CN106116152A - A kind of ceramic utensil glaze and preparation method thereof - Google Patents
A kind of ceramic utensil glaze and preparation method thereof Download PDFInfo
- Publication number
- CN106116152A CN106116152A CN201610498492.0A CN201610498492A CN106116152A CN 106116152 A CN106116152 A CN 106116152A CN 201610498492 A CN201610498492 A CN 201610498492A CN 106116152 A CN106116152 A CN 106116152A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- dolomite
- graphite
- lyt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ceramic utensil glaze, it is made up of according to the raw material of parts by weight following: dolomite 3 13 parts, 28 parts of zinc sulfate, 39 parts of magnesium sulfate, 17 parts of graphite, 5 15 parts of glass dust, 39 parts of modified verdelite powder, brium carbonate 28 parts, calcium oxide 4 12 parts, Cu-lyt. 2 12 parts, cobaltous acetate 2 14 parts.The present invention has the advantages such as structural strength is good and easy to process.
Description
Technical field
The present invention relates to ceramic field, particularly relate to a kind of ceramic utensil glaze and preparation method thereof.
Background technology
At present, along with the development of science and technology, the field such as pottery is also in fast development, and in the goods of pottery, and pottery
Glaze on pottery goods have important impact, directly felt pottery aesthetic measure, in the course of processing of tea set often
Need to sinter on tea set surface one layer of glaze, both reached effect attractive in appearance, have and can improve the structural strength of tea set but existing
Ceramic glaze because its course of processing is unreasonable or the problem such as material selection, cause the glaze on ceramic surface exist bubble or
The shortcomings such as low in glossiness, thus cause ceramic can not reach the demand of people.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of ceramic utensil glaze and system thereof
Preparation Method.
The present invention takes techniques below scheme to realize: a kind of ceramic utensil glaze, by following according to weight portion
The raw material composition of number: dolomite 3-13 part, zinc sulfate 2-8 part, magnesium sulfate 3-9 part, graphite 1-7 part, glass dust 5-15 part is modified
Tourmaline powder 3-9 part, brium carbonate 2-8 part, calcium oxide 4-12 part, Cu-lyt. 2-12 part, cobaltous acetate 2-14 part.
Above-mentioned a kind of ceramic utensil glaze, is made up of according to the raw material of parts by weight following: dolomite 3-11 part, sulfur
Acid zinc 2-6 part, magnesium sulfate 3-7 part, graphite 1-5 part, glass dust 5-12 part, modified verdelite powder 3-7 part, brium carbonate 2-6 part, oxygen
Change calcium 4-10 part, Cu-lyt. 2-10 part, cobaltous acetate 2-12 part.
Above-mentioned a kind of ceramic utensil glaze, is made up of according to the raw material of parts by weight following: dolomite 8 parts, sulphuric acid
5 parts of zinc, 6 parts of magnesium sulfate, 4 parts of graphite, 10 parts of glass dust, 6 parts of modified verdelite powder, brium carbonate 5 parts, calcium oxide 8 parts, protochloride
Copper 7 parts, cobaltous acetate 8 parts.
The preparation method of above-mentioned a kind of ceramic utensil glaze, comprises the steps of:
(1) choose the number of material in claim 3, dolomite, zinc sulfate, magnesium sulfate, graphite and glass dust are carried out powder
Broken process, grinding time is 20min, and the mesh screen being then passed to 200 mesh carries out screening process, obtains batch mixing A；
(2) modified verdelite powder, brium carbonate, calcium oxide, Cu-lyt. and cobaltous acetate are stirred so that it is sufficiently stir
Mix mixing, and sieved by the mesh screen of 300 mesh, obtain mixed material B；
(3) after batch mixing A and mixed material B being stirred together for, then by high-temperature heating, and heat time heating time is 30min, is then placed in cold
Water carries out the system of quenching, obtains frit；
(4) frit in step 3 is placed on grinding in ball grinder and becomes glaze slip, i.e. can get material requested.
The method have the advantages that the present invention has structural strength in sum good and easy to process etc. excellent
Point, can improve the structural strength of tea set further, and make it more aesthetically pleasing.
Detailed description of the invention
A kind of ceramic utensil glaze, is made up of according to the raw material of parts by weight following: dolomite 3-13 part, zinc sulfate 2-
8 parts, magnesium sulfate 3-9 part, graphite 1-7 part, glass dust 5-15 part, modified verdelite powder 3-9 part, brium carbonate 2-8 part, calcium oxide 4-
12 parts, Cu-lyt. 2-12 part, cobaltous acetate 2-14 part.
