CN106113235A - A kind of brick machine mould and manufacture method thereof - Google Patents

A kind of brick machine mould and manufacture method thereof Download PDF

Info

Publication number
CN106113235A
CN106113235A CN201610514660.0A CN201610514660A CN106113235A CN 106113235 A CN106113235 A CN 106113235A CN 201610514660 A CN201610514660 A CN 201610514660A CN 106113235 A CN106113235 A CN 106113235A
Authority
CN
China
Prior art keywords
chromium carbide
steel plate
resisting steel
framed
carbide compounded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610514660.0A
Other languages
Chinese (zh)
Inventor
姜海强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Rui Qiang Machinery Manufacturing Co Ltd
Original Assignee
Nantong Rui Qiang Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Rui Qiang Machinery Manufacturing Co Ltd filed Critical Nantong Rui Qiang Machinery Manufacturing Co Ltd
Priority to CN201610514660.0A priority Critical patent/CN106113235A/en
Publication of CN106113235A publication Critical patent/CN106113235A/en
Pending legal-status Critical Current

Abstract

The invention provides a kind of brick machine mould and manufacture method thereof, including upper die and lower die, in described upper mold, be provided with die cavity, framed, transverse plate and longitudinal plate, described framed be arranged in die cavity, and be close to cavity lateral;Longitudinal plate and transverse plate are connected with framed after being connected by plug-in mounting, also include chromium carbide compounded wear-resisting steel plate, described chromium carbide compounded wear-resisting steel plate by be perpendicular to framed in the way of be separately positioned on framed in, transverse plate two surface and longitudinal plate two surface, and be close to framed medial surface.The brick machine mould of the present invention, the use of chromium carbide compounded wear-resisting steel plate, make when blank plastic degeneration in mold cavity, when not only having flowed along mold cavity surface but also slided, contact at first is chromium carbide compounded wear-resisting steel plate, reduces and produces violent friction between mold cavity surface and blank, thus avoid result in mould and affect the quality of brick because of abrasion, the time of brick machine mould invalidation can also be extended simultaneously, be equal to extend brick machine die life, reduce industrial cost.

Description

A kind of brick machine mould and manufacture method thereof
Technical field
The present invention relates to brick equipment technical field, particularly relate to a kind of brick machine mould and manufacture method thereof.
Background technology
In order to energy-saving and cost-reducing, protecting farmland, China comes into effect taboo and glues, prohibits real policy, and it is novel to widely popularize application Construction material is such as: brick, building block etc..Fragment of brick is to utilize with clay, shale, and gangue etc. is raw material, and size-reduced, mixing pugging mullering is made , there is equipment simple, build fireballing advantage by laying bricks or stones.Brick machine mould is exactly the mold tool with brick machine series mechanical as core. The brick output core of the building machinery such as machine such as block building machine, cushion block machine.The brick of needs can be produced by mould.Such as mark The brick samples such as brick, porous brick, bread brick, Dutch brick, grass-planting brick, hollow brick, big square brick, curb brick, cushion block.Brick machine mould is existing In generation, builds a part necessary to environmental protection environment.
It is known that when blank plastic degeneration in mold cavity, not only flow but also slide along mold cavity surface, make die cavity table Producing violent friction between face and blank, thus cause mould to lose efficacy because of abrasion, how the focus of prior art is usually The quality of brick is improved by brick-making mould, but, if the quality of mould is the most really up to the mark, the brick natural quality of production also will not mistake Firmly, therefore, real focus is, the wearability of mold materials is one of mould performance most basic, most important.Hardness is Affecting the principal element of wearability, the working condition of mould is the most severe, and some often bears bigger impact load, thus Cause brittle fracture.For preventing mould parts operationally brittle failure suddenly, mould to have higher intensity and toughness.
