CN106116671A - A kind of energy-saving brick for garden landscape and preparation method thereof - Google Patents
A kind of energy-saving brick for garden landscape and preparation method thereof Download PDFInfo
- Publication number
- CN106116671A CN106116671A CN201610475701.XA CN201610475701A CN106116671A CN 106116671 A CN106116671 A CN 106116671A CN 201610475701 A CN201610475701 A CN 201610475701A CN 106116671 A CN106116671 A CN 106116671A
- Authority
- CN
- China
- Prior art keywords
- parts
- energy
- brick
- saving brick
- straw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of energy-saving brick for garden landscape and preparation method thereof, relate to garden equipment field, a kind of energy-saving brick for garden landscape, in parts by mass, described energy-saving brick includes clay 20 30 parts, mica powder 5 10 parts, light filler 10 15 parts, straw coated particle 5 10 parts, attapulgite 5 10 parts, binding agent 35 parts, Kaolin 5 10 parts, bentonite 5 10 parts, cement 15 20 parts, 0.5 2 parts of firming agent, use technical scheme, preparation process is reasonable, convenient to operate, production cost is low be easy to promote while, the energy-saving brick produced has light weight, insulation, waterproof, antidetonation, durable advantage, and good looking appearance.
Description
Technical field
The present invention relates to garden equipment field, be specifically related to a kind of energy-saving brick for garden landscape and preparation method thereof.
Background technology
After clay brick disabling, though walling has material light and heat-insulation and heat-preservation preferably air entraining cement building block, but investment big and
Being difficult to popularize, particularly material pineization, hanging easily takes off, and does exterior wall the most permeable, and intensity is low and fail-safe is poor, current cement porous
Brick only with cement and the broken material mixing manufacture such as sandstone material or ore deposit quarrel, either sandstone material brick, flyash brick or metallic ore quarrel powder
Brick and colliery wastes brick, all do not have light heat insulation material to mix preparation and make, and not only brick body is the heaviest, and easy to be permeable diathermanous, easy delamination and broken
Damage, the most durable, cost is high, long in time limit, and fragment of brick is as the important composition part of garden landscape, directly influences the cost in gardens
With attractive in appearance, garden landscape is played very important effect.
Wherein, air entraining cement brick is with stone powder and flyash as major ingredient, and cement is that gelating material foaming forms, so brick body is more loose
Changing, coal ash lightweight brick is with flyash as major ingredient and magnesium oxide is as gelating material, but the magnesite products such as magnesium oxide easily return halogen, and country is
Order within a certain time, and cost is high, later stage perishable pineization.
Patent No. CN 103332888 A is specifically related to a kind of light energy saving brick, and this light energy saving brick is by following material mixing
Make: gelating material 20 parts, main ballast 50 parts to 70 parts, light filler 10 parts to 20 parts, deodorization auxiliary agent 0.1 part-0.2 part, should
Although technical scheme adds the light material of agriculture and industry waste, after the techniques such as deodorization, make product, while exploitation new resources
Reduction cost, but its insulation, waterproof, antidetonation, durable deficiency.
Patent No. CN 105418016 A relates to honeycomb energy-saving brick and manufacture method thereof.This honeycomb energy-saving brick is mainly by rock wool
Comb core and these two parts of concrete net shelf structure composition, rock wool comb core is made up of granular rock wool, and concrete network frame is tied
Structure is made up of concrete mortar.By the making of rock wool comb core, the getting the raw materials ready and honeycomb energy-saving brick of concrete net shelf structure
The steps such as molding complete the manufacture of this material.Although the honeycomb energy-saving brick heat preservation and energy conservation effects that this technical scheme is produced is good, but
Production cost is high, is unfavorable for promoting.
Accordingly, it would be desirable to design a kind of energy-saving brick for garden landscape that can solve the problem that problem above and preparation side thereof
Method.
