).
5. a kind of tire according to claim 4, it is characterised in that wind guide tank (112) side wall is the wind-guiding block
(111) plane where the side of triangle base has angle with the planar shaped where the tire side (11), described
Angular range is 30 ° -45 °.
A kind of 6. tire according to claim 1, it is characterised in that including braking pattern block (121) described at least two rings,
And the number of rings of the braking pattern block (121) is even number, and an annular groove is formed between pattern block (121) described in adjacent two ring
(123)；Using the center line of the tire side face (12) as boundary, braking pattern block (121) direction of homonymy is consistent and described
Guiding gutter (122) is not orthogonal to the center line of the tire side face (12), the guiding gutter (122) and the wind guide tank (112)
Direction is consistent.
A kind of 7. tire according to claim 6, it is characterised in that braking pattern block (121) table positioned at outside
Face is provided with the breaker slot (1211) set along the tire body (1) axis, braking pattern block (121) table positioned at inner side
Face is provided with along the circumferentially disposed drag reduction groove (1212) of the tire body (1).