CN106113862B - The double-layer fabric film for being easy to human body water vapour to discharge - Google Patents

The double-layer fabric film for being easy to human body water vapour to discharge Download PDF

Info

Publication number
CN106113862B
CN106113862B CN201610481570.6A CN201610481570A CN106113862B CN 106113862 B CN106113862 B CN 106113862B CN 201610481570 A CN201610481570 A CN 201610481570A CN 106113862 B CN106113862 B CN 106113862B
Authority
CN
China
Prior art keywords
parts
film
pore type
human body
discharge
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201610481570.6A
Other languages
Chinese (zh)
Other versions
CN106113862A (en
Inventor
张子睿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
KUNSHAN HUAYANG NEW MATERIAL Co.,Ltd.
Original Assignee
Kunshan Huayang New Material Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Huayang New Material Ltd Co filed Critical Kunshan Huayang New Material Ltd Co
Priority to CN201610481570.6A priority Critical patent/CN106113862B/en
Publication of CN106113862A publication Critical patent/CN106113862A/en
Application granted granted Critical
Publication of CN106113862B publication Critical patent/CN106113862B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention discloses a kind of double-layer fabric film for being easy to human body water vapour to discharge, including pore type polyurethane film, polytetrafluoroethylene film, is bonded between the pore type polyurethane film, polytetrafluoroethylene film by adhesive layer；Pore type polyurethane film is scratched by prefabricated polyurethane slurry and toasted in silicon oil release paper and successively in the baking oven of 80 ~ 150 degree of thermogrades, and being cooled to normal temperature again after reaching 150 degree and being incubated obtains；Prefabricated polyurethane slurry is composed of the following components：100 parts of polyurethane resin, 20 ~ 25 parts of dimethylformamide, 32 ~ 35 parts of toluene, 12 ~ 15 parts of butanone, 8 ~ 9 parts of microspheres, 1.5 ~ 2.5 parts of one butanediol of Isosorbide-5-Nitrae, 1.2 ~ 1.8 parts of polyacrylamide, 0.3 ~ 0.5 part of acrylate, 0.2 ~ 0.3 part of organosiloxane emulsion.The multi-functional two-component compound fabric of the present invention can rainwater-proof, be advantageous to the discharge of human body sweat vapour again, and waterproof can be kept for a long time and perspire the performance of vapour so that fabric has more preferably comfort property and broader practice scope.