Summary of the invention
Problem to be solved by this invention is to provide a kind of energy-saving brick for garden landscape and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of energy-saving brick for garden landscape, in parts by mass, described energy-saving brick includes clay 20-30 part, mica powder 5-10
Part, light filler 10-15 part, straw coated particle 5-10 part, attapulgite 5-10 part, binding agent 3-5 part, Kaolin 5-10
Part, bentonite 5-10 part, cement 15-20 part, firming agent 0.5-2 part.
Preferably, in parts by mass, described energy-saving brick includes clay 25 parts, mica powder 8 parts, light filler 12 parts, straw
Stalk coated particle 8 parts, attapulgite 8 parts, binding agent 4 parts, Kaolin 7 parts, bentonite 8 parts, cement 17 parts, 1 part of firming agent.
Preferably, described straw coated particle is prepared by the raw material of following weight portion: kieselguhr 25-35 part, straw
Powder 20-30 part, waterglass 15-25 part, carboxymethyl cellulose 1-2 part, clay 3-5 part.
Preferably, the preparation process of described straw coated particle is: dried for kieselguhr and carboxymethyl cellulose are added
In high-speed mixer, at 110-120 DEG C, stir mixing 20-30min with the speed of 500-800rpm, add waterglass and continue
After continuous stirring 10-15min, be subsequently adding plant straw powder, clay is blended 5-10min with the speed of 1000-1500rpm, dries
Sending into pelletize in comminutor after Gan, size controlling, at 2-4mm, obtains straw coated particle.
Preferably, described light filler is agar slag or haydite.
A kind of preparation method of the energy-saving brick for garden landscape, described preparation method specifically includes following steps:
A. prepared by raw material, weighs clay 20-30 part, mica powder 5-10 part, light filler 10-15 part, Straw bale by mass parts
Cover granule 5-10 part, attapulgite 5-10 part, binding agent 3-5 part, Kaolin 5-10 part, bentonite 5-10 part, cement 15-20
Part, firming agent 0.5-2 part；
B. being crushed to particle diameter in clay, attapulgite, Kaolin, bentonite being sent into high speed centrifugation jet mill is 48 μm,
Prepare mixed powder；
C. mica powder, light filler, straw coated particle, attapulgite, binding agent, cement, firming agent are sufficiently mixed, and
Feeding blender is stirred, and prepares mixed powder；
D., after the mixed powder that step b and step c prepare being mixed to get homogeneous mixture, add and account for described homogeneous mixture matter
The water of amount 10% is stirred, and mixing time is 30-60min, obtains mixed slurry；
E. the described mixed slurry obtained is put into vibration moulding in mould, stands 3h, the demoulding, obtain adobe, then stand foster
Protect 2 days；
F. described adobe is first dried at 450 DEG C 2h, then by vacuum absorber, described adobe is put on backing plate, will
The described adobe being placed on described backing plate is burnt with the temperature of 1200 DEG C in sending into roller way kiln together with described backing plate
System, fires 1h, prepares the fragment of brick of molding；
G. the fragment of brick of molding is sent into vaporium and carry out maintenance 7h-8h at a temperature of 80 DEG C-100 DEG C；
H. the fragment of brick after maintenance is continued dried, then put storage in storage.
Using technical scheme, preparation process is reasonable, it is simple to operation, production cost is low be easy to promote while,
The energy-saving brick produced has light weight, insulation, waterproof, antidetonation, durable advantage, and good looking appearance.
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and be easy to understand with effect, below in conjunction with
Detailed description of the invention, is expanded on further the present invention.
Embodiment 1:
A kind of energy-saving brick for garden landscape, in parts by mass, described energy-saving brick includes clay 20 parts, mica powder 5 parts, lightweight
Inserts 10 parts, straw coated particle 5 parts, attapulgite 5 parts, binding agent 3 parts, Kaolin 5 parts, bentonite 5 parts, cement 15
Part, 0.5 part of firming agent.
