CN106116334A - A kind of environmental protection flame retardant mortar - Google Patents
A kind of environmental protection flame retardant mortar Download PDFInfo
- Publication number
- CN106116334A CN106116334A CN201610453337.7A CN201610453337A CN106116334A CN 106116334 A CN106116334 A CN 106116334A CN 201610453337 A CN201610453337 A CN 201610453337A CN 106116334 A CN106116334 A CN 106116334A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- portland cement
- flame retardant
- mortar
- protection flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environmental protection flame retardant mortar, it is characterized in that, be made up of following raw material ratio by weight: portland cement 100 200, aluminum-spinel powder 40 60, bentonite 20 40, aluminum oxide clinker 40 50, asbestos fibre 20 30, redispersable latex powder 24, itaconic acid 35, boron nitride 24, calcium lignosulfonate 24, sodium hexameta phosphate 23；Starch ether 24, glutinous rice flour 35, water 100 150.The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, stirs described raw material ratio by weight, is eventually adding portland cement, and mix homogeneously makes product.Environmental protection of the present invention, good flame resistance, heat conductivity is low, and caking property is good, it is possible to meet the requirement of the performance indications of building industry mortar.
Description
Technical field
The present invention relates to building material field, particularly relate to a kind of environmental protection mortar.
Background technology
Concrete mortar is widely used in the engineerings such as bridge, building, power station, not only needs higher intensity, toughness
And stability requirement, and must have self certain water resistance, at northern area, in addition it is also necessary to possess cold-resistant freeze proof simultaneously
Performance.
Thermal insulation mortar is with various light materials for gathering materials, and with cement as cementitious matter, adds some property-modifying additives, warp
Stirring is mixed.It is mainly used in the insulation of external wall, there is the advantage such as easy construction, good endurance.
Summary of the invention
The present invention provides a kind of environmental protection flame retardant mortar, environmental protection, good flame resistance, and heat conductivity is low, and caking property is good, meets building
The requirement of the performance indications of industry mortar.
In order to achieve the above object, the present invention realizes by the following technical solutions:
A kind of environmental protection flame retardant mortar, it is characterised in that be made up of following raw material ratio by weight: portland cement 100-
200, aluminum-spinel powder 40-60, bentonite 20-40, aluminum oxide clinker 40-50, asbestos fibre 20-30, redispersable latex powder
2-4, itaconic acid 3-5, boron nitride 2-4, calcium lignosulfonate 2-4, sodium hexameta phosphate 2-3；Starch ether 2-4, glutinous rice flour 3-5, water
100-150。
The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, by described raw material by weight
Example stirs, and is eventually adding portland cement, and mix homogeneously makes product.
Compared with prior art, the invention has the beneficial effects as follows:
Environmental protection of the present invention, good flame resistance, heat conductivity is low, and caking property is good, it is possible to meet the performance indications of building industry mortar
Requirement.
Detailed description of the invention
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1
A kind of environmental protection flame retardant mortar, is made up of following raw material ratio by weight: portland cement 150, aluminum-spinel
Powder 50, bentonite 30, aluminum oxide clinker 45, asbestos fibre 25, redispersable latex powder 3, itaconic acid 4, boron nitride 3, sulfomethylated lignin
Acid calcium 3, sodium hexameta phosphate 2.5；Starch ether 3, glutinous rice flour 4, water 120.
The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, by described raw material by weight
Example stirs, and is eventually adding portland cement, and mix homogeneously makes product.
Embodiment 2
A kind of environmental protection flame retardant mortar, is made up of following raw material ratio by weight: portland cement 100, aluminum-spinel
Powder 40, bentonite 20, aluminum oxide clinker 40, asbestos fibre 30, redispersable latex powder 2, itaconic acid 5, boron nitride 4, sulfomethylated lignin
Acid calcium 3, sodium hexameta phosphate 3；Starch ether 4, glutinous rice flour 5, water 150.
The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, by described raw material by weight
Example stirs, and is eventually adding portland cement, and mix homogeneously makes product.
Embodiment 3
A kind of environmental protection flame retardant mortar, is made up of following raw material ratio by weight: portland cement 200, aluminum-spinel
Powder 60, bentonite 30, aluminum oxide clinker 50, asbestos fibre 25, redispersable latex powder 4, itaconic acid 4, boron nitride 3, sulfomethylated lignin
Acid calcium 4, sodium hexameta phosphate 3；Starch ether 3, glutinous rice flour 4, water 130.
The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, by described raw material by weight
Example stirs, and is eventually adding portland cement, and mix homogeneously makes product.
Embodiment 4
A kind of environmental protection flame retardant mortar, is made up of following raw material ratio by weight: portland cement 120, aluminum-spinel
Powder 50, bentonite 25, aluminum oxide clinker 45, asbestos fibre 22, redispersable latex powder 2, itaconic acid 3, boron nitride 4, sulfomethylated lignin
Acid calcium 4, sodium hexameta phosphate 2；Starch ether 4, glutinous rice flour 5, water 130.
The preparation method of described environmental protection flame retardant mortar, in addition to portland cement, by described raw material by weight
Example stirs, and is eventually adding portland cement, and mix homogeneously makes product.
The test index of products obtained therefrom is as follows:
Claims (1)
1. an environmental protection flame retardant mortar, it is characterised in that be made up of following raw material ratio by weight: portland cement 100-
200, aluminum-spinel powder 40-60, bentonite 20-40, aluminum oxide clinker 40-50, asbestos fibre 20-30, redispersable latex powder
2-4, itaconic acid 3-5, boron nitride 2-4, calcium lignosulfonate 2-4, sodium hexameta phosphate 2-3；Starch ether 2-4, glutinous rice flour 3-5, water
100-150。