Description

The double-layer fabric film for being easy to human body water vapour to discharge
Technical field
The present invention relates to a kind of double-layer fabric film for being easy to human body water vapour to discharge, belong to technical field of textile fabric.
Background technology
Polyurethane fabric is a kind of artificial leather shell material, has the texture of corium, so the artificial leather that is otherwise known as.It is not only tied It is real durable, and because artificial synthesized technology maturation price is more cheap, be widely used in garment industry.The PU faces of prior art Expect for the fabric of single PU structure sheafs, because PU fabric water resistances are poor, thus the clothes of PU fabrics are not general washable, Dry-cleaning can only be used, improves use cost.PU fabric gas permeabilities are poor, reduce comfortable when PU fabric clothes is worn Degree, such as perspire and can not discharge when wearing.In addition, the wearability of PU fabrics is poor and cracking occurs in surface, comes off Phenomenon.
And polytetrafluoroethylene film, due to its special microcellular structure（In netted）Make it have pore type polyurethane film Wind and water preventing, the water vapour permeability that can not have, better than traditional microporous polyurethane film, but its shortcoming be also it is obvious, this Its elasticity of kind material is substantially zeroed, therefore this thin-film material is either in the recombination process with fabric or in high intensity Can not all be well adapted to during strenuous exercise fabric stretching caused by thin film damage, easily cause water resistance and its with The decline of the bond properties of fabric.
The content of the invention
It is an object of the present invention to provide a kind of double-layer fabric film for being easy to human body water vapour to discharge, the double-layer fabric film carries High elasticity and adaptability, are also avoided because pore type polytetrafluoroethylene film layer adsorbs the dust in empty vapour, the salt in sweat The materials such as part, grease cosmetics and detergent, realize the waterproof for keeping stable for a long time and perspire vapour performance, have simultaneously There is high intensity, do not absorb water, anti-wear performance.
To reach above-mentioned purpose, the technical solution adopted by the present invention is：A kind of dual-layer face for being easy to human body water vapour to discharge Material film, including pore type polyurethane film, polytetrafluoroethylene film, the pore type polyurethane film, polytetrafluoroethylene (PTFE) are thin Bonded between film by adhesive layer；
The pore type polyurethane film is scratched in silicon oil release paper and successively 80 ~ 150 by prefabricated polyurethane slurry The baking oven baking of thermograde is spent, being cooled to normal temperature again after reaching 150 degree and being incubated obtains；
The prefabricated polyurethane slurry is composed of the following components：100 parts of polyurethane resin, 25 parts of dimethylformamide, first 35 parts of benzene, 15 parts of butanone, 9 parts of microspheres, 2.2 parts of one butanediol of Isosorbide-5-Nitrae, 1.8 parts of polyacrylamide, 0.4 part of acrylate, 0.3 part of organosiloxane emulsion, the polytetrafluoroethylene film per square inch hole number be 85 ~ 9,500,000,000, the hole The average diameter in hole is 0.2 μm ~ 10 μm.
Further improved technical scheme is as follows in above-mentioned technical proposal：
Preferably, the volume of the polytetrafluoroethylene film Hole accounts for the 87 ~ 89% of polytetrafluoroethylene film volume.
Preferably, the mass ratio between the polytetrafluoroethylene film and pore type polyurethane film is 1：6.5 ~ 7, it is thick Degree is than being 1：0.3~0.6.
Preferably, the baking oven baking of 80 ~ 150 degree of thermogrades was specifically included with the next stage：
The first stage：Under conditions of 80 DEG C, and carried out under the empty vapour atmosphere of low speeds flow；
Second stage：Under conditions of 90 DEG C, and carried out under the empty vapour atmosphere of middling speed flowing；
Phase III：Under conditions of 110 DEG C, and carried out under the empty vapour atmosphere of strong speed flowing；
Fourth stage：Under conditions of 140 DEG C, and carried out under the empty vapour atmosphere of low speeds flow.
Preferably, the microspheres are akzonobel companies microspheres, contain in its flexible shell The low-boiling point materials such as iso-butane, propane, pentane.
Because above-mentioned technical proposal is used, the present invention has following advantages and effect compared with prior art：
1. the present invention is easy to the double-layer fabric film that human body water vapour is discharged, can avoid due to pore type polytetrafluoro Vinyl film layer adsorbs the materials such as dust, the salt in sweat, grease cosmetics and the detergent in empty vapour, when realizing long Between keep stable waterproof and perspire vapour performance；Secondly, combine with the hydrophilic layer of polyurethane and polytetrafluoroethylene (PTFE) for refusing oil Film layer, while external prevention rainwater performance is improved, there is the performance for enhancing internally discharge human body sweat vapour so that fabric Fabric has more preferably comfort property and broader practice scope；Again, because this two-component thin-film material has largely Even hole, and the microvoid polyurethane resin bed with the hydrophilic type for refusing oil, so as to be more beneficial for from human body water vapour Discharge, the moisture of residual polyurethane film layer surface is greatly reduced, so as to improve the wearability of coating fabric and wear Dry and comfortable, most importantly substantially increase the elasticity of PTFE film material, make clothes clothes in high sharp movement and pole Also there is good mechanical property under the conditions of end.
2. the present invention is easy to the double-layer fabric film that human body water vapour is discharged, for specific with polytetrafluoroethylene film Combination, the formula of pore type polyurethane film is optimized, so as to improve elasticity and adaptability, while there is high intensity, do not inhale Water, anti-wear performance.
Brief description of the drawings
Accompanying drawing 1 is easy to the double-layer fabric membrane structure schematic diagram of human body water vapour discharge for the present invention；
Accompanying drawing 2 is the partial structural diagram of accompanying drawing 1.
In the figures above：1st, pore type polyurethane film；2nd, polytetrafluoroethylene film；3rd, adhesive layer；4th, hole.
Embodiment
Below in conjunction with the accompanying drawings and embodiment the invention will be further described：
Embodiment：A kind of double-layer fabric film for being easy to human body water vapour to discharge, including it is pore type polyurethane film 1, poly- Tetrafluoroethene film 2, bonded between the pore type polyurethane film 1, polytetrafluoroethylene film 2 by adhesive layer 3, it is described poly- Tetrafluoroethene film 2 per square inch hole 4 number be 85 ~ 9,500,000,000, the average diameter of hole 4 is 0.2um ~ 10um；
The pore type polyurethane film 1 is scratched in silicon oil release paper and successively 80 ~ 150 by prefabricated polyurethane slurry The baking oven baking of thermograde is spent, being cooled to normal temperature again after reaching 150 degree and being incubated obtains；
The prefabricated polyurethane slurry is composed of the following components：
100 parts of polyurethane resin,
25 parts of dimethylformamide,
35 parts of toluene,
15 parts of butanone,
9 parts of microspheres,
2.2 parts of one butanediol of Isosorbide-5-Nitrae；
1.8 parts of polyacrylamide；
0.4 part of acrylate,
0.3 part of organosiloxane emulsion.
The volume of above-mentioned polytetrafluoroethylene film Hole accounts for the 87 ~ 89% of polytetrafluoroethylene film volume.
Mass ratio between above-mentioned polytetrafluoroethylene film 2 and pore type polyurethane film 1 is 1：6.5 ~ 7, thickness ratio is 1：0.3~0.6.
Above-mentioned microspheres are akzonobel companies microspheres, contain iso-butane, third in its flexible shell The low-boiling point materials such as alkane, pentane.
Specific targets numerical value of the present invention is as follows：
A. before hydrostatic pressing value is washed>12000mmH2O, after five washings>8000mmH2O（Washing methods ISO 6330, test Method ISO 811）,
B. vapor transfer rate：10000g/m2·24h（JIS 1099 A1）,
C. anti-flammability passes through（GB8965.2-2009）Criterion is B levels,
D. peel strength（GB11042-89）：4N,
E. resist cold reachable less than -150 DEG C, heat-resisting reachable+150 DEG C,（The standards of ISO 2136）Resistance to tortuous 9000 nothings are split,
F films extensibility 25%,
G films response rate 96%,
H. wind-proof performance：It is completely windproof（>10 grades）,
I. thermal impedance（GB/T 11048-2008 A methods）：0.1097m²·K/W.
During using the above-mentioned double-layer fabric film for being easy to human body water vapour to discharge, it can avoid due to pore type polytetrafluoro Vinyl film layer adsorbs the materials such as dust, the salt in sweat, grease cosmetics and the detergent in empty vapour, when realizing long Between keep stable waterproof and perspire vapour performance；Secondly, combine with the hydrophilic layer of polyurethane and polytetrafluoroethylene (PTFE) for refusing oil Film layer, while external prevention rainwater performance is improved, there is the performance for enhancing internally discharge human body sweat vapour so that fabric Fabric has more preferably comfort property and broader practice scope；Again, because this two-component thin-film material has largely Even hole, and the microvoid polyurethane resin bed with the hydrophilic type for refusing oil, so as to be more beneficial for from human body water vapour Discharge, the moisture of residual polyurethane film layer surface is greatly reduced, so as to improve the wearability of coating fabric and wear Dry and comfortable, most importantly substantially increase the elasticity of PTFE film material, make clothes clothes in high sharp movement and pole Also there is good mechanical property under the conditions of end；Secondly, it optimizes micropore for the particular combination with polytetrafluoroethylene film The formula of type polyurethane film, so as to improve elasticity and adaptability, while there is high intensity, do not absorb water, anti-wear performance.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art Scholar can understand present disclosure and implement according to this, and it is not intended to limit the scope of the present invention.It is all according to the present invention The equivalent change or modification that Spirit Essence is made, it should all be included within the scope of the present invention.