Wherein, described straw coated particle is prepared by the raw material of following weight portion: kieselguhr 25-35 part, plant straw powder
20-30 part, waterglass 15-25 part, carboxymethyl cellulose 1-2 part, clay 3-5 part.
Wherein, the preparation process of described straw coated particle is: dried for kieselguhr and carboxymethyl cellulose are added height
In speed mixer, at 110 DEG C, stir mixing 20min with the speed of 500rpm, add waterglass and continue stirring 10min
After, it is subsequently adding plant straw powder, clay is blended 5min with the speed of 1000rpm, after drying, sends into pelletize in comminutor, grain
Footpath controls at 2mm, obtains straw coated particle.
Wherein, described light filler is haydite.
A kind of preparation method of the energy-saving brick for garden landscape, described preparation method specifically includes following steps:
A. prepared by raw material, by mass parts weigh clay 20 parts, mica powder 5 parts, light filler 10 parts, straw coated particle 5 parts,
Attapulgite 5 parts, binding agent 3 parts, Kaolin 5 parts, bentonite 5 parts, cement 15 parts, 0.5 part of firming agent；
B. being crushed to particle diameter in clay, attapulgite, Kaolin, bentonite being sent into high speed centrifugation jet mill is 48 μm,
Prepare mixed powder；
C. mica powder, light filler, straw coated particle, attapulgite, binding agent, cement, firming agent are sufficiently mixed, and
Feeding blender is stirred, and prepares mixed powder；
D., after the mixed powder that step b and step c prepare being mixed to get homogeneous mixture, add and account for described homogeneous mixture matter
The water of amount 10% is stirred, and mixing time is 30min, obtains mixed slurry；
E. the described mixed slurry obtained is put into vibration moulding in mould, stands 3h, the demoulding, obtain adobe, then stand foster
Protect 2 days；
F. described adobe is first dried at 450 DEG C 2h, then by vacuum absorber, described adobe is put on backing plate, will
The described adobe being placed on described backing plate is burnt with the temperature of 1200 DEG C in sending into roller way kiln together with described backing plate
System, fires 1h, prepares the fragment of brick of molding；
G. the fragment of brick of molding is sent into vaporium and carry out maintenance 7h at a temperature of 80 DEG C；
H. the fragment of brick after maintenance is continued dried, then put storage in storage.
Embodiment 2:
A kind of energy-saving brick for garden landscape, in parts by mass, described energy-saving brick includes clay 30 parts, mica powder 10 parts, light
Matter inserts 15 parts, straw coated particle 10 parts, attapulgite 10 parts, binding agent 5 parts, Kaolin 10 parts, bentonite 10 parts, water
20 parts of mud, 2 parts of firming agent.
Wherein, described straw coated particle is prepared by the raw material of following weight portion: 35 parts of kieselguhr, plant straw powder 30
Part, waterglass 25 parts, carboxymethyl cellulose 2 parts, clay 5 parts.
Wherein, the preparation process of described straw coated particle is: dried for kieselguhr and carboxymethyl cellulose are added height
In speed mixer, at 120 DEG C, stir mixing 30min with the speed of 800rpm, add waterglass and continue stirring 15min
After, it is subsequently adding plant straw powder, clay is blended 10min with the speed of 1500rpm, after drying, sends into pelletize in comminutor, grain
Footpath controls at 4mm, obtains straw coated particle.
Wherein, described light filler is agar slag.
