CN106094434A - A kind of preparation method of high rapidity high stable novel photoactive glue - Google Patents
A kind of preparation method of high rapidity high stable novel photoactive glue Download PDFInfo
- Publication number
- CN106094434A CN106094434A CN201610715402.9A CN201610715402A CN106094434A CN 106094434 A CN106094434 A CN 106094434A CN 201610715402 A CN201610715402 A CN 201610715402A CN 106094434 A CN106094434 A CN 106094434A
- Authority
- CN
- China
- Prior art keywords
- solution
- gained
- glue
- preparation
- rapidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses the preparation method of a kind of high rapidity high stable novel photoactive glue, comprises the following steps: 1) fully dissolve, with 300ml water, the polyvinyl alcohol that 40g alkalizes, obtain the poly-vinyl alcohol solution that mass concentration is 0.114g/ml;2) in the solution of step (1) gained, 12g polyvinyl acetate emulsion, 20gSBQ light-hardening resin, 5g acrylamide, 3g ethyl methacrylate, 0.8g dibutyl ester, 0.4g ethylenediamine, 1.8g light trigger 0.3g polyacrylamide amine emulsifier, 0.2g polymerization inhibitor, 0.5g emulsified silicone oil defoamer and 0.8g stain are the most accurately added;3) by the solution of gained 85 DEG C reaction 3h in step (2), period is stirred continuously, forms finely dispersed emulsion system;4) solution of gained in step (3) being down to room temperature, after standing 24h froth breaking, sealing is kept in Dark Place;The preparation method of this high rapidity high stable novel photoactive glue is unlikely to deteriorate, holding time length, photosensitive property are good.
Description
Technical field
Present invention relates particularly to the preparation method of a kind of high rapidity high stable novel photoactive glue.
Background technology
Photosensitizer (photosensitizer), also known as sensitizer, sensitizer, photocrosslinking agent.In photochemical reaction,
Luminous energy is transferred on the reactant that some are insensitive to visible ray to improve or to expand the material of its photosensitive property.
In photochemical reaction, have molecule, they only absorb photons and transfer energy to those can not absorbing light
The molecule of son, promotees it and chemical reaction occurs, itself be then not involved in chemical reaction, return to original state, and this quasi-molecule claims
For photosensitizer.The photochemical reaction caused by photosensitizer is referred to as photosensitivity reaction.Generally, people are adjoint raw have oxygen molecule to participate in
The photosensitivity reaction of thing effect is referred to as photodynamic reaction, calls light power photodynamic reaction can be caused to destroy cyto-architectural medicine
Medicine, i.e. photosensitive drug.
What the present market of photosensitizer commonly used is that the diazo resin that common p-xylene-4-diazol synthesizes is photosensitive
Agent, exists apt to deteriorate, and the holding time is short, the shortcoming that photosensitive property is bad.
Summary of the invention
For overcoming the problems of the prior art, the invention provides a kind of use 3-methoxy diphenylamine-4-diazol with
Traditional hexichol amine salt 1:1 is used in mixed way, and is unlikely to deteriorate, the high novel sense of rapidity high stable that holding time length, photosensitive property are good
The preparation method of optical cement.
Technology and method in order to solve the employing of the above-mentioned problem present invention are as follows:
The preparation method of a kind of high rapidity high stable novel photoactive glue, it is characterised in that comprise the following steps:
1) fully dissolve the polyvinyl alcohol of 40g alkalization with 300ml water, obtain the polyvinyl alcohol that mass concentration is 0.114g/ml
Solution;
2) in the solution of step (1) gained, 12g polyvinyl acetate emulsion, 20gSBQ photo-hardening tree are the most accurately added
Fat, 5g acrylamide, 3g ethyl methacrylate, 0.8g dibutyl ester, 0.4g ethylenediamine, 1.8g light trigger 0.3g polyacrylamide
Amine emulsifier, 0.2g polymerization inhibitor, 0.5g emulsified silicone oil defoamer and 0.8g stain;
3) by the solution of gained 85 DEG C reaction 3h in step (2), period is stirred continuously, forms finely dispersed emulsion body
System;
4) solution of gained in step (3) being down to room temperature, after standing 24h froth breaking, sealing is kept in Dark Place.
The invention have the benefit that and use 3-methoxy diphenylamine-4-diazol with traditional hexichol amine salt 1:1 mixing
Using, make latex solid content, viscosity be obtained for bigger lifting, latex solid content reaches
30-43%, viscosity has reached 2000-7000mpa.s, and pH value is at 4.5-6.5, and time of exposure also controls at 0.2-
5.5min, resolution has reached below 0.09mm, and meanwhile, resolution and resistance to water have also been obtained raising, and pattern edge is apparent,
And can be under giant impacts, the 5-30 second does not falls off.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail, but they are not to technical solution of the present invention
Restriction, based on present invention teach that any conversion made, all fall within protection scope of the present invention.
The preparation method of a kind of high rapidity high stable novel photoactive glue, it is characterised in that comprise the following steps:
1) fully dissolve the polyvinyl alcohol of 40g alkalization with 300ml water, obtain the polyvinyl alcohol that mass concentration is 0.114g/ml
Solution;
2) in the solution of step (1) gained, 12g polyvinyl acetate emulsion, 20gSBQ photo-hardening tree are the most accurately added
Fat, 5g acrylamide, 3g ethyl methacrylate, 0.8g dibutyl ester, 0.4g ethylenediamine, 1.8g light trigger 0.3g polyacrylamide
Amine emulsifier, 0.2g polymerization inhibitor, 0.5g emulsified silicone oil defoamer and 0.8g stain;
3) by the solution of gained 85 DEG C reaction 3h in step (2), period is stirred continuously, forms finely dispersed emulsion body
System;
4) solution of gained in step (3) being down to room temperature, after standing 24h froth breaking, sealing is kept in Dark Place.
Experimental example
High rapidity high stable novel photoactive glue obtained by the present invention is carried out parameter testing, obtains parameter such as following table:
The invention have the benefit that and use 3-methoxy diphenylamine-4-diazol with traditional hexichol amine salt 1:1 mixing
Using, make latex solid content, viscosity be obtained for bigger lifting, latex solid content has reached 30-43%, and viscosity reaches
2000-7000, pH value is at 4.5-6.5, and time of exposure also controls at 0.2-5.5s, and resolution has reached below 0.09mm, meanwhile,
Resolution and resistance to water have also been obtained raising, and pattern edge is apparent, and can be under giant impacts, and the 5-30 second does not takes off
Fall.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
The change expected without creative work or replacement, all should contain within protection scope of the present invention, therefore, and the present invention's
Protection domain should be as the criterion with the protection domain that claims are limited.
Claims (1)
1. the preparation method of one kind high rapidity high stable novel photoactive glue, it is characterised in that comprise the following steps:
1) fully dissolve the polyvinyl alcohol of 40g alkalization with 300ml water, obtain the poly-vinyl alcohol solution that mass concentration is 0.114g/ml;
2) in the solution of step (1) gained, 12g polyvinyl acetate emulsion, 20gSBQ light-hardening resin, 5g are the most accurately added
Acrylamide, 3g ethyl methacrylate, 0.8g dibutyl ester, 0.4g ethylenediamine, 1.8g light trigger 0.3g polyacrylamide breast
Agent, 0.2g polymerization inhibitor, 0.5g emulsified silicone oil defoamer and 0.8g stain;
3) by the solution of gained 85 DEG C reaction 3h in step (2), period is stirred continuously, forms finely dispersed emulsion system;
4) solution of gained in step (3) being down to room temperature, after standing 24h froth breaking, sealing is kept in Dark Place.