CN106087443A - A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder and preparation technology thereof - Google Patents
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder and preparation technology thereof Download PDFInfo
- Publication number
- CN106087443A CN106087443A CN201610587229.9A CN201610587229A CN106087443A CN 106087443 A CN106087443 A CN 106087443A CN 201610587229 A CN201610587229 A CN 201610587229A CN 106087443 A CN106087443 A CN 106087443A
- Authority
- CN
- China
- Prior art keywords
- charcoal powder
- absorbent charcoal
- base fabric
- bamboo absorbent
- environment protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder; including base fabric and rubberised layer; described base fabric is contacted with weft yarn alternatively up and down by warp thread; constitute sine and cosine curve-like and stablize laminated structure; described warp thread is formed by many core-skin composite fiber long filament twisting; described core-skin composite fiber long filament is combined by PLA fibrocortex and PP core fiber layer; described weft yarn is formed by many chitin fiber long filament twisting; being fixed with bamboo absorbent charcoal powder in described base fabric, one side or the dual coating of described base fabric have rubberised layer.Present invention also offers the preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder.The manufacture fiber that present invention employing has the PLA/PP core-skin composite fiber long filament of biological degradability, chitin fiber long filament is machine textile lining cloth, having the advantages such as the feature of environmental protection, antibacterial activity, hygroscopicity, set bamboo absorbent charcoal powder has purification air, eliminates abnormal flavour, moisture absorption mildew-resistant, the effect of antibacterial deinsectization.
Description
[technical field]
The present invention relates to the technical field of adhesive lining, woven viscous particularly to a kind of Degradable environment protection containing bamboo absorbent charcoal powder
Close lining and preparation technology thereof.
[background technology]
Modern clothing stress wear embody in style comfortable, soft, slim and graceful and the most flexible.Adhesive lining is as " clothes
The skeleton of dress ", it is the adjuvants that can not suddenly lack of clothing, adhesive lining is a kind of lining scribbling PUR, is that cloth art makes through commonly using
One of adjuvant arrived.Adhesive lining is attached to the back side of cloth through pressing of heating, and " stitching with viscous generation " is greatly simplified production technology, and
Widely applicable, itself and the reasonable coordination of fabric, the design philosophy of designer can not only be fully demonstrated, and can reach good
Good takes effect.
But it is as the fast development of macromolecular material, while its advantage certainly, have also discovered its deficiency, the most greatly
The macromolecular material of part synthetic is difficult to degrade in nature, and nondegradable macromolecular material causes environment
White pollution.And the garbage of some chemical fibres is difficult to degrade, it has also become new polluter.Currently mainly use method of reproduction,
Combustion method and edman degradation Edman solve this problem.It is and current cloth is functional the most single, antibacterial, health effect is low,
In order to make adhesive lining have antibacterial, health effect, can also degrade simultaneously, there is the feature of environmental protection, it is necessary to propose one and live containing bamboo
The woven adhesive lining of Degradable environment protection of property powdered carbon and preparation technology thereof.
[summary of the invention]
It is an object of the invention to overcome above-mentioned the deficiencies in the prior art, it is provided that a kind of degradable ring containing bamboo absorbent charcoal powder
Protecting woven adhesive lining and preparation technology thereof, it aims to solve the problem that the functional the most single of adhesion lining cloth in prior art, antibacterial, protect
Strong property effect is low, difficult degradation, the technical problem that the feature of environmental protection is poor.
For achieving the above object, the present invention proposes a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, bag
Including base fabric and rubberised layer, described base fabric is contacted with weft yarn alternatively up and down by warp thread, constitutes sine and cosine curve-like and stably laminates knot
Structure, described warp thread is formed by many core-skin composite fiber long filament twisting, and described core-skin composite fiber long filament is by PLA fiber sheath
Layer and PP core fiber layer are combined, and described weft yarn is formed by many chitin fiber long filament twisting, and described base fabric is fixed with
Bamboo absorbent charcoal powder, one side or the dual coating of described base fabric have rubberised layer.
As preferably, described PP core fiber layer is made up of several polypropylene filaments, and several polypropylene filaments are the most logical
Cross PLA fibrocortex cladding.
As preferably, the radical of described polypropylene filaments is 1~3.
As preferably, in described base fabric, warp count is 75~95 pieces/inch, and weft count is 70~85 pieces/inch.
As preferably, the particle diameter of described bamboo absorbent charcoal powder is 150~200nm.
As preferably, described warp thread constitutes twill-weave structure with weft yarn.
The preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, comprises the steps:
Step one, prepare cellosilk: using 1~3 group of PP is core component, and PLA, as skin component, is spun by composite spinning machine
Silk prepares PLA/PP core-skin composite fiber long filament;With dimethyl acetylamide as solvent, anhydrous Lithium chloride is dispersant, stirs through magnetic force
After mixing machine mix homogeneously, add the chitin granule of 35%~85% (w/v), through sealing stirring, obtain thick transparent
Colloid spinning solution, obtains chitin fiber long filament by wet spinning, standby;
Step 2, braiding base fabric: using PLA/PP core-skin composite fiber long filament is warp thread, and chitin fiber long filament is weft yarn
Passing through shed open at water-jet loom by shower weft traction to weave, it is 75~95/English that braiding obtains warp count
Very little, weft count is the base fabric of 70~85 pieces/inch;
Step 3, coating pre-treatment: by the base fabric knitted through step 2 rope form, tension-free under the conditions of carry out desizing and
Refine, removes the oil preparation in base fabric and slurry, and temperature is 85~95 DEG C, fully washes and is dried, then at height after 25~30min
Carry out dyeing process in temperature high-pressure injection staining machine, on framing shaping machine, carry out heat treatment after having dyeed, pass through simultaneously
Vacuum dehydration makes base fabric be in low-down band liquid status, then pads process in the padding liquid containing bamboo absorbent charcoal powder;
Step 4, double-dot coating: using layer based on PA PUR, retardation PES hot melt adhesive is tack coat, base fabric one side or
Two sides carries out double-dot coating, then carries out 170~185 DEG C, the time be 5~8min bake melted, and cool down molding;
Step 5, inspection are batched: after inspection, carry out batching packing by up-to-standard adhesive lining product.
As preferably, the sealing mixing time in described step one is 3~4 days.
As preferably, in described step 3, the preparation method of padding liquid is: choose certain mass ratio dressing liquid and
Bamboo absorbent charcoal powder, and add appropriate dispersant, preliminary stirring is placed on ultrasonic oscillator 3~6min, is fully mixed to nothing
After precipitation, add suitable amount of adhesive, be again placed in ultrasonic oscillator 2~4min.
As preferably, the mass ratio of described dressing liquid and bamboo absorbent charcoal powder is 1:(0.1~0.2), described dressing liquid
Being made up of organic fluorine waterproof agent, silicone softening agent, antistatic additive and distilled water, the concentration of described organic fluorine waterproof agent is 8
~12g/L, the concentration of silicone softening agent is 20~35g/L, and antistatic additive is 2~5g/L, and described dispersant is for poly-own interior
Ester, binding agent is polyvinyl alcohol.
Beneficial effects of the present invention: compared with prior art, a kind of degradable containing bamboo absorbent charcoal powder that the present invention provides
The woven adhesive lining of environmental protection and preparation technology thereof, use and have the PLA/PP core-skin composite fiber long filament of biological degradability, chitin
Fiber filament is the manufacture fiber of machine textile lining cloth, can carry out natural degradation by biological degradation method, will not to environment,
Having a higher environmental-protecting performance, PLA/PP composite fibre has good stability, hydrophilic, dyeability, elasticity, hot sticky simultaneously
Conjunction property, heat sealability and against weather, chitin fiber has antibacterial activity and hygroscopicity, has health care, is lived by set bamboo
Property powdered carbon after, make adhesive lining have purification air, eliminate abnormal flavour, moisture absorption mildew-resistant, the effect of antibacterial deinsectization, use PA PUR be
Basal layer, retardation PES hot melt adhesive is tack coat, makes adhesive lining have preferable feel and resistance to dry-cleaning washing property by dual dot coating
Energy.
Inventive feature and advantage will combine accompanying drawing by embodiment and be described in detail.
[accompanying drawing explanation]
Fig. 1 is the schematic cross-section of the embodiment of the present invention woven adhesive lining of a kind of Degradable environment protection containing bamboo absorbent charcoal powder;
Fig. 2 is the structural representation of the base fabric of the embodiment of the present invention;
Fig. 3 is the organizational structure schematic diagram of the base fabric of the embodiment of the present invention;
Fig. 4 is the structural representation of the core-skin composite fiber long filament of the embodiment of the present invention.
In figure: 1-base fabric, 11-warp thread, 12-weft yarn, 13-core-skin composite fiber long filament, 130-PLA fibrocortex, 131-
PP core fiber layer, 2-rubberised layer, 3-bamboo absorbent charcoal powder.
[detailed description of the invention]
For making the object, technical solutions and advantages of the present invention of greater clarity, below by accompanying drawing and embodiment, right
The present invention is further elaborated.However, it should be understood that specific embodiment described herein is only in order to explain this
Bright, it is not limited to the scope of the present invention.Additionally, in the following description, eliminate the description to known features and technology, with
Avoid unnecessarily obscuring idea of the invention.