Above-mentioned a kind of ceramic utensil glaze, is made up of according to the raw material of parts by weight following: dolomite 3-11 part, sulfur
Acid zinc 2-6 part, magnesium sulfate 3-7 part, graphite 1-5 part, glass dust 5-12 part, modified verdelite powder 3-7 part, brium carbonate 2-6 part, oxygen
Change calcium 4-10 part, Cu-lyt. 2-10 part, cobaltous acetate 2-12 part.
Above-mentioned a kind of ceramic utensil glaze, is made up of according to the raw material of parts by weight following: dolomite 8 parts, sulphuric acid
5 parts of zinc, 6 parts of magnesium sulfate, 4 parts of graphite, 10 parts of glass dust, 6 parts of modified verdelite powder, brium carbonate 5 parts, calcium oxide 8 parts, protochloride
Copper 7 parts, cobaltous acetate 8 parts.
The preparation method of above-mentioned a kind of ceramic utensil glaze, comprises the steps of:
(1) choose the number of material in claim 3, dolomite, zinc sulfate, magnesium sulfate, graphite and glass dust are carried out powder
Broken process, grinding time is 20min, and the mesh screen being then passed to 200 mesh carries out screening process, obtains batch mixing A；
(2) modified verdelite powder, brium carbonate, calcium oxide, Cu-lyt. and cobaltous acetate are stirred so that it is sufficiently stir
Mix mixing, and sieved by the mesh screen of 300 mesh, obtain mixed material B；
(3) after batch mixing A and mixed material B being stirred together for, then by high-temperature heating, and heat time heating time is 30min, is then placed in cold
Water carries out the system of quenching, obtains frit；
(4) frit in step 3 is placed on grinding in ball grinder and becomes glaze slip, i.e. can get material requested.
The present invention has the advantages such as structural strength is good and easy to process, can improve the structural strength of tea set further,
And make it more aesthetically pleasing.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute
The equivalence change done or modification, in the range of being all included in present patent application.
Claims (4)
1. a ceramic utensil glaze, it is characterised in that be made up of according to the raw material of parts by weight following: dolomite 3-13
Part, zinc sulfate 2-8 part, magnesium sulfate 3-9 part, graphite 1-7 part, glass dust 5-15 part, modified verdelite powder 3-9 part, brium carbonate 2-8
Part, calcium oxide 4-12 part, Cu-lyt. 2-12 part, cobaltous acetate 2-14 part.
A kind of ceramic utensil glaze the most according to claim 1, it is characterised in that by following former according to parts by weight
Material composition: dolomite 3-11 part, zinc sulfate 2-6 part, magnesium sulfate 3-7 part, graphite 1-5 part, glass dust 5-12 part, modified verdelite
Powder 3-7 part, brium carbonate 2-6 part, calcium oxide 4-10 part, Cu-lyt. 2-10 part, cobaltous acetate 2-12 part.
A kind of ceramic utensil glaze the most according to claim 1, it is characterised in that by following former according to parts by weight
Material composition: dolomite 8 parts, 5 parts of zinc sulfate, 6 parts of magnesium sulfate, 4 parts of graphite, 10 parts of glass dust, 6 parts of modified verdelite powder, carbonic acid
Barium 5 parts, calcium oxide 8 parts, Cu-lyt. 7 parts, cobaltous acetate 8 parts.
The preparation method of a kind of ceramic utensil glaze the most according to claim 1, it is characterised in that by following steps group
Become:
(1) choose the number of material in claim 3, dolomite, zinc sulfate, magnesium sulfate, graphite and glass dust are carried out powder
Broken process, grinding time is 20min, and the mesh screen being then passed to 200 mesh carries out screening process, obtains batch mixing A；
(2) modified verdelite powder, brium carbonate, calcium oxide, Cu-lyt. and cobaltous acetate are stirred so that it is sufficiently stir
Mix mixing, and sieved by the mesh screen of 300 mesh, obtain mixed material B；
(3) after batch mixing A and mixed material B being stirred together for, then by high-temperature heating, and heat time heating time is 30min, is then placed in cold
Water carries out the system of quenching, obtains frit；
(4) frit in step 3 is placed on grinding in ball grinder and becomes glaze slip, i.e. can get material requested.