CN106117635A - A kind of lining of stabiliser bar - Google Patents
A kind of lining of stabiliser bar Download PDFInfo
- Publication number
- CN106117635A CN106117635A CN201610463527.7A CN201610463527A CN106117635A CN 106117635 A CN106117635 A CN 106117635A CN 201610463527 A CN201610463527 A CN 201610463527A CN 106117635 A CN106117635 A CN 106117635A
- Authority
- CN
- China
- Prior art keywords
- parts
- lining
- stabiliser bar
- time
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of lining of stabiliser bar, relate to auto parts machinery processing technical field, it is characterized in that: be made up of the material of following weight portion, natural gum 21.5 parts, reclaimed rubber 3.7 parts, zinc oxide 1.3 parts, stearic acid 0.5 part, 0.4 part of paraffin, microwax 0.35 part, antioxidant 4010 0.5 part, anti-aging agent RD 0.5 part, Vulcanization accelerator TMTD 0.03 part, accelerant CZ 0.25 part, 0.5 part of sulfur, calcium carbonate 3.8 parts, N550 white carbon black 10 parts, N330 white carbon black 7.5 parts, aromatic naphtha 3.6 parts, paraffin oil 300 2.7 parts.The inventive method rationally, reasonable mixture ratio antidetonation, wear-resisting, resistance to compression, service life long.
Description
Technical field:
The present invention relates to auto parts machinery processing technical field, be specifically related to the lining of a kind of stabiliser bar.
Background technology:
The full name of stabiliser bar is " QS ", also referred to as torsion-bar spring, English name Torsion-Bar
Spring, is a kind of auxiliary elastic element in automotive suspension.
Prevent vehicle body from excessive horizontal inclination occurring when turning.Purpose is to prevent automobile sideways overturning and improve smooth-going
Property.The torsion-bar spring that QS spring steel is made, shape in " U " shape, the horizontal front-end and back-end at automobile.Shaft
Middle part, hinged with vehicle frame with sleeve, the two ends of bar be separately fixed at left and right hang lower trailing arm or amortisseur traveller on.
When vehicle body is the most for vertical movement, both sides Suspension Deformation is equal, the suspension on both sides moves up and down simultaneously, the most surely
Fixed pole is freely rotatable in sleeve, and QS is inoperative.When vehicle is when turning, the strength born due to outer side mounting
Relatively big, both sides Suspension Deformation, vehicle body shifts near spring fastening for road-bank elevation, the side of vehicle frame, being somebody's turn to do of stabiliser bar
Side end upwards moves with respect to vehicle frame, and the opposite side of vehicle frame is away from spring fastening, and the end of corresponding stabiliser bar is the most relative
In vehicle frame to moving down, but when vehicle body and vehicle frame tilt, the middle part of QS there is no relative motion for vehicle frame.So
When body sway, the longitudinal component on stabiliser bar both sides deflects to different directions, and then stabiliser bar is just twisted.Elastic stablizes
The produced moment of resistance reversed of bar has prevented one from the deformation of bearing spring, thus reduces lateral inclination and the lateral angle of vehicle body
Vibration, thus improve vehicle run stability.
The lining of stabiliser bar is protection stabiliser bar, make parts of what stabiliser bar connected, and the lining that typically material is made
The situations such as set often cannot bear the lasting work of suspension and the pressure born of suspension, the most cracking, degumming, hold
Easily cause problem and the harm of many.
Summary of the invention:
The technical problem to be solved is to overcome existing technological deficiency to provide a kind of method reasonable, than rationally
Antidetonation, wear-resisting, resistance to compression, the lining of a kind of stabiliser bar of length in service life.