Such as Chinese patent CN104015248A discloses a kind of brick compacting mold, including framed, base plate and top board, framed sets Put on base plate, framed constituted cuboid framework by four pieces of rectangular steel plates, it is characterised in that: described top board and base plate are positioned at mould Part in frame is above surrounding and forms lobe, and lobe surface configuration has raised line.This technical scheme in use, thing Material to moving around, is thus easier to be extruded to the corner parts of adobe under the lobe effect of top board and base plate, The position, corner of the adobe suppressed is solid, and the quality of fragment of brick is high, mainly solving the technical problems that, really the mobility of material is not Time good, material is not easy to be extruded to the problem at the position, corner of adobe, but not about strengthen the quality of mould itself with The description of performance.
The most such as Chinese patent CN1931547 discloses one fire brick mold made of wear resistant alloy complex board, and it is special Levy and be: with mild steel as substrate (1), substrate uses welding process generate and there is certain thickness wearable hard alloy layer (2).In this technical scheme, carry out substantial amounts of description, including substrate thickness, material to how producing wearable hard alloy layer (2) Material, welding process, the ingredient etc. of wear-resistant alloy layer, but be not involved with how by wearable hard alloy layer (2) in Brick machine grinding tool is combined assembling, thus improves quality and the performance of brick machine grinding tool itself.
Summary of the invention
For overcoming brick machine mould present in prior art itself to there is problem easy to wear, that service life is short, this Bright provide a kind of brick machine mould and manufacture method thereof.
The technical solution used in the present invention is: a kind of brick machine mould, including upper die and lower die, is provided with type in described upper mold Chamber, framed, transverse plate and longitudinal plate, described framed be arranged in die cavity, and is close to cavity lateral;Longitudinal plate and transverse plate pass through Plug-in mounting is connected with framed after connecting, and its innovative point is: also include chromium carbide compounded wear-resisting steel plate, described chromium carbide compounded wear-resisting Steel plate by be perpendicular to framed in the way of arrange be separately positioned on framed in, transverse plate two surface and longitudinal plate two surface, and be close to In framed medial surface.
On this basis, described fixing be fitted in framed in chromium carbide compounded wear-resisting steel plate number be 140~260.
On this basis, the thickness of described chromium carbide compounded wear-resisting steel plate is 6~10mm, a length of 1600mm, 1800mm Or 2000mm, width is 140mm.
On this basis, on described chromium carbide compounded wear-resisting steel plate, the thickness of chromium carbide is 0.1-0.6mm.
On this basis, each described chromium carbide compounded wear-resisting steel plate is arranged on framed arbitrary medial surface;The most framed arbitrary One or more described chromium carbide compounded wear-resisting steel plates it are provided with on medial surface.
It is a further object to provide a kind of brick machine mould manufacturing method, its innovative point is: specifically include as Lower step:
Step1: use Water Cutting that chromium carbide compounded wear-resisting steel plate is carried out Water Cutting;
Step2: the grinding machine to chromium carbide compounded wear-resisting steel plate;
Step3: the common plate in upper mold, transverse plate, the processing of longitudinal plate, form die cavity after processing;
Step4: chromium carbide compounded wear-resisting steel plate punches;
Step5: overall welding fabrication, corrects straight, assembles with lower mold.
On this basis, the concretely comprising the following steps of described step Step1: initially with Water Cutting processing method by rectangular-shaped Chromium carbide compounded wear-resisting steel plate cuts, and the upper and lower both sides of the chromium carbide compounded wear-resisting steel plate of rectangle are cut with two same sizes Several the first groove one grooves, between adjacent two described first grooves be spaced;The chromium carbide compounded wear-resisting steel plate of rectangle two Side has been respectively cut second groove, and the position dimension of described second groove of dual-side is identical.