A kind of preparation method of the energy-saving brick for garden landscape, described preparation method specifically includes following steps:
A. prepared by raw material, weighs clay 30 parts, mica powder 10 parts, light filler 15 parts, straw coated particle 10 by mass parts
Part, attapulgite 10 parts, binding agent 5 parts, Kaolin 10 parts, bentonite 10 parts, cement 20 parts, 2 parts of firming agent；
B. being crushed to particle diameter in clay, attapulgite, Kaolin, bentonite being sent into high speed centrifugation jet mill is 48 μm,
Prepare mixed powder；
C. mica powder, light filler, straw coated particle, attapulgite, binding agent, cement, firming agent are sufficiently mixed, and
Feeding blender is stirred, and prepares mixed powder；
D., after the mixed powder that step b and step c prepare being mixed to get homogeneous mixture, add and account for described homogeneous mixture matter
The water of amount 10% is stirred, and mixing time is 60min, obtains mixed slurry；
E. the described mixed slurry obtained is put into vibration moulding in mould, stands 3h, the demoulding, obtain adobe, then stand foster
Protect 2 days；
F. described adobe is first dried at 450 DEG C 2h, then by vacuum absorber, described adobe is put on backing plate, will
The described adobe being placed on described backing plate is burnt with the temperature of 1200 DEG C in sending into roller way kiln together with described backing plate
System, fires 1h, prepares the fragment of brick of molding；
G. the fragment of brick of molding is sent into vaporium and carry out maintenance 8h at a temperature of 100 DEG C；
H. the fragment of brick after maintenance is continued dried, then put storage in storage.
Embodiment 3: a kind of energy-saving brick for garden landscape, in parts by mass, described energy-saving brick includes clay 25 parts, cloud
Female 8 parts of powder, light filler 12 parts, straw coated particle 8 parts, attapulgite 8 parts, binding agent 4 parts, Kaolin 7 parts, bentonite
8 parts, cement 17 parts, 1 part of firming agent.
Wherein, described straw coated particle is prepared by the raw material of following weight portion: 30 parts of kieselguhr, plant straw powder 25
Part, waterglass 20 parts, carboxymethyl cellulose 1 part, clay 4 parts.
Wherein, the preparation process of described straw coated particle is: dried for kieselguhr and carboxymethyl cellulose are added height
In speed mixer, at 115 DEG C, stir mixing 25min with the speed of 600rpm, add waterglass and continue stirring 13min
After, it is subsequently adding plant straw powder, clay is blended 8min with the speed of 1300rpm, after drying, sends into pelletize in comminutor, grain
Footpath controls at 3mm, obtains straw coated particle.
Wherein, described light filler is haydite.
A kind of preparation method of the energy-saving brick for garden landscape, described preparation method specifically includes following steps:
A. prepared by raw material, by mass parts weigh clay 25 parts, mica powder 8 parts, light filler 12 parts, straw coated particle 8 parts,
Attapulgite 8 parts, binding agent 4 parts, Kaolin 7 parts, bentonite 8 parts, cement 17 parts, 1 part of firming agent；
B. being crushed to particle diameter in clay, attapulgite, Kaolin, bentonite being sent into high speed centrifugation jet mill is 48 μm,
Prepare mixed powder；
C. mica powder, light filler, straw coated particle, attapulgite, binding agent, cement, firming agent are sufficiently mixed, and
Feeding blender is stirred, and prepares mixed powder；
D., after the mixed powder that step b and step c prepare being mixed to get homogeneous mixture, add and account for described homogeneous mixture matter
The water of amount 10% is stirred, and mixing time is 40min, obtains mixed slurry；
E. the described mixed slurry obtained is put into vibration moulding in mould, stands 3h, the demoulding, obtain adobe, then stand foster
Protect 2 days；
F. described adobe is first dried at 450 DEG C 2h, then by vacuum absorber, described adobe is put on backing plate, will
The described adobe being placed on described backing plate is burnt with the temperature of 1200 DEG C in sending into roller way kiln together with described backing plate
System, fires 1h, prepares the fragment of brick of molding；
G. the fragment of brick of molding is sent into vaporium and carry out maintenance 7h at a temperature of 90 DEG C；
H. the fragment of brick after maintenance is continued dried, then put storage in storage.
Based on above-mentioned, using technical scheme, preparation process is reasonable, it is simple to operation, low being easy to pushes away production cost
While Guang, the energy-saving brick produced has light weight, insulation, waterproof, antidetonation, durable advantage, and good looking appearance.