The technical problem to be solved uses following technical scheme to realize:
A kind of lining of stabiliser bar, it is characterised in that: it is made up of the material of following weight portion,
Natural gum 21.5 parts, reclaimed rubber 3.7 parts, zinc oxide 1.3 parts, stearic acid 0.5 part, 0.4 part of paraffin, microwax 0.35
Part, antioxidant 4010 0.5 part, anti-aging agent RD 0.5 part, Vulcanization accelerator TMTD 0.03 part, accelerant CZ 0.25 part, 0.5 part of sulfur, carbon
Acid calcium 3.8 parts, N550 white carbon black 10 parts, N330 white carbon black 7.5 parts, aromatic naphtha 3.6 parts, paraffin oil 3002.7 parts；
Including following preparation process,
Above-mentioned material is sent into and is carried out in rubber mixing machine refining glue by I, and glue furnacing temperature controls at 75-95 DEG C, and the time of refining glue is
20-30 minute；
After II refining glue completes, take out sizing material, place in room temperature, dry environment 30-38 hour, then carry out twice
Sulfidation, primary vulcanization temperature controls at 150-165 DEG C, and the time is 20-28 minute, and second time sulfuration is for 205-215 DEG C
Cure time is 25-35 minute；
III will complete in II after material put into machine-shaping in former.
The invention have the benefit that product is cold-resistant, resistance to ozone, heat-proof aging, material rebounds amount high, tearing strength is high,
Resistance to compression, service life are long.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, enter below
One step illustrates the present invention.
A kind of lining of stabiliser bar, it is characterised in that: it is made up of the material of following weight portion,
Natural gum 21.5 parts, reclaimed rubber 3.7 parts, zinc oxide 1.3 parts, stearic acid 0.5 part, 0.4 part of paraffin, microwax 0.35
Part, antioxidant 4010 0.5 part, anti-aging agent RD 0.5 part, Vulcanization accelerator TMTD 0.03 part, accelerant CZ 0.25 part, 0.5 part of sulfur, carbon
Acid calcium 3.8 parts, N550 white carbon black 10 parts, N330 white carbon black 7.5 parts, aromatic naphtha 3.6 parts, paraffin oil 3002.7 parts；
Including following preparation process,
Above-mentioned material is sent into and is carried out in rubber mixing machine refining glue by I, and glue furnacing temperature controls at 75-95 DEG C, and the time of refining glue is
20-30 minute；
After II refining glue completes, take out sizing material, place in room temperature, dry environment 30-38 hour, then carry out twice
Sulfidation, primary vulcanization temperature controls at 150-165 DEG C, and the time is 20-28 minute, and second time sulfuration is for 205-215 DEG C
Cure time is 25-35 minute；
III will complete in II after material put into machine-shaping in former.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.The technology of the industry
Personnel, it should be appreciated that the present invention is not restricted to the described embodiments, simply illustrating this described in above-described embodiment and description
The principle of invention, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, and these become
Change and improvement both falls within scope of the claimed invention.Claimed scope by appending claims and
Equivalent defines.
Claims (2)
1. the lining of a stabiliser bar, it is characterised in that: it is made up of the material of following weight portion,
Natural gum 21.5 parts, reclaimed rubber 3.7 parts, zinc oxide 1.3 parts, stearic acid 0.5 part, 0.4 part of paraffin, microwax 0.35 part,
Antioxidant 4010 0.5 part, anti-aging agent RD 0.5 part, Vulcanization accelerator TMTD 0.03 part, accelerant CZ 0.25 part, 0.5 part of sulfur, carbonic acid
Calcium 3.8 parts, N550 white carbon black 10 parts, N330 white carbon black 7.5 parts, aromatic naphtha 3.6 parts, paraffin oil 3002.7 parts.
The lining of a kind of stabiliser bar the most according to claim 1, it is characterised in that: include following preparation process,
I will carry out refining glue in above-mentioned material feeding rubber mixing machine, and glue furnacing temperature controls at 75-95 DEG C, and the time of refining glue is 20-30
Minute；
After II refining glue completes, take out sizing material, place in room temperature, dry environment 30-38 hour, then carry out twice sulfuration
Process, primary vulcanization temperature controls at 150-165 DEG C, and the time is 20-28 minute, and second time sulfuration is 205-215 DEG C of sulfuration
Time is 25-35 minute；
III will complete in II after material put into machine-shaping in former.