On this basis, described Water Cutting is processed method particularly includes:
(1), firm banking: coating water-soluble glue on base, in water-soluble glue, one end paving spills one layer of moist dry ice Grain, and the chromium carbide compounded wear-resisting steel plate that is to be cut is fixed on this water-soluble glue one end near moist dry ice particles, Etc. to be cut;
(2), heating: high pressure waterjet head is first placed in 250-300 DEG C of high temperature and carries out calcination;
(3), cooling: use thermostatted water as cooling on the high pressure waterjet head after clean calcination;
(4), shear: high pressure waterjet head cuts chromium carbide compounded wear-resisting steel plate according to required form.
On this basis, the concretely comprising the following steps of described step Step2: select suitable surface grinding machine;Pass through surface grinding machine The length dimension being milled to chromium carbide compounded wear-resisting steel plate is 1600~2000mm.
On this basis, that punches in described Step4 concretely comprises the following steps: on the basis of Step3 step, and chromium carbide is multiple Close wear-resisting steel plate alongst, a round is stamped on upper and lower limit successively, the quantity of every round be some each and every one, described upper row Hole is respectively distributed in the projection relative with the first groove cutting formation, the spacing between described first round and the second round It is 2~3mm.
Compared with prior art, the invention has the beneficial effects as follows:
(1) the brick machine mould of the present invention, also includes chromium carbide compounded wear-resisting steel plate, and chromium carbide compounded wear-resisting steel plate is with vertically In framed mode be arranged on framed in so that when blank plastic degeneration in mold cavity, not only flowed along mold cavity surface but also During slip, contact at first is chromium carbide compounded wear-resisting steel plate, reduces and produces violent friction between mold cavity surface and blank, thus Avoid result in mould and affect the quality of brick because of abrasion, the time of brick machine mould invalidation can also be extended simultaneously, be equal to extend brick Machine die life, reduces industrial cost.
(2) the brick machine mould of the present invention, is used for chromium carbide compounded wear-resisting steel plate in mould, it is contemplated that fragment of brick is general first Being to utilize with clay, shale, gangue etc. is made for raw material, the when that general other elements compounding becoming wearing plate, and meeting and brick The raw material of block, when becoming embryo brick, produces chemical reaction, affects fragment of brick quality.And chromium carbide compounded wear-resisting steel plate is in mould, Chemical reaction will not be produced with the raw material of fragment of brick when becoming embryo brick, improve yield and production efficiency.
(3) the brick machine mould manufacturing method of the present invention, selects specific Water Cutting to process chromium carbide compounded wear-resisting steel plate, energy Release the injury to steel plate that the substantial amounts of torrid zone is come when being enough greatly reduced cutting, improve steel plate excision forming effect, it is ensured that cutting Quality, cutting perfection.
(4) the brick machine mould manufacturing method of the present invention, Water Cutting process steps is simple, with low cost, is suitable for big rule Mould is promoted, and selects water-soluble glue one end paving to spill one layer of moist dry ice particles, and wet dry ice particles runs into the heat that cutting produces After absorbing so that the moisture on dry ice surface build-ups ice, thus reduces ambient temperature, it is ensured that cutting effect.
Accompanying drawing explanation
Fig. 1 is brick machine mould schematic diagram of the present invention;
Fig. 2 is chromium carbide compounded wear-resisting steel plate structural representation in brick machine mould of the present invention;
Fig. 3 is the chromium carbide compounded wear-resisting steel plate structural representation in brick machine mould of the present invention after punching.
Detailed description of the invention
Below in conjunction with drawings and Examples, the present invention is further elaborated.Should be appreciated that described herein Specific embodiment only in order to explain the present invention, is not intended to limit the present invention.