Obviously the present invention implements and is not subject to the restrictions described above, as long as have employed method design and the skill of the present invention
The improvement of the various unsubstantialities that art scheme is carried out, or the most improved design by the present invention and technical scheme directly apply to it
Its occasion, all within protection scope of the present invention.
Claims (6)
1. the energy-saving brick for garden landscape, it is characterised in that in parts by mass, described energy-saving brick includes clay 20-30
Part, mica powder 5-10 part, light filler 10-15 part, straw coated particle 5-10 part, attapulgite 5-10 part, binding agent 3-5
Part, Kaolin 5-10 part, bentonite 5-10 part, cement 15-20 part, firming agent 0.5-2 part.
A kind of energy-saving brick for garden landscape the most according to claim 1, it is characterised in that: in parts by mass, described
Energy-saving brick includes clay 25 parts, mica powder 8 parts, light filler 12 parts, straw coated particle 8 parts, attapulgite 8 parts, bonding
Agent 4 parts, Kaolin 7 parts, bentonite 8 parts, cement 17 parts, 1 part of firming agent.
A kind of energy-saving brick for garden landscape the most according to claim 1, it is characterised in that: described straw coated particle
Prepared by the raw material of following weight portion: kieselguhr 25-35 part, plant straw powder 20-30 part, waterglass 15-25 part, carboxymethyl fibre
Dimension element 1-2 part, clay 3-5 part.
A kind of energy-saving brick for garden landscape the most according to claim 3, it is characterised in that: described straw coated particle
Preparation process be: by dried for kieselguhr with in carboxymethyl cellulose addition high-speed mixer, with 500-at 110-120 DEG C
The speed stirring mixing 20-30min of 800rpm, after adding waterglass continuation stirring 10-15min, is subsequently adding plant straw
Stalk powder, clay are blended 5-10min with the speed of 1000-1500rpm, send into pelletize in comminutor after drying, and size controlling is at 2-
4mm, obtains straw coated particle.
A kind of energy-saving brick for garden landscape the most according to claim 1, it is characterised in that: described light filler is
Agar slag or haydite.
6. the method for the energy-saving brick for garden landscape prepared described in claim 1-5 any one, it is characterised in that
Described preparation method specifically includes following steps:
A. prepared by raw material, weighs clay 20-30 part, mica powder 5-10 part, light filler 10-15 part, Straw bale by mass parts
Cover granule 5-10 part, attapulgite 5-10 part, binding agent 3-5 part, Kaolin 5-10 part, bentonite 5-10 part, cement 15-20
Part, firming agent 0.5-2 part；
B. being crushed to particle diameter in clay, attapulgite, Kaolin, bentonite being sent into high speed centrifugation jet mill is 48 μm,
Prepare mixed powder；
C. mica powder, light filler, straw coated particle, attapulgite, binding agent, cement, firming agent are sufficiently mixed, and
Feeding blender is stirred, and prepares mixed powder；
D., after the mixed powder that step b and step c prepare being mixed to get homogeneous mixture, add and account for described homogeneous mixture matter
The water of amount 10% is stirred, and mixing time is 30-60min, obtains mixed slurry；
E. the described mixed slurry obtained is put into vibration moulding in mould, stands 3h, the demoulding, obtain adobe, then stand foster
Protect 2 days；
F. described adobe is first dried at 450 DEG C 2h, then by vacuum absorber, described adobe is put on backing plate, will
The described adobe being placed on described backing plate is burnt with the temperature of 1200 DEG C in sending into roller way kiln together with described backing plate
System, fires 1h, prepares the fragment of brick of molding；
G. the fragment of brick of molding is sent into vaporium and carry out maintenance 7h-8h at a temperature of 80 DEG C-100 DEG C；
H. the fragment of brick after maintenance is continued dried, then put storage in storage.