CN106115723A - 一种利用高炉渣制备含Al3+水玻璃的方法 - Google Patents

一种利用高炉渣制备含Al3+水玻璃的方法 Download PDF

Info

Publication number
CN106115723A
CN106115723A CN201610416411.8A CN201610416411A CN106115723A CN 106115723 A CN106115723 A CN 106115723A CN 201610416411 A CN201610416411 A CN 201610416411A CN 106115723 A CN106115723 A CN 106115723A
Authority
CN
China
Prior art keywords
blast furnace
furnace slag
waterglass
raw material
autoclave
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610416411.8A
Other languages
English (en)
Other versions
CN106115723B (zh
Inventor
李辽沙
尤润泽
林娜
申星梅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui University of Technology AHUT
Original Assignee
Anhui University of Technology AHUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui University of Technology AHUT filed Critical Anhui University of Technology AHUT
Priority to CN201610416411.8A priority Critical patent/CN106115723B/zh
Publication of CN106115723A publication Critical patent/CN106115723A/zh
Application granted granted Critical
Publication of CN106115723B publication Critical patent/CN106115723B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用高炉渣制备含Al3+水玻璃的方法，属于化工生产技术领域。该方法是以高炉渣为原料，将原料破碎、粉磨、过200目筛后置于高压反应釜中，以渣碱比1:(0.55‑1)的比例加入烧碱溶液，搅拌后置于电炉中加热至100‑180℃并在自生压力下产生水热反应；SiO2与烧碱反应进入溶液，经固液分离获得含少量Al3+(约w＝2％‑4％)水玻璃溶液。此方法不仅原料价格低廉，工艺简单，而且达到固废资源化利用的目的。

Description

一种利用高炉渣制备含Al3+水玻璃的方法
技术领域
本发明属于化工生产技术领域，具体涉及一种利用高炉渣制备含少量Al3+水玻璃的方法。
背景技术
水玻璃是由碱金属氧化物和二氧化硅结合而成的可溶性碱金属硅酸盐材料，是一种用途十分广泛的无机化工产品。水玻璃的生产有干法和湿法两种，其中干法是以石英石和碳酸钠或硫酸钠在1400-1500℃熔融反应制得；湿法是以石英石和烧碱为原料，在140-160℃，2-3个大气压条件下反应制得。CN103506213A公开了利用旋流器对铜硫尾矿进行分级等步骤，制取液体水玻璃产品；CN102583417A公开了一种利用盐酸酸浸煤矸石，再经过碱性水热反应得到水玻璃产品；CN102167342A公开了硼泥用蒸汽加热，固液分离，酸浸，碱热反应得到水玻璃产品；CN101456555公开了稻壳灰经碱洗后酸洗，再经二次活化得到高模数水玻璃和活性炭的方法；CN201010253539.X公开了一种将稻壳闷烧、炭化、活化制得煤气、高档活性炭、水玻璃和磷酸硅的方法。
高炉水淬渣是高炉熔渣用大量水淬冷后得到的以玻璃体为主的细粒水渣，其主要化学成分有：CaO、SiO2、Al2O3、MgO。经水淬冷所得到的高炉渣化学活性高，可以作为无机化工原料加以利用。目前，有研究人员采用酸解高炉水淬渣提取有价组分的方法制备精细化产品，不仅使高炉渣得到资源化利用，而且消除了高炉渣对环境的污染。然而，利用高炉渣作为硅源并结合碱溶水热联合消解高炉渣制备含Al3+水玻璃的方法未见报道。
发明内容
为克服现有技术的不足，本发明的目的在于提供一种用高炉渣制备含Al3+水玻璃的方法。
为了实现上述目的，本发明是通过以下技术方案予以实现的。
本发明提供了一种利用高炉渣制备含Al3+水玻璃的方法，该方法包括以下步骤：
(1)将高炉渣烘干、破碎、粉磨后，过200目筛，得高炉渣粉末；
(2)将步骤(1)得到的高炉渣粉末置于高压反应釜中，然后加入氢氧化钠溶液，搅拌得到碱渣混合物；
所述氢氧化钠和高炉渣粉末的碱渣质量比为0.55-1：1；
所述氢氧化钠溶液的浓度为2-4mol/L；
(3)将步骤(2)装有碱渣混合物的高压反应釜盖好后加热，温度控制在100-180℃，并在自生压力下反应4-8h，固液分离后所得滤液即为含Al3+水玻璃。
具体化学反应方程式为：
(mSiO2·nCaO·xAl2O3·yMgO)+2(m+x)NaOH→mNa2SiO3+nCa(OH)2↓+2xNaAlO2+yMgO↓+(m+x-n)H2O
本发明所使用的高炉渣的主要成分为：39.22wt％CaO，32.10wt％SiO2，16.41wt％Al2O3，7.93wt％MgO。化学式为(0.700CaO·0.535SiO2·0.161Al2O3·0.198MgO)。高炉渣中的SiO2含量占总组分的32％以上，为本发明制备含Al3+水玻璃提供了丰富的SiO2来源。
与现有技术相比，本发明具有以下技术效果：
1、通过碱溶水热联合消解高炉渣，使渣中SiO2组分进入溶液中，经固液分离制得含Al3+(约w＝2％-4％)水玻璃溶液。
2、本发明工艺成本低、操作简便，有效消除高炉渣对环境的污染的同时，又达到资源高附加值利用的目的。
具体实施方式
以下结合具体实施例详述本发明，但本发明不局限于下述实施例。
实施例1
将高炉渣烘干、破碎、粉磨后，过200目筛。取筛下物，称取14.968g置于高压反应釜中；称取烧碱试剂8.823g，加入80ml去离子水配制成溶液，将所述烧碱溶液加入高压反应釜中搅拌，然后在150℃加热炉中水热反应4h。固液分离后，所得滤液即为含Al3+(约w＝2％)水玻璃。
实施例2
将高炉渣烘干、破碎、粉磨后，过200目筛。取筛下物，称取15.367g置于高压反应釜中；称取烧碱试剂13.254g，加入80ml去离子水配制成溶液，将所述烧碱溶液加入高压反应釜中搅拌，然后在150℃加热炉中水热反应8h。固液分离后，所得滤液即为含Al3+(约w＝2％)水玻璃。
实施例3
将高炉渣烘干、破碎、粉磨后，过200目筛。取筛下物，称取14.582g置于高压反应釜中；称取烧碱试剂10.568g，加入80ml去离子水配制成溶液，将所述烧碱溶液加入高压反应釜中搅拌，然后在150℃加热炉中水热反应6h。固液分离后，所得滤液即为含Al3+(约w＝3％)水玻璃。

Claims (1)

1.一种利用高炉渣制备含Al3+水玻璃的方法，其特征在于，该方法包括以下步骤：
(1)将高炉渣烘干、破碎、粉磨后，过200目筛，得高炉渣粉末；
(2)将步骤(1)得到的高炉渣粉末置于高压反应釜中，然后加入氢氧化钠溶液，搅拌得到碱渣混合物；
所述氢氧化钠和高炉渣粉末的碱渣质量比为0.55-1：1；
所述氢氧化钠溶液的浓度为2-4mol/L；
(3)将步骤(2)装有碱渣混合物的高压反应釜盖好后加热，温度控制在100-180℃，并在自生压力下反应4-8h，固液分离后所得滤液即为含Al3+水玻璃。
CN201610416411.8A 2016-06-07 2016-06-07 一种利用高炉渣制备含Al3+水玻璃的方法 Active CN106115723B (zh)