The present invention discloses a kind of brick machine mould, as shown in Figure 1: include upper mold 1 and lower mold 2, be provided with in described upper mold 1 Die cavity 11, die cavity 11 is rectangle, more smaller than die cavity 11 area framed 12 (framed 12 also for rectangle, and a length of 60cm, width are 40cm), transverse plate 13 (and width identical with upper mold length is the rectangular slab of 3cm) and longitudinal plate 14 (identical with upper mold width and The rectangular slab of a length of 3cm), described framed 12 inlay and are arranged in die cavity 11, and are close to die cavity 11 sidewall;Longitudinal plate 14 and horizontal stroke Being connected with framed 12 after plate 13 is connected by plug-in mounting, as the preferred embodiment of present embodiment, the number of longitudinal plate 14 is 4 Individual, the number of transverse plate 13 is set as 1.
As shown in Figure 1: also including chromium carbide compounded wear-resisting steel plate 15, described chromium carbide compounded wear-resisting steel plate 15 is to be perpendicular to The mode of framed 12 is separately positioned on framed 12 interior, 13 liang of surfaces of transverse plate and longitudinal 14 liang of surfaces of plate, and is close to framed 12 Medial surface.It is to say, the number of longitudinal plate 14 is 4, when the number of transverse plate 13 is set as 1, plate 14, horizontal stroke longitudinally in each Chromium carbide compounded wear-resisting steel plate 15 all it is fitted with to two surfaces of plate 13;Preferably, each described chromium carbide compounded abrasion-resistant stee Plate 15 is arranged on framed 12 arbitrary medial surface;It is provided with one or more described chromium carbide compounded on the most framed 12 arbitrary medial surface Wear-resisting steel plate 15.As preferably, according to framed number, the fixing chromium carbide compounded abrasion-resistant stee being fitted in framed 12 Plate 15 number selects to be advisable at 140~260.Such as: simple, by 1 framed as a example by, when the carbonization being fitted in framed 12 When chromium compound wear-resisting steel plates 15 number is chosen as 1, this chromium carbide compounded wear-resisting steel plate 15 is solid in the way of being perpendicular to framed 12 Surely it is fitted on framed 12 arbitrary medial surface;When chromium carbide compounded wear-resisting steel plate 15 number being fitted in framed 12 is chosen as 2 Time individual, this chromium carbide compounded wear-resisting steel plate 15 is fixing in the way of being perpendicular to framed 12 is fitted in framed 12 any two medial surface On;When chromium carbide compounded wear-resisting steel plate 15 number being fitted in framed 12 is chosen as 3, this chromium carbide compounded wear-resisting steel plate 15 fixing in the way of being perpendicular to framed 12 are fitted on framed 12 any three medial surface;When the carbonization being fitted in framed 12 When chromium compound wear-resisting steel plates 15 number is chosen as 4, this chromium carbide compounded wear-resisting steel plate 15 is solid in the way of being perpendicular to framed 12 Surely it is fitted on four medial surface of framed 12.Certainly, each medial surface of framed 12 can fix laminating and can also have 2 Above chromium carbide compounded wear-resisting steel plate 15, is not restricted at this.In present embodiment chromium carbide compounded wear-resisting steel plate 15 with In the mode of framed 12 of being perpendicular to is arranged on framed 12 so that when blank plastic degeneration in mold cavity 11, along die cavity 11 Time not only flowing but also slided in surface, contact at first is chromium carbide compounded wear-resisting steel plate 15, reduces and produces between die cavity 11 surface and blank Raw violent friction, thus avoid result in mould and affect the quality of brick because of abrasion, brick machine mould invalidation can also be extended simultaneously Time, it is equal to extend brick machine die life, reduces industrial cost.