Refering to Fig. 1 to Fig. 4, the embodiment of the present invention provides a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder,
Including base fabric 1 and rubberised layer 2, described base fabric 1 is contacted with weft yarn 12 alternatively up and down by warp thread 11, constitutes sine and cosine curve-like steady
Determining laminated structure, described warp thread 11 is formed by many core-skin composite fiber long filament 13 twisting, and described core-skin composite fiber is long
Silk 13 is combined by PLA fibrocortex 130 and PP core fiber layer 131, and described weft yarn 12 is twisted by many chitin fiber long filaments
Forming, described base fabric 1 is fixed with bamboo absorbent charcoal powder 3, one side or the dual coating of described base fabric 1 have rubberised layer 2.
Wherein, described PP core fiber layer 131 is made up of several polypropylene filaments, and several polypropylene filaments are all passed through
PLA fibrocortex 130 is coated with, and the radical of described polypropylene filaments is 1~3, and in described base fabric 1, warp thread 11 density is
75~95 pieces/inch, weft yarn 12 density is 70~85 pieces/inch, and the particle diameter of described bamboo absorbent charcoal powder 3 is 150~200nm,
Described warp thread 11 constitutes twill-weave structure with weft yarn 12.
In embodiments of the present invention, the radical of polypropylene filaments is 3.
The present embodiment also provides for the preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, including such as
Lower step:
Step one, prepare cellosilk: using 1~3 group of PP is core component, and PLA, as skin component, is spun by composite spinning machine
Silk prepares PLA/PP core-skin composite fiber long filament 13;With dimethyl acetylamide as solvent, anhydrous Lithium chloride is dispersant, through magnetic force
After blender mix homogeneously, add the chitin granule of 35%~85% (w/v), through sealing stirring, obtain thick saturating
Gelatin matter spinning solution, obtains chitin fiber long filament by wet spinning, standby.
Wherein, sealing mixing time is 3~4 days.
Step 2, braiding base fabric: using PLA/PP core-skin composite fiber long filament 13 is warp thread 11, and chitin fiber long filament is
Weft yarn 12 passes through shed open at water-jet loom by shower weft traction and weaves, braiding obtain warp thread 11 density be 75~
95 pieces/inch, weft yarn 12 density is the base fabric 1 of 70~85 pieces/inch.
Step 3, coating pre-treatment: by the base fabric 1 knitted through step 2 rope form, tension-free under the conditions of carry out desizing
And refine, remove the oil preparation in base fabric 1 and slurry, temperature is 85~95 DEG C, fully washes and is dried, then after 25~30min
HTHP Jet Dyeing Machine carries out dyeing process, on framing shaping machine, carries out heat treatment after having dyeed, simultaneously
Make base fabric 1 be in low-down band liquid status by vacuum dehydration, then pad process in the padding liquid containing bamboo absorbent charcoal powder.
Wherein, the preparation method of padding liquid is: chooses dressing liquid and the bamboo absorbent charcoal powder of certain mass ratio, and adds suitable
The dispersant of amount, preliminary stirring is placed on ultrasonic oscillator 3~6min, after being fully mixed to without precipitation, adds appropriate bonding
Agent, is again placed in ultrasonic oscillator 2~4min.
Further, the mass ratio of dressing liquid and bamboo absorbent charcoal powder is 1:(0.1~0.2), described dressing liquid is by organic
Fluoro water proofing agent, silicone softening agent, antistatic additive and distilled water composition, the concentration of described organic fluorine waterproof agent is 8~12g/
L, the concentration of silicone softening agent is 20~35g/L, and antistatic additive is 2~5g/L, and described dispersant is polycaprolactone, bonding
Agent is polyvinyl alcohol.
Step 4, double-dot coating: using layer based on PA PUR, retardation PES hot melt adhesive is tack coat, in the one side of base fabric 1
Or two sides carries out double-dot coating, then carry out 170~185 DEG C, the time be 5~8min bake melted, and cool down molding.
Step 5, inspection are batched: after inspection, carry out batching packing by up-to-standard adhesive lining product.
The present invention woven adhesive lining of a kind of Degradable environment protection containing bamboo absorbent charcoal powder and preparation technology thereof, use and have biology
The PLA/PP core-skin composite fiber long filament of degradability, chitin fiber long filament are the manufacture fiber of machine textile lining cloth, can be by biology
Edman degradation Edman carries out natural degradation, environment will not be had higher environmental-protecting performance, simultaneously PLA/PP composite fibre tool
Having good stability, hydrophilic, dyeability, elasticity, Thermoadhesive, heat sealability and against weather, chitin fiber has anti-
Bacterium activity and hygroscopicity, have health care, after set bamboo absorbent charcoal powder, make adhesive lining have purification air, eliminate abnormal flavour,
Moisture absorption mildew-resistant, the effect of antibacterial deinsectization, use layer based on PA PUR, and retardation PES hot melt adhesive is tack coat, by dual dot coating
Adhesive lining is made to have preferable feel and the washing performance of resistance to dry-cleaning.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Any amendment, equivalent or the improvement etc. made within god and principle, should be included within the scope of the present invention.