Claims (1)

  1. A kind of 1. double-layer fabric film for being easy to human body water vapour to discharge, it is characterised in that：Including pore type polyurethane film （1）, polytetrafluoroethylene film（2）, the pore type polyurethane film（1）, polytetrafluoroethylene film（2）Between pass through adhesive layer （3）Bonding, the polytetrafluoroethylene film（2）The number of hole is 85 ~ 9,500,000,000 per square inch, and being averaged for described hole is straight Footpath is 0.2 μm ~ 10 μm；
    The pore type polyurethane film（1）Scratched by prefabricated polyurethane slurry in silicon oil release paper and successively at 80 ~ 150 degree The baking oven baking of thermograde, is cooled to normal temperature acquisition again after reaching 150 degree and being incubated；
    The prefabricated polyurethane slurry is composed of the following components：100 parts of polyurethane resin, 25 parts of dimethylformamide, toluene 35 It is part, 15 parts of butanone, 9 parts of microspheres, 2.2 parts of one butanediol of Isosorbide-5-Nitrae, 1.8 parts of polyacrylamide, 0.4 part of acrylate, organic 0.3 part of silicone emulsion；The volume of the polytetrafluoroethylene film Hole accounts for the 87 ~ 89% of polytetrafluoroethylene film volume；Institute It is akzonobel companies microspheres to state microspheres, contains iso-butane, propane, pentane in its flexible shell.
CN201610481570.6A 2015-02-25 2015-02-25 The double-layer fabric film for being easy to human body water vapour to discharge Active CN106113862B (en)