As preferably, selecting the thickness of chromium carbide on chromium carbide compounded wear-resisting steel plate 15 is 0.1-0.6mm, as preferably , on chromium carbide compounded wear-resisting steel plate 15, the thickness of chromium carbide is set as 0.35mm.Select chromium carbide compounded wear-resisting steel plate 15 During thickness, be mainly in view of the relation between cost and rub proofness, optimal, when thickness selects at 0.35mm, cost with Relation between rub proofness reaches optimal meeting point.It addition, the thickness of chromium carbide compounded wear-resisting steel plate is 6~10mm, length For 1600mm, 1800mm or 2000mm, width is 140mm, such size design, it is possible to obtain bigger wear-resisting cost ratio, In application aspect, there is the biggest advantage.In present embodiment, first chromium carbide compounded wear-resisting steel plate 15 is used in mould, Being usually utilization in view of fragment of brick to make for raw material with clay, shale, gangue etc., general other elements compounding becomes wearing plate When, chemical reaction can be produced, affects fragment of brick quality with the raw material of fragment of brick when becoming embryo brick.And chromium carbide compounded abrasion-resistant stee Plate, in mould, will not produce chemical reaction with the raw material of fragment of brick when becoming embryo brick, improves yield and production efficiency.
A kind of brick machine mould manufacturing method is provided in another embodiment, selects specific Water Cutting processing chromium carbide multiple Close wear-resisting steel plate, it is possible to when being greatly reduced cutting, release the injury to steel plate that the substantial amounts of torrid zone is come, improve steel plate excision forming Effect, it is ensured that cut quality, cutting perfection.
Specifically include following steps:
Step1: the Water Cutting of chromium carbide compounded wear-resisting steel plate;
Step2: by the grinding machine of chromium carbide compounded wear-resisting steel plate;
Step3: the common plate in upper mold, transverse plate, the processing of longitudinal plate, form die cavity after processing;
Step4: chromium carbide compounded wear-resisting steel plate punches;
Step5: overall welding fabrication, corrects straight, assembles with lower mold.
Further, described step Step1 is mainly the Water Cutting to chromium carbide compounded wear-resisting steel plate, has very important Status, the cutting form of steel plate and cutting achievement, be that on the other hand, water is cut to the follow-up prerequisite carrying out grinding machine, combination The cutting efficiency cut is high, utilizes relatively low hydraulic pressure can to cut steel plate, pottery, marble, cement products etc..This embodiment party In formula, mainly comprising the following steps of cutting: use Water Cutting processing method to be cut by rectangular-shaped chromium carbide compounded wear-resisting steel plate. Secondly, it is determined the shape of cutting, needs to carry out with processed brick machine mould coordinating to fix, (processed brick machine mould Can be standard brick mould, many rounds insulating brick mould, Dutch brick mould, porous brick die, grassed brick mould, curb mould, Mould shake mould etc., this is not restricted) processed brick machine mould is chosen as many rounds insulating brick mould in the present embodiment, Therefore, as shown in Figure 2: it is first recessed that the upper and lower both sides of the chromium carbide compounded wear-resisting steel plate of rectangle 15 are cut with several same sizes Groove 151 (being not fully shown in figure), is spaced 2~3mm and is advisable between adjacent two the first grooves 151;Rectangle is chromium carbide compounded wear-resisting Steel plate 15 dual-side has been respectively cut several the second grooves 152 (being not fully shown in figure), the position of the second groove 152 of dual-side Put equivalently-sized, be spaced between adjacent two the second grooves 152 and 1~2mm be advisable. the spacing between above-mentioned adjacent first groove with And the setting of the spacing between adjacent second groove, it is considered to the chromium carbide compounded wear-resisting steel plate of rectangle on groove primarily serve profit Carry out horizontal and longitudinally cutting brick machine die products with water jet cutting, and groove can also be arranged for any and all Other water jet cutting.
As preferably, Water Cutting is processed method particularly includes:
(1), firm banking: coating water-soluble glue on base, in water-soluble glue, one end paving spills one layer of moist dry ice Grain, and the chromium carbide compounded wear-resisting steel plate that is to be cut is fixed on this water-soluble glue one end near moist dry ice particles, Etc. to be cut;In present embodiment, Water Cutting process steps is simple, with low cost, is suitable for large-scale promotion, selects water-soluble Property Jiao Yiduanpu spill one layer of moist dry ice particles, wet dry ice particles run into cutting produce heat absorb after so that The moisture on dry ice surface build-ups ice, thus reduces ambient temperature, it is ensured that cutting effect.