Claims (10)
1. the woven adhesive lining of Degradable environment protection containing bamboo absorbent charcoal powder, including base fabric (1) and rubberised layer (2), its feature exists
In: described base fabric (1) is contacted with weft yarn (12) alternatively up and down by warp thread (11), constitutes sine and cosine curve-like and stably laminates knot
Structure, described warp thread (11) is formed by many core-skin composite fiber long filament (13) twisting, described core-skin composite fiber long filament
(13) being combined by PLA fibrocortex (130) and PP core fiber layer (131), described weft yarn (12) is long by many chitin fibers
Silk twisting forms, and described base fabric (1) is fixed with bamboo absorbent charcoal powder (3), and one side or the dual coating of described base fabric (1) have
Rubberised layer (2).
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: described
PP core fiber layer (131) be made up of several polypropylene filaments, several polypropylene filaments are all by PLA fibrocortex
(130) cladding.
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: described
The radical of polypropylene filaments be 1~3.
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: described
Upper warp thread (11) density of base fabric (1) be 75~95 pieces/inch, weft yarn (12) density is 70~85 pieces/inch.
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: described
The particle diameter of bamboo absorbent charcoal powder (3) be 150~200nm.
A kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: described
Warp thread (11) and weft yarn (12) constitute twill-weave structure.
7. the preparation technology of the woven adhesive lining of Degradable environment protection containing bamboo absorbent charcoal powder, it is characterised in that: include walking as follows
Rapid:
Step one, prepare cellosilk: using 1~3 group of PP is core component, and PLA is as skin component, by composite spinning machine spinning system
Obtain PLA/PP core-skin composite fiber long filament (13);With dimethyl acetylamide as solvent, anhydrous Lithium chloride is dispersant, stirs through magnetic force
After mixing machine mix homogeneously, add the chitin granule of 35%~85% (w/v), through sealing stirring, obtain thick transparent
Colloid spinning solution, obtains chitin fiber long filament (14) by wet spinning, standby;
Step 2, braiding base fabric: using PLA/PP core-skin composite fiber long filament (13) is warp thread (11), and chitin fiber long filament is
Weft yarn (12) passes through shed open at water-jet loom by shower weft traction and weaves, and braiding obtains warp thread (11) density and is
75~95 pieces/inch, weft yarn (12) density is the base fabric (1) of 70~85 pieces/inch;
Step 3, coating pre-treatment: by the base fabric (1) knitted through step 2 rope form, tension-free under the conditions of carry out desizing and
Refine, removes the oil preparation in base fabric (1) and slurry, and temperature is 85~95 DEG C, fully washes and is dried, then after 25~30min
HTHP Jet Dyeing Machine carries out dyeing process, on framing shaping machine, carries out heat treatment after having dyeed, simultaneously
Make base fabric (1) be in low-down band liquid status by vacuum dehydration, then pad place in the padding liquid containing bamboo absorbent charcoal powder
Reason;
Step 4, double-dot coating: using layer based on PA PUR, retardation PES hot melt adhesive is tack coat, base fabric (1) one side or
Two sides carries out double-dot coating, then carries out 170~185 DEG C, the time be 5~8min bake melted, and cool down molding;
Step 5, inspection are batched: after inspection, carry out batching packing by up-to-standard adhesive lining product.
The preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is special
Levy and be: the sealing mixing time in described step one is 3~4 days.
The preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is special
Levy and be: in described step 3, the preparation method of padding liquid is: choose dressing liquid and the bamboo absorbent charcoal powder of certain mass ratio,
And adding appropriate dispersant, preliminary stirring is placed on ultrasonic oscillator 3~6min, after being fully mixed to without precipitation, adds
Suitable amount of adhesive, is again placed in ultrasonic oscillator 2~4min.
The preparation technology of a kind of woven adhesive lining of the Degradable environment protection containing bamboo absorbent charcoal powder, it is special
Levy and be: the mass ratio of described dressing liquid and bamboo absorbent charcoal powder is 1:(0.1~0.2), described dressing liquid is prevented by Organic fluoride
Water preparation, silicone softening agent, antistatic additive and distilled water composition, the concentration of described organic fluorine waterproof agent is 8~12g/L, has
The concentration of machine silicone softener is 20~35g/L, and antistatic additive is 2~5g/L, and described dispersant is polycaprolactone, and binding agent is
Polyvinyl alcohol.