(2), heating: high pressure waterjet head is first placed in 250-300 DEG C of high temperature and carries out calcination;
(3), cooling: use thermostatted water as cooling on the high pressure waterjet head after clean calcination;
(4), shear: high pressure waterjet head cuts chromium carbide compounded wear-resisting steel plate according to required form.
As it is further preferred that described step Step2 mentions chromium carbide compounded wear-resisting steel plate carries out grinding machine process;To this For embodiment, concretely comprise the following steps: first select suitable surface grinding machine, be milled to chromium carbide compounded resistance to by controlling surface grinding machine The length dimension of mill steel plate meets production requirement, in order to ensure to adapt to most of brick machine equipment, by chromium carbide compounded wear-resisting steel plate Length dimension be chosen as 1600~2000mm, it is ensured that before use, it is not necessary to carry out secondary operations.
As it is further preferred that in described Step3 mainly by prior art by upper mold use arrive except carbon Change the common plate outside chromium compound wear-resisting steel plates, transverse plate, the processing of longitudinal plate, after processing, form the rectangle mold cavity of arc.
As it is further preferred that described Step4 mainly punches on chromium carbide compounded wear-resisting steel plate;Punching Concretely comprise the following steps: by chromium carbide compounded wear-resisting steel plate alongst, stamp a round successively in the position on upper and lower limit 153, the quantity of every round 153 is that (the groove number+1 of the length direction of setting) is individual, it is also possible to be (the length direction of setting recessed Groove number+1) individual multiple or more, averagely punches as long as meeting.On the other hand, the upper round 153 of punching is preferably distinguished In relative protruding of the first groove 151 of being distributed in and cut formation, the spacing between described first round and the second round is 2 ~3mm, the purpose of punching, primarily to the effect that gas when playing convenient manufacture is released, therefore, the number in hole 153 is not With, then the hole density between aperture and the Kong Yukong in hole can be caused to change, such as, as shown in Figure 3: when selecting every round Quantity one timing of 153, the spacing between the first round and the second round is 1/10th mm of hole number, the hole such as punched Footpath is 0.3mm, and hole density is 4~6/cm3;When the quantity selecting every round 153 is 6, the first round and the second round it Between spacing be 0.5~1mm, the aperture of punching is 0.2mm, and hole density is 8~10/cm3
As it is further preferred that transverse plate, longitudinal plate are mainly passed through by the way of plug-in mounting by Step5 with common plate The die cavity formed after processing assembles, then by above-mentioned carrying out cutting, chromium carbide compounded wear-resisting steel plate that perforation processing is crossed is with total Body welding fabrication, then corrects straight, and last and lower mold assembles the brick machine mould forming the present invention.
Through authenticating authority, the brick machine grinding tool that present embodiment produces, wear-resisting reach 200,000 times, be common standards in industry The number of times all not reached, such as Standard are that the wear-resisting need of brick machine grinding tool reach 60,000 times, and present embodiment is Standard 3~4 times, substantially prolongs the service life of equipment, cost reduces about 30%, and present embodiment is extremely to have using value Mould and production method.
Described above illustrate and describes the preferred embodiments of the present invention, as previously mentioned, it should be understood that the present invention not office Be limited to form disclosed herein, be not to be taken as the eliminating to other embodiments, and can be used for other combinations various, amendment and Environment, and can be changed by above-mentioned teaching or the technology of association area or knowledge in invention contemplated scope described herein Dynamic.And the change that those skilled in the art are carried out and change are without departing from the spirit and scope of the present invention, the most all should be appended by the present invention In scope of the claims.

Claims (10)

1. a brick machine mould, including upper die and lower die, is provided with die cavity, framed, transverse plate and longitudinal plate, institute in described upper mold State framed being arranged in die cavity, and be close to cavity lateral;Longitudinal plate and transverse plate are connected with framed after being connected by plug-in mounting, and it is special Levy and be: also include chromium carbide compounded wear-resisting steel plate, described chromium carbide compounded wear-resisting steel plate by be perpendicular to framed in the way of arrange It is separately positioned on framed interior, transverse plate two surface and longitudinal plate two surface, and is close to framed medial surface.
Brick machine mould the most according to claim 1, it is characterised in that: described fixing be fitted in framed in chromium carbide compounded Wear-resisting steel plate number is 140~260.
Brick machine mould the most according to claim 1 and 2, it is characterised in that: the thickness of described chromium carbide compounded wear-resisting steel plate Being 6~10mm, a length of 1600mm, 1800mm or 2000mm, width is 140mm.
Brick machine mould the most according to claim 3, it is characterised in that: chromium carbide on described chromium carbide compounded wear-resisting steel plate Thickness is 0.1-0.6mm.
Brick machine mould the most according to claim 1, it is characterised in that: each described chromium carbide compounded wear-resisting steel plate is arranged on Framed arbitrary medial surface;One or more described chromium carbide compounded wear-resisting steel plates it are provided with on the most framed arbitrary medial surface.
6. the brick machine mould manufacturing method described in a claim 1, it is characterised in that: specifically include following steps:
Step1: use Water Cutting that chromium carbide compounded wear-resisting steel plate is carried out Water Cutting;
Step2: the grinding machine to chromium carbide compounded wear-resisting steel plate;
Step3: the common plate in upper mold, transverse plate, the processing of longitudinal plate, form die cavity after processing;
Step4: chromium carbide compounded wear-resisting steel plate punches;
Step5: overall welding fabrication, corrects straight, assembles with lower mold.
Brick machine mould manufacturing method the most according to claim 6, it is characterised in that: the concrete steps of described step Step1 For: being cut by rectangular-shaped chromium carbide compounded wear-resisting steel plate initially with Water Cutting processing method, rectangle is chromium carbide compounded The upper and lower both sides of wear-resisting steel plate are cut with several the first groove one grooves of two same sizes, adjacent two described first recessed It is spaced between groove;Rectangle chromium carbide compounded wear-resisting steel plate dual-side has been respectively cut second groove, described the of dual-side The position dimension of two grooves is identical.
Brick machine mould manufacturing method the most according to claim 7, it is characterised in that: the concrete grammar of described Water Cutting processing For:
(1), firm banking: on base coat water-soluble glue, in water-soluble glue one end paving spill one layer of moist dry ice particles, and The chromium carbide compounded wear-resisting steel plate that one is to be cut is fixed on this water-soluble glue one end near moist dry ice particles, waits to be cut Cut;
(2), heating: high pressure waterjet head is first placed in 250-300 DEG C of high temperature and carries out calcination;
(3), cooling: use thermostatted water as cooling on the high pressure waterjet head after clean calcination;
(4), shear: high pressure waterjet head cuts chromium carbide compounded wear-resisting steel plate according to required form.
Brick machine mould manufacturing method the most according to claim 7, it is characterised in that: the concrete steps of described step Step2 For: select suitable surface grinding machine;By surface grinding machine be milled to the length dimension of chromium carbide compounded wear-resisting steel plate be 1600~ 2000mm。
Brick machine mould manufacturing method the most according to claim 7, it is characterised in that: the concrete step of punching in described Step4 Suddenly it is: on the basis of Step3 step that by chromium carbide compounded wear-resisting steel plate alongst, a row is stamped on upper and lower limit successively Hole, the quantity of every round is several, and described upper round is respectively distributed in the projection relative with the first groove cutting formation, Spacing between described first round and the second round is 2~3mm.
CN201610514660.0A 2016-06-30 2016-06-30 A kind of brick machine mould and manufacture method thereof Pending CN106113235A (en)